The effects of heat treatment on the fatigue life and welding residual stress of welded plates were investigated in this study. The plates were welded by flux cored arc welding process, and post weld heat treated at $600^{\circ}C$ for 1 hour. The residual stresses of welded plates before and after post weld heat treatment were measured by hole drilling method. To measure the fatigue life of welded plates, low cycle fatigue tests under strain control and high cycle fatigue tests under load control were performed respectively, by using cylindrical specimens containing weld metal and heat affected zone. The obtained result shows that the post weld heat treatment reduces the residual stress, and resultantly changes the fatigue life of welded plate. Goodman diagrammatic analysis has also been performed to study the effect of post weld heat treatment on the high cycle fatigue life.

• 융합신호처리학회논문지
• /
• 제15권4호
• /
• pp.155-161
• /
• 2014

본 논문에서는 비교적 밀도가 높게 전개되는 무선 센서네트워크에서 센서노드들의 에너지를 균형있게 소비할 수 있는 클러스터-기반 에너지 소비 균형을 위한 라우팅 프로토콜을 제안하였다. 본 프로토콜은 계층적 구조를 가지는 클러스터-기반으로 구현된다. 클러스터는 위치적으로 가까운 거리에 있는 센서노드들로 형성되며, 해당 클러스터 멤버들 중에서 잔류 에너지가 가장 높은 노드가 헤드노드로 선정된다. 경로 선정에서, 이웃하는 클러스터와 통신의 범위가 중첩되게 하여 그 공통영역 내에 있는 하나의 노드를 중계노드로 선택하여, 통신에너지 소비의 균형을 고려하여 노드들의 수명을 연장할 수 있게 하였다.

• 대한기계학회논문집A
• /
• 제29권10호
• /
• pp.1384-1391
• /
• 2005

Damage often occurs on the surface of railway wheels due to wheel-rail contact fatigue. It should be removed before reaching wheel failure, because wheel failure can cause derailment with loss of life and property. The increase or decrease of the contact fatigue lift by the metal removal of the contact surface were investigated by many researchers, but they have not considered initial residual stress and traction force. The railway wheel has the initial residual stress formed during the manufacturing process, and the residual stress is changed by thermal stress induced by braking. The traction force and residual stress are operated on wheels of locomotive and electric motor vehicle. In this study, the effect of metal removal depth on the contact fatigue life for a railway wheel has been evaluated by applying lolling contact fatigue test. The effect of the traction force and metal removal on the contact fatigue life has been estimated by finite element analysis. It has been found that the initial residual stress determines the amount of metal removal depth if the traction coefficient is less than 0.15. If the traction coefficient is greater than 0.2, however, the amount of metal removal depth is independent on the intial residual stress.

• 한국자동차공학회논문집
• /
• 제14권3호
• /
• pp.88-94
• /
• 2006

The compressive residual stress, which is induced by shot peening process, has the effect of increasing the intrinsic fatigue strength of surface and therefore would be beneficial in reducing the probability of fatigue damage. However, the effect of shot peening in corrosion environment was not known. In this study, investigated is the effect of shot peening on corrosion fatigue crack growth of SAE 5155 steel immersed in 6% $FeCl_3$ solution and corrosion characteristics with considering fracture mechanics. The results of the experimental study corrosion fatigue characteristics of SAE 5155 are as follows; the fatigue crack growth rate of the shot peening material was lower than that of the non-peening material. And fatigue life shows more improvement in the shot peening material than in non-peening material. This is due to the compressive residual stress of surface increases resistance of corrosion fatigue crack propagation. It is assumed that the shot peening process improve corrosive resistance and mechanical property.

• 한국공작기계학회:학술대회논문집
• /
• 한국공작기계학회 2005년도 춘계학술대회 논문집
• /
• pp.185-190
• /
• 2005

The shot peening process is often used to improve fatigue properties of metal parts. Among them, It is the most use in an auto-component. In order to achieve optimum, repeatable and reliable fatigue enhancement from the shot peening process, the important shot peening parameters must be controlled. In this paper, the optimum peening intensity (Almen intensity) condition is investigated by experiment. The Spur Gear steel was used to investigate shot peening effects. The fatigue life at $\sigma_a=1,050$ and $\sigma_a=1,250MPa$ first gently increases, then drops gently as peening intensity increases compared with unpeened specimen. Experimental results show that the optimum peening intensity range is $0.391\~0.434mmA$..So the fatigue strength and fatigue life have been tremendously increased by optimum-peening treatment. However, the fatigue strength and fatigue life have been decreased by over peeing.

• 한국생산제조학회지
• /
• 제25권4호
• /
• pp.253-257
• /
• 2016

The effects of re-peening on the compressive residual stress and fatigue life of Al7075-T6 were investigated. The compressive residual stress induced on the surface of components by shot peening is known to increase the fatigue life. However, the fatigue load relaxes the compressive residual stress of components. Re-peening is a technique to again induce the relaxed compressive residual stress and increase the total fatigue life of components. In this study, the re-peening process was applied to fatigue-loaded specimens. The compressive residual stress and fatigue life were examined for re-peened specimens with fatigue ratios of 30%, 50%, and 70%. The results showed that the compressive residual stress of the specimens was relaxed under the fatigue load. The re-peening process significantly increases the compressive residual stress and total fatigue life.

• 비파괴검사학회지
• /
• 제33권2호
• /
• pp.165-172
• /
• 2013

발전설비 구조물은 기대 수명동안의 안전성을 확보하기 위하여 정해진 규격에 부합하도록 설계하여 건설된다. 하지만 가동 중 다양한 복합 환경에 노출됨에 따라 구조물을 이루고 있는 재료의 열화 현상이 가속화 되어 예상하지 못한 파손이 발생할 수 있기 때문에, 용접부와 같은 구조물의 취약부에 대하여 기계적 물성을 정확하게 측정하는 기술은 안전과 직결되는 필수적인 연구 분야이다. 인장시험 등의 기존의 역학물성 측정 시험법들은 특정 크기의 시편을 요구하고 파괴적인 시험이기 때문에 가동 중 구조물에 적용하는 것이 불가능하였다. 이러한 한계점을 극복하고자 비파괴적이고 간편한 방법으로 다양한 역학물성 평가가 가능한 연속압입시험법이 각광받는 시험법으로서 연구되고 있다. 본 연구에서는 연속압입시험에서 압입자 하부에 발생하는 응력장 해석을 기반으로 하여 인장물성 및 잔류응력을 평가할 수 있는 최신 기법을 소개한다. 또한, 원전 구조물의 취약부로 알려진 용접부에 대하여 실험을 수행하여 산업상에서 연속압입시험이 건전성 평가에 유용하게 적용할 수 있음을 확인하였다.

• 한국펄프종이공학회:학술대회논문집
• /
• 한국펄프종이공학회 2001년도 춘계학술발표논문집
• /
• pp.80-80
• /
• 2001

제지 공정의 효율적인 운영을 위한 수단으로 보류 및 탈수성의 분석은 매우 중요한 작 업 이 다. 보류 및 탈수 특성 을 평 가하기 위 하여 SR(Shopper-Riegler), CSF(Canadian S Standard Freeness tester) 그리고 원형 수초지기 등의 비난류 상태의 자연탈수 특성 평가 장치와 동적 조건의 감압식 탈수성 분석기 등이 사용되고 있다. 하지만 이것들은 제지 공정 에 보다 더 근접한 탈수 및 보류 특성을 평가하기에는 부족한 점이 있다. 특히 wet-end 첨 가제들의 효능을 보다 정확히 분석하는 것이 불가능하다. 이런 이유로 난류 발생과 감압 탈 수 둥을 유도한 탈수 특성 평가 장치 개발의 필요성이 커지고 있다. R RDA - HSF(Retention Drainage Analyzer- Handsheet Former)는 지료조성, 감압탈수 및 습지의 성형이 자동화되어 보류도와 탈수성, 종이지합 및 강도를 종합 평가 할 수 있는 새 로운 실험실용 초지기이다. 보다 현장에 가까운 초지 조건을 구현하기 위해서 지료의 농도 를 높이고 진공 탈수를 실시함에 따라 기존의 탈수성 분석기나 보류도 측정기의 단점을 보 완하게 되 었다. 본 연 구에 서 는 Canadian Standard Freeness test와 Dynamic Drainage Jar test 및 원 형 수초지기를 활용한 기존의 탈수성, 보류도 분석 결과와 RDA-HSF를 비교하여, 자연 탈수를 이용하는 기존의 탈수 및 보류 설비에 비해 현장 공정을 보다 현실적으로 재현할 수 있는 감압 탈수 초지 설비로서 RDA-HSF의 활용 가능성을 분석하였다. RDA-HSF를 활용한 실험실적 분석을 통해 현장의 상황올 유사하게 재현함에 따라 공정 운영 인자의 변화에 따른 제품의 품질 및 생산효율을 예측할 수 있게 된 바, 보다 효율적 인 공정 관리가 가능할 것으로 기대된다. 안료 입자의 경우 피인쇄체의 표면 공극을 채우고, 비히클의 경우 미세한 공극속으로 침투되어 경화됨으로써 피인쇄체가 지니고 있는 공극량을 감소시커 게 될 것이다. 그리고 피인쇄체의 각종 형태의 공극으로 침투된 잉크의 양에 반비례적으로 피인쇄체의 표변에 잉크가 잔류하게 될 것이다. 따라서 본 연구에서는 여러가지 안료를 사용하여 각각 다른 공극 특성을 지니는 도공지를 제조한 후 이들이 가지는 공극 특성과 잉크의 잔류 거동에 대해 고찰해 보고자 하였다.여 표면 유효층 일부만 오버레이시키며I 주조 및 단조가 불가능한 재료까지도 표면부에 오버레이 시킴으로 서 부품 및 설비의 제조에 있어 재료비의 절감과 제품의 수명이 획기적으로 개선될 수 있다. 그리고 최근에는 도금 빛 용사 둥과 같은 표면처리를 할 경우임의 소재 표면에 도금 및 용 사에 용이한 재료를 오버레이용접시킨 후 표면처리를 함으로써 보다 고품질의 표면층을 얻기위한 시도가 이루어지고 있다. 따라서 국내, 외의 오버레이 용접기술의 적용현황 및 대표적인 적용사례, 오버레이 용접기술 및 용접재료의 개발현황 둥을 중심으로 살펴봄으로서 아직 국내에서는 널리 알려지지 않은 본 기 술의 활용을 넓이고자 한다. within minimum time from beginning of the shutdown.및 12.36%, $101{\sim}200$일의 경우 12.78% 및 12.44%, 201일 이상의 경우 13.17% 및 11.30%로 201일 이상의 유기의 경우에만 대조구와 삭제 구간에 유의적인(p<0.05) 차이를 나타내었다.는 담수(淡水)에서 10%o의 해수(海水)로 이주된지 14일(日) 이후에 신장(腎臟)에서 수축된 것으로 나타났다. 30%o의 해수(海水)에 적응(適應)된 틸라피아의 평균 신사구체(腎絲球體)의 면적은 담수(淡水)에 적응된 개체의 면적보다 유의성있게 나타났다. 해수(海水)에 적응(適應

• 대한기계학회논문집A
• /
• 제41권4호
• /
• pp.263-270
• /
• 2017

조선소에서 사용되는 대형 셧오프 밸브의 개폐를 위한 용기의 경우, 저압의 고정식 대형 공기탱크가 사용되고 있는데, 이는 먼 거리에 있는 밸브에 공압을 공급해야 할 경우, 추가 배관이 필요하며 수송도중 압력 강하가 발생하는 문제점이 있다. 이에 본 논문에서는 작업자들의 편의성을 증대시키고, 공기누설로 인한 폭발 방지를 위하여 고압의 휴대형 용접식 질소용기(11 kg, 10 L 및 50 bar)의 설계를 수행하였다. 구조적으로 취약한 용접부를 최소화하기 위하여 용기의 외형을 타원형으로 설계하였으며, 기준 무게 및 용적 충족과 사용압력에 대한 구조안전성을 확립하기 위하여 용기의 두께와 장단축 비를 설계하였다. 또한 용접 잔류응력 예측을 위해 APDL(ANSYS Parametric Design Language)을 이용하여 과도 열-구조 연성해석을 수행하였으며, 내압에 의한 구조안전 및 피로수명을 검증하였다.

• 마이크로전자및패키징학회지
• /
• 제13권3호
• /
• pp.47-51
• /
• 2006

디바이스의 고집적화로 인한 다층 배선구조로 인해 초점심도가 중요해짐에 따라 표면의 평탄도가 디바이스에 매우 큰 영향을 주게 되어, 표면의 평탄도를 결정지어주는 CMP(Chemical Mechanical Polishing) 공정이 매우 중요한 요소가 되었다. CMP 공정에는 슬러리, 연마패드, 컨디셔닝 디스크와 같은 소모품들이 사용된다. 이러한 소모품 중 하나인 컨디셔닝 디스크를 이용한 컨디셔닝 공정은 CMP 공정이 끝난 후 패드의 기공과 groove 내에 잔류 하는 화학반응물이나 슬러리와 같은 잔유물들을 컨디셔닝 디스크 표면에 부착되어 있는 다이아몬드를 이용하여 제거 함으로써 연마율을 높이고, 연마 패드의 수명을 증가 시켜주는 역할을 한다. 컨디셔닝 공정을 실시함으로써 연마 패드의 수명이 연장되기 때문에 경제적인 부분에서도 큰 이점을 가지게 된다. 본 연구에서는 이러한 CMP 공정에서 중요한 역할을 하는 소모품 중 하나인 컨디셔닝 디스크 표면에 존재하는 다이아몬드의 밀도, 형상 그리고 크기에 따라 연마 패드의 회복력 변화를 알아봄으로써 효율적인 컨디션닝 디스크의 특성을 평가해 보았다.