• Polymer(Korea)
• /
• v.37 no.1
• /
• pp.66-73
• /
• 2013

Three reactive dichroic dyes with 3,5-dichloro-2,4,6-triazine moiety were synthesized by reaction between dichroic dyes (such as congo red, direct black 22 or direct black 4) and cyanuric chloride. Poly(vinyl alcohol) (PVA) films were dyed with the obtained three reactive dichroic dyes. After 400% drawing of the PVA films, their optical properties were compared with an iodine-doped PVA film prepared in the same condition. Durability test was performed at $50^{\circ}C$ in 85% of relative humidity for 120 hrs. We found that compared with the iodine-doped PVA polarizing film, the relative durability of the PVA polarizing film dyed with the reactive dichroic dyes was greatly improved.

• Polymer(Korea)
• /
• v.35 no.5
• /
• pp.458-466
• /
• 2011

In the mixed system of supercritical carbon dioxide/organic solvents, poly(vinyl alcohol)(PVA) film of high degree of hydrolysis could be dyed with a dichroic dye of C. I. direct black 22(DB22) and as a result, high durability was obtained. Especially, as a dye dispersant in a supercritical fluid phase, a mixed solvent system of ethylene glycol: dimethyl sulfoxide=4 : 6 weight ratio was investigated. Then the optimum pressure for dyeing could be reduced down to 200 bar. Using this supercritical fluid system, the maximum dyeing appeared as the transmittance of less than 1% and the waste amount was reduced to the level of 1/10. After 500% drawing of this PVA film, both the polarizing efficiency of 94% and the single piece transmittance of 30% were obtained. The limitation of DB22 and further improvements were also discussed.

• Korean Journal of Optics and Photonics
• /
• v.26 no.2
• /
• pp.110-114
• /
• 2015

We propose a reflective cholesteric liquid crystal cell with reduced color shift, using dichroic dyes. Color-shifted light is absorbed by dye molecules in the proposed dye-doped cholesteric liquid crystal (DDCLC) cell. We have shown that the color shift can be reduced by increasing the concentration of dye molecules in the proposed DDCLC cell.

• Information Display
• /
• v.2 no.6
• /
• pp.29-35
• /
• 2001

• Journal of Adhesion and Interface
• /
• v.13 no.3
• /
• pp.131-136
• /
• 2012

In this study, commercial poly(vinyl alcohol) (PVA) film was dyed with reactive dichroic dyes under mild conditions using organic solvents in stead of strong basic aqueous solution. After drawing of 500% of this PVA film, the polarizing efficiency and the single piece transmittance were measured. The degree of saponification of the commercialized PVA film was determined by using NMR and FT-IR spectromety. The commercial PVA film, with ca. 100% of the degree of saponification determined by NMR spectrometry, was dyed with the reactive dichroic dyes, which have 3,5-dichloro-2,4,6-triazine moiety. As a result, we found that the PVA film dyed with the reactive congo red showed relatively good polarization efficiency, and the PVA film dyed with the reactive direct black 22 exhibited relatively good single piece transmittance.

• Polymer(Korea)
• /
• v.31 no.5
• /
• pp.393-398
• /
• 2007

We studied the mechanism of liquid crystal alignment on polyvinylfluorocinnamate (PVCN-F) films which were irradiated by UV using polarized fourier transform infrared (FT-IR) spectroscopy and ultraviolet/visible (UV/Vis) spectroscopy. UV irradiation of PVCN-F films caused decrease of vinylene -C=C- stretching peak area at $1638cm^{-1}$ and shift of conjugated C:0 stretching vibration at $1712cm^{-1}\;to\;1734cm^{-1}$ which is caused by nonconjugated C=O stretching nitration. To study the orientation direction of 5CB liquid crystal (LC) molecules in the liquid crystal cell with PUV irradiation, rubbing treatment or without any treatment on the PVCN-F alignment layer, we used polarized FT-IR dichroism technique. We successfully measured 5CB LC alignment directions, which are perpendicular to the irradiated PUV polarization direction and parallel to the rubbing direction in the liquid crystal cell without using dichroic dyes.