• Journal of the Society of Disaster Information
• /
• v.20 no.2
• /
• pp.390-397
• /
• 2024

Purpose: In this study, PCM was used to give thermal performance to concrete and analyze its effect on durability to prevent disasters that may occur in concrete when exposed to hot and cold environments. Method: After preparing concrete specimens containing 10, 30, and 50% of the two types of PCMs compared to the cement volume, the pore volume, freeze melting resistance, and scaling resistance were evaluated. Result: Regardless of the type, when PCM powder was mixed with concrete, the amount of pores decreased, and when 10% and 30% were mixed, the freeze-melting resistance was also improved. It was also confirmed that the higher the mixing amount, the better the scaling resistance. Conclusion: When mixing powdered PCM into concrete, it is believed that durability can be improved to a certain level by the filling effect, and additional various studies should be supported for actual field application.

• Journal of Korean Society of Steel Construction
• /
• v.24 no.1
• /
• pp.23-34
• /
• 2012

In this study, stub columns subjected to concentrical and eccentrical loads were tested to check the applicability of the current local stability criteria (KBC2009, AISC2005) to 800MPa high-strength steel (HSA800). The key test variables in the concentrically loaded tests included the plate-edge restraints and the width-to-thickness ratio normalized by the yield strength of steel. Specimens made of ordinary steel (SM490) were also tested for comparative purposes. Eccentrically loaded stub column tests were conducted for a range of the P-M combinations by controlling the loading eccentricity. All the concentrically loaded specimens with non-compact and slender sections developed sufficient strengths according to the current local stability criteria. All the eccentrically loaded specimens with non-compact H sections also exhibited a sufficient P-M interaction strength that was even higher than that of compact H- section counterparts. Residual stresses were also measured by using the non-destructive indentation method to demonstrate their dependency or independency on the steel material's yield strength. The measured results of this study also indicated that the magnitude of residual stresses bears no strong relation to the yield strength of the steel material.

• Journal of the Korea Concrete Institute
• /
• v.29 no.3
• /
• pp.275-281
• /
• 2017

This study examined the effect of water-to-binder ratio (W/B) and phosphate-to-binder ratio (P/B) on the flow, setting time, compressive strength development, and pH variation of magnesium-potassium phosphate composites, MKPC mortars. Ten mortars mixtures were prepared with the W/B varying from 20% to 40% at each P/B of 0.3 or 0.5. The hydration products and microstructural pore distribution of the MKPC pastes were investigated using X-ray diffraction (XRD), scanning electron microscope (SEM) and mercury intrusion porosimetry (MIP). The initial flow and setting time of MKPC mortars tended to decrease with an increase of P/B, indicating that the final setting time was shortened by approximately 24% when P/B increased from 0.3 to 0.5. The slope of the early-strength development measured in the MKPC mortars was considerably higher than that of cement concrete specified in code provisions. For obtaining a relatively good 28-day strength (above 30 MPa) and a near neutral pH (below 9.0) in MKPC mortars, the P/B and W/B need to be selected as 0.5 and 30%, respectively. The strubite-K crystal increased with the increases of P/B and W/B, which leads to the decrease of the macro-capillary pores.

• Journal of the Korea Concrete Institute
• /
• v.23 no.1
• /
• pp.121-127
• /
• 2011

In this study, possible use of indigenous natural loess (Hwangtoh) as a new binding material via geopolymerization process is examined. Hwangtoh pastes with four different mix proportions of varying alkali liquid concentrations (6 M, 8 M) and the constituents of the binder as well as the alkali liquid at a constant liquid-to-binder ratio of 0.55 were prepared. Analysis of the natural loess (Hwangtoh) paste was carried out as follows : 1) Measurement of compressive strength and weight of cubic specimens versus curing time; 2) Analysis by X-ray diffraction (XRD) and scanning electron microscope (SEM) about reaction product; 3) Porosity analysis of hardened Hwangtoh paste. The result showed that it is possible to prepare Hwangtoh paste with 29.1 MPa at the age of 7 day by using alkali solution (made as 1 : 4.5 the mass ratio of liquefied $Na_2SiO_3$ and NaOH solution and applying the curing temperature of $60^{\circ}C$). Compressive strength development with respect to the degree of moisture evaporation from the paste seems to be independent of curing temperature. Therefore, it seems that higher early strength of the paste specimens cured at higher temperature can be attributed to both higher rate of reaction and moisture evaporation.

• Journal of the Korea Concrete Institute
• /
• v.25 no.2
• /
• pp.209-215
• /
• 2013

This study is aimed to identify the method to use the CaO-$Al_2O_3$ system of rapidly cooled steel making slag (RCSS) as the environment-friendly inorganic accelerating agent by analyzing its physical and chemical properties. The fraction of rapidly cooled steel making slag is distinguished from its fibrous, and the contents of CaO and $Fe_2O_3$ are inversely proportional across different fractions. In addition, as the content of CaO decreased and the content of $Fe_2O_3$ increased, the loss ignition tended to become negative (-) and the density increased. The pore distribution by mercury intrusion porosimetry is very low as compared to the slowly cooled steel-making slag, which indicates that the internal defect and the microspore rate are remarkably lowered by the rapid cooling. To analyze the major minerals the rapidly cooled steel-making slag, XRD, f-CaO quantification and SEM-EDAX analysis have been performed. The results shows that f-CaO does not exist, and the components are mainly consisted of $C_{12}A_7$ and reactive ${\beta}-C_2S$.

• KSCE Journal of Civil and Environmental Engineering Research
• /
• v.28 no.5A
• /
• pp.737-746
• /
• 2008

Recently, NDTs (Non-Destructive Techniques) using electromagnetic(EM) properties are applied to the performance evaluation for RC (Reinforced Concrete) structures. Since nonmetallic materials which are cement-based system have their unique dielectric constant and conductivity, they can be characterized and changed with different mixture conditions like W/C (water to cement) ratios and unit cement weight. In a room condition, cement mortar is generally dry so that porosity plays a major role in EM properties, which is determined at early-aged stage and also be affected by curing condition. In this paper, EM properties (dielectric constant and conductivity) in cement mortar specimens with 4 different W/C ratios are measured in the wide region of 0.2 GHz~20 GHz. Each specimen has different submerged curing period from 0 to 28 days and then EM measurement is performed after 4 weeks. Furthermore, porosity at the age of 28 days is measured through MIP (Mercury Intrusion Porosimeter) and saturation is also measured through amount of water loss in room condition. In order to evaluate the porosity from the initial curing stage, numerical analysis based on the modeling for the behavior in early-aged concrete is performed and the calculated results of porosity and measured EM properties are analyzed. For the convenient comparison with influencing parameters like W/C ratios and curing period, EM properties from 5 GHz to 15 GHz are averaged as one value. For 4 weeks, the averaged dielectric constant and conductivity in cement mortar are linearly decrease with higher W/C ratios and they increase in proportion to the square root of curing period regardless of W/C ratios.