• Transactions of Materials Processing
• /
• v.18 no.5
• /
• pp.377-384
• /
• 2009

The shape of edge cracking in rolling process generally occurred "V" shape. This cracking is successively generated at width edge of strip. The edge cracking is developed to center of strip during rolling process. In the results, the strip is occurred fracture, and the productivity is gone down because of the extensive production time. Accordingly, we need to control crack propagation during rolling process. But, the control of cracking is very difficult in rolling process. Previously the studies of edge cracking were mainly performed on hot rolling process. In this paper, the shape of the edge cracking in rolling was estimated according to process conditions such as initial edge crack size, reduction ratio and tension using FE-simulation and the simplicity experiments on cold rolling process.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2009.04a
• /
• pp.117-120
• /
• 2009

The rolling of flat slabs or sheet metal is probably the most advanced technique of metalworking technology. In spite of this very intensive activity, the problem if edge cracking has not been resolved. Although edge cracking is a major industrial problem, relatively little well-documented experimental work has been published on subject. Despite the paucity of exact experiments, it is reasonably certain from published data that three causes contribute to its occurrence; (1) limited ductility of the rolled material (2) uneven deformation at the edges and (3) variations in stresses along the width of the rolled material, particular near the edge. The present study was carried out to show the generation of edge cracking using ductile fracture criteria and FE-simulation. The validity of simulated results was verified by rolling experiments of steel strip.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2009.05a
• /
• pp.405-408
• /
• 2009

Edge cracks in cold rolling always influence to the quality of productions, while the "V" shaped cracks were propagated by passing the roll gap. We set up the sizes and shapes of initial cracks in simulation according to the references from real productions. Different to in hot rolling, the cracks in cold rolling couldn't be reduced from propagation automatically after generated, even if these could be reduced by changing the process parameters. In this paper, we described the affections of process parameters on the propagation of edge cracks, such as reduction ratio and tension. We predicted that the dependence of the cracks propagations of changing of process conditions and expected to gain the smaller edge cracks. By raising the reduction ratio, the cracks were propagated increasingly in both transverse and rolling directions. And as tension raise, the cracks became propagated in both directions in which transverse direction was less effectively.