• International Journal of Highway Engineering
• /
• v.10 no.4
• /
• pp.281-292
• /
• 2008

In Korea-LTPP(Long Tenn Pavement Performance) project, the full depth asphalt pavement test sections are constructed on the national highway to evaluate the structural capacity of asphalt pavement reinforced with glass fiber. Truck loading test and FWD test were performed to measure the structural capacity of test sections. Test results showed that the reinforcement of glass fiber installed at between surface and intermediate asphalt layer decreased the strain at the bottom of surface layer and moved up the stress neutral axis in asphalt layer. As a result, the tensile stress was developed at the bottom of intermediate asphalt layer of reinforced asphalt pavement, while the compressive stress was developed at the bottom of intermediate asphalt layer of unreinforced asphalt pavement. On the other hand, the tensile strain at the bottom of asphalt base layer didn't show a difference between glass fiber reinforced and unreinforced pavements. From the FWD test, it was shown that the surface deflection of asphalt pavement reinforced with glass fiber decreased 24 percents comparing to that of unreinforced asphalt pavement. This shows that the reinforcement with glass fiber appears to improve the rutting resistance of asphalt pavement.

• Journal of the Korean Society of Hazard Mitigation
• /
• v.9 no.3
• /
• pp.41-47
• /
• 2009

Post-tensioned concrete pavement(PTCP) was developed to built long-span concrete pavement(120 m span) and to maintain long-term service life(over 40 years) of concrete pavement. In the present study, research for high-durable concrete was conducted to utilize the advantage of PTCP construction method efficiently. First of all, 20% of fly ash(by binder weight) was replaced to control alkali silica reaction. Second, silica fume was applied to improve the water-permeability and early-age strength. Results of tests for mechanical properties, water-permeability resistance, and surface-scaling resistance of ternary blended cement concrete showed that the early-age strength was improved significantly with addition of silica fume. The water-permeability resistance was improved from "Low" to "Very Low"(ASTM C 1202). However, surface-scaling resistance was decreased with an increase of silica fume, therefore, content of silica fume should be kept in less than 5%(by binder weight) to assure field application considering durability. The results of air-void analysis showed that durability factors were improved since spacing factors were estimated as 250$\pm$15 micron in adjusted mixtures.

• Journal of the Korean Society of Hazard Mitigation
• /
• v.8 no.3
• /
• pp.51-58
• /
• 2008

Development of a new design guide which is based on empirical-mechanistic concept for pavement design is in action. It is called AASHTO 2002 Design Guide in USA and the KPRP(Korean Pavement Research Project) in Korea. The material characteristic of hot mix asphalt is a key role in the design guide. Therefore it is urgent to get a proper materials database, especially the dynamic modulus of hot mix asphalt. In this research, dynamic modulus test, which is based on aged asphalt binder, has been carried out and proposed the predicted equation of dynamic modulus. Nine different hot mix asphalt with three different asphalt binder have been used for the dynamic modulus test. Short-term aging, which is covers the time for the production of asphalt plant, transportation, lay-down, and compaction, can be simulated at $135^{\circ}C$ with 2 hour curing. Long-term aging has been carried out for a performance period of asphalt pavement. The dynamic modulus of asphalt pavement increases with aging time. As the nominal aggregate size increases, the change of dynamic modulus is not big.

• International Journal of Highway Engineering
• /
• v.8 no.4 s.30
• /
• pp.135-143
• /
• 2006

This study evaluated the fatigue resistance characteristics of hot-mix recycled asphalt mixtures which were prepared by a new blending method. Since the binder of RAP shows higher viscosity without being rejuvenated in the ordinary recycled mixture, this new(modified) blending method was developed for obtaining more uniform level of binder viscosity in the recycled mixture. Cold-planned RAP was collected and mix design was performed using 15% RAP content for two virgin aggregate, gneiss and granite. Penetration grade of 60-80 asphalt was used in mixing recycled mixture together with a polymer modifier, LDPE. Indirect tensile fatigue tests were carried out to evaluate characteristics of fatigue resistance of performance of recycled asphalt mixtures. The recycled mixtures with LDPE 6% showed higher repeated loading fatigue life. Fatigue life ratio of new(N) mixing method mixtures was approximately 0.6-0.7 before aging and 0.8-1.0 after aging treatment of ordinary(O) mixing method mixture. This means the N mixture becomes stronger with aging process increase. If further aging is treated, N mixture may be showing stronger resistance than O mixture.

• International Journal of Highway Engineering
• /
• v.19 no.3
• /
• pp.31-43
• /
• 2017

PURPOSES : The objective of this study is to verify the effect of fiber grid reinforcement on the long-term performance of asphalt pavement overlaid on old concrete pavement by performing field investigation, laboratory test, and finite element analysis. METHODS : The reflection cracking, roughness, and rutting of fiber grid reinforced overlay sections and ordinary overlay sections were compared. Cores were obtained from both the fiber grid reinforced and ordinary sections to measure bonding shear strength between the asphalt intermediate and asphalt overlay layers. Fracture energy, displacement after yield, shear stiffnesses of the cores were also obtained by analyzing the test results. Finite element analysis was performed using the test results to validate the effect of the fiber grid reinforcement on long-term performance of asphalt pavement overlaid on the old concrete pavement. The fatigue cracking and reflection-cracking were predicted for three cases: 1) fiber grid was not used; 2) glass fiber grid was used; 3) carbon fiber grid was used. RESULTS : The reflection-cracking ratio of fiber grid reinforced sections was much smaller than that of ordinary sections. The fiber grid reinforcement also showed reduction effect on rutting while that on roughness was not clear. The reflection-cracking was not affected by traffic volume but by slab deformation and joint movement caused by temperature variation. The bonding shear strength of the fiber grid reinforced sections was larger than that of the ordinary sections. The fracture energy, displacement after yield, and shear stiffnesses of the cores of the fiber grid reinforced sections were also larger than those of the ordinary sections. Finite element analysis results showed that fatigue cracking of glass or carbon fiber grid reinforced pavement was much smaller than that of ordinary pavement. Carbon fiber grid reinforcement showed larger effect in elongating the fatigue life of the ordinary overlay pavement compared to glass fiber grid reinforcement. The binder type of the overlay layer also affected the fatigue life. The fiber grid reinforcement resisted reflection-cracking and the carbon fiber grid showed the greater effect. CONCLUSIONS :The results of field investigation, laboratory test, and finite element analysis showed that the fiber grid reinforcement had a better effect on improving long-term performance of asphalt pavement overlaid on the old concrete pavement.