• Journal of Welding and Joining
• /
• v.34 no.5
• /
• pp.33-40
• /
• 2016

The microstructures and the creep rupture properties of dissimilar welds between the Ni-based superalloy Inconel 740H and the non-stabilized austenitic stainless steel TP316H have been characterized. The welds were produced by shielded metal arc (SMA) welding process with the AWS A5.11 Class ENiCrFe-3 filler metal, commonly known as Inconel 182 superalloy. Postweld heat treatment at $760^{\circ}C$ for 4 hours was conducted to form ${\gamma}^{\prime}$ strengthener in Inconel 740H. The austenitic weld metal produced by Inconel 182 had a dendritic microstructure, and grew epitaxially from the both sides of Inconel 740H and TP316H base metals. Since both Inconel 740H and TP316H did not undergo any solid-state transformation during welding process, there were no heat-affected-zone (HAZ) sub-regions and the coarsoned grains near the weld interface were limited to a narrow region. The hardness of Inconel 182 weld metal was ~220 Hv. The gradual hardness decrease was detected at HAZ of TP316H, and the TP316H base metal displayed the lowest hardness value (~180 Hv) whilst the Inconel 740H showed the highest hardness value (~400 Hv). Fracture after creep occurred at the center of weld metal, regardless of creep condition. It was found that during creep the cracks initiated and propagated along interdendritic regions and grain boundaries at which Laves particles enriched in Nb, Si and Cr were present. The appropriate design of weld metal was discussed to suppress the creep-induced cracking of the present dissimilar weld.

• Journal of the Korean Society for Nondestructive Testing
• /
• v.29 no.2
• /
• pp.153-161
• /
• 2009

After several PWSCCs were found in Bugey(France), Ringhals(Sweden), Tihange(Belgium), Oconee, Arkansas, Crystal Fever, Davis-Basse, VC Summer(U.S.A.), Thuruga(Japan), USNRC and PNNL started the research on PWSCC, that is, PINC project. The aim of this project is to fabricate and obtain representative NDE mock-ups with flaws to simulate tight PWSCC cracks, to identify and quantitatively assess NDE methods for accurately detecting, sizing and characterizing tight cracks such as PWSCC, to document the range of locations and crack morphologies associated with PWSCC and observed responses and to incorporate findings from other ongoing PWSCC research programs, as appropriate. By participating in PINC project, Korean morphology technique about PWSCC and NDE technique have improved and become similar lever with other advanced country. Therefore, the evaluation technique of integrity for nickel alloy component has been improved by cooperation with university, research institute and industries.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2018.06a
• /
• pp.106-106
• /
• 2018

해양환경용 선박재료는 전기화학적인 부식을 발생시키는 염소이온($Cl^-$)이 다량 포함된 부식 환경에 장기간 노출되어 있어 부식에 대해 취약하다. 따라서 우수한 내식성 및 내침식성을 가진 재료를 선정하는 것은 매우 중요하다. 알루미늄 합금은 충분한 강도와 부동태 피막 형성으로 인해 내식성이 우수하여 해양환경용 선박 재료로서 널리 이용되고 있으며, 이에 따른 부식 특성에 관한 연구도 활발히 이뤄지고 있다. 그러나 선박에서는 부식에 의한 손상뿐만 아니라 전식에 의한 부식 손상도 발생할 수 있다. 특히 선미 부분은 프로펠러의 동합금과 알루미늄 합금의 이종금속 간 전위차에 의한 전식이 발생하여 선체의 다른 부위에 비해 부식이 더 심하게 진행될 수도 있다. 또한 전식은 해안 부두에 접안된 선박의 용접 시미주전류(stray current)에 의한 부식손상이 발생할 수 있으나 이에 대한 연구는 미미한 실정이다. 따라서 본 연구는 해양환경에서의 전식을 인위적으로 모사할 수 있는 부식 정전류 시험법을 이용하여 다양한 크기의 전식 손상을 유발시켰으며, 해양환경 하에서 선박재료로 주로 사용되는 알루미늄 합금인 Al5083-H321, Al5052-O, Al6061-T6에 대한 전식 특성을 비교, 분석하였다. 실험 방법으로 작동전극은 각 재료의 시험편을 $2cm{\times}2cm$ 으로 절단하여 sand paper # 2000 번까지 연마 후 아세톤과 증류수로 세척하고 건조하였으며, 제작된 시험편은 자체 제작한 홀더를 이용하여 $1cm^2$만 노출시킨 후 정전류 가속 실험을 실시하였다. 기준전극은 은/염화은(Ag/AgCl) 전극을, 대응전극은 백금(Pt) 전극을 사용하였다. 정전류 가속 조건은 $0.001mA/cm^2$, $0.1mA/cm^2$, $1mA/cm^2$, $5mA/cm^2$, $10mA/cm^2$의 전류 밀도를 천연해수에서 30분간 인가하였다. 각 재료에 대한 전식 특성은 실험 전후의 무게 감소량으로 전식의 저항 특성을 확인하였다. 그리고 3D 현미경으로 표면 손상 경향과 깊이를 측정하였으며, 주사전자현미경 (SEM)을 통해 표면 형상을 미시적으로 관찰하였다. 부식 정전류 시험 결과 모든 시편에서 $0.01mA/cm^2$에서 미세한 국부적인 부식이 일어났으며, 전류밀도가 증가할수록 표면 전반에 부식이 진행되고 성장하였다. 그리고 모든 인가 전류밀도의 조건에서 Al6061-T6가 5000계열(Al5083-H321, Al5052-O)보다 더 우수한 내식성을 나타났다.