• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.35 no.5
• /
• pp.543-547
• /
• 2011

Primary water stress corrosion cracking has occurred in dissimilar weld areas in nuclear power plants. Residual stress is a driving force in the crack. Residual stress may be generated by weld or surface machining. Residual stress due to surface machining depends on the machining method, e.g., milling, grinding, or EDM. The stress is usually distributed on or near the surface of the material. We present the measured residual stress for machining on SA 508 and austenitic stainless steels such as TP304 and F316. The residual stress can be tensile or compressive depending on the machining method. The depth and the magnitude of the residual stress depend on the material and the machining method.

• Journal of Advanced Marine Engineering and Technology
• /
• v.19 no.4
• /
• pp.42-50
• /
• 1995

To study the effect of welding methods on the Stress Corrosion Cracking (SCC) behavior of welded AISI type 316L and 304 austenitic stainless steel, the Slow Strain Rate Technique(SSRT) has been adopted in the boiling 45 wt% $MgCl_2$ solution. The results are as follows. 1) Welded sections are more susceptible than base metal in SCC, and the rank of SCC, and the rasistance in welding method is TIG, MIG, $CO_2$ and ARC. 2) The Ultimate tensile strength(UTS) and the strain of both base metal and welded joint are reduced as decreasing extension rate. 3) The SCC resistance of 316L base metal and welded sections are superior than that of 304. 4) The tendency of pitting and the SCC suseptibility are agreed well, and the SCC site is welded deposit section in 316L whereas HAZ in 304.

• Journal of Korea Foundry Society
• /
• v.18 no.6
• /
• pp.586-592
• /
• 1998

2.3%C-26%Cr-1%Ni-0.5%Mo 조성의 아공정 백주철을 여러형태로 열처리를 한 후 잔류오스테나이트함량(Vr), 거시 및 미소경도 그리고 내마찰마모성사이의 상호관계를 연구하였다. 주방상태에서의 Vr가 70.2%인 반면 열처리시편들의 경우 0.3-65.4%의 분포를 나타내었다. 초기마모구간 이외에는 마찰마모량과 마모시간과의 사이에 직선적 관계가 얻어졌으며 그 직선의 기울기(Rw)를 내마모성의 비교시 지표로 사용하였다. Rw는 주방상태에서 $2.77{\times}10^{-2}\;mg/s$로 가장 낮았으며 l173k에서 18ks동안 균질화 열처리만 한 시편의 경우 $4.12{\times}10^{-2}\;mg/s$로 내마모성이 가장 열악하였다. 주방상태에서 내마모성이 가장 좋은 이유는 마찰마모시 오스테나이트가 가공경화를 일으켜 마르텐사이트로 변태되었기 때문으로 여겨진다. 미소경도는 HV 358-HV 756, 거시경도는 이 보다 높은 HV 529-HV 785의 분포를 나타내었는데 이는 거시경도의 측정시 공정탄화물인 $M_7C_3$가 포함되었기 때문이다. 가장 높은 미소 및 거시경도는 1323k에서 7.2ks동안 오스테나이화열처리한 시편에서 얻어졌으며 주방상태의 시편이 가장 낮은 경도치를 나타내었다.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 1996.04a
• /
• pp.92-96
• /
• 1996

최근 유용한 신소재로많은 광심을 보이고 있는 오스템퍼처리 구상흑연 주철(Austempered Ductile Cast Iron 이하 ADI라 한다) 은 기지조직이 베이나이트와 잔류 오스테나이트로 구성되어있기 때문에 같은 화학 조성을 갖는 일반 구상 흑연 주철에 비하여 연성 및 연성의 감소가 없이 2배 정도의 강도를 증가 시킬수 있기 때문에 자동차, 선박 부품 및 각종 기계부품에 적용시키기 위한 많은 연구가 진행되고 있다. 본 연구에서는 서로 재질의 성분이 다른 고속도강 드릴인 소경드릴을 이용하여 ADI재료를 보통(비관통)이송 및 단계이송 절삭가공시 발생되는 공구의 마멸량과 표면조도와의 관계, 절삭력의 변화에 따른 공구마멸과 공구수명과의 관계를 실험적으로 규명하여 ADI재료 의 보통 및 단계이송절삭시 공구수명에 미치는 제반 절삭특성의 영향에 관해 고찰 하고자 한다.

• Journal of the Society of Disaster Information
• /
• v.13 no.2
• /
• pp.147-154
• /
• 2017

Duplex stainless steel finds increasing use as an alternative to austenitic stainless steel, particularly where chloride or sulphide stress corrosion cracking is of primary concern, due to the excellent combination of strength and corrosion resistance. During welding, duplex stainless steel does not create the same magnitude or distribution of weld-induced residual stresses as those in welded austenitic stainless steel due to the different physical and mechanical properties between them. In this work, an experimental study on the residual stresses in butt-welded duplex stainless steel is performed utilizing the layering technique to investigate the characteristics of residual stresses in the weldment.

• Journal of Power System Engineering
• /
• v.12 no.3
• /
• pp.72-77
• /
• 2008

This study was investigated to know the effect of Cu addition on austempered ductile cast iron at various temperatures and times. Test results showed that the volume fraction of retained austenite and the carbon contents of retained austenite showed the greatest value at $400^{\circ}C$. Also, in case of specimens having more Cu contents, the volume fraction of retained austenite and the carbon contents of retained austenite showed the lower value. After austempering treatment, tensile strength and Impact value increased, but elongation decreased. With increasing austempering treatment temperature, tensile strength, elongation, and impact value decreased. In case of specimen having more Cu contents, tensile strength showed the higher value, but elongation showed the lower value. Damping capacity was decreased by austempering treatment and was not affected on austempering temperature and time. In case of specimen having more Cu contents, damping capacity showed the higher value.

• Journal of Korea Foundry Society
• /
• v.17 no.2
• /
• pp.151-157
• /
• 1997

다섯 조성의 서로 다른 Mo, Ni 및 Mn함량을 지닌 3 mass% C-20 mass% Cr 공정조성의 백주철을 질소분위기하에서, 1173, 1273 및 1373 $^{\circ}K$의 온도로 3.6, 7.2, 14.4 및 28.8 ks동안 불안정화열처리를 행한 후 공냉시켜 잔류오스테나이트를 측정한 결과 합금원소함량, 불안정화열처리조건 및 $V{\Upsilon}$사이에 다음과 같은 관계를 얻었다. 즉 Mo, Ni 및 Mn을 첨가한 결과, 주방상태에서 79.89${\sim}$91.65 vol.%범위의 $V{\Upsilon}$가 얻어 졌으며 퍼얼라이트는 전혀 생성되지 않았다. 1173 $^{\circ}K$에서 불안정화열처리를 한 경우에는 무수히 작은 이차탄화물이 석출하였으나 온도가 높아 질수록 그 수는 점차 감소하여 1373 $^{\circ}K$에서는 거의 관찰되지 않았다. 1173 및 1373 $^{\circ}K$에서 불안정화열처리를 한 경우, 불안정화열처리시간의 증가에 따른 $V{\Upsilon}$의 변화는 미미하였으나 1273 $^{\circ}K$의 경우에는 감소하였다. 또한 Mo, Ni 및 Mn의 첨가량이 많아짐에 따라 $V{\Upsilon}$는 증가하였으며 이 두 함수사이의 관계식을 정립시키기 위하여 P인자를 도입하였다.

• Journal of the Korean Society for Heat Treatment
• /
• v.13 no.4
• /
• pp.253-258
• /
• 2000

The present study aimed to develop the TRIP(transformation induced plasticity) aided high strength low carbon steel sheets using reverse transformation process. The cold-rolled 0.14C-6.5Mn steel was reverse-transformed by slow heating to intercritical temperature region and air cooling to room temperature. An excellant combination of tensile strength and elongation of $98.3kgf/mm^2$ and 44.4% appears. This combination comes from TRIP phenomena of retained austenite during deformation. The stability of retained austenite Is very Important for the good ductility and it depends on diffusion of carbon and manganese during reverse transformation. The air cooling after holding at intercritical temperature retards the formation of pearlite and provides the carbon enrichment in retained austenite, resulting the increase of elongation in cold-roiled TRIP steel.

• Proceedings of the KAIS Fall Conference
• /
• 2003.06a
• /
• pp.83-86
• /
• 2003

SKD11은 자이로 펌프의 로타와 붓싱 재질로 사용되는데, 자이로펌프는 임펠러의 회전이 없고 원판의 기울기 운동으로 흡입과 토출을 반복하는 고압용적식 펌프이다. 이 펌프의 내구성을 향상시키기 위하여 우수한 내압성과 내마모성을 갖는 재질선정이 요구한다. 따라서 현재 가장 널리 사용되고있는 SKD11에 심냉처리를 통하여 미세조직의 개선을 수행하였고, 가스질화처리에 의한 표면경화로 내압성과 내마모성을 증가시키고자 하였다. SKD11의 미세조직 변화를 조사하기 위하여 광학현미경과 X-선 회절기를 사용하여 미세조직 관찰과 상변화를 조사하였으며, Rockwell 경도기틀 사용하여 각 변수에 따른 경도변화를 조사하였다. 연구 결과 기지조직은 모두 마르텐사이트로 나타났으며, 이 이외에 각각의 조건에 따라 크롬탄화물, PFZ, 잔류오스테나이트가 확인되었다. SKD11을 액화질소로 냉각한 후 500℃에서의 템퍼링으로 가장 큰 경도값을 얻을 수 있었다. 또한 가스질화처리에 의하여 표면경도를 크게 증가시킬 수 있었다.

• Proceedings of the KWS Conference
• /
• 2010.05a
• /
• pp.84-92
• /
• 2010

현재 가동 중인 몇몇 가압 경수로 원전 안전 1등급 설비의 이종금속 용접부는 일차수응력부식균열(PWSCC : Primary Stress Corrosion Cracking) 발생의 세가지 조건(민감 재질, 부식 환경, 인장응력)을 동시에 충족하고 있다. 즉, 이종금속 용접부는 PWSCC에 민감한 재질인 Alloy 600 계열 합금으로 제작 또는 용접되어 있으며 고온 수화학 부식 환경 하에 놓여있다. 아울러 오스테나이트 스테인리스 강의 예민화 예방을 위한 용접 후열처리 미실시로 높은 인장 용접 잔류응력이 작용하고 있다. 이러한 이종금속 용접부의 특성상 PWSCC가 발생할 잠재성이 있을 뿐만 아니라 국내외적으로 Alloy 600 계열 합금으로 제작 및 용접된 가압 경수로 원전 안전 1등급 설비의 이종금속 용접부에 실제 PWSCC가 발생된 사례들이 다수 보고되고 있다. 운전 환경 및 재질 변화 없이 PWSCC 발생을 예방하기 위해서는 인장 잔류응력을 이완시켜 낮은 인장 또는 압축 응력화하여야 한다. 이러한 인장 잔류응력 이완방법들로는 PWOL(Pre-emptive Weld Overlay), 레이저 피닝(Laser Peening), MSIP(Mechanical Stress Improvement Process), 워터 제트 피닝(Water Jet Peening), IHSI(Induction Heating Stress Improvement) 방법들이 있는데 공정 시간이 짧고 열 에너지 원이 필요 없으며 전체적인 소성 변형을 야기시키지 않는 레이저 피닝을 본 연구의 대상 방법으로 한다. 본 연구에서는 동적 유한요소 해석을 통해 용접 잔류응력을 이완시키는 레이저 피닝의 효과를 검증하고 용접 잔류응력에 미치는 레이저 피닝 변수의 영향을 고찰하고자 한다. 내부 보수용접이 수행된 경수로 원전 가압기 노즐 이종금속 용접부에 레이저 피닝을 적용한 경우에 대해 상용 유한요소 해석 프로그램인 ABAQUS를 이용하여 동적 유한요소해석을 수행한 결과, 고온 수화학 일차수와 접하는 Alloy 600 계열 합금 내면에서의 인장 잔류응력이 상당히 이완됨을 확인하였다. 또한, 최대충격 압력이 증가할수록, 충격압력 지속시간이 증가할수록, 레이저 스팟 직경이 증가할수록 내표면 인장 잔류응력 이완 정도는 감소하나 이완되는 영역의 깊이는 증가함을 알 수 있다. 또한, 레이저 피닝 방향이 잔류응력 이완에 미치는 영향은 미미함을 알 수 있다.