• Applied Chemistry for Engineering
• /
• v.16 no.6
• /
• pp.809-814
• /
• 2005

In this work, the thermal properties of epoxy coating system on the liner plate in the containment structure of nuclear power plants had been examined by irradiation and design basis accident (DBA) conditions. The effect of immersion in hot water on adhesion strength of the coating system had been also studied. The glass transition temperature ($T_g$) and thermal stability of ET-5290/carbon steel A 32 epoxy coating systems were measured by DSC and TGA analyses, respectively. Contact angle measurements were used to determine the effect of immersion on the surface energetics of epoxy coating system, with a viewpoint of surface free energy. Adhesion tests were also executed to evaluate the adhesion strength at interfaces between carbon steel plate and epoxy resins. As a result, it was found that the irradiation led to an improvement of internal crosslinked structure in cured epoxy systems, resulting in significantly increasing the thermal stability, as well as the $T_g$. Also, the immersion in hot water made a role in the post-curing of epoxy resins and increased the mechanical interlocking of the network system, resulting in increasing the adhesion strength of the epoxy coating system.

• Applied Chemistry for Engineering
• /
• v.9 no.5
• /
• pp.704-709
• /
• 1998

Non-linear optical polymer based on poly (${\alpha}$-methylstyrene-co-maleic anhydride) (MSMA) substrate polymer was prepared by polymer reaction method and its thermal and electro-optic properties were examined. In the polymer reaction between MSMA substrate polymer and 2-[4-(4-nitrophenylazo)-N-ethylphenylamino]ethanol (DR1) chromophore, the degree of substitution of DR1 into MSMA was higher with the 4-dimethylaminopyridine (DMAP) as catalyst and 3-dicyclohexyl carbodiimide (DCC) as dehydrating agent (sample, MSMA-DC) than the one with just 4-dimethylaminopyridine as catalyst (sample, MSMA-D). The synthesized NLO polymer (MSMA-DC) exhibited electro-optic coefficient of 18 pm/V (632.8 nm) and glass transition temperature ($T_g$) of about $175^{\circ}C$.

• Applied Chemistry for Engineering
• /
• v.25 no.1
• /
• pp.90-95
• /
• 2014

Nylon66 extrudates as a function of the extrusion number were prepared by a twin screw extruder. Chemical structures, thermal properties, melt index, crystal structures, mechanical properties such as the tensile strength, elongation at break and impact strength, and rheological property were measured by FT-IR, $^1H$-NMR, melt indexer, DSC, TGA, XRD, universal tensile tester, Izod impact tester, and rheometer. FT-IR and $^1H$-NMR characterizations indicated that the number of extrusions did not affect the chemical structure. The decrease in the molecular weight was checked by the melt index of extrudates. There were no effects of the thermal history on the melting and degradation temperature. The tensile and impact strength and modulus were found to be similar, regardless of the number of extrusions, but the elongation decreased significantly. The complex viscosity of extrudates at low frequencies decreased with the extrusion number. No structural changes after extrusion were confirmed from the fact that there was no change in the slope and shape of G'-G" plot.

• Applied Chemistry for Engineering
• /
• v.25 no.1
• /
• pp.72-77
• /
• 2014

Microstructure and thermal stability of mechanically ball milled $FeS_2$ were investigated. The average particle size and distribution of $FeS_2$ powder were changed in two steps with the increased ball milling time. The average particle size drastically decreased from $98.4{\mu}m$ to 1.01 and $0.89{\mu}m$ after ball milling of 10 h and 30 h, respectively. However, the distribution was broad and a shoulder appeared at $2{\mu}m$ because the pulverization was still in process at 10 h ball milling. After 60 h ball milling, the distribution became narrower. After ball milling of 120 h, the average particle size increased because of $FeS_2$ particle agglomeration. Therefore, the particle size distribution became broaden again. Finally, after ball milling of 170 h, $FeS_2$ with the narrowest size distribution can be obtained. Thermal stability of $FeS_2$ was unstable as the $FeS_2$ particle was pulverized. Therefore, the activation energy of the fine size particles is 27% lower than that of the as-received $FeS_2$.

• Applied Chemistry for Engineering
• /
• v.23 no.2
• /
• pp.217-221
• /
• 2012

Blending films having enhanced water-resistance and barrier properties were prepared using the mixtures of poly(vinyl alcohol) (PVA) aqueous solution and poly(ethylene-co-acrylic acid) (EAA) dispersed in water. Thermal-mechanical properties, contact angles, water-vapor transmission rates (WVTR) and oxygen transmission rates $(O_2TR)$ were measured with the content of EAA of blending films, and their water-resistance was evaluated. The tensile strength of the films was found to be $9.16{\sim}11.75\;kg/mm^2$ which showed no significant difference compared with that of PVA, and the hardness increased with the content of EAA. The glass transition temperature and melting temperature of the blending films were slightly improved. The film prepared with PVA/EAA (= 90/10), of which the swelling and solubility were measured to be 109 and 0%, respectively, showed improved water-resistance. The WVTR and $O_2TR$ for the PET film (thickness $50\;{\mu}m$) coated with PVA/EAA (= 90/10) film (thickness $2.5\;{\mu}m$) were measured to be $9.1\;g/m^2/day$ and $2.0\;cc/m^2/day$, respectively.

• Applied Chemistry for Engineering
• /
• v.25 no.3
• /
• pp.318-323
• /
• 2014

In order to analyze the effect of maleic anhydride (MAH) content and styrene monomer (SM)/MAH mole ratio on reactive extrusion of maleic anhydride grafted random polypropylenes (MAH-g-rPP), MAH-g-rPPs were prepared by using a twin screw extruder. MAH contents were 0.5, 1.0, 3.0, and 5.0 phr and SM/initiator mole ratio was 0.0, 1.0, and 2.0. Dicumyl peroxide (DCP) was used as an initiator. The graft degree of MAH was confirmed by the existence of carbonyl group (C = O) stretching peak at $1700cm^{-1}$ from FT-IR spectrum. The degree of graft reaction increased up to 3.0 phr MAH and showed the optimum value at 1.0 SM/MAH mole ratio from the area ratio of C = O and C-H stretching peak. Thermal and crystallization properties of MAH-g-rPP and PP/MAH-g-rPP/pulp composites were investigated by DSC, TGA, XRD, and POM. There was a decrease in non-isothermal crystallization temperature of PP/MAH-g-PP/pulp composites. Based on tensile properties and SEM pictures for the fractured surface of PP/MAH-g-PP/pulp composites, MAH content of 1.0 wt% and SM/MAH mole ratio of 1.0 were the optimum formulation as the compatibilizer. The rheological properties of the composites were measured by dynamic Rheometer to compare the processability of the composites with and without compatibilizer. The power law index showed slightly low value at the composites with compatibilizer.

• Applied Chemistry for Engineering
• /
• v.25 no.3
• /
• pp.254-261
• /
• 2014

The transformer is a static electrical device that transfers energy by inductive coupling. Then, heat is occurred at coils, inner transformer was filled with insulating oils for cooling and insulation. Although mineral oil as insulating oil has been widely used, it does not meet health and current environmental laws because it is not biodegradable. Therefore, in this study, the diglycerol ester was synthesized with diglycerol and fatty acids (oleic acid and caprylic acid) over various catalysts for insulating oil having biodegradability, high flash points and low pour points. The sulfated zirconia ($SO_4{^{2-}}/ZrO_2$) catalyst prepared at different calcination temperature shows the highest conversion of fatty acids at $600^{\circ}C$ due to crystallinity and high density of acid sites per surface area. When the molar ratio of oleic acid and caprylic acid is 1:3, the diglycerol ester shows superior insulation properties that are the flash point of $306^{\circ}C$ and pour point of $-50^{\circ}C$. The insulation properties of synthesized diglycerol ester shows the pour point of $-50^{\circ}C$ and the flash point of over $300^{\circ}C$. Therefore, diglycerol ester is superior to the vegetable oils in insulation properties.

• Fire Science and Engineering
• /
• v.26 no.4
• /
• pp.55-62
• /
• 2012

The suppression mechanisms of carbon dioxide ($CO_2$) as a representative fire suppression agent were revisited using a counterflow diffusion flame which could be applied the concept of a local application system. To end this, the low strain rate $CH_4$/air counterflow diffusions with $CO_2$ addition in either fuel or oxidizer stream were examined numerically using detailed-kinetic chemistry. Radiative heat loss due to radiating gas species including $CO_2$ added was considered by the optically thin model (OTM). As a result, the critical $CO_2$ volume fractions in the oxidizer stream required to extinguish the flame were in good agreement with the experimental data reported in the literature, while somewhat under-prediction was observed with $CO_2$ added in the fuel stream. The surrogate agents were adopted to estimate the quantitative contribution with changing in global strain rate ($a_g$) on the flame extinguishment among pure dilution effect, thermal effects including radiation heat loss and chemical effect due to the $CO_2$ fire suppression agent.

• Fire Science and Engineering
• /
• v.23 no.6
• /
• pp.126-134
• /
• 2009

In an attempt to control the spalling in high strength concrete, spalling reducer was mixed to identify the effect and thermal characteristics of concrete beam member at high temperature. The member was manufactured in such as way of adding 40~60MPa of high strength concrete into spalling reducer, and then fire resistance performance were monitored under the ISO standard fire load condition in accordance with KS F 2257. As a result of test, fore rate performance of 40MPa beam without spalling reducer was 180minutes, 50MPa was 174minutes and 60MPa was 152minutes, indicating that 50MPa and 60MPa beam appeared 6~28minutes short to become a 3-hour rate. However, 50 and 60MPa beam mixed with spalling reducer appeared to have satisfied the requirements for 180minutes. A spalling was occurred in surface of 50 and 60MPa beam mixed without spalling reducer, while no spalling or surface failure was occurred with 50 and 60MPa beam mixed with spalling reducer. Thus polypropylene fiber mixed with the concrete proved to be effective, but viewing that the surface of 60MPa was peeled off partially, the steel fiber mixed appeared not to be effective for the beam more than 60MPa.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.15 no.5
• /
• pp.3286-3291
• /
• 2014

A study on the crack protection and thermal insulation properties of the expanded perlite inorganic composites was performed. Mixed expanded perlite with a water glass was stabilized for 24 hrs at room temperature in the mold and, thereafter, converted into a massive foamed body through complete drying process at $150^{\circ}C$. Aluminum phosphate and micron size mica powder were used as a reaction accelerator and a stabilizer for thermal crack, respectively. Especially, use of mica exhibited a remarkable effect on the protection of thermal crack at higher temperature over $500^{\circ}C$, and thermal conductivity of the composites was enhanced with higher perlite contents, showing ca. 0.09 W/mK for the sample of 100/200/10/1.5 water glass/perlite/mica/Al phosphate by weight. A severe dimensional deformation of the composite materials was observed over $600^{\circ}C$, however, showing a temperature limitation for a practical application. The facts were considered as the results from the glass transition temperature of the water glass, of which main component is sodium silicate.