• Journal of the Korea Concrete Institute
• /
• v.18 no.5 s.95
• /
• pp.649-656
• /
• 2006

In this study, powered superplasticizer(PSP) agents to improve the slump loss rate of recycled aggregate concrete were developed. To evaluate the variation of fluidity against elapsed time and the mechanical properties, twenty four specimens whose main variables had the mixing condition of aggregates, such as natural and recycled gravels, and natural and recycled fine aggregates, were tested. The concrete slump with a liquid superplasticizer greatly decreased against the elapsed time and dropped by less than 50% of initial slump after two hours. However the concrete slump with the PSP agents hardly varied until after half an hour and maintained more than 85% of initial slump even after an hour. Also the PSP agents made the compressive, splitting tensile, and flexural strength of concrete increased and the shrinkage strain decreased. Considering the properties improvement of concrete, it can be recommended that optimum mixing amount of the PSP agents should be 5% of the amount of cement.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2014.05a
• /
• pp.250-251
• /
• 2014

With the recent movement toward sustainable development, many efforts have been made to reduce environmental loads in various domains of industry. In particular, a great deal of research and technology development has been underway on approaches to reducing industrial waste and the emission of greenhouse gases. For this reason, a quantitative analysis of the reduction in CO₂ emission that could be achieved by replacing limestone material with cementitious waste powder was performed in this study. Through the analysis, it was found that CO₂ emissions were reduced by up to 50 percent compared with the scenario in which OPC was used, which suggests that it is possible to reduce global CO₂ emissions by approximately 5percent, or by 446.4 Tg of the 965 Tg of CO₂ emissions generated by the cement industry, in the total global CO₂ emissions of 19300Tg.

• Applied Chemistry for Engineering
• /
• v.23 no.3
• /
• pp.259-265
• /
• 2012

Differently from fly ash, the bottom ash produced from thermal power generation has been treated as an industrial waste matter, and almost reclaimed or was applied with the additive of the part concrete. Bottom ash has various problems to use with the aggregate. Bottom ash is lighter than typically the sand or the gravel and it's physical properties (compressive strength etc.) is somewhat low because of high absorptance. In order to manufacture the ash concrete, we used a bottom ash as a main material and a pure sulfur as a binder. In this study, fundamental research methods that vary the grain-size of bottom ash and the ratio of sulfur vs ash were investigated to improve the quality of ash concrete such as compressive strength. Bottom ash in this research which occurs from domestic 4 place power plants, was checked physical and chemical properties. The compressive strength seems the result which simultaneously undergoes an influence in content of the sulfur and Bottom ash grain-size. We got the result of the maximum 92 MPa. The compressive strength was high result for grain size below 1.2 mm and high sulfur content.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2017.05a
• /
• pp.120-121
• /
• 2017

Generally, slump of plain concrete slab is about 120~150mm and slump loss is easy to occur. So, water is added to concrete because this method is convenient for Placing. In order to solve this problem, performance evaluation of concrete using improvement type PC admixture was carried out. Target slump is 210mm and compressive strength is 18MPa. As a result, slump reference value was satisfied 60 minutes after placing and 7-day compressive strength was 21~25MPa.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.5 no.2
• /
• pp.105-115
• /
• 2010

In this study, as one of solutions associated with the shortage of treatment area of industrial waste and the containment of its harmful components, the bottom ash which is known to be by-products of thermoelectric power plant was selected and its applicability for aggregate of concrete mixture was measured. Hardness test, sieve analysis, water-absorption test and SEM analysis were carried out to investigate the possibility of using bottom ash as a replacement of coarse and fine aggregate. Chemical analyses such as ignition loss test and X-ray incidence were carried out also. In addition, values for slump, strength, permeability, freeze and thaw, and carbonation were evaluated in terms of effects of replacement ratio of bottom ash. As the results, it was found that, though bottom ash is in short supply of fine particles and is in lack of cohesion, these problems can be solved by partially mixing with natural aggregates or improving in a process of production. In addition, bottom ash has not only advantage of durability but also acquirement of general compressive strengths in case that a certain proportion of natural aggregate is applied to mixture, in spite that unit water or chemical admixture should be increased to acquire good workability due to plenty of porosity.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.1 no.2
• /
• pp.107-113
• /
• 2013

This study is the study desiring to solve the problem by utilizing the kinds of recycled resources considered to be troubled complementarily. Namely the reaction of potential hydraulicity of Blast Furnace Slag Powder (BS) shall be reacted with the alkali of Recycled Fine Aggregates Coarse Aggregate, it has been experimented to obtain the optimum value with the replacement ratio of incineration plant ash (WA) treated with the slaked lime as the experiment variable by solving the alkali of shortage with the Ordinary Portland Cement (OPC). As a result, the liquidity and the air volume are declined slightly as the replacement ratio of incineration plant ash WA increases, the mixture of incineration plant ash WA 1% has been analyzed to be the most suitable considering the viewpoint of effective handling of waste as the compression and the tensile strength showed the maximum value before and after 1% even though it was disadvantageous with the increase of chloride content.

• Economic and Environmental Geology
• /
• v.51 no.4
• /
• pp.359-370
• /
• 2018

The batch and column experiments were performed to overcome the limitation of the neutralization process using the $scCO_2$-water-recycled aggregate, reducing its treatment time to 3 hour. The waste cement mortar and two kinds of recycled aggregate were used for the experiment. In the extraction batch experiment, three different types of waste mortar were reacted with water and $scCO_2$ for 1 ~ 24 hour and the pH of extracted solution from the treated waste mortar was measured to determine the minimum reaction time maintaining below 9.8 of pH. The continuous column experiment was also performed to identify the pH reduction effect of the neutralization process for the massive recycled aggregate, considering the non-equilibrium reaction in the field. Thirty five gram of waste mortar was mixed with 70 mL of distilled water in a high pressurized stainless steel cell at 100 bar and $50^{\circ}C$ for 1 ~ 24 hour as the neutralization process. The dried waste mortar was mixed with water at 150 rpm for 10 min. and the pH of water was measured for 15 days. The XRD and TG/DTA analyses for the waste mortar before and after the reaction were performed to identify the mineralogical change during the neutralization process. The acryl column (16 cm in diameter, 1 m in length) was packed with 3 hour treated (or untreated) recycled aggregate and 220 liter of distilled water was flushed down into the column. The pH and $Ca^{2+}$ concentration of the effluent from the column were measured at the certain time interval. The pH of extracted water from 3 hour treated waste mortar (10 ~ 13 mm in diameter) maintained below 9.8 (the legal limit). From XRD and TG/DTA analyses, the amount of portlandite in the waste mortar decreased after the neutralization process but the calcite was created as the secondary mineral. From the column experiment, the pH of the effluent from the column packed with 3 hour treated recycled aggregate kept below 9.8 regardless of their sizes, identifying that the recycled aggregate with 3 hour $scCO_2$ treatment can be reused in real construction sites.

• Journal of the Korea Concrete Institute
• /
• v.18 no.5 s.95
• /
• pp.667-675
• /
• 2006

Concrete is much more easily damaged by various parameters than by the only one and performance reducing mechanism grows more complicated in that condition. In addition, the factors which really act in concrete structure tend to be activated in turn and the degradation of concrete is very rapidly progressed. The purpose of this study is to evaluate the properties of polymer cement mortars under combined cures. The polymer cement mortars are prepared with various polymer types, polymer-cement ratios and cement-fine aggregate ratio, and tested for compressive and flexural strengths, accelerated carbonation, chloride ion penetration and acid resistance test, and freezing-thawing test. The properties of polymer cement mortars under combined cures is discussed. From the test results, polymer cement mortars have superior strengths compared with plain cement mortar under combined cures. The strengths of polymer cement mortars are markedly increased at curing condition II and V, however strengths are not improved at curing condition I and IV irregardless of polymer types. The carbonation and chloride ion penetration depths of polymer cement mortars tend to decrease in curing conditions, III-C, IV-B, V-A order, and decrease with increasing polymer cement ratios. It is concluded that polymer cement ratio of 10 to 15% are considered optimum for the preparation of such polymer cement mortars.

• Applied Chemistry for Engineering
• /
• v.23 no.2
• /
• pp.210-216
• /
• 2012

For the recycling of rapid-cooled steel slag, various specimens were prepared with the various replacement ratios of the rapid-cooled steel slag and the addition ratios of polymer binders. The physical properties of these specimens were then investigated by absorption test, compressive strength test, flexural strength test and hot water resistance test, and the pore and the micro-structure analysis was performed using scanning electron microscope. Results showed that the flexural strength increased with the increase of rapid-cooled steel slag and polymer binder, but the compressive strength showed a maximum strength at a certain proportion. By the hot water resistance test, compressive strength and flexural strength decreased remarkably and the total pore volume increased but the pore diameter decreased. SEM observation of the structure before the hot water resistance test revealed a very compact infusion of structure but the decomposition or thermal degradation appeared in polymer binders when observed after the hot water resistance test.

• Journal of the Korea Concrete Institute
• /
• v.25 no.3
• /
• pp.339-345
• /
• 2013

This study is to derive from the required performances and the optimum mix proportion of the roof concrete placed in the in-ground LNG storage tank with a capacity of 200000 $m^3$, and propose the actual data for site concrete work. The concrete placing work without sliding and segregation in the fresh concrete condition is very important because the slope of domed roof is varied in the large range by its curvature. Also the control of hydration heat and the strength development at test ages are classified with massive section about 1.4 m thick and considered to the pre-stressing work and removal of air support after concrete placing work. Considering above condition, slump range is selected $100{\pm}25$ mm under the slope $20^{\circ}$ and $150{\pm}25$ mm over the slope $20^{\circ}$ s until 60 minutes of elapsed time. Also, the roof concrete is satisfied with compressive strength range including design strength at 91 days (30 MPa), pre-stressing work at 7 days (10 MPa), air support removal work at 21 days (14 MPa). Replacement ratio of limestone powder is determined by confined water ratio test and main design factors include water-cement ratio (W/C), sand-aggregate ratio and dosage of admixture. As test results, the optimum mix proportion of the roof concrete used low heat cement is as followings. 1) Replacement ratio of limestone powder 25% by confined water ratio test 2) Water-cement ratio 57.8% 3) Sand-aggregate ratio 42.0%. Also, test results for the adiabatic temperature rising test is satisfied with its criteria and shown the lower value compared to preceding storage tank (TK-13, 14). These required performances and the optimum mix proportion is to apply the actual construction work.