• Journal of the Korea Concrete Institute
• /
• v.25 no.3
• /
• pp.305-312
• /
• 2013

This paper reports the results of an investigation into the effects of silica fume on strength properties of alkali-activated slag cement (AASC) with water-binder (W/B) ratio and replacement ratio of silica fume content. The W/B ratio varied between 0.50 and 0.60 at a constant increment of 0.05. The silica fume content varied from 0% to 50% by weight of slag. The activators was used sodium hydroxide (NaOH) and the dosage of activator was 3M. The strength development with W/B ratio has been studied at different ages of 1, 3, 7 and 28 days. For mixes of AASC mortars with varying silica fume content, the flow values were lower than the control mixes (without silica fume). The flow value was decrease as the content of silica fume increase. This is because the higher surface areas of silica fume particles increase the water requirement. The analysis of these results indicates that, increasing the silica fume content in AASC mortar also increased the compressive strength. Moreover, the strength decreases with the W/B ratios increases. This is because the particle sizes of silica fume are smaller than slag. The high compressive strength of blended slag-silica fume mortars was due to both the filler effect and the activated reaction of silica fume evidently giving the mortar matrix a denser microstructure, thereby resulting in a significant gain in strength.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.25 no.6
• /
• pp.257-262
• /
• 2015

Recently the world wide efforts reduce occurrence of $CO_2$; global warming main reason. The aim of this study is to improve recycling rate of the fly ash (FA) and fused waste slag (FWS) from the power plant and to carbonate under supercritical condition ($40^{\circ}C$, $80kgf/cm^2$ pressure, 60 min) for $CO_2$ fixation. Specimens of mortar with various mixing ratios of FA, FWS (from 100:0 to 20:80 in 5 steps of 20 % reduction each time), distilled water and 3 M NaOH alkali activators were prepared. As a result, the proportion of weight change ratio increases with CaO content, to 12 % after carbonation under the supercritical condition. There is difference of compressive strength between the carbonated and the alkali activator mortar specimens. The stabilization of $CO_2$ fixation through carbonation which could confirm the applicability of the eco-friendly materials without loss of compressive strength.

• Journal of the Korea Concrete Institute
• /
• v.24 no.3
• /
• pp.315-322
• /
• 2012

Alkali-activated slag (AAS) is the most obvious alternative materials that can replace OPC. But, AAS industrial usage as a structural material should be evaluated for its durability. Carbonation resistance is one of the most important factors in durability evaluation. Test results for 18 slag-based mortars activated by sodium silicate and 6 OPC mortars were obtained in this study to verify the carbonation property. Main variables considered in the study were flow, compressive strength before and after carbonation, and carbonation depth. Mineralogical and micro-structural analysis of OPC and AAS specimens prior to and after carbonation was conducted using XRD, TGA, FTIR FE-SEM. Test results showed that CHS was major hydration products of AAS and, unlike OPC, no other hydration products were found. After carbonation, CSH of hydration product in AAS turned into an amorphous silica gel, and alumina compounds was not detected. From the analysis of the results, it was estimated that the micro-structures of CSH in AAS easily collapsed during carbonation. Also, the results showed that this collapse of chemical chain of CSH lowered the compressive strength of concrete after carbonation. By increasing the dosage of activators, carbonation resistance and compressive strength were effectively improved.

• Journal of the Korea Concrete Institute
• /
• v.18 no.4 s.94
• /
• pp.449-458
• /
• 2006

The discharge of fly ash that is produced by coal-fired electric power plants is rapidly increasing in Korea. The utilization of fly ash in the raw materials would contribute to the elimination of an environmental problem and to the development of new high-performance materials. So it is needed to study the binder obtained by chemically activation of pozzolanic materials by means of a substitute for the cement. Fly ash consists of a glass phase. As it is produced from high temperature, it is a chemically stable material. Fly ash mostly consists of $SiO_2\;and\;Al_2O_3$, and it assumes the form of an oxide in the inside of fly ash. Because this reaction has not broken out by itself, it is need to supply it with additional $OH^-$ through alkali activators. Alkali activators were used for supplying it with additional $OH^-$. This paper concentrated on the strength development according to the kind of chemical activators, the curing temperature, the heat curing time. Also, according to scanning electron microscopy and X-Ray diffraction, the main reaction product in the alkali activated fly ash mortar is Zeolite of $Na_6-(AlO_2)_6-(SiO_2)_{10}-12H_2O$ type.

• Journal of the Korea Concrete Institute
• /
• v.27 no.5
• /
• pp.511-519
• /
• 2015

Methods such table flow, slump and outflow time have used to be as a main evaluation criteria regards to fluidity of concrete. Since those methods mentioned above have some inaccuracies which are up to its condition of test. Studies that evaluate fluidity applying the rheology has increased its portion in this field. Meanwhile, demands for AAS binder have been increased in accordance with its demand for this market, studies for rheology of AAS binder are little though. Therefore, this paper mainly deals a rheological peculiarity of AAS binder according to its condition of W/B ratio and alkali activators. The fluidity of AAS paste was evaluated with the index of table flow and outflow time. And shear stress following its shear rate was analyzed through rheological test. Rheological parameters were deduced through this rheological test of Bingham model and analyzed its interrelation with fluidity test. As the final outcome, it proposed the interrelation among table flow, yield stress, viscosity and outflow time. In basis of this study, we would like to suggest a reference for mixing AAS mortars and concretes.

• International Journal of Highway Engineering
• /
• v.15 no.3
• /
• pp.1-8
• /
• 2013

PURPOSES : This study is to evaluate the feasibility of using the alkali activated cement concrete for application of partial-depth repair in pavement. METHODS : This study analyzes the compressive strength of alkali activated cement mortar based on the changes in the amount/type/composition of binder(portland cement, fly ash, slag) and activator(NaOH, $Na_2SiO_3$, $Na_2CO_3$, $Na_2SO_4$). The mixture design is divided in case I of adding one kind-activator and case II of adding two kind-activators. RESULTS : The results of case I show that $Na_2SO_4$ based mixture has superior the long-term strength when compared to other mixtures, and that $Na_2CO_3$ based mixture has superior the early strength when compared to other mixtures. But the mixtures of case I is difficult to apply in the material for early-opening-to-traffic, because the strength of all mixtures isn't meet the criterion of traffic-opening. The results of case II show that NaOH-$Na_2SiO_3$ based mixtures has superior the early/long-term strength when compared to NaOH-$Na_2SiO_3$ based mixtures. In particular, the NaOH-$Na_2SiO_3$ based some mixtures turned out to pass the reference strength(1-day) of 21MPa as required for traffic-opening. CONCLUSIONS : With these results, it could be concluded that NaOH-$Na_2SiO_3$ based mixtures can be used as the material of pavement repair.

• Resources Recycling
• /
• v.22 no.3
• /
• pp.36-42
• /
• 2013

According to the recent community-based structures enlargement, specification, and diversification. It needs appropriate construction materials in terms of intensity and environmental aspects. Thus, in manufacturing the cement using micro limestone powder which is main material. It is also expected to save energies and reduces $CO_2$, by using the blast furnace slag and fly ash which are mitigated environmental load construction materials that emerged. In this research, The durability aspect tries to be grasped considering the chemical property according to the coherence of the hydration product. Consequently, The compressive strength was measured over 30 Mpa on 3rd. In addition, according to the content of the limestone powder, the setting time is promoted. It has the feature expanded in the length change. And it is determined because the possibility of replacing the existing for construction material such as it is measured compared with the time to use the portland cement usually that flexural strength is high with the age 7 days ago, so it is sufficient.

• Journal of the Korea Concrete Institute
• /
• v.27 no.1
• /
• pp.65-73
• /
• 2015

This study discussed the pozzolanic properties of calcined sewage sludge (CSS) according to calcination and fineness conditions. The chemical and mineralogical analysis of CSS according to calcination temperature and time were carried out and compared with that of the existing pozzolanic materials such as fly-ash, blast furnance slag and meta-kaolin. Various mortars were made by mixing those CSS and $Ca(OH)_2$ (1:1 wt. %), and their compressive strength and hydrates according to experimental factors such as fineness of CSS and curing age were also investigated in detail. The results show clearly the potentiality of calcined sewage sludge (CSS) as an admixture materials in concrete, but the CSS should be controlled by calcination temperature and time, and fineness etc. In this experimental condition, the calcination temperature of $800^{\circ}C$, calcination time of 2 hours and fineness of $5,000cm^2/g$ were optimum conditions in consideration of the mechanical properties and economic efficiency of CSS. The compressive strength of CSS mortars was higher than that of fly-ash mortars and blast furnace slag mortars, especially at the early ages. Then, the utilization of CSS in construction fields was greatly expected.

• Resources Recycling
• /
• v.25 no.6
• /
• pp.73-81
• /
• 2016

Geopolymers produced from aluminosilicate materials such as metakaolin and coal ash react with alkali activators and show higher fire resistance than portland cement, due to amorphous inorganic polymer. The percentage of thermal shrinkage of geopolymers ranges from less than 0.5 % to about 3 % until $600^{\circ}C$, and reaches about 5 ~ 7 % before melting. In this study, geopolymers paste having Si/Al = 1.5 and being mixed with carbon nanofibers, silicon carbide, pyrex glass, and vermiculite, and ISO sand were studied in order to understand the compressive strength and the effects of thermal shrinkage of geopolymers. The compressive strength of geopolymers mixed by carbon nanofibers, silicon carbide, pyrex glass, or vermiculite was similar in the range from 35 to 40 MPa. The average compressive strength of a geopolymers mixed with 30 wt.% of ISO sand was lowest of 28 MPa. Thermal shrinkage of geopolymers mixed with ISO sand decreased to about 25 % of paste. This is because the aggregate particles expanded on firing and to compensate the shrinkage of paste. The densification of the geopolymer matrix and the increase of porosity by sintering at $900^{\circ}C$ were observed regardless of fillers.