• Journal of Welding and Joining
• /
• v.28 no.3
• /
• pp.79-85
• /
• 2010

Hardfacing is one of the frequently applying method to increase surface hardness in hot forging die. Recently, hardfacing receives great attention due to it's repair availability and low cost. In hot forging die, crack resistance and thermal shock resistance have been considered as major properties, However there are few studies for the assessment of these properties. So, it is necessary to establish the assessment method for crack resistance and thermal shock resistance in hardfacing for hot forging die. In this study, flux cored arc welding was applied to make hardfacing welds. Three point bending test was carried out to assess hardfacing weld's crack resistance, and high temperature bending test using salt bath was developed for thermal shock resistance. Consequently, it was possible to assess crack resistance and thermal shock resistance of hardfacing welds for hot forging die quantitatively.

• Journal of Welding and Joining
• /
• v.15 no.5
• /
• pp.134-143
• /
• 1997

The formation of thick alloyed layer with high Si content have been investigated on the surface of Al alloy (A5083) plate by PTA process with Si powder. Hardening characteristics and wear resistance of alloyed layer was examined in relation to the microstructure of alloyed layer. Thick hardened layer in mm-order thickness on the surface of A5083 plate can be formed by PTA process with wide range of process condition by using Si powder as alloying element because of eutectic reaction of Al-Si binary alloy. High temperature and rapid solidification rate of molten pool, which are features of PTA process, enable the formation of high Si content alloyed layer with uniform distribution of fine primary Si paticle. High plasma arc current was beneficial to make the alloyed layer with smooth surface appearance in wide range of powder feeding rate, because enough volume of molten pool was necessary make alloyed layer. Uniform dispersion of fine primary Si particle with about 30${\mu}{\textrm}{m}$ in particle size can be obtained in layer with Si content ranging from 30 to 50 mass %. Hardness of alloyed layer increased with increasing Si content, but increasing rate of hardness differed with macrostructure of alloyed layer. Wear resistance of alloyed layer depended on $V_{si}$(volume fraction of primary Si) and was remarkably improved to two times of base metal at 20-30% $V_{si}$ without cracking, but no more improvement was obtained at larger $V_{si}$.

• Journal of Welding and Joining
• /
• v.23 no.6
• /
• pp.72-76
• /
• 2005

Friction surfacing of STS304 consumable rod on S45C substrate was investigated by microstructural observation and mechanical tests. STS304 layer formed a strongly-bonded thick layer under a wide range of surfacing conditions. The highest coating eefficiency was obtained in the condition of 1000rpm-2.5mm/sec-2.5mm/sec. The hardness distribution showed the peak value in the boundary layer and as the consumable rotation speed increased, the boundary layer also hardness increasing. As the consumable rotation speed and the traveling speed increased, the coating efficiency tended to decrease. On the other hand, as the feeding speed increased, the coating efficiency appeared to be increased. The new Fe-Cr-Ni alloy layer is showed in the interface layer on $5\~15{\mu}m$ width. After friction surfacing, corrosion resistance of STS 304 surfacing layers were equaled to that of STS304 consumable rod.