• Journal of the Korean Magnetics Society
• /
• v.15 no.3
• /
• pp.198-201
• /
• 2005

We investigated the effects of organic additives on the properties of nickel-copper thin films prepared by electroplating. Compared with thin films fabricated by pure electrolyte only, the films utilizing organic additives show different crystalline orientations. With no alteration of plating conditions simply adding the organic materials changed the composition of copper and nickel. The concentration of nickel could be varied to $65-95\%$ depending on the species and concentration of the additives. The change of material property has contributed to the increase or decrease of the magnetoresistance.

• Journal of the Korean Vacuum Society
• /
• v.20 no.5
• /
• pp.327-332
• /
• 2011

Plasma polymerized styrene (ppS) thin films were prepared on ITO coated glass substrates for a MIM (metal-insulator-metal) structure with thermally evaporated Au thin film as metal contact. Also the ppS thin films were applied as organic insulator to a MIS (metal-insulatorsemiconductor) device with thermally evaporated pentacene thin film as organic semiconductor layer. After the I-V and C-V measurements with MIM and MIS structures, the ppS revealed relatively higher dielectric constant of k=3.7 than those of the conventional poly styrene and very low leakage current density of $1{\times}10^{-8}Acm^{-2}$ at electric field strength of $1MVcm^{-1}$. The MIS structure with the ppS dielectric layer showed negligible hysteresis in C-V characteristics. It would be therefore expected that the proposed ppS could be applied as a promising dielectric/insulator to organic thin film transistors, organic memory devices, and flexible organic electronic devices.

• Proceedings of the KAIS Fall Conference
• /
• 2007.05a
• /
• pp.136-138
• /
• 2007

본 연구에서는 유기박막트랜지스터 (OTFT, Organic Thin film Transistor) 제작을 위한 채널막으로 pentacene의 soluble 공정 과 soluble 공정 올 통하여 제작된 pentacene 박막의 특성 을 분석 하여 유기박막트랜지스터에 적용 여부를 조사하였다. Pentacene을 용해시키기 위한 용제로는 toluene과 chloroform을 사용하였으며, 각각의 용제에 대하여 열처리를 하여 pentacene 용액을 준비하였다. Spin-coating 법으로 pentacene 유기 박막을 제작하여 각 박막의 결정화 특성을 관찰하였다. XRD 회절 분석 결과 chloroform 올 이용한 pentacene 박막에서만 결정화가 된 것이 확인이 되었다. Hall effect measurement 분석 결과 chloroform올 이 용한, pentacene 박막의 전하농도 (Carrier Concentration)는 $-3.225{\times}1014(c{\cdot}cm^{-3})$를 나타내었고, 이동도 (Mobility)는 $3.5{\times}10^{-l}(cm^2{\cdot}V^{-1}{\cdot}S^{-1})$를 각각 나타내었다.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2013.02a
• /
• pp.596-596
• /
• 2013

본 연구에서는 Carbon nanotube 용액을 brush-painting 시스템을 이용하여 유연성 있는 PET 기판 위에 고품위의 플렉시블 투명전극을 제작하였다. CNT 박막의 두께에 따른 특성을 알아보기 위해 brushing 횟수를 증가시켜 UV/Vis Spectrometry, four-point probe 및 Hall measurement를 이용하여 전기적, 광학적특성을 알아보았다. 최적조건인 bilayer의 CNT 박막은 244 Ohm/sq.의 면 저항과 550 nm에서 68％의 투과도를 얻을 수 있었다. CNT 박막의 기계적 응력에 따른 전기적 안정성을 알아보기 위해 bending test를 진행하였다. 10,000번 구부려도 저항의 변화가 거의 없어 이 박막이 플렉시블한 소자에 적합하다는 것을 알았다. 유기태양전지의 적용 가능성을 알아보기 위해 CNT 박막을 유기태양전지의 anode 층으로 적용하여 1.6％ (VOC: 0.566(V), $J_{SC}$: 7.118(mA/$cm^2$), Fill Factor: 40.49(％))의 효율을 얻어 유기태양전지 소자의 적용 가능성을 알았다. 최종적으로 실험에서 성막된 CNT 박막은 기존의 CVD공정과 같은 복잡한 공정 대신에 쉽고 간편하게 고품위의 flexible brush-painting Carbon nanotube (CNT) 투명전극을 제작 하여 플렉시블한 유기태양전지 소자의 가능성을 알아보았다.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2011.02a
• /
• pp.111-111
• /
• 2011

유기박막트랜지스터는 각 박막계면의 접촉성에 따라 그 성능이 좌우 된다는 것은 널리 알려진 사실이다. 이 때문에 계면간의 접촉성 및 결함을 최소화 하고 효율적인 패턴 형성을 위해 자기조립단분자막의 이용이 최근에 많이 시도되고 있다. 고품질 자기조립단분자막의 제작을 위해 RCA 세척을 통해 웨이퍼 표면에 OH기를 도입 보다 완벽한 단분자막의 형성을 촉진 하였으며 패턴제작은수분이엄격이조절된환경에서 alkyilsilane과 aminosilane 자기조립단분자막을 각각 ${\mu}CP$과 용액공정을 통해 시도되었다. 이 과정에서 물리적 흡착이나 OH기 부족으로 생성된 결함을 보안하기 위하여 SC1용액을 사용 단순 물리흡착된 자기조립단분자 물질의 제거와 다시 OH기 도입 용액공정을 통해 자기조립단분자막 형성을 반복적으로 실시하였다. 그 결과 자기조립단분자막의 결함이 최소화 되었고 자기조립단분자막의 질에 따라 유기전극재료 증착 시 선택적인 성장 과 형성된 유기전극재료 층의 형상이 다르게 관찰 되었다. 이런 반복적인 용액공정을 통해 결함이 최소화된 고품질 자기조립단분자막은 박막계면 간 옴성접촉을 형성하여 유기박막트랜지스터 제작 시 성능 향상이 기대되어진다.

• Journal of the Microelectronics and Packaging Society
• /
• v.6 no.1
• /
• pp.39-49
• /
• 1999

Monolayer thick fluorocarbon films were characterized by the contact angle measurements. The contact angles of three different liquids, water, formamide and diiodomethane were measured on spun coated, vapor phased deposited films and Teflon surface. The highest contact angle over $130^{\circ}$was observed on fluorocarbon films deposited on Al substrates while the lowest angles below $70^{\circ}$deposited on oxide. The surface energies were calculated based on Lewis acid /base theory. The surface energies of Teflon and spin coated FC films were calculated to have 18 and 8.4 dynes /cm, respectively. Higher energies of 31 to .35 dynes /cm were calculated on vapor phase deposited films on silicon and oxide. However vapor phase deposited films on aluminum only showed a large Lewis base energy term. It might be explained by the surface roughness and heterogeneity as observed by dynamic contact angles and AFM measurements.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2003.11a
• /
• pp.72-72
• /
• 2003

반점착막으로 활용되고 있는 불화유기박막의 형성을 ICP를 이용하여 나노미터로 성장시키고 이를 기계적/화학적 관점에서 특성평가를 수행했다. 증착된 불차유기 박막은 알루미늄 시편위에서 110도 근처를 나타냈으며 30도 근처의 낮은 히스테리시스를 보이는 안정한 박막이 형성되었다. 극성과 비극성 용액을 사용하여 표면에너지를 검사한 결과 약 20 mN/m 이하의 낮은 표면에너지를 얻을 수 있었다. AFM을 이용한 실험결과 표면의 점착력이 약 4nN으로 매우 낮은 점착력을 가짐을 확인 할 수 있었다. FTIR 실험결과 표면에 CF$_2$ 와 같은 불화유기 그룹이 발견되었다.

• 전기의세계
• /
• v.46 no.4
• /
• pp.15-21
• /
• 1997

이 논문에서는 기능성유기박막의 박막제조방법과 박막의 특성, 금후의 연구과제 등에 대해 기술하고자 한다.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2014.02a
• /
• pp.395.1-395.1
• /
• 2014

차세대 디스플레이 소자 기술로 많은 주목을 받고 있는 유기발광소자는 현재 전류효율 향상과 낮은 구동전압과 관련하여 연구가 활발하게 진행되고 있다. 음극과 양극 전극에서 유기물 층으로 전자와 정공의 주입이 많아져도 유기발광 층에서 재결합하는 전자와 정공의 균형이 맞지 않으면 전류 효율과 휘도가 낮아지는 문제점이 있다. 유기발광소자에서 홀 주입 층으로 사용하는 자기조립박막층은 일반적인 유기발광소자에서 정공의 이동도가 낮은 단점을 보완하여 발광층에서 전자와 정공의 균형을 향상하여 전류효율을 향상과 낮은 구동전압 특성을 나타낸다. 본 연구에서는 홀 주입 층으로 사용되는 각각의 자가조립박막을 형성할 물질이 용해되어 있는 에탄올 용액에 ITO를 담가 자가조립박막을 ITO 위에 형성 시킨다. 각각의 홀 주입 층으로 사용된 자가조립박막층의 chain group의 길이와 ITO와 결합하는 head group에 따라 달라지는 쌍극자 모멘트에 의한 홀 주입의 변화를 통해 각 소자의 전류효율과 구동전압 관찰할 수 있었다. 자가조립박막층의 chain group의 길이가 길어질수록 전극으로부터 유기물 층으로의 홀 주입을 방해하여 발광 층에서의 전자와 정공의 재결합 균형이 무너짐으로써 전류효율과 휘도가 낮아지는 경향을 볼 수 있었다. 이 연구 결과는 자가조립박막층을 홀 주입 층으로 대체하는 구조로 유기발광소자의 효율 향상에 대한 기초자료로 활용할 수 있다.

• Proceedings of the KIEE Conference
• /
• 2009.07a
• /
• pp.1336_1337
• /
• 2009

본 논문에서는 유기 박막 트랜지스터의 전극을 잉크젯 프린팅과 스크린 프린팅 방법을 이용하여 유기 박막 트랜지스터를 제작하였다. 전극으로 PEDOT:PSS와 Ag 잉크를 사용하였고, 게이트 절연막으로 polymethyl methacrylate (PMMA)와 poly(4-vinylphenol) (PVP)를 사용하였다. 유기물 활성층으로 pentacene을 진공 증착하였다. 잉크젯 프린팅 방법을 이용하여 제작한 유기 박막 트랜지스터는 전계이동도 (${\mu}_{FET}$) $0.068\;cm^2$/Vs, 문턱전압 ($V_{th}$) -15 V, 전류 점멸비 ($I_{on}/I_{off}$ current ratio) >$10^4$의 전기적 특성을 보였고, 스크린 인쇄 방법을 이용하여 제작한 유기 박막 트랜지스터는 전계이동도 (${\mu}_{FET}$) $0.016\;cm^2$/Vs, 문턱전압 ($V_{th}$) 6 V, 전류 점멸비 ($I_{on}/I_{off}$ current ratio) >$10^4$의 전기적 특성을 보였다. 이를 통하여 프린팅 방법을 이용한 유기 박막 트랜지스터 단일 소자 및 유기 전자 회로 제작의 가능성을 확인 하였다.