• Journal of Welding and Joining
• /
• v.5 no.1
• /
• pp.42-56
• /
• 1987

Fatigue Fracture behaviors of the TIG-welded aluminum alloys, such as Al 2024-T4, A1 5050-0 and Al 7075-T7 were investigated when a crack propagated from tensile residual stress region and compressive residual stress region. The experimental values were compared with the values expected by the Forman equation. The experimental results are summarized as the following: (1) In case of fatigue crack propagation from residual stress region, the values predicted by Forman equation were Found to exactly corresponded to the experimental values. (2) When the stress intensityfactors affected by compressive residual stress, Kres, were greater than the stress intensity factors by minimum applied stresses. Kmin, the Forman equation was found to be improper to be applied directly, but the equation appeared to be proper, if the stress ratio was modified to zero. (3) The experimental results confirmed that residual stress was relaxed by repeated tensile loading and the relaxing trend was greater in case of compressive residual stress than that of tensile residual stress.

• Proceedings of the Korean Reliability Society Conference
• /
• 2011.06a
• /
• pp.125-130
• /
• 2011

발전 설비는 기대 수명동안의 안정성을 확보하기 위하여 해당 규격에 부합하도록 설계하여 건설된다. 하지만 가동 중 다양한 복합 환경에 노출됨에 따라 구조물을 이루고 있는 재료의 열화 현상이 가속화되어 예기치 못한 파손이 발생할 수 있다. 기계적 물성은 재료의 기계적 거동을 나타내는 주요 척도가 되며 이는 신뢰성 및 안전과 직결된다. 하지만 기존의 역학물성을 측정하는 대부분의 시험법들은 특정 크기의 시편을 요구하고 파괴적인 시험법이기 때문에 가동 중 시설물에 적용하기가 불가능하였다. 이러한 한계점을 극복하고자 비파괴적이고 정량적인 시험이 가능한 연속압입시험법이 최근 각광받는 시험법으로서 많은 연구자들에 의해 연구되고 있다. 이 시험법은 시험 대상물의 형상에 제약을 받지 않으며 시험 절차가 매우 간단하다는 장점을 가진다. 또한 대상의 국소 부위에 시험할 수 있어 취약 부위 판별이 가능하다. 본 연구에서는 대표응력-대표변형률 기법을 통하여 인장물성을 평가하고, 압입 하중 차이를 이용하여 소재에 존재하는 잔류응력을 평가하는 기법을 소개한다. 또한, 연속압입시험을 이용하여 실제 발전소 파이프의 취약부위로 알려진 용접부에 대하여 인장물성 및 잔류응력을 측정함으로써 실제 산업체의 신뢰성 평가가 적용할 수 있음을 확인하였다.

• Journal of the Korean Society for Nondestructive Testing
• /
• v.26 no.5
• /
• pp.306-314
• /
• 2006

Instrumented indentation technique is a new way to evaluate nondestructive such mechanical properties as flow properties, residual stress and fracture toughness by analyzing indentation load-depth curves. This study evaluated quantitatively the flow properties of steels and residual stress of weldments. First, flow properties can be evaluated by defining a representative stress and strain from analysis of deformation behavior beneath the rigid spherical indenter and the parameters obtained from instrumented indentation tests. For estimating residual stress, the deviatoric-stress part of the residual stress affects the indentation load-depth curve, so that by analyzing the difference between the residual-stress-induced indentation curve and residual-stress-free curve, the quantitative residual stress of the target region can be evaluated. The algorithm for flow property evaluation was verified by comparison with uniaxial tensile test and the residual stress evaluation model was compared to mechanical cutting and ED-XRD results.

• Journal of Korean Society of Steel Construction
• /
• v.18 no.3
• /
• pp.395-403
• /
• 2006

Recently constructed bridges often have long spans and simple structure details considering not only the function but other important factors such as aesthetics, maintenance, construction duration and life cycle cost. Therefore, bridges require high-performance steels like extra-thick plate steels and thermo-mechanical control process (TMCP) steels. TMCP stels are now gaining wide attention due to their weldability improved strength and toughness. Recently, SM570-TMC steel, which is a high-strength TMCP steel with a tensile strength of 600 MPa, has been developed and applied to steel structures. However, using this steel in building steel structures requires the elucidation of not only material characteristics but also the mechanical characteristic of welded joints. In this study, high-temperature tensile properties of SM570-TMC steel were investigated through the elevated temperature welded joints of SM570-TMC steel were studied through the three-dimensional thermal elasticplastic analyses on the basis of mechanical properties at high temperatures obtained from the experiment.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.36 no.6
• /
• pp.599-608
• /
• 2012

A numerical analysis has been performed through implicit dynamic finite element analysis using the commercial package, ABAQUS in order to investigate effect of laser peening on welding residual stress mitigation of dissimilar metal welds in a safety injection nozzle of integral reactor. The implicit dynamic finite element analysis are compared with the previous experimental results. By comparison, it is identified that the implicit dynamic finite element analysis is valid for residual stress mitigation via laser peening. Implicit static finite element residual stress analysis has been performed for the dissimilar metal welds subject to inner repair welding. The analysis results represent that both axial and hoop residual stresses are tensile on inner surface of safety injection nozzle due to inner repair welding. Also Parametric study has performed to investigate effect of laser peening variables such as maximum impact pressure, duration time of pressure, spot diameter and peening direction on the welding residual stress mitigation. As a result, it is found that laser peening has the preventive maintenance effect to mitigate mainly residual stresses of region near inner surface.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.30 no.7 s.250
• /
• pp.826-832
• /
• 2006

For the improvement of safety and endurance in welded steel structure, it is needed to consider welding residual stress distribution and rolling directional characteristics of materials. In this study, it was investigated experimentally about characteristics of fatigue crack propagation according to welding residual stress and rolling in FCAW(flux cored arc welding) butt-jointed steel plates. SS400 steel plates of 3mm thickness were selected and tested for this study. When the angles between tensile loading direction and rolling direction in welded materials are increased from $0^{\circ}\;to\;90^{\circ}$, their fatigue crack propagation rates are increased. These results are same as predicted increments of fatigue crack propagation rate when stress ratio is increased from 0 to 0.5. When the angles of rolling direction and welding direction to tensile loading direction are $0^{\circ}\;and\;90^{\circ}$ respectively, fatigue crack propagation rate in welded material is lowest.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.36 no.10
• /
• pp.1115-1130
• /
• 2012

In nuclear power plants, the reactor pressure vessel (RPV) upper head control rod drive mechanism (CRDM) penetration nozzles are fabricated using J-groove weld geometry. Recently, the incidences of cracking in Alloy 600 CRDM nozzles and their associated welds have increased significantly. The cracking mechanism has been attributed to primary water stress corrosion cracking (PWSCC), and it has been shown to be driven by welding residual stresses and operational stresses in the weld region. The weld-induced residual stress is the main factor contributing to crack growth. Therefore, an exact estimation of the residual stress is important for ensuring reliable operation. This study presents the residual stress computation performed for an RPV CRDM penetration nozzle in Korea. Based on two and three dimensional finite element analyses, the effect of welding variables on the residual stress variation is estimated for sensitivity analysis.

• Journal of Power System Engineering
• /
• v.5 no.1
• /
• pp.80-88
• /
• 2001

The spot welding method has been used in the joining of structures, automotive body, railway carriage, aircraft, household electric appliances, precision parts etc., because of brief working, easy automation, available mass production, and convenience. In this paper, the effects of welding conditions on the fatigue life and the prediction of fatigue life based on fracture mechanics theory of spot welded joint were investigated. Fatigue tests were conducted with the tensile-shear specimens welded in the various current using cold rolled steel sheets. Fatigue life of spot welded joint was predicted and compared with experimental results. Using FEM(finite element method), we analysed the distribution of stress and the condition of deformation on the environments of nugget.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.35 no.10
• /
• pp.1179-1185
• /
• 2011

Cold and hot-rolled carbon steel sheets are commonly used in railroad cars or commercial vehicles such as the automobile. The sheets used in these applications are mainly fabricated by spot welding, which is a type of electric resistance welding. However, the fatigue strength of a spot-welded joint is lower than that of the base metal because of high stress concentration at the nugget edge of the spot-welded part. In particular, the fatigue strength of the joint is influenced by not only geometrical and mechanical factors but also the welding conditions for the spot-welded joint. Therefore, there is a need for establishing a reasonable criterion for a long-life design for spot-welded structures. In this thesis, ${\Delta}P-N_f$ relation curves have been used to determine a long-life fatigue-design criterion for thin-sheet structures. However, as these curves vary under the influence of welding conditions, mechanical conditions, geometrical factors, etc. It is very difficult to systematically determine a fatigue-design criterion on the basis of these curves. Therefore, in order to eliminate such problems, the welding residual stresses generated during welding and the stress distributions around the weld generated by external forces were numerically and experimentally analyzed on the basis of the results, reassessed fatigue strength of gas welded joints.

• Journal of Korean Society of Steel Construction
• /
• v.11 no.3 s.40
• /
• pp.319-327
• /
• 1999

This study makes mechanism of the fatigue strength improvement by the processing of weld toe clear for the vertical cross rib specimens which was made fillet weld joint, also it proposes to the appropriate later processing. As a result of tension fatigue test, the fatigue strength improvement could have been seen in later processed specimens than as-weld specimens. Especially fatigue crack initial life $N_c$ increased in specimens which processed grinder after hammer-peening. Also, fatigue crack propagation life $N_p$ improved more in hammer-peening specimens than as-weld or TIG specimens. It thinks that $N_c$ is because of the geometrical shape of weld toe, i.e. the relaxation of the stress concentration and also that $N_p$ is because the big compression residual stress which was introduced in the surface by hammer-peening is restraining the propagation of fatigue crack.