• Journal of the Korean Magnetics Society
• /
• v.5 no.4
• /
• pp.251-260
• /
• 1995

It has been reported that Co-based amorphous ferromagnetic alloys annealed in a small magnetic field develop a reproducible, asymmetric hysteresis loop. If the direction of the field during annealing is regarded as +, the magnetization reversal from - to + is smooth and reversible, with its slope determined by the demagnetizing field of the sample. This phenomenon is called the asymmetric magnetization reversal (AMR). The shape of the hyster-esis loop depends sensitively on the condition during the anneal and the alloy composition. Here, we report on the effect of the annealing temperature and time on AMR in a zero magnetostrictive ferromagnetic amorphous alloy. The AMR effect develops in a very short time at a reasonably high temperature, but is stabilized by annealing for a prolonged time.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2003.11a
• /
• pp.61-61
• /
• 2003

다결정 실리콘 박막은 박막 트랜지스터와 실리콘 태양전지등에 응용되며, 비정질 실리콘을 재결정화 하여 얻어지는 다결정 실리콘 박막이 주로 이용되고 있다. 비정질 실리콘 박막을 금속 원소와 접촉시킨 상태에서 열처리할 경우 결정화 온도가 낮아지고 결정화에 필요한 열처리 시간이 짧아지게 된다. 금속을 실리콘 박막 표면에 가하는 방법은 진공증착법등으로 비정질 실리콘 박막 위에 금속원소 층을 형성하는 방법이 주로 이용되었다. 본 연구에서는 AlCl$_3$와 NiCl$_2$ 금속화합물 분위기에서 LPCVD 비정질 실리콘 박막을 열처리하여 결정화 거동을 관찰하였다. 금속화합물과 결정화할 비정질 실리콘 박막을 각각 다른 온도로 가열해 줄 수 있는 노를 이용하여 열처리를 시행하였다. AlCl$_3$와 NiCl$_2$ 분말을 혼합하여 소스로 이용한 경우 48$0^{\circ}C$ 5시간 열처리로 결정화가 완료되었으며, 박막 전체에 걸친 균일도와 재현성이 우수하였다. AlCl$_3$와 NiCl$_2$를 이용한 결정화 초기 상태에는 박막 전면에 걸쳐 등근 형태의 결정립이 균일한 핵 생성으로 나타났다. 이와 같은 결과는 Al과 Ni이 고상결정화에 동시에 작용하면서 나타난 것으로, Al이 가해진 비정질 실리콘으로 인해 결정화 속도가 빨라지고 결함이 작은 결정립을 얻을 수 있었으며, Ni로 인해 결정화의 균일성과 재현성을 높일 수 있었다.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2013.08a
• /
• pp.234-234
• /
• 2013

VOx 박막은 마이크로볼로미터 적외선 센서의 감지재료로 주로 사용된다. 일반적으로 VOx 박막은 RF sputtering 방법으로 증착이 되며, 이 때 저항 값은 수 kohm~수 Mohm, TCR 값은 -1.5~-2.0%/K까지 다양하게 변화되어 나타난다. 이는 산소의 phase가 여러가지로 변화되기 때문에 재현성이 떨어지는 단점이 있으며, 결정성있는 박막을 증착하기 어려운 문제들이 있다. 본 연구에서는 VOx 박막의 재현성 및 재료의 안정성을 위해 ZnO 물질을 첨가하여 sandwich 구조의 나노박막을 증착하여 산소 열처리를 통해 산소의 phase가 어떻게 변화되는가를 XRD 측정을 통해 조사하였다. ZnO 나노박막을 첨가함으로써 갓 증착되었을 때의 XRD는 V2O5 주된 상을 이루고 있었으며, 산소열처리에 의해 VO2상이 나타남을 알 수 있었다. 또한 V2O5 phase가 표면쪽의 얇은 층에서 주로 나타나고, 중간층은 V2O5와 VO2 phase 가 혼합된 형태로 존재함을 X-ray diffraction 분석을 통해 알 수 있었다. 또한 GIXRD 측정을 통해 깊이에 따른 혼합 phase가 주로 VO2에 의해 형성된 것임을 확인할 수 있었다. 또한 산소열처리의 온도 및 시간에 따라 XRD 특성을 조사하였으며, 최적의 열처리 조건을 XRD 피크를 통해 찾고자 하였다.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2012.08a
• /
• pp.258-258
• /
• 2012

플렉시블 디스플레이를 위해 저온 공정은 필수적이며, 이를 위해 플라스틱 기판을 이용한 연구가 한창 진행 중이다. 이번 연구에서는 도핑처리 하지않고 알루미늄을 이용한 self-aligned 소오스-드레인 구조의 비휘발성 메모리를 ELA 폴리실리콘 기판 상에 제작하였다. 소오스-드레인 부분은 lift-off 공정을 이용하여 pattern 작업을 진행하였다. $250^{\circ}C$에서 1시간의 후속 열처리 공정을 진행한 self-aligned 소오스-드레인 구조의 비휘발성 메모리는 후속 열처리 공정을 진행하지 않았을 때와 비교하여 다음과 같은 메모리의 특성향상을 나타내었다. 메모리 윈도우 특성의 경우 1.15 V에서 3.47 V의 커다란 증가를 보였으며 retention 특성의 경우 12%에서 46%로 증가하였다. 이를 통해 비록 도핑 되지 않은 비휘발성 메모리 소자일지라도 self-aligned 구조와 저온 열처리를 이용할 시 향후 플렉시블 전자소자에의 적용이 가능함을 확인하였다.

• Journal of Conservation Science
• /
• v.28 no.1
• /
• pp.29-37
• /
• 2012

This study discusses a mercury amalgam gilding technique and examines how the color, surface and section of the gilt layer changes as the condition of heat treatment with mercury amalgam gilt object is changed. Some previous studies have mentioned reasons for various colors on gilt bronze artifacts depending on gilding manufacture and environment. However, reason for reddish color with gold on the artifacts' surface brought on high temperature corrosion has yet to be discussed and analyzed. A methodology was found in representing the mercury amalgam gilding technique and heat treatment test. According to the result of the heat treatment test, in the conditions of higher temperature and longer time, the oxidized layer on the gilt layer was distributed more widely and in the part when the oxide layer was eliminated, the gilt layer with a reddish color was observed. Moreover, in the surface observation of the specimen on which yellow and reddish colors were agitated, the changing aspects of its surface condition differed by colors. When investigated the section, it was observed that the void density and size became larger. After a test, the surface components changed; the temperature of heat treatment increased, component ratio of Hg and Au decreased gradually but component ratio of Cu increased. In regard to the gilt layer, as the time was longer and the temperature became higher for the heat treatment, the component ratio of Au and Cu by layers tended to change in inverse proportion. It is concluded that gilding techniques and the burial environment can make a difference in the surface color of the gilt layer on the gilt bronze artifacts, the high temperature corrosion that occurs by heat after they are manufactured is also one of the factors that affects their surface color.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2016.02a
• /
• pp.244.2-244.2
• /
• 2016

폴리 실리콘 박막은 저온 안정성, 산화 안정성, 가스 투과성 및 전기재료로서의 우수한 물성 때문에 산업에서 계속적으로 넓게 쓰이고 있다. 특히 최근 높은 색 재현율과 고화질로 각광을 받고 있는 능동형 유기발광 다이오드 (AMOLED)를 위한 Thin Film Transistor (TFT)는 신뢰성 및 우수한 특성이 요구되기 때문에 반드시 폴리실리콘 TFT가 적용되어야 한다. 이러한 이유 때문에 아모포스 실리콘을 폴리실리콘으로 결정화 시키는 방법들이 많이 연구 되어져왔다. 이 연구에서는 아모포스 실리콘 박막을 고품질의 폴리실리콘 박막으로 제조하기 위해, 기판에 positive DC 전압을 펄스 형태로 인가함으로써, 기판에 입사되는 전자를 이용한 열처리 방법을 사용하였다. 열처리 온도는 기판에 들어오는 current값을 조절함으로써 제어할 수 있었다. 열처리를 위해 사용 된 수소화 된 아모포스 실리콘은 Low Pressure Chemical Vapor Deposition (LPCVD)장비로 530도에서 증착 되었으며, 이러한 아모포스 실리콘 박막은 공정시간 60 s 이내에 샘플 표면온도가 600도 이상으로 증가함으로써 균일한 폴리실리콘 막으로 제조 되었다.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2011.06a
• /
• pp.153-154
• /
• 2011

• Journal of the Korean Institute of Telematics and Electronics
• /
• v.14 no.1
• /
• pp.5-14
• /
• 1977

"Electrical Properties of Barium Titanates with Addition Sb2O3." PTC BaTiO3 in low resistance at room temperature was prepatred. Al2O3, SiO2 and TiO2 were doped with a view to improving reproduction. Sb2O3 was doped as impurity in order to control of resistivity of the specimens. The relations between the amount of Sb3O3 and electrical properties wereinvestigated. Of the compositions studied, additions of 3.75mole% Al2O3, 1.25mole% SiO2, 2.25mole% TiO2 and 0.16~0.25wt% Sb2O3 to BaTiC3 was low resistivity in 14-300 ohm-cm.00 ohm-cm.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2013.08a
• /
• pp.236-236
• /
• 2013

비냉각 적외선 검출기는 산업용 군사용으로 최근 각광을 받고 있다. 이는 주야간 빛이 없는 곳에서도 사물의 열을 감지할 수 있어 인체감지 및 보안감시, 에너지 절감 등에 응용될 수 있는 핵심부품이다. 비냉각 적외선 검출기로는 재료의 저항의 변화를 감지하는 마이크로볼로미터형이 가장 많이 사용된다. 감지재료로는 비정질 실리콘(a-Si)과 산화바나듐(VOx)이 가장 많이 사용된다. VOx 박막은 일반적으로 RF sputtering 방법으로 증착이 되며, 저항이 낮고, 저항의 온도변화 계수(TCR)가 크며 신호 대 잡음 특성이 우수한 반면 산소(oxygen) phase가 다양하여 갓 증착된 상태의 박막은 재현성이 떨어지는 단점이 있다. 본 연구에서는 기존의 V 타겟을 사용한 VOx 박막을 증착하는 방법을 개선하여 ZnO 나노박막을 중간에 삽입하여 저항 특성을 조절할 뿐만 아니라 열처리에 의해 TCR 값을 향상시키고, VO2 phase 가 주로 나타나는 박막 증착 및 공정 방법을 소개한다. RF sputtering 장비를 이용하여 산소와 아르곤 가스의 혼합비를 4.5로 하였으며, VOx 증착 시 플라즈마 Power는 150 W 로 하여 상온에서 증착하였다. 갓 증착된 VOx 다층박막의 XRD 스펙트럼은 V2O5 피크가 주된 상을 이루고 있었으며, 산소열처리에 의해 VO2 상이 주로 나타남을 알 수 있었다. TCR 값은 갓 증착된 샘플에서 -0.13%/K의 값을 얻었으며, $300^{\circ}C$에서 50분간 열처리 후 -3.37%/K 으로 급격히 향상됨을 알 수 있었다. 저항은 열처리 후 약 100 kohm으로 낮아져 검출소자를 위한 조건에 적합한 특성을 얻을 수 있었다. 또한 산소열처리의 온도 및 시간에 따라 TCR 및 표면 거칠기 특성을 조사하였으며, 최적의 열처리 조건을 얻고자 하였다.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2008.06a
• /
• pp.200-201
• /
• 2008

태양전지 제작 시 반사방지막(Anti-reflection Coating)이 태양전지 효율에 미치는 영향을 알아보기 위한 실험으로 최적의 가스비를 알아보기 위하여 Plasma Enhanced Chemical Vapor Deposition(PECVD)를 이용한 Silicon nitride 증착 실험이다. SiH4 가스를 45 sccm으로 고정시킨 상태에서 NH3를 25,45,60,90,135 sccm으로 가변하여 Carrier Lifetime과 Refractive index를 측정하였다. PECVD의 조건은 기판온도 $450^{\circ}C$, Chamber 압력 1 Torr, 증착두께 $1000\AA$으로 고정하였다. 증착 후 500, 600, 700, $800^{\circ}C$로 열처리를 하고나서 Carrier Lifetime을 측정하여 열처리에 대한 효과도 알아보았다.