Coal ash generated from thermal power plants using briquettes contains Si, Al, and Fe components. These components are the main components required for the manufacture of cement clinker. In particular, Al and Fe components form the interstitial phase of cement clinker and have an important effect on the sintering of cement clinker. In this study, a large amount of coal ash was applied as a raw material for cement clinker by content, and the mineral formation process of cement clinker to which coal ash was applied was confirmed by sintering temperature. It was confirmed that the intermediate phase was generated in the sintering temperature range of 1050 ~ 1150 ℃ in the cement clinker to which a large amount of coal ash was applied. As the content of coal ash increased, the production amount of the intermediate phase increased. The phase produced by the addition of coal ash is expected to be converted to calcium silicate phase and interstitial phase and disappear above 1350 ℃. The cement clinker applied with a large amount of coal ash at 1450 ℃ formed well-developed minerals equivalent to the standard cement clinker.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.8 no.4
• /
• pp.514-519
• /
• 2020

In this study, cement clinkers were sintered at each temperature by replacing some of the clay components of cement clinkers with coal materials. The mineral phase change of sintered cement clinker was quantitatively analyzed by XRD-Rietveld method. As the sintering temperature of cement clinker increased, the amount of belite decreased, the amount of alite increased, and the amount of free-CaO decreased. The form of alite and belite could be distinguished at sintering temperature of 1450℃ or higher. The crystal size was greatly increased at 1500℃ sintering. It was confirmed that the excessive sintering was progressed. Free-CaO decreased with the increase of sintering temperature. At 1450 ℃ or higher, it was less than 0.5%. In 1450℃ or greater, it is determined that enough sintering is included. Therefore, the application of fly ash as a raw material of cement clinker was judged to be usable as a source of chemical components of alumina and iron raw materials.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.10 no.3
• /
• pp.211-218
• /
• 2022

Coal ash is being considered as a source of silica and alumina for cement clinker. The purpose of this study was to investigate the effect on cement clinker sintering by confirming the high-temperature microstructural change according to the firing temperature in the cement clinker sintering process of coal ash. In the coal ash used as a raw material for cement clinker, the shape change of the particle surface was confirmed from the sintering tem perature of 950 ℃. The shape of the coal ash disappeared from the sintering temperature higher than 1250 ℃. It was confirmed that the Al and Fe components of the coal ash were converted to the cement interstitial phase at a temperature higher than 1350 ℃. In addition, the clinker using a large amount of coal ash as a raw material showed a low content of Lime and a high content of Belite in the sintering tem perature range of 1150~1200 ℃. From this, it was confirmed that the formation of calcium silicate mineral proceeds more easily at the initial sintering temperature by the application of coal ash.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.9 no.1
• /
• pp.20-25
• /
• 2021

The cement clinker, the main raw material of cement, is manufactured using limestone as the main material. Depending on the quality of limestone, the use of subsidiary materials changes, and has a great influence on the production of cement clinkers. In this study, the effect of CaO content of limestone, a cement clinker material, on Raw Mill grinding and sintering of cement clinker was investigated. The grinding time of the union materials changed in the content of limestone CaO was measured to identify the grinding properties. The raw material combination was cleaned within a range of 1,350-1,500℃. The sintering performance of cement clinker by Burnability index calculation was identified. The lower the grade of limestone, the lower the grinding quality of the raw material combination. The lower the CaO content of limestone, the greater the variation in F-CaO for sintering temperature. The lower the class of limestone, the higher B. I. value was calculated, indicating the lower cement clinker sintering. In addition, the mineral analysis results of cement clinker showed that if the F-CaO value was low due to the increase in sintering temperature, the Belite content decreased and the Alite content increased. In the case of Alite, the ratio of R-type decreased and that of M-type increased as the content of limestone CaO increased.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.11 no.4
• /
• pp.364-372
• /
• 2023

By applying coarse-grained limestone and unprocessed coal ash as sintering raw materials for cement clinker, the microstructure and distribution of chemical components of cement clinker were compared and examined. Samples using coarse limestone as a raw material for cement clinker showed a decrease in sinterability compared to samples using reagent-grade raw materials. Samples using coal ash showed a tendency for some increase in sinterability. In samples using coarse limestone and coal ash, the formation of Belite was high at 1350 ℃. The conversion rate from Belite to Alite was high in the range of 1350~1450 ℃. Samples using coal ash showed stable formation of interstitial phase in the range of 1350 to 1450 ℃. The microstructure and chemical composition distribution of cement clinker sintered at 1350~1450 ℃ showed that all samples showed a form and composition distribution in which the calcium silicate phase and interstitial phase were clearly distinguished.

• Resources Recycling
• /
• v.20 no.6
• /
• pp.71-77
• /
• 2011

Raw mix of molten clinker was fabricated using blast furnace slag as starting material. Raw mix was melted at 1620 for molten clinker fabrication. Color and mineral composition of molten clinker was investigated by XRD and colorimeter. It was found that the molten clinker contains alite and belite equivalent to OPC clinker mineral and shows higher whiteness value than that of OPC. Whiteness of the molten clinker decreased with LSF and SM. Also the whiteness value of the slag cement using molten clinker was higher than that of common slag cement.

• Cement Symposium
• /
• no.17
• /
• pp.77-81
• /
• 1989

• Cement Symposium
• /
• s.36
• /
• pp.55-60
• /
• 2009

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.9 no.4
• /
• pp.553-560
• /
• 2021

In this study, cement clinker using a pure sample and clinker using 7% coal ash were sintered at a temperature of 1050~1500℃. Changes in the content of cement minerals and changes in microstructure by sintering temperature were reviewed. The application of coal ash as a raw material for cement clinker was applicable as a source of Al₂O₃ and SiO₂. At a sintering temperature of 1350℃ or higher, the cement clinker applied with coal ash showed the same level of mineral content as compared to the cement clinker applied with pure raw material. The microstructure also showed a similar state, confirming that coal ash can be used as a raw material for cement. In XRD-Reitveld analysis, a maximum amount of Belite was produced at 1250℃. The conversion from Belite to Alite was observed from 1350℃. From 1350℃, the interstitial phase and the mineral phase presumed to be alite were distinguished. It was clearly distinguished from 1400℃. As the sintering temperature increased, the shape and boundary of the crystal phase became clear, and the size of the crystal phase was also increased.