• 한국분말재료학회지
• /
• 제7권1호
• /
• pp.42-49
• /
• 2000

Densificationbehavior of conventional austenitic stainless steel powder compacts was studied by comparing the relative density of sintered compact(Ds)with that of green compacts(Dg)prepared with various catbon contents and P/M process. Dg of 304and 316 powders by warm compaction under pressure of 686 MPa at heating temperature of powder(553K) and dies (573K) were 80% and 81%, repectively, whichwere 2 and 3% higher than those of conventional green compacts at the same pressure. Ds of 304 compacts sintered at 1373K in H2 gas has the same value of 84% max. regardless of compacting temperature, and Ds of 316 compacts at the same sintering conditions were 80% by conventional compaction and 83% by warm compaction. Oxygen contents of 304 and 316 sintered compacts were increased 1.43∼2.94% and 0.010∼0.921% higher than those of raw powders and warm green compacts, respectively. In other case, Ds of 316 compacts sintered at 1573K in vacuum had the same value of 86%max. And Ds of 316 compacts at the same sintering conditions were 83% and 86% by conventional and warm compaction, respectively. Oxygen contents of 304 sintered compacts were 0.321% and 0.360%, and in case of 316, they were 0.419% and 0.182% by the respective compating condition. With carbon additions in the range 0.1∼0.6% Ds increased to the extent of 86∼89% in 304 sintered compacts, and to 82∼84% and 85∼87% in 316 according to different two compacting peocesses compared to those of sintered compacts without carbon addition.

• 소성∙가공
• /
• 제24권1호
• /
• pp.5-12
• /
• 2015

In the current study, fundamental deep drawing characteristics of Ti-6Al-4V alloy sheets were investigated to establish the effect of processing conditions on large size square deep drawn cups. To accomplish this study, FE-simulations (Abaqus) were performed to determine optimum blank size, friction coefficient, the gap between punch and die, etc. The simulated processing parameters were verified experimentally. Based on the FE-simulation results, deep drawing was performed with various blank holding loads and sample sizes. In order to improve the formability of Ti-6Al-4V sheet, various lubricant methods were evaluated. Tensile tests and thickness measurements were conducted on the formed sheets. Processing parameters including blank holding force, lubricants, and optimum blank size, were selected to achieve improved drawing quality. With the optimum processing condition, a $200mm{\times}200mm$ cup was deep drawn successfully.

• 소성∙가공
• /
• 제9권6호
• /
• pp.670-680
• /
• 2000

The purpose of this study is to provide the database of forming limit diagram applicable to the warm forming of oil pan. The test materials are SCP1 and SCP3C with the thickness of 1.4mm which is used for the oil pan of automobile. The testing temperature is 5$^{\circ}C$~15$0^{\circ}C$ which is In the range of practical usage. The results are the forming limit diagram limiting dome height and the maximum punch load at each temperature such as 5$^{\circ}C$, $25^{\circ}C$, 6$0^{\circ}C$, 9$0^{\circ}C$, 12$0^{\circ}C$ and 15$0^{\circ}C$. From these results, we can see that the forming limit curves are translated depending upon the temperature and that FLC at low temperature is higher than at high temperature. Both of limiting dome height and maximum punch load also decrease as the temperature increases. Present results can be useful for die trial and forming analysis as a tool of evaluating the forming severity for the sheet metal forming processes at the warm working condition by comparing the practical strains with FLC.

• 한국소성가공학회:학술대회논문집
• /
• 한국소성가공학회 2005년도 춘계학술대회 논문집
• /
• pp.407-410
• /
• 2005

The drawability of AZ31B magnesium sheet is estimated according to the variable temperatures (200, 250, 300, 350 and $400^{\circ}C$), forming speed (20, 50, 100 mm/min), thickness (0.8, 1.4 t), blank holding force (1.0, 1.4, 1.7kN). The deep drawing process (DDP) of circular cup is used in forming experiments. The results of deep drawing experiences show that the drawability is well at the range from 250 to $300^{\circ}C$, 50mm/min forming speed and 1.4kN blank holding force. The 0.8t magnesium sheets were deformed better than 1.4t. BHF was controlled in order to improve drawability and protect the change of cup thickness. When BHF was controlled, tearing and thickness change were decreased and LDR. was improved from 2.1 to 3.0.

• 한국자기학회지
• /
• 제21권2호
• /
• pp.77-82
• /
• 2011

우리 삶의 질을 좌우하는 전자기 기기의 고기능화, 자동화, 소형화 추이에 따라 사용량이 급격히 증가하고 있는 연자성 소재로서 가장 널리 사용되고 있는 전기강판과 에너지 고효율화라는 시대의 요구에 따라 새롭게 부상되고 있는 연자성 복합 분말 소재에 대해 각 연자성 소재 분야에서 철손 제어 인자 및 이들 인자들의 제어 방안에 대해 문헌을 고찰했다. 전기강판에서는 히스테리시스 손실을 낮추기 위해 정련공정을 통해 자구이동을 방해하는 결함을 제거하고 결정립의 크기를 최적화하고 있으며, 와전류 손실의 감소를 위해 합금첨가원소를 통해 비저항을 높이고 판재의 두께를 박판화하고 있다. 이와 동시에 코팅을 통해 자구의 이동이 용이하도록 응력의 방향 및 크기를 제어하며, 압연기술과 열처리 기술을 통해 집합조직을 최적화하여 고투자율 및 저철손을 동시에 충족시켜 나가고 있다. 연자성 복합 분말 소재의 경우, 분말 표면의 복합화를 통해 철계 조성, 코팅, 윤활재 및 바인더, 성형 및 열처리 조건 등에 복합적으로 의존하는 연자성 코어의 최종 자기특성을 제어하고 있다. 온간 및 다단 성형과 같은 새로운 성형공정, 2단 소둔/자성 열처리와 같은 소둔 조건, 나노결정질, 비정질 및 벌크 비정질 등과 같은 새로운 조성, 적절한 코팅층의 변수들을 최적화할 경우, 연자성 복합 소재의 자성특성은 향상될 것으로 기대된다.

• 한국산학기술학회논문지
• /
• 제11권1호
• /
• pp.49-54
• /
• 2010

자동차의 A.C 제너레이터(alternating current generator) 부품으로 사용되는 로터폴(rotor pole)을 가공할 때는 트랜스퍼온간단조금형(transfer warm forging die)으로 성형한다. 소재를 온간가공 영역으로 가열한 후 즉시 금형안으로 이송시켜 제1스테이지(1st stage)에서 업세팅가공(upsetting work)하고 제2스테이지(2nd stage)로 이송하여 측방압출(lateral extrusion)가공을 한다. 이때 측방압출 스테이지의 금형에서 다이블록(die block), 다이부싱(die bushing), 센터펀치(center punch), 사이드펀치(side punch)의 접촉면이 압출시의 과혹(過酷)한 조건에 견디지 못하여 쉽게 마멸(abrasion)되어 금형수명(die life)을 단축시키고 있다. 이 때문에 생산량 감소로 인한 납기지연, 금형의 수리보수시간 과다, 제품의 정밀도 저하 등의 문제점이 발생되고 있다. 이러한 문제점을 해결하기 위하여 금형재질 선정과 열처리 작업 싸이클 개선, 방전가공시의 트러블 해소, 핵심부품의 구조변경 등을 연구하여 금형수명을 40~50% 연장 하고자 하였다.