• Proceedings of the Korean Fiber Society Conference
• /
• 1996.04a
• /
• pp.237-239
• /
• 1996

• Proceedings of the Korean Fiber Society Conference
• /
• 1995.10a
• /
• pp.92-92
• /
• 1995

• Polymer(Korea)
• /
• v.31 no.6
• /
• pp.518-525
• /
• 2007

The thermomechanical properties and morphologies of nanocomposite fibers of poly(ethylene terephthalate)(PET) incorporating thermally stable organoclays are compared. Dodecyltriphenyl-phosphonium-mica($C_{12}PPh-Mica$) and 1-hexadecane benzimidazole-mica ($C_{16}BIMD-Mica$) were used as reinforcing fillers in the fabrication of PET hybrid fibers. Dispersions of organoclays with PET were studied by using the in-situ polymerization method at various organoclay contents to produce nano-scale composites. The thermo-mechanical properties and morphologies of the PET hybrid fibers were determined using differential scanning calorimetry (DSC), thermogravimetric analysis (TGA), wide angle X-ray diffraction (XRD), electron microscopy (SEM and TEM), and a universal tensile machine (UTM). Transmission electron microscopy (TEM) micrographs show that some of the clay layers are dispersed homogeneously within the polymer matrix on the nano-scale, although some clay particles are agglomerated. We also found that the addition of only a small amount of organoclay is enough to improve the thermal stabilities and mechanical properties of the PET nanocomposite fibers. Even polymers with low organoclay content (<5 wt%) were found to exhibit much higher thermo-mechanical values than pure PET fibers.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2017.11a
• /
• pp.100-101
• /
• 2017

LEFC(Light Emotion Friendly Conceret) was developed in Korea with demands of esthentic requirements in line with the recent developmental trend of concrete technology. The LEFC is made by inserting transparent transparent rods, and this forms a heterogeneous structure in the concrete matrix causing the LEFC substrate to crack due low adhesion between the rod and the cement. In this study, as a way to strengthen the bonding to the rod inserted in the LEFC, high strength vinylon fibers of varying mixture ratios were applied and physical properties were tested accordingly. To study the effect of different spacing of the bars on the LEFC, physical property testing was conducted on respective specimens with two different diameters (5mm, 10mm) inserted in different intervals of spacing (10mm, 15mm, and 20mm).

• Proceedings of the Korean Fiber Society Conference
• /
• 2003.10b
• /
• pp.279-280
• /
• 2003

아크릴계 섬유를 포함하여 기존 섬유의 새로운 용도 창출 및 부가가치를 높이기 위하여 특수한 기능성을 나타내는 섬유들에 대한 관심이 꾸준히 증가하고 있다[1]. 이러한 이유로 유기물질과 무기물질의 복합체 제조는 일찍이 1980년대 초부터 연구되고 있고, 새로운 성능 및 기능 화대를 목표로 계속 이루어지고 있다[2]. 폴리아크릴로니트릴(Polyacrylonitrile, PAN)은 용액방사를 하는 대표적인 합성섬유로 담요, 카페트, 커튼 등 다양한 제품으로 응용되고 있으며, 그 성질이 천연섬유인 양모와 유사하기 때문에 양모 대체용으로 많이 사용되고 있다[1]. (중략)

• Journal of the Mineralogical Society of Korea
• /
• v.28 no.2
• /
• pp.165-171
• /
• 2015

Dust samples collected from air in metropolitan areas of Busan and Ulsan were analyzed by phase contrast microscopy, phase contrast dispersion microscopy and SEM. Asbestos concentration in dust samples was lower than detection limit. Many fibrous materials were observed in dust samples, but most of them were organic fibers. Inorganic fibers such as rock fiber, ceramic fiber and gypsum were contained in the samples and non-fibrous minerals such as quartz, calcite and feldspar were also occasionally observed. Domestic law requires that asbestos in air dust is mainly analyzed by phase contrast microscopy. From this study, however, precise analysis of asbestos was almost impossible by this method only. As indicated in JIS method of Japan, therefore, count and identification of asbestos were more efficient by dispersion staining method after removing organic materials in samples by low temperature incinerator.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.13 no.3 s.55
• /
• pp.119-126
• /
• 2009

This study investigated the fire resistance of RC columns applying Fiber addition method, Fire board attaching method, and Fire proof sparying method. The results were summarized as following. The test showed that increase of fiber content, as expected, decreased the fluidity of fresh concrete, but for the types of fiber, the specimens containing nylon(NY) was favorable. The incline of fiber content also affected on the air content of concrete, which the specimens adding polypropylene(PP) fiber was the lowest, followed by a less decrease in polyvinyl alchhol(PVA) and then NY respectively. For the compressive strength at 28days, it was over 50MPa and showed slight increasing tendency by rising fiber contents. After the fire test completed, control concrete exhibited the severe demage, while the specimens containing more than 0.05vol.% of PP and NY was able to protect from spalling. In the case of splay, the partly spalling occurred at the all finishing material, however the RC columns were protected from spalling. For the methods attached with boards, all RC columns were protected except the dry attaching method. The reduced weight ratio was favorable because it was below 8 % except for plain concrete.

• Proceedings of the Korean Fiber Society Conference
• /
• 2003.10b
• /
• pp.67-69
• /
• 2003

콘크리트는 경제성과 압축강도, 내구성 및 강성 등의 우수한 물성을 가지고 있으나 인장, 휨 및 충격강도가 낮고 에너지 흡수능력이 작아 취성적이며 균열에 대한 저항성이 작은 단점을 가지고 있다. 이러한 단점을 개선하기 위해서 각종 섬유를 콘크리트에 분산시켜 만든 섬유보강시멘트(FRC : Fiber Reinforced Cement)의 개발 및 이용이 활발히 진행되고 있다. PVA 섬유는 우수한 선형성, 입체구조의 간략함과 규칙성, 고결정성 그리고 우수한 접착성을 가지며, 유기 고분자로는 유일하게 PH 13.5이상의 격렬한 알칼리 조건에서도 거의 손상되지 않는 우수한 내알칼리성을 가지고 있다. (중략)

• Applied Chemistry for Engineering
• /
• v.7 no.3
• /
• pp.424-432
• /
• 1996

The fiber reinforced thermoplastic composites(FRTP) were prepared with polypropylene fiber(PPF) as matrix and vinylon(VF), Aramid(KF) or nylon fiber(PAF) as reinforcing materials using the integrated fiber mixing apparatus. The composite sheets were prepared by compression molding and their impact and morphological properties were characterized. VF/PP system showed the maximum value in Izod impact strength, while KF/PP system showed the maximum value in high rate impact properties. Ductility Index(DI) order was VF/PP>KF/PP>PAF/PP. A maximum DI for VF/PP, 2.43, was obtained when the weight fraction of VF was 20%. The optimum amount of the reinforcing organic fiber was found to be 20~30%. As a result, it is concluded that VF/PP system has better interfacial adhesion properties than either KF/PP or PAF/PP.

• Journal of the Korea Institute of Building Construction
• /
• v.16 no.3
• /
• pp.201-209
• /
• 2016

This study is to examine experimentally on the engineering properties of fiber reinforced concrete using kenaf(KN) fiber and another organic fibers for comparing test, and propose the usable method of KN fiber as an natural fiber in the concrete industry. It is to select 4 contents(0, 0.3, 0.6 and $0.9kg/m^3$) of KN fiber and 4 organic fibers (Jute, Cellulose, Polypropylene and Nylon). For this study, it is to perform various tests including slump, air content, plastic and drying shrinkage, flexural and tensile strength, carbonation depth for the fiber reinforced concrete according to contents of KN fiber and 4 organic fibers. The results of this study are as follows : In case of KN fiber contents $0.6kg/m^3$, it shows the effective results from increasing concrete strength including flexural and tensile, from decreasing plastic and drying shrinkage, carbonation depth. Also KN fiber is confirmed having excellent performances by comparing with test results of another organic fibers as same contents $0.6kg/m^3$. Therefore, considering concrete test results, cost and environment, KN fiber is proposed as the optimum contents in the range of $0.6kg/m^3$ and an effective fiber materials, and needs to keep up these study on the site application.