• KSCE Journal of Civil and Environmental Engineering Research
• /
• v.31 no.1D
• /
• pp.91-98
• /
• 2011

Recently, the usage of elastic paving using EPDM Chip instead of pedestrian sidewalk blocks or permeable concrete used mostly for pedestrian walk, trails and in parks has been increassed as it can absorb impact during walking and produce wide range of colors and designs. However, the properties of EPDM Chip including elasticity and durability are decreased when exposed to ultraviolet ray and scenic paving functions through various colors are lowered due to the yellowing phenomenon. In this study, ultraviolet ray accelerated weathering test has been conducted to analyze the color changes in EPDM Chip and polyurethane resin, which are the main ingredients of elastic paving, when exposed to ultraviolet ray. The color differences are quantitatively analyzed through the color value coordination of the colored space by using the color difference scheme. The experimental results show that the color changes in BL polyurethane resin which is used most frequently at present was larger than that of EPDM Chip. Moreover, the total color difference, ${\Delta}E$, of BC polyurethane resin are 3.162 on the $14^{th}$ day of commencement of acceleration, which is 6 times greater color change resistance against ultraviolet ray than that of BL polyurethane resin with total color difference of 20.639. Therefore, the usage of BC polyurethane resin, which is manufactured to have chain-type molecular structure by using the isocyanate as the HMDI at the time of producing polymer, as binder in elastic paving with EPDM Chip is found to be a highly efficient method of restraining the color changes due to the ultraviolet ray.

• Journal of Conservation Science
• /
• v.36 no.6
• /
• pp.549-561
• /
• 2020

This study aimed to assess the performance and life of nine natural mineral dancheong pigments: Seokganju, Jinsa, Hwangto, Jahwang, Wunghwang, Seokrok, Noerok, Seokcheong, and Baekto. The design of the accelerated weathering test considered the domestic climate characteristics and the location of Dancheong. Outdoor weathering tests were conducted at the Research Institute in Daejeon and the Sungnyemun Gate in Seoul to confirm the field reproducibility of the accelerated weathering test. Monitoring of the physical changes in pigments through accelerated and outdoor weathering tests are based on ultraviolet exposure dose. Despite small cracks at the beginning of the tests, the monitoring showed that Seokganju and Baekto had no marked physical changes, but the surface cracks of Jinsa and Seorok continue to expand. Hwangto and Noerok were marked with water or were resin stained, and the particles of Jahwang, Wunghwang, and Seokcheong had lost their luster. Despite the absolute difference in color change in each test, the final chromaticity change patterns of pigments were similar in that the color difference between Baekto and Noerok was below five, and Jina was above 28. The physical and surface color pigment changes were more concentrated in outdoor weathering tests than in accelerated tests, and the Seoul site was more intense than the Daejeon site. This is because outdoor weathering tests are exposed to severe variations of temperature and moisture or deposition of dust particles and, in the case of Seoul, the site is more exposed to the external environment than the Daejeon site.

• Journal of the Korean Wood Science and Technology
• /
• v.44 no.1
• /
• pp.9-18
• /
• 2016

This study was performed to understand wood durability to climate deterioration of planted Indonesian wood specie such as Albizia, Gmelina, Mangium and Mindi. Wood samples were exposed to indoor and outdoor condition. $L^*a^*b^*$ and Color changes (${\Delta}E*ab$) were determined by a spectrophotometer. As a result, color of all samples was changed more markedly by ultraviolet radiation. In indoor test with UV, brightness of wood specimens from four species was not changed and all samples were changed into more reddish and yellowish. In accelerated weathering test, all samples were bleached and changed into more greenish and blueish. In outdoor test, brightness of wood specimens decreased in Albizia and Gmelina and increased in Mangium and Mindi. All wood specimens in outdoor test were changed into more greenish and blueish. Albizia and Gmleina woods showed greater color change than those of Mangium and Mindi. Especially, color change of wood samples might be influenced greatly by moisture. In conclusion, wood color changed into more clearly by UV radiation. Therefore, exposing woods to UV radiation could be one of reasonable methods to improve wood quality on visual characteristic.

• Polymer(Korea)
• /
• v.29 no.5
• /
• pp.508-517
• /
• 2005

The thermal degradation behavior and reliability analysis were investigated using dynamic thermogravimetric analysis (TGA) and accelerated degradation test (ADT) to characterize the dynamic parameters related to thermal degradation of plastic meterials for household electric appliances. In addition, the weathering of the plastic were performed by ADT using Xenon uc, and the color difference of the samples after ADT were measured with Color Eye 3010 specoophotometer. he activation energy for thermal degradation of the samples increased with increasing the rate of weight loss. The Kim-Park method was found to be more effective analysis in describing thermal degradation of plastic meterials. Plastic materials were very sensitive to ultra-violet rays in faster degradation.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.30 no.4
• /
• pp.156-161
• /
• 2020

Recently, as there has been growing demand for aesthetic quality in structural materials, the development of excellent color cement concrete having good coloration properties has become a requirement. This study is designed to analyze the basic physical properties of mortar and the properties of keeping the coloration under an ultraviolet ray accelerated weathering test environment according to changes in the mixing ratio between carbon black and iron oxide used as colorants. The test results show that the use of carbon black and iron oxide reduces the initial flow by 6.3~17.2 % and the air content by 3.5~31.5 % but increases the unit volume weight by 3.4~5.5 %, compared to ordinary Portland cement (OPC). In addition, the study shows that the addition of iron oxide increases the self drying shrinkage. So, caution needs to be taken on the workability of the concrete. The brightness value L^⁎ represented by black showed the most excellent black colour when carbon black 3 % and iron oxide 5 % are added. According to UV accelerated weatherproof test, the brightness value L^⁎ was found to increase in all experiment specimens by 4.28~11.97 %, and the color change by UV was found to be higher for the case where carbon black colorant was not used. Therefore, in terms of color revelation characteristics, the case using carbon black 3 % and iron oxide 5 % was found to show the best black color.

• Journal of Conservation Science
• /
• v.31 no.4
• /
• pp.457-476
• /
• 2015

This study is expected to present instructions and analysis of Modern Dancheong pigments by its physical characteristics. Search pigments currently used and experiments proper mixing ratio of Jangdanyuksaek(Incarnadine). Samples are made by based on presented a mixture ratio which is less exfoliation, cracks and color change. And put into accelerated weathering test and ultraviolet ray degradation test. As a result in case of Jidang($TiO_2$) Rutile type is superior in discoloration and durability. Rutile type makes color difference remarkably because of oil absorption difference while mixing with Jangdan. Water paints which are used as a alternative present yellowness which means water paints lack in durability. whiting should be taken carefully as it has high brightness after degradation.

• KSCE Journal of Civil and Environmental Engineering Research
• /
• v.33 no.1
• /
• pp.317-327
• /
• 2013

Air pollution and artificial heat of urban areas have caused the urban heat island in which asphalt pavements absorb solar heat during the daytime and release the heat at night. Hence, in order to improve the environment of urban areas, it is necessary to examine cooling pavements that can reduce heat on road pavements in urban areas. The application of temperature insulation paints on road pavements require to reduce black brightness for visibility, to increase the reflection rate of infrared light and minimize the reflection rate of visible light. In the study, one part of Acrylic-emulsion was used as a main binder, and the changes in black brightness and the changes of addition ratio (0%, 15%, 30%) of hollow ceramics, as well as kinds of paints (carbon black pigment, mixed mineral pigment) were selected as the main experimental factors. The performance of temperature reduction of cooling pavements was analyzed through the reflection rate of spectrum, the reflection rate of solar heat, and the lamp test. Abrasion resistance, UV accelerated weather resistance, and sliding resistance were tested in real situations. In addition, the performance of heat reduction of testing pavements covered with high-reflection paints was analyzed by using an infrared camera. As the test results, when using mixed mineral paints and hollow ceramic of 30%, the reflection rate of spectrum was 43% in the area of near-infrared ray and 17% in the area of visible light at black brightness of $L^*$=42.89 and the reflection rate of solar heat was 27.5%. Total color difference was ${\Delta}E$=0.27 in the test of UV Accelerated Weather Resistance, indicating almost no changes in color. BPN was more than 53 when scattering #2 and #4 silica sand of more than $0.12kg/m^2$. In Taber's abrasion resistance test, abrasion loss was up to 86.4mg at 500 rotations. The performance of heat reduction was evaluated using an infrared camera at the test section applying high-reflection paints to asphalt pavements, in which the results showed that the temperature was reduced by $12.7^{\circ}C$ on CI-30-40 cooling pavements ($L^*$=38.76) and by $14.2^{\circ}C$ on CI-30-60 cooling pavements ($L^*$=57.12).