• Journal of the korean academy of Pediatric Dentistry
• /
• v.35 no.3
• /
• pp.456-468
• /
• 2008

This study was performed to evaluate the quality of newly offered dentin bonding system($AdheSE^{(R)}$ One) by comparing the degree of microleakage measured with those of several conventional adhesive materials(AQ Bond Plus and $Adper^{TM}$ Single Bond 2). The quality of hybrid layer and resin tags was analyzed by observing restoration/ tooth interface under SEM. All-in-one system is in the limelight for having advantage of reducing chair time of children with difficult behavior pattern. Therefore the possibility of clinical application of All-in-one system was evaluated. The results obtained are as follows; 1. At the enamel margin, group II(AQ Bond Plus) showed the highest value of microleakage, and the other groups showed decreased value in order of group III($AdheSE^{(R)}$ One) and I($Adper^{TM}$ Single Bond 2). There was statistically significant difference between group II and the others(p<0.05), and no statistical difference was found between group I and III. 2. At the dentin margin, microleakage value was increased in order of group II, I, III and significant difference between all groups(p<0.05). 3. In group I and III, microleakage value measured at the enamel margin was significantly lower than that seen at the dentin margin(p<0.05), and there was no statistical difference in group II. 4. Resin tags observed under SEM were very weak and tangled in group II and III while the strong and thick tags were observed in group I. In conclusion, careful case selection and accurate clinical application is recommended in using AQ Bond Plus and $AdheSE^{(R)}$ One, giving consideration of the results showing its higher microleakage and weaker strength than $Adper^{TM}$ Single Bond 2.

• Restorative Dentistry and Endodontics
• /
• v.25 no.3
• /
• pp.359-370
• /
• 2000

The purpose of this investigation was to observe the viscoelastic properties of five commercial flowable(Aeliteflo, Flow it, Revolution, Tetric flow, Compoglass flow), three conventional hybrid(Z-100, Z-250, P-60) and two condensable(Synergy compact, SureFil) resin composites. A dynamic oscillatory shear test was done to evaluate the storage shear modulus (G'), loss shear modulus(G"), loss tangent(tan ${\delta}$) and complex viscosity(${\eta}^*$) of the resin composites as a function of frequency - dynamic frequency sweep test from 0.01 to 100 rad/s at $25^{\circ}C$ - by using Advanced Rheometric Expansion System(ARES). To investigate the effect on the viscosity of resin composites of filler volume fraction, the filler weight % and volume % were measured by means of Archimedes' principle using a pyknometer. The results were as follows 1. The complex viscosity ${\eta}^*$ of flowable resins was lower than that of hybrid resins and significant differences were observed between brands. The complex viscosity ${\eta}^*$ of condensable resins was higher than that of hybrid resins. The order of complex viscosity ${\eta}^*$ at ${\omega}$=10 rad/s was as follows, Surefil, Synergy compact, P-60, Z-250, Z-100, Aeliteflo, Tetric flow, Compoglass flow, Flow it, Revolution. The relative complex viscosity of flowable resins compared to Z-100 was 0.04~0.56 but Surefil was 30.4 times higher than that of Z-100. 2. The storage shear modulus G' and the loss shear modulus G" of flowable resins were lower than those of hybrid resins but those of condensable resins were higher. The patterns of the change of loss tangent, tan ${\delta}$, of resin composites with increasing frequency were significantly different between brands. The phase angles, ${\delta}$, ranged from $30.2{\sim}78.1^{\circ}$ at ${\omega}$=10 rad/s. 3. All composite resins represent pseudoplastic nature with increasing shear rate. 4. The complex shear modulus $G^*$ and the phase angle ${\delta}$ was represented by the frequency domain phasor form, $G^*({\omega})=G^*e^{i{\delta}}=G^*{\angle}{\delta}$. The locus of frequency domain phasor plots in a complex plane was a valuable method that represent the viscoelastic properties of composite resins. 5. There was no direct linear correlationship but a weak positive relation was observed between filler volume % or weight % and the viscosity of the resin composites.