• Journal of Adhesion and Interface
• /
• v.22 no.4
• /
• pp.118-127
• /
• 2021

In this study, the mechanical properties of vulcanized rubber were evaluated through compounding by controlling filler content to improve the mechanical properties of NBR rubber. Aramid and glass fibers with excellent heat resistance were used as fillers, and ceramics were additionally used in anticipation of a complementary effect, and as for the ceramic materials, needle-shaped and plate-shaped ceramics were used. Each filler was used in an amount of 5.0, 10.0, 15.0, and 20.0 phr in order to investigate the basic properties according to the amount of filler. To confirm the complementary effect through ceramic application, each 10.0 phr fiber and ceramic were mixed with 1:1 ratio to evaluate mechanical properties. As a result, it was confirmed that the decreasing ratio of tensile strength after heat aging was small in the order of aramid fiber, acicular ceramic, glass fiber, and plate ceramic in the case of applying the filler alone. In addition, the mechanical characteristics of vulcanized rubber using composite filler based on fibers and ceramics were evaluated, and it was confirmed that the composite filler had a complementary effect on thermal aging.

• Proceedings of the International Microelectronics And Packaging Society Conference
• /
• 2002.11a
• /
• pp.59-63
• /
• 2002

Zinc-Magnesium borosilicate 유리에 CaF$_2$입자를 충진재로 첨가하여 혼합체의 소결거동, 결정화 거동 및 최종 소결체의 마이크로파 유전특성을 측정하였다. CaF$_2$첨가는 유리의 점도를 감소 시켜 결정화 및 수축개시온도를 감소시켰다. 이러한 CaF$_2$의 최대 첨가량은 주어진 유리조성에 있어서 15 vol. % 이었다. 이러한 소결성 및 결정화 개시온도의 변화는 모 유리와 CaF$_2$의 반응에 의한 결과로 보여지며 이 반응은 결정상의 변화나 이차상의 형성에는 영향을 미치지 않았다. 따라서 유전율 6.1에 품질계수가 40000GHz 인 CaF$_2$입자를 15 vol.% 첨가시 유전상수는 7.1에서 5.6로 품질계수는 2200에서 5000GHz로 유전특성이 향상되었고 소결온도는 75$0^{\circ}C$이었다.

• Mineral and Industry
• /
• v.29
• /
• pp.1-17
• /
• 2016

점토광물은 자연 산출되는 광물로써 양이 풍부하고 가격이 저렴하여 여러 가지 산업자원으로써 오래전부터 다양하게 활용되어 왔다. 전통적인 주요 활용분야로는 제지 및 코팅 산업의 충진제, 내화재, 세라믹, 유리섬유, 시멘트 등에 90% 이상이 사용되어왔다. 최근에야 고무, 플라스틱 및 페인트의 물성 강화용 충진제로, 넓은 표면적을 활용한 촉매제로 일부 사용되고 있지만 대부분 판상용 점토광물을 대상으로 하고 있다. 고령토가 국내 생산 주요 품목에 들어가지만 그 비중은 2014년 기준 1.9%로 낮으며, 그나마 자급율도 77% 수준이라 수입에 의존하고 있다. 생산되는 고령토의 양이 매년 감소하고 있는 추세이며, 2014년 기준 고품질인 Wa와 Wb의 생산량이 각각 600 톤과 227 톤으로 미미한 수준이며 P급이 4.1만 톤 수준이라 부가가치가 매우 낮은 상품 중의 하나로 보인다. 다행히 우리나라에서 생산되는 고령토의 많은 부분이 할로이사이트 계열 고령토이고, 할로이사이트의 독특한 나노튜브 형태는 신소재 개발과 더불어 부가가치가 높은 새로운 활용분야를 개척하기 아주 적절한 광물이어서 그 특성과 산업적 활용 특성을 중심으로 최신 연구동향과 활용분야를 소개하고자 한다.

• Proceedings of the Korean Society of Propulsion Engineers Conference
• /
• 2009.05a
• /
• pp.103-106
• /
• 2009

Fracture characteristics of plate shape using shock tube for glass filled ceramics was carried out. Glass filled ceramics have been considered as a promising candidate material for the dome port cover of air breathing engine. This part of the air breathing engine has an important role separating solid and liquid fuel, and needs the frangible characteristics that the fracture of a part should not affect the internal components of combustion. The objectives of this study are to evaluate the fracture pressures for various thicknesses and diameters of shock impact area. Also fracture phenomena of separated membrane using a shock tube are observed. The experimental apparatus of shock tube consists of a driver, a driven section and a dump tank. The used material is glass filled ceramic made from Corning company. Specimens are used 3, 4.5 and 6mm thickness. Also diameters of shock wave area are chosen 70, 60 and 50 mm. It is expected that the results obtained from this study can be used in the basic data for the dome port cover design of an air breathing engine.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.33 no.11
• /
• pp.1274-1278
• /
• 2009

Fracture characteristics for plate and dome shapes of glass filled ceramics using shock tube were carried out. Glass filled ceramics have been considered as a promising candidate material for the dome port cover of air breathing engine. This part of the air breathing engine has an important role as separated membrane between combustion and external air, and needs the frangible characteristics that the particles of fractured glass filled ceramics should not affect the internal components of combustion. The objectives of this study are to evaluate the fracture pressures for various thicknesses and diameters of shock impact area. Also fracture phenomena of separated membrane using a shock tube compare with analytical method. The experimental apparatus consists of a driver, a driven section and a dump tank. The used material is glass filled ceramic made from Corning company. Specimens have the thickness of 3, 4.5 and 6mm. It is expected that the results obtained from this study can be used in the basic data for the dome port cover design of an air breathing engine.

• Journal of the Korean Ceramic Society
• /
• v.41 no.10 s.269
• /
• pp.766-770
• /
• 2004

High-transmittance film was coated by using spherical silica nano colloids. Silica colloid sol was preservred between two inclined slide glasses by capillary force, and particles were stacked to form a film onto the substrate as the upper glass was sliding. As the sliding speed increased, the thickness of the film decreased and light transmittance varied. The microstructure observed by SEM showed that silica particles were nearly close packed, which enabled the calculation of the effective refractive index of the film. The film thickness calculated from the wavelength of maximum transmittance and the effective refractive index was well coincided with the thickness observed by SEM and measured by profiler. The maximum transmittance of $94.7\%$ was obtained. This means that $97.4\%$ of transmittance or $1.3\%$ of reflectance can be achieved by simple process if both sides of the substrate are coated.

• Journal of the Korean Ceramic Society
• /
• v.38 no.9
• /
• pp.799-805
• /
• 2001

Two commercial alumina powders having different particle size of $0.5{\mu}m$ and 3${\mu}$m were presintered at 1120$^{\circ}$C for 2h and then lanthanum aluminosilicate glass was infiltrated at 1100$^{\circ}$C for up to 4h to obtain the densified glass-alumina composites. The effect of alumina particle size on packing factor, microstructure, wetting, porosity and pore size, and mechanical properties of the composite was investigated. The optimum mechanical properties and compaction behavior were observed for the 3${\mu}$m alumina particle dispersed composite. The 3${\mu}$m alumina particle size and distribution for he preform were within 0.1 to 48${\mu}$m and bimodal and random orientation. The strength and the fracture toughness of the composite having 3${\mu}$m alumina particles were 519MPa and $4.5MPa{\cdot}m^{1/2}$, respectively.

• Journal of the Korean Ceramic Society
• /
• v.39 no.2
• /
• pp.145-152
• /
• 2002

Four commercial alumina powders having different particle size of $0.5{\mu}m,\;2.8{\mu}m,\;12{\mu}m,\;and\;45{\mu}m$ were presintered at 1120$^{\circ}C$ for 2h and then lanthanum aluminosilicate glass was infiltrated at 1100$^{\circ}C$ for 2h in the interval of 0.1h to investigate the penetration kinetic of the glass into the alumina preforms. The infiltration distance is parabolic with respect to time as described by the Washburn equation and the penetration rate constant, K, increases with raising the alumina particle size. The strength of glass-alumina composites increases as the alumina particle size reaches to 2.8${\mu}m$ due to the increase in packing, however, decreases with further increasing the alumina particle size. The fracture toughness of the composites rises with increasing the alumina particle size due to the crack bowing and the interaction between crack and alumina particles.

• Journal of the Microelectronics and Packaging Society
• /
• v.6 no.3
• /
• pp.37-43
• /
• 1999

Co-firing incompatibility between the low temperature sinterable Glass/ceramic and Ag-thick film was studied. The dielectric material, which has been developed for microwave frequency applications, consists of $SiO_2-TiO_2-Bi_2O_3$-$Bi_2O_3$-RO system(RO:BaO -CaO-SrO) crystallizable glass and $Al_2O_3$as a ceramic filler. The large camber in the sintered specimen and cracks at the Ag-film under the influence of the camber occurred due to the difference of densification rate between the ceramic sheet and the Ag-film $B_2O_3$addition to the Glass/ceramic mixture reduced the severe camber. The cambers decreased with increasing the $B_2O_3$ content, and completely disappeared with 14 vol% $B_2O_3$addition. With additions of $B_2O_3$, $\varepsilon_{r}$ decreased abruptly, Q$\times$f value increased largely and the $\tau_f$ value of the material quickly shifted to positive one.