• Journal of the Korea institute for structural maintenance and inspection
• /
• v.21 no.5
• /
• pp.163-169
• /
• 2017

Although the strength of polyethylene terephthalate (PET) fibers which are generally used to make plastic bottles is low, the deformability of PET fibers is substantially high. Due to these material characteristics, a PET fiber can be used as a reliable strengthening material to resist a large deformation caused by earthquake and research pertinent to application of PET fibers is actively conducted in Japan. Therefore, in this study, experiments have been carried out to investigate the lateral confinement effect of PET fibers and to assess the applicability of PET fibers to construction fields by comparing the strengthening effect of PET fibers to that of carbon and glass fiber sheets. For this purpose, concrete cylinder specimens with parameters of different concrete strength and strengthening layers of carbon fiber sheets, glass fiber sheets, and PET fibers were respectively tested using two sets of cylinders for each parameter. As a result, specimens strengthened with carbon fiber sheets and glass fiber sheets failed due to sudden decrease of strength as with existing studies. However, specimens with PET fibers reached their maximum strength and then failed after gradual decrease strength without failure of PET fibers. In addition, although the strength of specimens with PET fibers did not significantly increase in comparison with that of specimens with carbon fiber sheets and glass fiber sheets, specimens with PET fibers indicated considerable deformability. Thus, a PET fiber can be considered as an effective strengthening material.

• Journal of the Korea Concrete Institute
• /
• v.19 no.6
• /
• pp.677-684
• /
• 2007

This study investigates the failure mechanism of RC beams strengthened with GFRP (glass fiber reinforced polymer) sheets. After analyzing failure mechanisms, the various methods to prevent the debonding failures, such as increasing bonded length of GFRP sheets, U-shape wrappings and epoxy shear keys are examined. The bonded length of GFRP sheets are calculated based on the assumed bond strengths of epoxy resin. The U-shape wrappings are either adopted at the end or center of the CFRP sheets bonded to the beam soft. The epoxy shear keys are embedded to the beam soft to provide sufficient bond strength. The end U-wrappings and the center U-wrappings are conventional, while epoxy shear keys are new details developed in this study. A total six half-scale RC beams have been constructed and tested to investigate the effectiveness of each methods to prevent debonding failure of GFRP sheets. From the experimental results, it was found that increasing bonded length or end U-wrappings do not prevent debonding failure. On the other hand, the beams with center U-wrappings and shear keys reached an ultimate state with their sufficient performance. The center U-wrappings tended to control debonding of the longitudinal GFRP sheets because the growth of the longitudinal cracks along the edges of the composites was delayed. In the case of shear keys, it was sufficient to prevent debonding and the beam was failed by GFRP sheets rupture.

• Journal of the Korean Society for Railway
• /
• v.12 no.3
• /
• pp.388-395
• /
• 2009

To investigate the flexural behavior of RC beams strengthened with glass fiber sheets, 1 control beam and 8 strengthened beams (4 NU-beams without U-shaped band and 4 U-beams with U-shaped band) are tested. The variables of experiment are composed of the number of glass fiber sheets and the existence of U-shaped band, etc. The maximum load was increased by 48% and 34%, and the flexural rigidity by 920% and 880% for NU-beam and U-beam, respectively, compared with those of the control beam. The ductility ratios were 1.43$\sim$2.60 for NU-beam and U-beam. The experimental results showed that the strengthening system with U-shaped band controls the premature debonding and provides a more ductile failure mode than the strengthening system without U-shaped band. It can be found from the load-deflection curves that as the number of fiber sheets is increased, the maximum strength and the flexural rigidity is increased. The experimental results are compared with the analytical results of nonlinear flexural behaviors for strengthened RC beam. The experimental and analytical results were well agreed.

• Journal of the Korean Wood Science and Technology
• /
• v.43 no.6
• /
• pp.861-867
• /
• 2015

The Compact Tension (CT) type test was performed in order to evaluate the fracture toughness performance of glass fiber-reinforced laminated timber. Glass fiber textile and sheet Glass fiber reinforced plastic were used as reinforcement. The reinforced laminated timber was formed by inserting and laminating the reinforcement between laminated woods. Compact tension samples are produced under ASTM D5045. The sample length was determined by taking account of the end distance of 7D, and bolt holes (12 mm, 16 mm, 20 mm) had been made at the end of artificial notches in advance. The fracture toughness load of sheet fiberglass reinforced plastic reinforced laminated timber was increased 33 % in comparison to unreinforced laminated timber while the glass fiber textile reinforced laminated timber was increased 152 %. According to Double Cantilever Beam theory, the stress intensity factor was 1.08~1.38 for sheet glass fiber reinforced plastic reinforced laminated timber and 1.38~1.86 for glass fiber textile reinforced laminated timber, respectively. That was because, for the glass fiber textile reinforced laminated timber, the fiber array direction of glass fiber and laminated wood orthogonal to each other suppressed the split propagation in the wood.

• Journal of Korea Foundry Society
• /
• v.27 no.6
• /
• pp.258-262
• /
• 2007

단섬유강화 고분자 복합재료의 고온압축 프레스 성형 시 유리섬유의 유동을 지배하는 인자인 유리섬유와 모재의 유동성에 관하여 연구하기 위하여 ?h트 스트랜드의 교차각도를 $30^{\circ},\;45^{\circ},\;60^{\circ}$로 배향하여 모재와 적층시킨 다음 열압축프레스를 사용하여 1차로 시트를 제작하고, 이 제작된 시트를 가열로로 가열하여 열압축프레스로 2차 고온압축 프레스 성형한다. 여기서, 압축속도와 압축비를 변화시켰을 때 발생되는 유리섬유의 배향에 관한 실험결과를 고찰한다.

• Magazine of the Korea Concrete Institute
• /
• v.14 no.2
• /
• pp.45-50
• /
• 2002

근년, 철근 콘크리트조 구조부재의 열화 및 건축물의 용도변경에 따라 건축물의 보수 및 보강에 관한 공법의 개발 및 그 효과를 검증하려는 연구가 활발히 진행되고 있다. 이에 따라, 보강공법으로서는 경제성ㆍ시공성 면에서 우수한 탄소섬유시트, 아라미드섬유 시트, 유리섬유시트 보강공법 및 FRP판 보강공법 등 합성수지 접착제를 사용하는 새로운 보강공법들이 폭넓게 연구되어 현장 실용화되어 사용 중에 있다. 그러나, 이들 보강공법에 관한 연구는 주로 구조적인 내력 보강효과 산정에 관한 것이 대부분이고 보강후의 내화성능 및 내구성능에 관한 연구는 매우 부족한 실정이다. 이들 보강공법은 주로 에폭시수지계 접착제에 의하여 콘크리트와 보강재의 접착력에 의하여 내력이 전달되는 메커니즘으로 되어있어 화재가 발생한 경우 내화피복이 없다면 접착제 자체의 연소에 의하여 유독가스의 발생 및 접착강도가 크게 저하되어 그 구조적인 보강성능은 급속히 저하할 것으로 판단된다. 또한, 현재 이들 보강공사는 내화성능의 검토 없이 실제 시공이 이루어지고 있으므로 화재시에는 대형참사를 일으킬 위험성이 있다.(중략)

• Journal of the Korea Concrete Institute
• /
• v.20 no.2
• /
• pp.239-247
• /
• 2008

Use of both carbon fiber (CF) and glass fiber (GF) at the same time to strengthen existing flexural members was exploited. Using a proper volumetric GF / CF ratio, the CF can rupture first followed by subsequent rupture of GF at higher stress and strain showing a pseudo-ductile behavior. A theoretical study indicated that the ratio is 4.62 : 1 and higher where the pseudoductile effect can be shown. Flexural tests of plain concrete beams strengthened using fibers were first carried out. Hybrid FRP sheet using 8.8 : 1 ratio was then fabricated and the sheet was used to strengthen reinforced concrete beams. The RC beams strengthened using 1-ply and 2-ply hybrid sheets both revealed increased strength over a non-strengthened beam and ductile flexural behavior. A comparable beam strengthened using CF also showed increased strength but with limited ductility.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.11 no.1
• /
• pp.130-140
• /
• 2007

Fiber-sheet and steel-plate strengthening methods have been mainly used for strengthening the RC structures. However, recently the application of these two methods have dramatically decreased due to premature debonding failure between concrete surface and fiber-sheet and heavy self-weight of steel-plate. This article presents experimental results of shear behavior in RC beams strengthened with GSP(Glass fiber-Steel composite Plate). The thin steel plate in GSP makes usage of the anchoring system possible, which could delay or prevent the premature debonding failure. Three reference beams and 60 strengthened beams with GSP were tested. The experimental results showed that strengthened beams with GSP considerably increased in shear capacity compared with the reference beams.

• Journal of the Korean Geosynthetics Society
• /
• v.1 no.1
• /
• pp.53-61
• /
• 2002

Even though a lot of laboratory and field tests for asphalt pavements using geosynthetics have been conducted recently, any rational and systematic analysis for the economic efficiency of the asphalt pavement systems reinforced by using geosynthetics has not been proposed yet. In this study, the economic analysis considering the traffic characteristics for the glass fiber sheet reinforced asphalt pavement was performed using the Life Cycle Cost Analysis(LCCA) which is commonly used for the economic analysis technique. The economic efficiency for the glass fiber sheet reinforcement and the traffic characteristics was examined by applying the test results from the literature review to the economic analysis model.

• Journal of the Korea Concrete Institute
• /
• v.21 no.1
• /
• pp.47-53
• /
• 2009

12 concrete blocks, on which hybrid fibrous sheets (carbon fiber and glass fiber) had been bonded, were subjected to tensile load in order to estimate properties of the bonded interface. the sheet length was varied by 100mm, 200mm and 400mm. It was found that more than 150mm bond length is required to achieve the maximum bearing capacity of the interface. In this study, maximum bond stress $\tau_{F,max}$, ultimate slip $S_{FU}$ of the interface were estimated $\tau_{F,max}$=3.0MPa and $S_{FU}$= 0.175mm, respectively.