• Journal of the Korea Institute of Building Construction
• /
• v.23 no.4
• /
• pp.337-348
• /
• 2023

The central objective of this study is to curtail the leakage of mortar or cement paste, often resultant of ill-constructed formwork, by implementing thixotropy in the formulation of high-fluidity, standard-strength concrete. When such concrete is utilized in smaller scale construction projects, instances of formwork gaps due to suboptimal construction precision may lead to significant leakage of mortar and paste, a problem not typically encountered with traditional slump-flow concrete. In this investigation, Polyvinyl Alcohol(PVA) and borax are incorporated into the concrete mixture to induce thixotropy. The experimental design includes varying methodologies for integrating PVA and borax, while assessing alterations in diverse concrete performances, including thixotropy and leakage reduction potential that simulates formwork gap conditions. Under the experimental conditions defined within this study, it was found that replacing, rather than merely adding PVA and borax, aids in averting water addition via suspensions. This approach yielded promising results in terms of concrete properties and proved efficacious in stemming leakage in concrete possessing sufficient thixotropy. Notably, when a 6% PVA suspension was substituted, a significant reduction in leakage was observed. Consequently, it is projected that construction quality can be ensured, even with lower precision formwork, by applying thixotropy to concrete through the use of PVA and borax.

• Korean Journal of Agricultural Science
• /
• v.11 no.1
• /
• pp.146-159
• /
• 1984

This study was the contrast of the compressive strength, the tensile strength, the reducing ratio and the flow of mortar using dispersing agent and high fluid admix. 1. The admix ratio of chemical admixtures espressing maximum strength appeared the same result high fluid admix SP was 0.6%, the dispersing agents LG and C211 were 0.2%, SK was 0.3%, C376 was 0.5%. But two or three times more than standard quantity made the strength's fast lowness, which influenced bad to wateriness and retard the soli-dification. 2. When proper quantity of chemical admixture was used, the increment of compressive strength was as follows. High fluid admix SP was 40.7% and the average increasing rate of dispersing agents(C211 was 19.5%, LG was 19.1%, C376 was 17.9%) was 18.7% more than normal mortar in the codition of 7 days. Also, in the condition of 28 days, high fluid admix SP was about 24.4% and the average of dispersing agents(LG was 21.1%, C211 was 16.4%, SK was 11.1%, C376 was 7.6%) was 14.1%. 3. When proper quantity of chemical admixture was used, the increment of tensile strength was as follows. High fluid admixture SP was 26.6% and the average increasing agents(SK was 16.0%, C376 was 14.7%, LG was 10%, C211 was 5.8%) was 11.6%. Also, in the condition of 28 days, high fluid admix SP was 16.5% and the average increasing rate of dispersing agents(LG was 19.1%, SK was 10.6%, C211 was 10.1%, C376 was 8.7%) was 12.1%. 4. As for the reducing ratio of each dispersing agent, he flow of mortar was less than the slump of concrete. That is; the reducing ratio of concrete was 15% adding each dispersing agent, but the reducing ratio of mortar was in the range of from 5.8% to 13.5% in 1 : 1 mixture, from 7.6% to 14.2% in 1 : 2, from 9.5% to 18.8% in 1 : 3. 5. The fluidity of each chemical admixture was as follows. High fluid admix SP in the condition of 1: 1 and 1 : 2 showed the best result than other dispersing agent and 1 : 3 showed the same result like other agents. Therefore these good dispersing agents were suitable in the prepact concrete construction using intrusion mortar.