• Journal of the Korean Recycled Construction Resources Institute
• /
• v.9 no.2
• /
• pp.185-190
• /
• 2021

Cement has been used as a main material in the modern construction industry. However, it has been pointed out as a main cause of global warming due to carbon dioxide generated during manufactured. Recently, research that replacing cement substitute to industrial by-products such as Blast Furnace Slag which is by-producted in steelworks. When Blast Furnace Slag is used as a cement substitute, it shows a problem of lower initial strength, which is caused by glassy membrane on the particle surface. In this study, we used Electrolysis Alkaline Aqueous to improve the usability and problem of lower initial strength. As a result of the experiment, cement matrix using Blast Furnace Slag and Alkaline Aqueous showed initial strength and hydrate product were developed than that using general mixing water. Also, as a result of porosity analysis, It was confirmed that cement matrix using Alkaline Aqueous and Blast Furnace Slag has a tighter structure in internal porosity and porosity distribution than using general mixing water.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.14 no.3
• /
• pp.144-151
• /
• 2010

In this study, it is investigated the mechanical chemical properties of cement matrix using phosphogypsum and kaolin as a admixture for the substitutive materials to silica fume which is so expensive. For the test, phosphogypsum is modified as dihydrate, hemihydrate, type III anhydrite, and type II anhydrite, respectively and furnaced kaolin at $900^{\circ}C$ was also manufactured into meta kaolin by air cooling and water cooling method. The chemical characteristic and mechanical properties of various type of blended cements contained above mentioned gypsum and meta kaolin materials analyzed and compared with those characteristics of cement matrix with silica fume. From the test, the cement mixed meta kaolin made in water cooling has more excellent quality than other material.

• Journal of the Korea Concrete Institute
• /
• v.13 no.2
• /
• pp.123-129
• /
• 2001

Pozzolan is to improve the strength and the durability of concrete as a result of the pozzolanic reaction, Broadly speaking, pozzolanic materials can be artificial materials, such as slica fume and fly ash, and natural material, such as rice husk ash, clay, volcanic ash, clayish pozzolan. Hwangtoh is a mineral which belongs to a group of matakaolin, especially halloysite, and the main elements is SiO$_2$, Al$_2$O$_3$, Fe$_2$O$_3$. The purpose of this study is to examine the application of Hwangtoh for the concrete admixtures, the composition of this study is shown as follows. Chapter I is analysis for properties of concrete as the kinds of admixture, and Chapter H is analysis for properties of concrete as the replacement ratio of activated Hwangtoh. As a result of this study, Hwangtoh is found to have high practical use as pozzolanic material, and the pertinent range of replacement ratios of Hwangtoh on cement are 10∼20 %.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.18 no.3
• /
• pp.356-363
• /
• 2017

Blast furnace slag(BFS) is a by-product generated during the manufacture of pig ion, and is divided into water-cooled slag(WS) and air-cooled slag(AS) by the coking method of BFS. In this study, concrete specimens with ternary binders were produced at the various replacement levels of cement by AS. Various mechanical properties of concrete, such as compressive and split tensile strengths, absorption and water permeable pore, were measured. In addition, the chloride ions penetration resistance and carbonation resistance were tested to evaluate the durability of concrete incorporating AS. The experimental data indicated that the use of AS up to a maximum of 10% replacement level enhanced the concrete performance. However, a higher replacement of AS exhibited poor mechanical properties and concrete durability.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.6 no.1
• /
• pp.88-94
• /
• 2011

To make recycling aggregate, quantity of fine particles increase due to multi-crushing. Though this particles were mixed with recycling aggregate, those have to be disparted from aggregate in the high quality recycling aggregate, because of the cause of low quality. Considering reactivity, fine particles is better than coarse one. Therefore, it needs to develop suitable usage. We try to make cement extruding material by using the fine particles from concrete recycling, as a silicious replacement. Test results are as follows ; 1) Waste concrete powder has major ingredients such as $SiO_2$ and CaO, its density is $2.45g/cm^3$ being similar to silica powder, its diameter is range 13 to $141{\mu}m$. 2) Considering to strength properties according to particle size, specimen was made using small particles is higher strength than large one. 3) Despite of exception in the autoclaved curing, when the replacement of waste fine particle increase, strength of extruding panel shows almost same level.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.34 no.2
• /
• pp.66-72
• /
• 2024

In this study, the applicability of CCMs (Carbondioxide conversion capture materials) manufactured by reacting carbon dioxide gas with DG (Desulfurization gypsum) as a cement substitute for secondary concrete products were evaluated and the basic physical properties of CCMs-mixed mortar and concrete specimens were measured to derive the optimal mixing ratio. The main chemical oxides of CCMs were CaO and SO₃, and the main crystalline phases were CaSO₄·2H₂O, Ca(OH)₂, CaCO₃, and CaSO₄. In addition, by the results of particle size analysis and heavy metal measurement, the applicability of CCMs as a cement substitute for secondary concrete products was confirmed. As a result of measuring the strength behavior using mortar and concrete specimens with CCMs, the compressive and flexural strength decreased as the mix ratio of CCMs increased, but requirements by the standards for interlocking blocks and retaining wall blocks, which are target products in this study, were satisfied up to the optimal mixing ratio of 10 wt.% substitution. Therefore, its applicability as a cement substitute for secondary concrete products was confirmed.

• Journal of the Korea Institute of Building Construction
• /
• v.15 no.6
• /
• pp.553-559
• /
• 2015

In this study, to suggest the application method of recycled fine aggregate, the non-cement mortar was prepared and studied with the binders of blast furnace slag, fly ash, and fly ash from combined heat power plant. As a basic experiment, a series of tests was conducted to determine the potions of the binders and types of activator. When the binder was consisted with 20% of fly ash and 40% of fly ash from combined heat power plant, the highest strength of the mortar was obtained, and as an activator, the combination of sodium hydroxide 2.5%, and calcium hydroxide 7.5% showed the highest strength of the mortar. Therefore, this study focuses on engineering properties of mortar contains fly ash from combined heat power plant and recycled fine aggregate according to replacement ratio of recycled fine aggregate based on the optimum mix from the basic experiment. As a result, the best replacement ratio of recycled fine aggregate is 75%.

• Proceedings of the Korean Society For Composite Materials Conference
• /
• 1999.11a
• /
• pp.177-182
• /
• 1999

사용한 보수.보강재, Rod, Fabric, Strand 형상을 콘크리트 구조물등에 보강재로 사용되어왔다. 이 재료는 해양환경하에서 내식성과 내구성을 갖는 철근및 철골대체용 복합소재와 초고층 경량 연속섬유보강 시멘트 복합재료는 탄소섬유, 아라미드섬유, 유리섬유등의 쉬트(sheet)형상을 신건재, 비자성, 비전도성, 전파차폐용 재료등에 사용할수있다. 그러나 FRP Rod를 내식성이 요구되는 철근 및 철골대체재로 사용할 경우에는 폴리머 매트릭스의 열화, 섬유와 폴리머간 계면 접착강도의 한계, 화재시 내화성, 보강재의 인발성등의 단점들을 갖고있다[1]. (중략)

• The Journal of the Korea Contents Association
• /
• v.13 no.9
• /
• pp.392-399
• /
• 2013

The purpose of this study is to identify the manufacturing possibility of non-cement mortar using blast furnace slag and alkali accelerator. In this experimental study, the blast furnace slag which is the by-product of the steel industry substitute for cement, and the potassium hydroxide(KOH), calcium hydroxide ($Ca(OH)_2$) and sodium hydroxide(NaOH) as stimulus were added to each specimen. And the analysis on reaction property of non-cement mortar was conducted by measurement such as flexural and compressive strength, XRD, EDS and SEM. From the test results, it can be founded that $SiO_2$ and CaO included in the blast furnace slag are released and make the calcium silicate hydrate like the hydration reaction of the cement. Also, the continued study is need to reduce emission of $CO_2$ because of major content in filed of the building construction.

• Journal of the Korea Concrete Institute
• /
• v.25 no.4
• /
• pp.371-379
• /
• 2013

This paper investigates the cracking and tension-stiffening behavior of 100 MPa shrinkage-compensated strain-hardening cement composite (SHCC) and conventional concrete tie elements in monotonic and cyclic tension. Strain and surface crack formation of tension ties were monitored with two strain displacement transducers and a photo microscope with a lens of magnification 50 times. Three different cement composites such as conventional concrete, shrinkage-compensated SHCC, and normal SHCC were used in the tie specimens to investigate the influence of the cement composite type on the tension stiffening and cracking behavior. Test results indicated that initial shrinkage of the ultra high-strength cement composites is greatly reduced as the 10% replacement of cement by the shrinkage-compensating admixture based on calcium sulfo-aluminate (CSA). The test results on the SHCC tension ties showed that the first cracking load decreases proportionally to the initial shrinkage strain. Reinforced ultra high-strength SHCC ties with the initial shrinkage compensation exhibited improved tension stiffening and smaller crack spacings, i.e. the reduction in crack width. Cyclic loading did not have a significant effect on tension stiffening and cracking behavior of tension ties with normal concrete and SHCC materials.