• Magazine of the Korea Concrete Institute
• /
• v.9 no.5
• /
• pp.177-187
• /
• 1997

철근 콘크리트 구조부재는 철근과 콘크리트로 구성된 합성부재이므로, 철근콘크리트 구조부재의 피로강도는 철근과 콘크리트 고유의 피로특성에 따라 변화하게 된다. 철근자체의 피로특성은 철근의 정적강도 특성과 상이함으로, 실험을 통하여 규명할 필요가 있다. 본 논문에서는 대표적인 국내 2개사에서 생산되는 철근에 대하여 직접인장 피로실험을 실시하여 이들의 피로특성을 규명하였으며, 철근콘크리트 휨부재 내부의 철근 피로특성과 철근만의 직접인장 피로특성의 비교 분석으로부터 직접인장 피로실험만으로 철근콘크리트 휨부재의 피로특성을 평가할 수 있음을 밝혔다. 또한 반복하중을 받는 철근콘크리트 부재의 피로점토를 위한 기준을 제시하였다.

• Journal of the Korea Concrete Institute
• /
• v.16 no.5 s.83
• /
• pp.581-589
• /
• 2004

This paper compares the fatigue behaviors of concretes subjected to flexural and split-tensional loadings, and proposes the fatigue reliability models based on experimental results and reliability analysis. The fatigue tests were performed for the specimens of $150 mm{\times}75 mm$ split tensional cylinders and $150 mm{\times}150 mm{\times}550 mm$ flexural beams under constant loadings at three levels (70, 80 and $90\%$) with 0.1 stress ratio, 20 Hz loading speed and sine wave. The reliability analysis on fatigue data was based on Weibull distribution of two-parameters. From fatigue test results, two criteria were proposed to reject the experimental fatigue data because of statistical variation of concrete fatigue data. Two parameters ($\alpha$and u) of Weibull distribution were obtained using graphical method, moment method and maximum likelihood method. The probability density function(P.D.F) and cumulative distribution function(C.D.F) of the Weibull distribution for fatigue life of pavement concrete were derived for various stress levels using parameters, $\alpha$ and u. The goodness-of-fit test by Kolmogorov-Smirnov test was acceptable at $5\%$ level of significance. Based on reliability analysis, a fatigue model for pavement concrete was proposed and compared from existing models.

• KSCE Journal of Civil and Environmental Engineering Research
• /
• v.28 no.2A
• /
• pp.165-170
• /
• 2008

New high strength bolts are required due to the development of the high strength steel, the ultra-thick steel plates, and the long-span bridge, though high strength bolts with tensile strength of 1,000 MPa are mainly used in construction site of every country. The high strength bolts are often subjected to a repeated tension-type of loading in which the fatigue failure is a major mode of failure. However, the theoretical and experimental study for the fatigue failure of tension bolt has not been well established in Korea. In this study, we performed a tensile fatigue test of F8T, F10T and F13T, F13T-N high strength bolts under tension. We proposed three fatigue strength specifications by performing 95% survival probability analysis for F8T, F10T, F13T, and F13T-N bolt under the $2{\times}10^6$ cycles of repeated loading. And the fatigue strength for the advanced screw thread shape bolt developed in this study are compared with the previous KS screw thread shape bolt.

• Journal of Korean Society of Steel Construction
• /
• v.15 no.2
• /
• pp.137-145
• /
• 2003

In this study, direct tensile fatigue tests of the PS bar were performed in terms of diameter, minimum stress level, and maximum stress level. In the static test, the stress - strain curve and ultimate streng th of the PS bar were determined. Results of the fatigue test indicate that the diameter of the PS bar was not influenced by fatigue life. Minimum stress also had quite an influence on the fatigue of the PS bar. Thus, the fatigue characteristic equation was proposed in terms of stress range and minimum stress through statistical process. Strains on specimen that loaded direct tension were measured in the fatigue test, with the secant modulus of elasticity calculated from measured strains. The strain development consisted of three different stages, i.e., rapid increases during the initial fatigue life, uniform increases during the middle stage, and rapid increases until failure. The secant modulus of elasticity decreased during the fatigue life with increasing strain. However, stress level seemed to have no influence on the secant modulus of elasticity.

• Journal of Korean Society of Steel Construction
• /
• v.8 no.4 s.29
• /
• pp.95-103
• /
• 1996

단순 전단연결 구조를 가진 강철도교의 세로보 단부의 절취부위에서 많은 피로균열이 발견되었으며, 이러한 부위의 피로균열은 피로손상의 전형적인 예이다. 피로균열을 가진 세로보 절취부위의 보강방법을 연구하기 위하여 가로보 및 세로보의 상부 플랜지에 인장판을 부착한 경우와 부착하지 않은 경우로 구분하여 피로실험을 수행하였다. 피로실험에 사용된 하중은 현장에서 측정된 실동응력을 기초하여 빈도해석을 통해 산정하였다. 피로실험 결과, 인장판으로 보강한 모멘트 저항 연결구조상세가 철도교에서 균열성장을 효과적으로 정지시킬 수 있는 것으로 판명되었으며, 피로손상을 가진 절취부위의 보강방법으로 제시될 수 있을 것으로 사료된다.

• International Journal of Highway Engineering
• /
• v.5 no.3 s.17
• /
• pp.11-20
• /
• 2003

Concrete structures such as bridges, pavement, and offshore structures are normally subjected to repeated load. Because highway and airfield pavements are to resist tension in bending, fatigue failure behavior is very important the fatigue life of materials. Therefore, in this paper was carried according to the fatigue test method and experiment variables for pavement concrete. The fatigue tests were applied split tension($150{\times}75$ in size) and flexural($150mm{\times}150mm{\times}550mm$ in size) beam fatigue test method. Major experimental variable in the fatigue tests in order to consideration of fatigue life were conducted loading frequency of 1, 5, 10, 20Hz and loading shape of block, sine, triangle and moisture condition of dry and wet condition and curing age of 28day and 56day. The test results show that the effect of loading frequency increasing the frequency increased fatigue life, decreased significant at frequencies below 200 cycles. The effect of loading wave form on fatigue life show that a block decreased, triangular increased in comparison with sine. The effect of moisture condition decreased in wet condition in comparison with dry condition. The effect of curing age increased in 564ays in comparison with 28day.

• Journal of Welding and Joining
• /
• v.15 no.3
• /
• pp.12-20
• /
• 1997

구조의 용접접합부에는 재료의 항복응력 크기의 용접잔류응력이 발생되고, 이 잔류응력 상태에서는 응력비(최소응력/최대응력)의 영향이 거의 없다는 것이 일정 진폭 하중조건의 피로실험결과로부터 알려져 있다. 이와 관련하여, 용접구조의 설계 단계에서는 초기 용접잔류응력이 그래도 잔류한 소형실험편의 일정진폭하중 상태의 피로실험 결과로부터 도출된 피로설계선도(S-N 선도)를 이용, 변동하중에 의한 응력 진폭의 밀도분포만으로 일생동안의 누적피해도를 구해 피로강도를 평가하는 것이 일 반적이다. 지금까지는 선박용접구조의 경우도 이러한 개념으로 피로강도 평가를 수행 하였으나, 일반적인 육상 또는 해상 용접구조물과는 달리, 화물의 적재 등의 정하중 이력에 의한 응력변동폭은 피로를 유발하는 파랑 응력변동폭보다 상당히 크다. 그리 고, 정하중에 의해 용접접합부에 인장응력을 발생시키는 하중이력을 받을 경우, 초기 용접잔류 응력은 상당히 저하될 것으로 생각된다. 본 연구에서는 인장응력을 유발하는 정하중 이력에 의해 저하된 용접잔류응력분포와 이러한 잔류응력분포를 가진 선측 종늑골 용접접합부의 피로강도를 검토한다.

• Journal of the Korea Concrete Institute
• /
• v.16 no.1 s.79
• /
• pp.27-35
• /
• 2004

Most of concrete fatigue tests currently used are flexural tension or compression methods to investigate the tensile or compressive properties, respectively. However, the concrete pavement or concrete slab is actually subjected to a combined stress condition such as biaxial or triaxial. The split tension test may result in similar stress condition to biaxial stress condition. The purposes of this study were to evaluate the split tension fatigue test method for application in concrete. These were done by a finite element analysis and experimental series. The results were as follows: The optimum configuration of split tension fatigue test was a cylinder of 15cm in diameter and 7.5cm in thickness, which had a little different thickness compared to the KS standard cylinder of ${\phi}15{\times}30cm$. The concrete stress ratio of compressive against horizontal from FEA was 3.1, while that from theory was 3.0. The stress distributions of mortar and steel were almost similar at different thicknesses. The measured static split tensile strengths of concrete and mortar were quite similar at 30cm and 7.5cm thickness cylinders. The measured stress-strain relationship showed their consistency at all specimens regardless of thickness, and confirmed the results from FEA. As a results, the concrete split tension specimen, cylinder of 15cm in diameter and 7.5cm in thickness, could be used at fatigue test because of its accuracy, simplicity and convenience.

• Journal of Korean Society of Steel Construction
• /
• v.28 no.6
• /
• pp.459-465
• /
• 2016

In this paper, it was performed the fatigue test to examine the effect of cyclic loading for the simple T-joint. Axial force of bolt by clamping and the change of the force by applied load were measured in the joint. And the bolt force, the failure mode and the fatigue strength under cyclic loading were investigated. The parameters of the tension joint were set to be the flange thickness and the diameter of bolt to a different stiffness of the joint in response to the combination. From the fatigue test, failure mode of tensile joints under cyclic loading could be evaluated using a static ultimate load of the specific failure mode in EC3. The fatigue strength of the tension joints was considerably higher than the fatigue strength of the EC3(36) that does not consider a lever action. However, the additional axial force by lever action occurs to an increase in the axial force of the bolt it requires a careful evaluation of the fatigue strength.

• Journal of Power System Engineering
• /
• v.16 no.4
• /
• pp.66-73
• /
• 2012

본 연구는 횡방향 TIG 용접된 Al6013-T4 알루미늄 합금 용접부의 피로균열전파거동에 미치는 용접후열처리(PWHT)의 영향을 조사하는 것이 주목적이다. 기초적으로 인장시험, 경도 및 미세조직이 조사되었으며, 피로균열전파거동을 고찰하기 위한 피로 시험은 모두 중앙균열인장(CCT) 시험편에 대하여 수행되었다. T82열처리에 있어서 시효시간은 피로균열전파율, 인장강도 및 경도에 대단히 민감함을 나타내었으며, 모재와 열영향부재의 경우가 용접재보다 기계적 성질이 우수하였다. 횡방향 TIG 용접한 Al6013-T4 시험재의 용접후열처리 조건에 따라서 피로균열전파 저항에는 차이가 나타났으며, 본 실험의 조건하에서 24시간 인공시효 PWHT-82 시험편이 피로균열전파 저항이 가장 우수한 결과를 나타내었다.