• Magazine of the Korea Concrete Institute
• /
• v.7 no.6
• /
• pp.224-232
• /
• 1995

Recently, in other.view of underwater concrete construction, special admixture agent of concrete has been developed for antiwashout of concrete under water with easy carrying out method in some foreign nations. They had successful cases in experiment and construction and it trend to use in many cases with many scales. However, in domestic, there was rare record in carrying out. In this paper, reference for successful results of experiment and construction about antiwashout underwater concrete, as variable add of special admixture agent and other agents. We have carried out property tests of fresh and hardened concrete, certified the properties and made the antiwashout underwater concrete have enough strength to endure with ea.sy construction. And we have decided the optimal mix proportion for antiwashout underwater concrete under standard state.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2010.05a
• /
• pp.345-346
• /
• 2010

The overall quality of underwater concrete will ultimately be affected by factors such as performance of antiwashout admixture and mix proportions of concrete. Of these, performance of antiwashout admixture may significantly influence quality of underwater concrete. Thus, objectives of this experimental research are to evaluate the performance such as slump flow, setting time, compressive strength, and water segregation of the concrete containing antiwashout admixture. It was observed from the test results that concrete containing antiwashout admixture was found to improve quality of concrete such as fluidity, compressive strength, and antiwashout compared to plain concrete.

• Magazine of the Korea Concrete Institute
• /
• v.8 no.5
• /
• pp.179-187
• /
• 1996

Many underwater concrete structures have been constructed recently in proportion to the increase of ocean developments. The research for the underwater concrete construction was mainly focused in view of placing method. Recently, special admixture agents of concrete were developed for antiwashout concrete under water in some foreign nations. They had successful results in experiments and site constructions. However. there are seldom experimental results or placements in domestic contry. In this paper. We had carried out property tests of fresh and hardened concrete with refer to successful results in experiments and site construction and investigated the physical variation of the antiwashout underwater concrete considering the interaction between antiwashout admixture and other ones. We have decided the optimal mix proportion fb;r antiwashout underwater concrete under standerd sea state.

• Magazine of the Korean Society of Agricultural Engineers
• /
• v.38 no.6
• /
• pp.74-82
• /
• 1996

In this study, the characteristics of antiwashout underwater concrete according to the using types of admixture were experimentally investigated. Especially, the comparison on the performance of seven types(CO-A, B, C, D, E, F, G) of the manufactured admixtures was carried out in the same mixing condition and proportions. Based on the results of experiments, the conclusions were summarized as follows : (1) The slump flow on most of specimens except by CO-F type were progressed very well. (2) In most of products, the measured values of suspensions, pH's and air contents were lower than their reference values. However, CO-B, CO-F and CO-G types exceeded the reference ones in suspension and pH. (3) The time lags between initial and final setting were about three hours in most of tests, however, the maximum difference of total setting time was ten hours in comparing with the admixture types. The unit weights were mostly lower than $2300kg/m^3$ and the compressive strengths cured by salt water were about 80% of the ones by fresh water. (4) Finally, in spite of some problems, most of the manufactured admixtures may be performed well their functions in antiwashout under-water concrete if the using quantities are properly controlled by the site experiments.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.13 no.8
• /
• pp.3704-3712
• /
• 2012

Recently, antiwashout underwater concrete has been increasingly used for marine foundations of long span bridges. However, to shorten the construction period of antiwashout underwater concrete used in marine foundations, high fluidity antiwashout underwater concrete should be manufactured largely improving fluidity than the previous one. Thus, the objective of this experimental research is to suggest optimum mix proportions of high fluidity antiwashout underwater concrete. For this purpose, concrete specimens containing ground granulated blast furnace slag were manufactured according to the dosage of antiwashout admixture for unit binder contents of 550 and 600kg/$m^3$, respectively. And then, their quality performances such as slump flow, setting time, underwater segregation resistance, and ratio of compressive strength were evaluated according to the related specification of Korea Concrete Institute. It was observed from the test results that the minimum dosage of antiwashout admixture was necessary to satisfy the related specification.

• Magazine of the Korea Concrete Institute
• /
• v.10 no.6
• /
• pp.223-231
• /
• 1998

Existing cast in place piles made by grouting cement mortar have many problems that cracks by autogeneous and drying shrinkage bring about the deterioration of force for piles, segregations by the submersion of ground water occur and also, high cement contents lead to rise the manufacturing cost. Therefore, this study is intended to investigate the mechanical properties of high performance mortar, incorporating expansive additives and fly ash. for cast in place piles. According to the experimental results, as the contents of expansive additives increase in mortar mixture, fluidity decrease and air contents shows inverse tendency. Setting time is delayed. Although compressive strength at 7days shows a decline tendency. compressive strength at 28days and 91days increase slightly with 5% of expansive additives. As fly ash increase in mortar mixture, high fluidity is shown, air contents increase and setting time is delayed at fresh state, and additives are, the larger length change is, whereas shrinkage decrease with the increase of fly ash.