• Journal of the Korea institute for structural maintenance and inspection
• /
• v.25 no.1
• /
• pp.85-92
• /
• 2021

The purpose of this study is to investigate the properties of hardener-free epoxy-modified mortars(EMMs) using ground granulated blast furnace slag(GGBFS) and alkali activators. The hardener-free EMMs with a GGBFS content of 20% using 4 types of alkali activators were prepared with various polymer-binder ratios, and tested for strengths, water absorption, carbonation depth, chloride ion and H2SO4 penetration depth. The conclusions obtained from the test results are summarized as follows: The compressive strength of the EMMs with a GGBFS content of 20% attains a maximum at a polymer-binder ratio of 10%. The flexural strength of the hardener-free EMMs using Ca(OH)2 as a alkali activator is improved with increasing polymer-binder ratios. However, the flexural strength of the EMMs using NaCO3, Na2SO4 and Li2CO3 is gradually decreased with increasing polymer-binder ratios. Regardless of the type of alkali activator, the water absorption, chloride ion penetration and carbonation depth are remarkably decreased with increasing polymer-binder ratios due to the epoxy film formed in the EMMs. The H2SO4 penetration depth of the hardener-free EMMs with a GGBFS content of 20% is gradually increased with increasing polymer-binder ratio. In this study, the properties of hardener-free EMMs using Ca(OH)2 as a alkali activator are more excellent than those of other alkali activators.

• Journal of the Korea Concrete Institute
• /
• v.16 no.6 s.84
• /
• pp.805-811
• /
• 2004

In this paper, effects of mixture proportion and material condition on both fundamental properties, drying and autogenous shrinkage of high performance concrete are discussed. According to the results, for the effect of mixture proportion on the fundamental properties, decrease in W/B and unit water content results in reduction of fluidity, while air content has no variation. Compressive strength exhibits an decreasing tendency with an increase in W/B and unit water content do not remarkable affect the compressive strength. For the effect of materials on the fluidity, the fluidity of low heat portland cement(LPC) is smaller than that of ordinary portland cement(OPC). The use of Polycarbonic acid based superplasticizer(PS) has more favorable effect on enhancing fluidity than Naphtalene based superplasticlzer(NS) and Melamine based superplasticizer(MS). Air content of concrete using LPC is larger than that using OPC. The effects of superplasticizer type on the air content is larger in order of MS, PS and NS. The use of LPC exhibited lower strength development at early age than OPC, whereas after 91days, similar level of compressive strength is achieved regardless of cement type. Compressive strength of concrete is not affected by SP type. For the effect of mixture proportion and materials on drying and autogenous shrinkage, an increase in W/B results in reduction of drying shrinkage and an decrease in water content leads to reduce drying shrinkage. Autogenous shrinkage is not observed until 49 days with the concrete mixture with $35\%$ of W/B and $145 kg/m^3$ of water content. This is due to the combination effects of expansion admixture and shrinkage reducing admixture, which causes an offset of autogenous shrinkage. The use of LPC results in a reduction in autogenous shrinkage compared with OPC. SP type has little influence on the autogenous shrinkage. It is found from the results that mixture proportioning of high performance concrete incorporating fly ash, silica fume, expansion admixture and shrinkage reducing admixture is need to focus on the increase in W/B and the reduction in water content and the use of LPC and MS is also required to use to secure the stability against shrinkage properties.

• Journal of the Korean GEO-environmental Society
• /
• v.17 no.4
• /
• pp.33-37
• /
• 2016

The hydration process of Controlled Low Strength Material (CLSM) used for backfill is the primary factor to determine the construction period. The objective of this study is to monitor the hydration process of CLSM using the Time Domain Reflectometry (TDR) and to establish the relationship between dielectric constant and compressive strength. The CLSM specimen is composed of cement, flyash, silt, sand, accelerator, and water. The material characteristics of the CLSM including flow, unit weight, compressive strength are investigated. To measure the dielectric constant of the CLSM during the curing time, TDR probe incorporated with a mold and a reflectometer are used. Experimental results show that the dielectric constant remains constant at early stage, and then decreases as the curing time increases. In addition, the dielectric constant is related to the compressive strength in inverse power function. This paper suggests that the TDR technique may be used as a non-destructive testing method in order to estimate the compressive strength of the CLSM mixture under construction.

• Polymer(Korea)
• /
• v.29 no.2
• /
• pp.190-197
• /
• 2005

Nanocomposites of three different polyesters with dodecyltriphenylphosphonium-montmorillonite $(C_{12}PPh-MMT)$ as an organoclay are compared with their thermal properties, mechanical properties, and morphologies. Poly (butylene terephthalate) (PBT), poly(ethylene terephthalate) (PET), and poly(trimethylene terephthalate) (PTT) were used as matrix polymers in the fabrication of polyester nanocomposite fibers. The variations of their properties with organoclay content in the polymer matrix and draw ratio (DR) are discussed. Transmission electron microscopy (TEM) micrographs show that some of the clay layers are dispersed homogeneously within the polymer matrix on the nano-scale, although some clay particles are agglomerated. We also found that the addition of only a small amount of organoclay is enough to improve the thermal stabilities and mechanical properties of the polyester nanocomposite fibers. Even polymers with low organoclay contents $(<5\;wt\%)$ were found to exhibit much higher strength and modulus values than pure polyester fibers. In the cases of all polyester hybrid fibers, the values of the tensile mechanical properties were found to decrease linearly with increasing DR. However, the initial tensile modulus of the PTT hybrid fibers were found to be independent of DR.

• Korean Journal of Fisheries and Aquatic Sciences
• /
• v.30 no.4
• /
• pp.652-659
• /
• 1997

For the effective utilization of the fish bone waste from seafood industry, the physical properties of the isolated hydroxyapatite from tuna bon have been investigated. On X-ray measurements, the chemical formula and phase of the bone calcined by various temperature were detected as $Ca_{10}\;(PO_4)_6\;(OH)_2$, and hydroxyapatite, respectively. It was shown that the chemical properties of apatite separated from tuna bone were controlled by Ca/P ratio. The mean agglomerate particle diameter was changed as a function of temperature. However, the particle shape has a geometrically non-regular types. These trends are consistent with SEM images. The composition of the glass-ceramic batch by calcined tuna bone was not perfectly agreed with the suggested data, but the partially substituted composition possibly shows the application of it as a bioceramic material.

• Journal of the Korea Concrete Institute
• /
• v.17 no.5 s.89
• /
• pp.769-774
• /
• 2005

Fluosilicic acid(H2SiF6) is recovered as an aqueous solution which absorbs $SiF_4$ produced from the manufacturing of industrial-graded H3PO4 or HF. Generally, fluosilicates are the salts produced by the reaction of H2SiF6 and metal salts. Addition of fluosilicates to cement endows odd properties through unique chemical reaction with the fresh and hardened cement. This study was performed to know mechanical properties and watertightness using fluosilicates based composite made from fluosilicates and other compounds. Mix proportions for experiments were modulated at 0.45 of water to cement ratio and $0.0-2.0\%$ of adding ratio of fluosilicates based composite. Evaluation for mechanical properties of concrete was conducted to know fresh state of concrete, hardening state of concrete, and watertightness. Evaluation for watertightness of concrete was carried out permeability, absorption test and porosity analysis. In addition. Scanning Electron Microscopy(SEM) and Energy Dispersive X-Ray(EDX) used for investigating micro-structure and atomic component distributed in hardened concrete. It is ascertained that characteristics of mechanical properties and watertightness was more improved than non-added because of packing role of fluosilicates based composite and pozzolanic reaction of soluble $SiO_2$. Also, concrete added fluosilicates based composite had a tendency to delay setting time and only $0.5\%$ addition of fluosilicates based composite delayed 150 minutes compared with non-added.

• Journal of the Korean Society of Clothing and Textiles
• /
• v.30 no.12 s.159
• /
• pp.1730-1736
• /
• 2006

To utilize hanji for fashion accessory efficiently, dyeability of Hanji should be improved. Though Hanji mostly consists of cellulose such as cotton and ramie, also has various impurities, and has the different internal and surface structure from textile materials. Because of them, Hanji might show different dyeing behavior. As physical properties of Hanji are reduced in wet condition, dyeing process would damage the physical properties of Hanji Therefore, in this study, dyeing properties of Hanji using direct dye were examined in comparison with cotton and ramie. Effect of dyeing on tensile strength, and bleeding of direct dye by water from Hanji, colorfastness to light were also estimated. While Hanji showed the maximun dye exhaustion at $25^{\circ}C$, cotton and ramie showed those at $60^{\circ}C$. Tensile strength of Hanji reduced after Hanji was dyed. When Hanji was dyed at $25^{\circ}C$, the more bleeding occurred than at higher dyeing temperature. Hanji which had higher K/S values were bled more than those had lower K/S value. Colorfastness to light of Hanji dyed with direct dye was not inferior to those of cotton and ramie.

• Journal of Conservation Science
• /
• v.25 no.4
• /
• pp.439-450
• /
• 2009

The purpose of this study is to find out characteristics of the fillers made by epoxy resin (L-30) and filling epoxy resin (L-50) with talc, quartz sand and wollastonite with different mixture ratio of 5%, 50%, 80%, 120%, and 150%. The viscometer and colorimeter were used to measure the viscosity and chromaticity of the fillers. Additionally, IC and SEM were used to reveal characteristics of the filler, and checked ultrasonic wave velocity, compressive strength and contact angle to estimate the stability between the filler and stones which are essential for conservation treatments. The filler mixed with the talc had the lowest value in the ultrasonic wave velocity analysis, and its compressive strength decreased as the mixing rate of talc increased. On the other hand, wollastonite had higher values than others in the ultrasonic wave velocity and the compressive strength regardless of epoxy resin type, also, these values increased as mixing rate increased. The properties of the filler, which include the granularity and shape, have influence on characteristics of the stone conservation adhesives. Thus, the filler type, characteristic, and mixture ratio must be considered for effective conservation treatment.

• The korean journal of orthodontics
• /
• v.31 no.4 s.87
• /
• pp.459-465
• /
• 2001

The purpose of this study was to evaluate the feasibility of the combined use of paste resin with sealant as an adhesive of the indirect bonding. The resin bases made of light-cured resin were bonded to the bovine incisors at a distance of 0.0, 0.2 or 0.4 mm using the sealant only or the mixture of sealant and paste resin. Bond strength of each group was measured using universal testing machine. The results were as follows : 1. The bond strength was reduced in both groups as the distance between enamel surface and resin base increased. 2. The bond strength showed no statistical difference between two groups in case the distance between enamel surface and resin base was 0.0 mm. 3. In case the distance between enamel surface and resin base was 0.2 or 0.4 mm, the sealant with paste resin group showed significantly higher bond strength than the sealant only group. The results of the present study indicate that the use of paste resin with sealant may be desirable as an adhesive in indirect bonding, particularly in case a gap is suspected between enamel surface and resin base.

• 전기의세계
• /
• v.24 no.4
• /
• pp.6-10
• /
• 1975

반도체와 그의 응용소자는 지난 20여년간 눈부식 발전을 이룩하였다. 이는 주로 단결정의 제작기술 진보에 의한 것으로 본다. 그러나 최근 단결정과는 전연 다른 유리질반도체가 국제회의에서도 그 우수성을 의논하기에 이르렀다. 유리질 반도체가 주목을 끌게 된겻은 1968년 Ovshinsky가 "무질서 구조에 있어서 가역적 스위칭현상"이라는 논문이 발표되고 유리질 반도체를 사용한 Ovonic 스위칭 소자의 출현에 기인된다. 유리질 반도체가 전기스위칭 작용, 기억작용을 나타낸다고 하는 Ovshinsky의 발표는 전자제치로서의 응용에 대해 찬반되는 의견이 있었지만 물성적 연구의 교량적인 역할을했다고 할 수 있다. 이런 반도체에 속하는 재료는 호칭도 여러가지로 유리질반도체, 비정질반도체 무정형반도체등으로 불리어진다. 단결정체가 각 격자간에 장거리질서를 갖는 반면 유리질 반도체는 무질서한 구조로 각 격자간에 단거리 질서를 갖는 것이 단결정과는 본질적으로 다른 점이라 본다. 유리 반도체의 종류는 첫째, 원소성 유리반도체로서 Ge, Si, Se, Te 들과 같이 단일원소로 된 겻과, 둘째 IV, V, VI족 원소로 된 공유결합 합금인 As$_{2}$Se$_{3}$-As$_{2}$Te$_{3}$ 계 Ge Si As Te계등의 칼코게나이드 유리등으로 금지대는 어느 것이나 2eV이하이다. 셋째 이론결합인 SiO $Al_{2}$O$_{3}$ Ta$_{2}$O$_{3}$Si$_{3}$N$_{4}$등의 산화물 및 질화물로 대표되는 분자성 비정질 물질로서 금지대는 2eV보다 큰 세종류로 크게 분류할 수 있다. 분류할 수 있다. 한다. 단 개개의 문제에 관한 구체적인 해석 또는 검토에 관하여는 다음 기회에 미루기로하고, 우선 여기서는 당면문제로서 대처하지 않으면 안될 자동주파수제어문제및 계통의 경제운용문제만에 한정하여, 이것을 우리나라의 현상과 관련시켜 개설하고, 이들의 자동화에 관한 기본적인 문제를 간단히 적어 보겠다. 가능하다. 제작완료된 ASIC은 기능시험을 완료했으며 실제 line-of-sight(LOS) 시스템 구현에 적용중이다. 시대를 살아 갈 회원들이다. '컨텐츠의 시대'가 개막되는 것이며, 신세기통신과 SK텔레콤은 선의의 경쟁 과 협력을 통해 이동인터넷 서비스의 컨텐츠를 개발해 나가게 될 것이다. 3배가 높았다. 효소 활성에 필수적인 물의 양에 따른 DIAION WA30의 라세미화 효율에 관하여 실험한 결과, 물의 양이 증가할수록 그 효율은 감소하였다. DIAION WA30을 라세미화 촉매로 사용하여 아이소옥탄 내에서 라세믹 나프록센 2,2,2-트리플로로에틸 씨오에스터의 효소적 DKR 반응을 수행해 보았다. 그 결과 DIAION WA30을 사용하지 않은 경우에 비해 반응 전환율과 생성물의 광학 순도는 급격히 향상되었다. 전통적 광학분할 반응의 최대 50%라는 전환율의 제한이 본 연구에서 찾은 DIAION WA30을 첨가함으로써 성공적으로 극복되었다. 또한 고체 염기촉매인 DIAION WA30의 사용은 라세미화 촉매의 회수 및 재사용이 가능하게 해준다.해준다.다. TN5 세포주를 0.2 L 규모 (1 L spinner flask)oJl에서 세포간의 응집현상 없이 부유배양에 적응,배양시킨 후 세포성장 시기에 따른 발현을 조사한 결과 1 MOI의 감염조건 하에서는 $0.6\times10^6$cell/mL의 early exponential시기의 세포밀도에서 72시간 배양하였을 대 최대 발현양을