The Influence of Vanadium Addition on Fracture Behavior and Martensite Substructure in a Ni-36.5at.%Al Alloy (Ni-36.5at.%Al 합금에서 V 첨가가 파괴거동 및 마르텐사이트 내부조직에 미치는 영향)

  • Kim, Young Do;Choi, Ju;Wayman, C. Marvin
    • Analytical Science and Technology
    • /
    • v.5 no.2
    • /
    • pp.203-211
    • /
    • 1992
  • Fracture behavior and martensite substructure of Ni-36.5at.%Al alloy were investigated with the addition of vanadium which is known as scavenging element of grain boundary. The fracture surfaces were examined by scanning electron microscopy and the EDX spectrometer was applied for composition analysis of fracture surfaces. The substructure of martensite was studied by transmission electron microscopy. By addition of vanadium, fracture surfaces show mixed modes of intergranular and transgranular fracture and more Al content is found on the grain boundaries. For Ni-36.5at.%Al alloy, the planar faults observed in the martensite plates are the internal twins. By increasing the vanadium content, the modulated structure with stacking faults and dislocations dominates while the twinned martensite disappears. The stacking fault is determined to be extrinsic due to the substitution of V for Al. It is concluded that the segregation of sulfur on the high-energy state stacking fault area suppresses the intergranular fracture.

  • PDF

Friction Welding of Ni-Base ODS Alloy Prepared by Mechanical Alloying (기계적 합금법으로 제조된 Ni기 산화물 분산강화 합금의 마찰압접에 관한 연구)

  • 강지훈;박성계;김지순;권영순
    • Proceedings of the Korean Powder Metallurgy Institute Conference
    • /
    • 1994.10b
    • /
    • pp.15-15
    • /
    • 1994
  • M MA ODS 합금의 보다 폭넓용 실용확훌 위해 크게 요구되고 있는 적정 접합기술 개발의 한 방안£로, 마찰압접(Friction Welding) 방법의 가능성옳 조사하기 위하여 마찰압력과 시간, 마 찰 후 접촉압력(Upset Pressure) 풍을 다양하게 변화시켜 접합체톨 제조한 후, 접합체 강도에 대한 인장시험과 접합계연의 결합 및 미세구조에 대한 현미경 관찰, EDS에 의한 원소분석, 접 합이옴부의 경도분포와 파단면 분석 풍율 행하였다. 실험에 사용된 모재는 기계적 합금법으로 제조된 Inca사의 Ni기 MA 754 합금이었으며, 직경 l 10 mm, 길이 50 mm로 가공한 후, 아세통£로 초음파 세척하여 접합에 사용하였다. 접합온 브 레이크식 마찰압접기틀 사용하여 행하였으며, 회전시험편의 회전수는 2400 rpm이었A며, 다른 한쪽의 고정시험편과의 마찰압력 및 마찰시간온 각각 50 - 500 MPa과 1-5초로, 또한 업셋압 력도 50 - 600 MPa로 변화시켰다. 이때 업셋압력은 모든 시편에 대해 일정하게 6초동안 가하 였다. 얻어진 접합체는 각 압접조건 당 2개 이상의 접합시험편에 대해 상온 인장강도톨 측정하 였으며, 파단이 일어난 위치를 확인한 후 파면에 대한 분석율 주사전자현미경(SEM)과 에너지 분산형 분광분석기mDS)릎 사용하여 행하였다. 컵합이옴부의 첩합성올 확인하기 위하여, 접합 체를 접합변에 수직으로 절단, 연마한 후 광학현미경과 SEM, EDS 퉁으로 관찰, 분석하여 접 합부의 형상과 결합형성 여부, 접합계면의 미세조직 퉁옳 조사하였다. 또한 마찰압접에 따론 모재와 접합계연부의 경도분포훌 접합이옴부로부터 모재쪽으로 일정 간격율 두어 마이크로 비 커스 경도기로 측정, 조사하였다. 이상의 설험 결과, 다옴과 같온 결론옳 얻었다. ( (1) 접합체 강도가 모채 강도의 95% 이상이 되는 양호한 렵합체흩 얻기 위한 마찰압력 조건 온, 2400 rpm의 회전속도와 6초의 업셋압력 유지시간에서 마찰압력과 업셋압력, 그리고 마찰시 간이 각각 400 MPa 이상과 500 MPa 이상,2초입율 확인하였다. ( (2) 컵합이옴부의 관찰 결과, 모든 마찰압접 조건에서 컵합이옴부는, 기폰 모재의 texture 조직 을 유지하고 있는 모재부 영역(영역 ill)과 첩합계면부에 인접하여 업셋압력이 주어질 때 단조 효과에 의해 계연 외부로 metal flow가 일어나면서 형성된 영역 II, 매우 미세한 결정립으로 구성된 중앙부의 영역 1 로 이투어져 있옴융 확인하였다. ( (3) 최적접합조건이 충족되지 않온 경우, 접합부의 영역 I 에서 관찰된 void와 균열, 불균일한 접합계면 통의 접합결함에 Al과 Y. Ti 퉁£로 구성된 산화물률이 용집되어 있옴을 확인하였 다-( (4) 접합체의 파단 양상온 크게 접합부 파단과 모재부 파단, 이률의 혼합형 파단i로 나눌수 있었다. 모재부 파단의 경우, 파단면이 매끄럽고 파변상의 결정립도 매우 미세하였으며, 산확물 의 용집도 찾아보기 어려웠 나, 접합부 파단의 경우에는 파변의 굴곡이 비교척 심하고 연성 입계파괴의 형태를 보였£며, 결정립도 모채부 파단의 경우에 비해 조대하였다. 조대하였다.

  • PDF

Accelerated Ultrasonic Fatigue Testing Applications and Research Trends (초음파 가속피로시험 적용 사례 및 연구 동향)

  • Cho, In-Sik;Shin, Choong-Shig;Kim, Jong-Yup;Jeon, Yong-Ho
    • Transactions of the Korean Society of Mechanical Engineers A
    • /
    • v.36 no.6
    • /
    • pp.707-712
    • /
    • 2012
  • Very high cycle fatigue (VHCF) behavior of aerospace components has emerged much attention due to their long service life. In this study, a piezoelectric ultrasonic fatigue testing (UFT) system has been developed by Mbrosiatec Co., Ltd. to study the high cycle fatigue (HCF) strength of Ti-6Al-4V alloy. Hourglass-shaped specimens have been investigated in the range from $10^6$ to $10^9$ cycles at room temperature under completely reversed R = -1 loading conditions,. Scanning electron microscopy (SEM) analysis revealed that failures occurred in the entire range up to the gigacycle regime, and the fractures have beenfound to be initiated from the surface, unlike in steels. However, it was found from the SEM microgprahs that microcracks transformed into intergranular fractures. Thus, it can be concluded from according to the results that this test method can be applicable to commercialized automotive and railroad parts that require high cycle fatigue strength.

Grain Boundary Character Changes and IGA/PWSCC Behavior of Alloy 600 Material by Thermomechanical Treatment (가공열처리에 의한 Alloy 600 재료의 결정립계특성 변화와 입계부식 및 1차측 응력부식균열 거동)

  • Kim, J.;Han, J.H.;Lee, D.H.;Kim, Y.S.;Roh, H.S.;Kim, G.H.;Kim, J.S.
    • Korean Journal of Materials Research
    • /
    • v.9 no.9
    • /
    • pp.919-925
    • /
    • 1999
  • Grain boundary characteristics and corrosion behavior of Alloy 600 material were investigated using the concept of grain boundary control by thermomechanical treatment(TMT). The grain boundary character distribution (GBCD) was analyzed by electron backscattered diffraction pattern. The effects of GBeD variation on intergranular at tack(JGA) and primary water stress corrosion cracking(PWSeC) were also evaluated. Changes in the fraction of coinci dence site lattice(CSL) boundaries in each cycle of TMT process were not distinguishable, but the total eSL boundary frequencies for TMT specimens increased about 10% compared with those of the commercial Alloy 600 material. It was found from IGA tests that the resistance to IGA was improved by TMT process. However, it was found from PWSCC test that repeating of TMT cycles resulted in the gradual decrease of the time to failure and the maximum load due to change in grain boundary characteristics, while the average crack propagation rate of primary crack increased mainly due to suppression of secondary crack propagation. It is considered that these corrosion characteristics in TMT specimens is attributed to 'fine tuning of grain boundary' mechanism.

  • PDF

Study for Fracture in the Last Stage Blade of a Low Pressure Turbine (화력발전용 저압터빈 최종 단 블레이드에 대한 파손 연구)

  • Lee, Gil Jae;Kim, Jae Hoon
    • Transactions of the Korean Society of Mechanical Engineers A
    • /
    • v.40 no.4
    • /
    • pp.423-428
    • /
    • 2016
  • The last stage blades of a low pressure (LP) turbine get frequently fractured because of stress corrosion cracking. This is because they operate in a severe corrosive environment that is caused by the impurities dissolved in condensed steam and high stress due to high speed rotation. To improve the reliability of the blades under severe conditions, 12% Cr martensitic stainless steel, having excellent corrosion resistance and higher strength, is widely used as the blade material. This paper shows the result of root cause analysis on a blade which got fractured suddenly during normal operation. Testing of mechanical properties and microstructure examination were performed on the fractured blade and on a blade in sound condition. The results of testing of mechanical properties of the fractured blade showed that the hardness were higher but impact energy were lower, and were not meeting the criteria as per the material certificate specification. This result showed that the fractured blade became embrittled. The branch-type crack was found to have propagated through the grain boundary and components of chloride and sulfur were detected on the fractured surface. Based on these results, the root cause of fracture was confirmed to be stress corrosion cracking.

Creep Properties of Sn-3.5Ag-xBi Solders (Sn-3.5Ag-Bi 솔더의 크리프 특성)

  • Shin, S. W.;Yu, Jin
    • Journal of the Microelectronics and Packaging Society
    • /
    • v.8 no.4
    • /
    • pp.25-33
    • /
    • 2001
  • Sn-3.5Ag-xBi alloys with five different levels of Bi (0, 2.5, 4.8, 7.5, 10 wt%) were prepared for evaluating creep properties. Cast alloys were roiled and heat treated to provide stable microstructures during the subsequent creep tests, which were conducted under constant load using dog-bone specimens. For the Bi containing alloys, creep strength showed the maximum around 2.5 wt%Bi and tended to decrease with increasing Bi content. The stress exponent of the alloy was around 4, suggesting typical dislocation creep, but the exponent was 2 for the 10 wt%Bi alloy, suggesting creep assisted by grain boundary Sliding. For the Bi containing alloys, the brittle fracture mode appeared showing small amount of reduction of area, while the ductile fracture mode was true for the Bi free alloy. Microstructural examination of ruptured specimens showed cavitations on grain boundaries normal to the load axis, and a significant of grain boundary sliding for the Bi containing alloys.

  • PDF

Effect of Aging Treatment on Fracture Characteristics of High Strength Al-Alloy (고력 알루미늄 합금의 파괴특성에 관한 시효처리의 영향)

  • Moon, Chang-Kweon;Oh , Sae-Kyoo
    • Journal of the Korean Society of Fisheries and Ocean Technology
    • /
    • v.20 no.1
    • /
    • pp.23-29
    • /
    • 1984
  • Nowdays, the high strength aluminum alloys are broadly used for structural purpose, but the practical strengthening method by aging treatment are not much available. So that, in this study, in order to investigate the effect of aging treatment for strengthening on the fracture characteristics of the domestic high strength Al alloy (A2024BE), the variations of the aging temperature and time were taken after solution treatment. By microstructural examination, and by SEM fractographs of the fractures, the effects of aging temperature and time were investigated, considering on the fracture behaviour. The results obtained are as follows: 1) It was confirmed by microstructural investigation that the aging temperature of $190^{\circ}C$ and the aging time of 12hours were optimal to get more sound microstructure with distribution of uniform precipitation. 2) By step aging treatment, the proper aging time for obtaining the similar microstructure without any microstructural defects could be shortened in half the normal aging time. 3)By examining the SEM fractographs of the fracture surface, it was found that, regardless of the aging treatment time and temperature, all were intergranular ductile fractures, but the aging treatment at $190^{\circ}C$ for 12 hours resulted in dimple-type-transgranular and intergranular-ductile-frature.

  • PDF

Characteristics of microstructure and mechanical strength of ASTM A387-Gr.91 Steel deteriorated under high-temperature (고온 열화된 ASTM A387-Gr. 91 강의 미세 조직 및 기계적 강도 특성)

  • Jeong, Gwang-Hu;Han, Min-Su;Kim, Seong-Jong
    • Proceedings of the Korean Institute of Surface Engineering Conference
    • /
    • 2018.06a
    • /
    • pp.111-111
    • /
    • 2018
  • ASTM A387-Gr.91 강은 우수한 고온 강도, 크리이프 저항성 그리고 내산화성 등으로 인해 화력 및 바이오매스 발전 시설과 같은 고온 설비의 구조재료로 널리 사용되고 있다. 고온 환경에서 높은 강도는 탄화물과 탄질화물에 의한 석출강화가 주 요인으로 작용한다. 열처리 과정에서 Mo, Cr, Mn, 그리고 Fe는 구-오스테나이트 및 마르텐사이트 라스 입계에 $M_{23}C_6$ 탄화물로 석출되며, V, Nb, 및 N은 조직 내부에 미세한 MX 탄질화물로 석출된다. 따라서 합금의 고온 강도는 조직 내 석출물의 개수밀도와 크기에 크게 의존한다. 그러나 적용 환경의 특성 상 고온 노출에 따른 2차상 석출 및 조대화의 조직열화 현상이 발생하며, 이는 재료의 강도를 저하시킨다. 본 연구에서는 ASTM A387-Gr.91 강의 미세조직 열화에 따른 강도저하 및 파괴 양상을 고찰하는데 그 목적을 두었다. 본 연구에서 사용된 ASTM A387-Gr.91 강의 화학성분(wt, %)은 0.1 C, 0.38 Si, 0.46 Mn, 0.25 Ni, 8.38 Cr, 0.93 Mo, 0.18 V, 0.09 Nb, 그리고 나머지는 Fe 이다. 조직열화 및 기계적 강도저하 특성을 평가하기 위한 등온열화는 $650^{\circ}C$의 대기 환경에서 최대 1000시간동안 실시하였다. 열화된 시험편의 미세조직 및 탄화물에 대한 분석은 SEM과 EDS를 이용하여 실시하였다. 그리고 기계적 강도 평가는 인장실험과 비커스 경도시험을 통해 실시하였다. 또한 열화 시간에 따른 파단양상의 변화를 관찰하기 위해 인장시험편의 파단면을 SEM과 EDS를 이용하여 분석하였다. 그 결과, 열화에 따른 마르텐사이트 라스의 소실, 탄화물의 조대화, 그리고 2차상 석출의 조직 열화현상이 나타났다. 또한 기계적 강도는 조직 열화에 따라 저하되는 경향을 나타냈다.

  • PDF

A study on the KLA behaviors in HAZ and the mechanical properties of austenitic stainless steel weld (스테인레스강용접 열영향부의 KLA거동 및 기계적 특성에 관한 연구)

  • 조종춘;김영석;김학민
    • Journal of Welding and Joining
    • /
    • v.8 no.4
    • /
    • pp.27-34
    • /
    • 1990
  • Integranular corrosion behaviors of KAL (Knife Line Attack) and mechanical properties such as tensile and creep rupture were investigated for the tube material used for nearly 20 years under the condition of 463.deg. C and 28 $kg/cm^2$. Based and weld metal were austenitic stainless steel AISI 321 containing Ti, AISI 347 containing Nb, respectively. KLA is a kind of the intergranular corrosion which often occurs just near the HAZ (heat affected zone) of AISI 321 and AISI 347 stainless steel due to the grain boundary sensitization. In KLA zone, intergranular corrosion crack has propagated outwards from the inner surface and carbides of white and narrow band type assuming as (Cr, Fe) carbide were confirmed. All the delta-ferrite formed in the weld metal during weld solidification has been transformed into sigma-phase since delta-ferrte was exposed for 20 years at 463.deg. C. Elongation was very low at the range from room temperature to 600.deg. C and it was confirmed that creep-rupture properties were not consideralbly affected.

  • PDF

초내식성 오스테나이트계 스테인리스강의 증기발생기 전열관 적용가능성 평가

  • 김택준;박용수;김영식
    • Proceedings of the Korean Nuclear Society Conference
    • /
    • 1997.05b
    • /
    • pp.201-206
    • /
    • 1997
  • 본 연구에서는 Ni-기 합금인 합금 600과 합금 690, Fe-기 합금인 합금 800 및 초내식성 오스테나이트계 스테인리스강인 SR-50A에 대하여 부식 환경의 변화에 따른 특성 평가를 행하였다. 전기화학적 부식 평가는 양극 분극 시험을 통하여 행하였으며 부식 환경은 NaCl, HCI, NaOH(+$Na_2$SO$_4$) 액이었다. 응력 부식 균열 시험으로는 CERT(Constant Extension Rate Test)를 행하였으며 부식환경은 40%NaOH, 40%OH+12%$Na_2$SO$_4$ 용액이었다. CERT시험 후 그 파면을 SEM관찰하여 파괴 양상을 관찰하였다. 각 합금의 양극 분극 특성을 부식 환경에 따라 평가한 결과, 부식 용액의 증류에 따라 서로 다른 분극 거동을 보이고 있는데 산성과 중성 용액에서는 SR-50A가 가장 큰 저항성을 보이는 반면, 강 알카리용액인 NaOH용액에서는 Ni-기 합금의 저항성이 Fe-기 합금의 저항성보다 우수하게 나타났다. 응력 부식 균열 저항성은 전반적으로 Fe-기 합금보다 Ni-기 합금이 우수하게 나타났다. 파단면을 SEM관찰한 결과 합금 800과 SR-50A(tube)는 용액에 관계없이 입내 파괴 모드를 나타내고 있으며, 합금 600과 SR-50A판재는 입계 파괴 양상을 보이고 있다. 또한 가성 용액 중에 $Na_2$SO$_4$를 첨가할 경우, 부식 속도를 가속화시키고 응력 부식 균열 저항성을 감소시키고 있다.

  • PDF