• Polymer(Korea)
• /
• v.26 no.5
• /
• pp.615-622
• /
• 2002

Weather-resistant coatings were prepared by mixing a synthesized mill-base and let-down silicone/acrylic resin in weight ratios of 4 : 6, 3 : 7, and 2 : 8. The weatherability of the prepared coatings was tested. The thermal stability, general physical properties, and weatherability of the films of the coatings were improved with silicone content. Among the three mixing ratios mentioned, the ratio of 2 : 8 was the most suitable for the preparation of weather-resistant Coatings. The coatings containing 30 wt% of silicone proved to be a high weather-resistant coating.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2021.11a
• /
• pp.162-163
• /
• 2021

To prepare the waterborne silicone acrylic resin coatings, acrylic resin was prepared by a radical polymerization. Glass transition temperature(Tg) of the acrylic copolymer was fixed at 30℃ and the contents of tertiary amine monomer(DMAEMA), were varied to be 5, 10, 15 and 20 wt%, hydroxyl monomer, and carboxyl monomer were fixed 10 wt%, and 4 wt% respectively. γ-Glycidoxypropyltrimethoxysilane(GPTMS) containing epoxy group was used for curing agents. The eqivalent ratio of amine to epoxy was 1:1. The prepared coatings exhibited excellent adhesion to various substrates, and various physical properties of the coatings were satisfactory. The gloss retension and color difference were improved at low tertiary amine concentration. The coatings containing 10wt% tertiary amine concentration have especially good weather resistant properties.

• Polymer(Korea)
• /
• v.30 no.4
• /
• pp.350-356
• /
• 2006

In order to investigate the effect of the composition of weather-resistant coatings on physical properties, three different weather-resistant coatings were prepared by varying the ratio of a mill-base silicone/acrylic resin and let-down silicone/acrylic resin in weight ratios of 2 : 8, 3 : 7, and 4 : 6. The physical properties and weather-resistance of the prepared coatings were tested. It was found that the thermal stability, salt spray exposure, and weather-resistance were improved with increasing the amount of silicone. The optimum mixing ratio of mill-base silicone/acrylic resin to the let-down silicone/acrylic resin was 2 : 8. The coating containing silicone component of 30 wt% was found to be suitable as high weather-resistant coatings.

• Polymer(Korea)
• /
• v.25 no.3
• /
• pp.349-358
• /
• 2001

Silyl group-containing acrylic resins were synthesized to prepare weather resistant coatings. Acrylic copolymer was synthesized by the addition copolymerization of n-butyl methacrylate, methyl methacrylate, n-butyl acrylate and 3-methacryloxypropyl trimethoxysilane (MPTS). Acrylic copolymer were synthesized such that their $T_g$'s were adjusted to $20^{\circ}C$ and their MPTS contents were varied to 10, 20 and 30 wt%. As the content of MPTS increased, viscosity of coatings increased and thermal stability at the high temperature was improved. Coatings was prepared by blending the synthesized resins with a white pigment. The adhesion performance of coatings was superior with various substrates and their other properties were on the whole suitable. Weatherability was tested by outdoor exposure test, WOM test and QUV test. It was proved that resin with 30 wt% MPTS was suitable as the binder for weather resistant coatings.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2021.11a
• /
• pp.164-165
• /
• 2021

To prepare the good-adherent and weather-resistant acrylic resin coatings, acrylic resin was prepared by a radical polymerization. Glass transition temperature(Tg) of the acrylic copolymer was fixed at 30℃ and the contents of tertiary amine monomer(DMAEMA) was varied to be 5, 10, 15, 20 wt% respectively. γ-Glycidoxypropyltrimethoxysilane(GPTMS) containing epoxy group was used for curing agents and di-n-butyltindilaurate(DBTDL) was used for drying accelerator. The equivalent ratio of amine to epoxy was 1:1. The prepared coatings exhibited excellent adhesion to various substrates, and various physical properties of the coatings were satisfactory. The gloss retention and color difference were improved at low tertiary amine concentration. The coatings containing 10wt% tertiary amine concentration have especially good weather resistant properties.

• Proceedings of the KIEE Conference
• /
• 2006.07a
• /
• pp.427-428
• /
• 2006

최근 대기환경 악화로 송전용 철탑 도장의 열화가 촉진되어 내후성이 강한 신도료를 송전철탑에 적용이 필요하게 되었다. 도료 제조업체의 신도료로 도장시편을 제작하여 옥외에 폭로후 전문기관에서 성능을 확인하였으며, 이를 토대로 도료의 재질을 실리콘 아크릴우레탄계로 변경하였으며, 철탑용 도료 성능시험 기준을 강화하여 철탑 재도장에 따른 유지보수 비용 절감이 될 수 있도록 개선하였다.

• Journal of the Korean Applied Science and Technology
• /
• v.16 no.2
• /
• pp.171-177
• /
• 1999

The objectives of this study is to investigate the optimum reaction conditions and to identify the product formula in the synthesis of a silicone/acrylic resin that curing in moisture at room temperature. By the addition polymerization of monomers, n-butyl acrylate, methyl methacrylate, n-butyl methacrylate, and 3-methacryloxypropyltrimethoxysilane. a quarter polymer was obtained. Among various initiators investigated in this study, 2.2'-azobisisobutyronitrille was found to be the most suitable initiator. The optimum reaction conditions found in this study are 70 wt% of initial solvent amount, 120 minutes of dropping time, 3 times of initiator addition, $82{\sim}105^{\circ}C$ of reaction temperature, and 8 hrs of reaction time. Also, number average molecular weight of $11700{\sim}33100$ and molecular weight distribution of $1.81{\sim}3.44$ were obtained.

• Journal of the Korean Applied Science and Technology
• /
• v.24 no.1
• /
• pp.10-22
• /
• 2007

To prepare weather-resistant silicone/acrylic resin coatings for an architectural purpose, tetrapolymers were synthesized by a radical polymerization. 3-Methacryloxypropyltrimethoxysilane (MPTS) as a silicone monomer and n-butyl acrylate, methyl methacrylate, and n-butyl methacrylate as acrylic monomers were used. The compositions of monomers were adjusted to fix the glass transition temperature of acrylic polymer for $20^{\circ}C$. The composition of MPTS in the synthesized polymer were varied from 10 wt% to 30 wt%. On the basis of synthesized resin amber paints were prepared and their physical properties and effects for weatherability were examined. The presence of MPTS in silicone/acrylic resins generally resulted in low molecular weight and broad molecular weight distribution, and also lowered the viscosity of the copolymers. The coated films prepared from these resins showed good and balanced properties in general. Adhesion to the substrate was outstanding in particular. Weatherability tests were carried out in three different types such as outdoor exposure, QUV, and SWO. The test results showed that the silicone/acrylic resins containing 30 wt% of MPTS had weather-resistant properties.