• Proceedings of the KWS Conference
• /
• 2005.11a
• /
• pp.38-40
• /
• 2005

Fracture mechanics evaluation of stress corrosion cracking (SCC) in the dissimilar metal weld (DMW) for the nuclear piping system is performed; simulating the transition joint of the ferritic nozzle to austenitic safe-end fabricated with the Inconel Alloy A82/182 buttering and welds. Residual stresses in the DMW are computed by the finite element (FE) analyses Then, to investigate the SCC in the weld root under the combined residual and system operation stresses, the fracture mechanics parameters for a semi-elliptical surface crack are evaluated using the finite element alternating method (FEAM). As a result, it is found that the effect of weld residual stresses on the crack-driving forces is dominant, as high as three times or more than the operation stresses.

• Proceedings of the KWS Conference
• /
• 1999.05a
• /
• pp.241-244
• /
• 1999

The purpose of this study is to examine the characteristics of stress corrosion cracking(SCC) and acoustic emission(AE) signals for the weld HAZ of HT-60 steel under corrosion control in synthetic seawater. Corrosive environment was controlled by potentiostat, and SCC experiment was conducted using a slow strain rate test method at strain rate of 10$^{-5}$ /sec. In order to verify the miroscopic fracture behaviour of the weldment during SCC phenomena, AE test was done simultaneously. Besides, correlationship between mechanical parameters and AE ones was investigated. In case of the parent, reduction of area(ROA) at -0.5V was samller than any other applied voltage such as -0.8V and -1.1V. In addition, reduction of area for the PWHT specimens at -0.8mV was larger than that of the weldment due to the softening effect according to PWHT. In case of the weldment, a lots of events was produced because of the singularities of the weld HAZ compared with the parent.

• Journal of the Korean Society of Manufacturing Process Engineers
• /
• v.5 no.3
• /
• pp.58-64
• /
• 2006

The security of stability for fractures of all sorts of parts and structure has become a first subject these days. We have need to organize fatigue characteristics of weldment because fatigue break out suddenly without a change of shape. In this study, we execute the fatigue test according to different of the welding method at the same materials. It was investigated about a fatigue limit according to welding methods of SMAW, FCAW and SAW at normal temperature and a frequency of 10Hz. The important results of the experimental study on fatigue characteristics of weldment are as follows: The fatigue limit of welding methods became low in the order of SMAW, FCAW, SAW.

• Proceedings of the KWS Conference
• /
• 2001.10a
• /
• pp.65-68
• /
• 2001

Corrosion and tensile properties of zircaloy-4 cladding tube having a laser welding part in elevated temperature are studied to present the criterion of quality evaluation in nuclear reactor and to found the scientific basis of SCC, with laser welding method using by coupling up cladding tube to end cap. In the result of tensile test(40$0^{\circ}C$), the fracture is not happened in the welding part but base metal and the result of corrosion test(40$0^{\circ}C$ 1500psi steam), corrosion rate of the molten zone and PMZ is a little higher than the other zone

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.35 no.10
• /
• pp.1337-1345
• /
• 2011

In pressurized water reactors (PWRs), the reactor pressure vessel (RPV) upper head contains numerous control rod drive mechanism (CRDM) nozzles. In the last 10 years, the incidences of cracking in alloy 600 CRDM nozzles and their associated welds has increased significantly. Several axial and circumferential cracks have been found in CRDM nozzles in European PWRs and U.S. nuclear power plants. These cracks are caused by primary water stress corrosion cracking (PWSCC) and have been shown to be driven by welding residual stresses and operational stresses in the weld region. Therefore, detailed finite-element (FE) simulations for the Korea Nuclear Reactor Pressure Vessel have been conducted in order to predict the magnitudes of the weld residual stresses in the tube materials. In particular, the weld residual stress results are compared in terms for nozzle location, geometry factor$r_o$/t, geometry of fillet, and adjacent nozzle.

• Transactions of the Korean Society of Pressure Vessels and Piping
• /
• v.7 no.4
• /
• pp.1-11
• /
• 2011

This paper presents the effects of preventive maintenance schemes on the residual stress distributions in dissimilar metal welds. Dissimilar metal weld is known susceptible to PWSCC and thus, effective maintenance schemes to prevent PWSCC are needed. Three preventive maintenances schemes, i.e. weld overlay, MSIP and inlay weld which are widely used in nuclear power plants, are selected and their effects on welding residual stresses are investigated via finite element analyses. As results, weld overlay and MSIP were proved effective method to mitigate residual stresses and inlay weld, on the other hand, produces strong tensile residual stresses in the inner surface. Although Alloy 690 known to be resistant to PWSCC are used in inlay weld, continuous careful observation are needed since tensile welding residual stresses are key parameter for PWSCC.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.35 no.5
• /
• pp.543-547
• /
• 2011

Primary water stress corrosion cracking has occurred in dissimilar weld areas in nuclear power plants. Residual stress is a driving force in the crack. Residual stress may be generated by weld or surface machining. Residual stress due to surface machining depends on the machining method, e.g., milling, grinding, or EDM. The stress is usually distributed on or near the surface of the material. We present the measured residual stress for machining on SA 508 and austenitic stainless steels such as TP304 and F316. The residual stress can be tensile or compressive depending on the machining method. The depth and the magnitude of the residual stress depend on the material and the machining method.

• Journal of Ocean Engineering and Technology
• /
• v.11 no.2
• /
• pp.57-69
• /
• 1997

The objetive of this study is to compare the mechanical proprties of 6000 series Al-Mg-Si aluminum alloy (AC120) with 5000 series Al-Mg aluminum alloy (TG25), and to investigate the influence of corrosion solution for fatigue life. Comparing of TG25 and AC120 alloy sheets, TG25 alloy sheets showing higher plastic ratio and total elongation have better formability than AC120 alloy sheets. The hardness of nugget area was a little higher than that of base metal area. Also, grain coarsening was observed in HAZ(Heat Affected Zone). In a corrosion fatigue experiment, the fatigue life decreased as concentration increased, when a dipping time was constant. The life decreased as dippling time increased, when a concentration was constant.

• Journal of the Korean Institute of Gas
• /
• v.9 no.4 s.29
• /
• pp.11-16
• /
• 2005

In this paper, the hydrogen osmosis test and the mechanical tensile test were carried out to examine hydrogen cracking behavior of STS444 with welding conditions. In $0.5MH_2SO_4+0.001M \;As_2O_3$ solution, the hydrogen embrittlement characteristics of weld zone of STS444 added to load of $1,400 kg/cm^2$ together with hydrogen osmosis by current of $30mA/cm^2$ for 60 min. was considered. As a result of study on the hydrogen embrittlement and mechanical characteristics of STS444외와 with welding conditions the tensile stress and elongation of STS444 get lower by the absorption of oil or water before welding. Also, the reduction rate of tensile stress and elongation of STS444 is larger because of hydrogen embrittlement by the absorption of oil or water. STS444 by the absorption of water before welding is more sensitive to hydrogen embrittlement than oil.

• Journal of Ocean Engineering and Technology
• /
• v.21 no.5
• /
• pp.39-46
• /
• 2007

The sea water pipe of a ship's engine room is a severely corrosive environment caused by fast flawing sea water containing chloride ions and high conductivity. Therefore, leaking of sea water may occur as a result of local corrosion of the welded zone. Leaking is usually controlled by various welding methods. In this study, when the sea water pipe is welded with certain welding methods and welding electrodes, the corrosion resistance of WM (Welding metal) and HAZ (Heat affected zone) was investigated using electrochemical methods. Although the corrosion potential of the HAZ is higher than that of WM, the corrosion resistance of WM is superior to HAZ. However, when WM and HAZ are both opened to the sea water, the WM part with the anode was more seriously corroded than was the HAZ of the cathode by performance of a galvanic cell due to difference of the corrosion potential between HAZ and WM. In particular TIG welding showed relatively good results in corrosion resistance of both HAZ and WM compared to other welding methods.