• Journal of Conservation Science
• /
• v.28 no.1
• /
• pp.29-37
• /
• 2012

This study discusses a mercury amalgam gilding technique and examines how the color, surface and section of the gilt layer changes as the condition of heat treatment with mercury amalgam gilt object is changed. Some previous studies have mentioned reasons for various colors on gilt bronze artifacts depending on gilding manufacture and environment. However, reason for reddish color with gold on the artifacts' surface brought on high temperature corrosion has yet to be discussed and analyzed. A methodology was found in representing the mercury amalgam gilding technique and heat treatment test. According to the result of the heat treatment test, in the conditions of higher temperature and longer time, the oxidized layer on the gilt layer was distributed more widely and in the part when the oxide layer was eliminated, the gilt layer with a reddish color was observed. Moreover, in the surface observation of the specimen on which yellow and reddish colors were agitated, the changing aspects of its surface condition differed by colors. When investigated the section, it was observed that the void density and size became larger. After a test, the surface components changed; the temperature of heat treatment increased, component ratio of Hg and Au decreased gradually but component ratio of Cu increased. In regard to the gilt layer, as the time was longer and the temperature became higher for the heat treatment, the component ratio of Au and Cu by layers tended to change in inverse proportion. It is concluded that gilding techniques and the burial environment can make a difference in the surface color of the gilt layer on the gilt bronze artifacts, the high temperature corrosion that occurs by heat after they are manufactured is also one of the factors that affects their surface color.

• Conservation Science in Museum
• /
• v.23
• /
• pp.1-16
• /
• 2020

In this paper, Gilt-bronze Standing Avaolkiteshvara (National Treasure No. 293, M355) excavated at Gyuam-ri in Buyeo was observed with a microscope to identify the production technique applied to it. It was also analyzed with XRF and hard X-ray to identify the composition and the surface treatment techniques and casting method applied. In this statue, Avalokiteshvara is standing upright on a lotus pedestal. The lotus designs on the pedestal and those on the shawl flowing down on both sides of the statue are characteristic of Buddhist statues from the seventh century or later. The use of supports to affix the outer and inner molds and traces of injected cast were observed in the interior of the pedestal. The blisters on the arms and pedestal created during the bronze casting indicate the use of lost-wax casting, which was popularly employed for the production of mid- or small-sized gilt-bronze Buddhist statues in ancient times. The composition analysis identified a copper-tin-lead ternary alloy in the interior of the statue that was conventional used in the sixth and seventh centuries. It is likely that this simple alloy was used to facilitate casting and produce clearer expressions of designs and ornaments on the statue. Mercury (Hg) was detected on the surface of the statue, indicating the use of amalgam-plating with gold (Au) dissolved in mercury. This plating method is a common surface treatment technique used for small gilt-bronze statutes in ancient Korea.

• Journal of Conservation Science
• /
• v.22
• /
• pp.87-98
• /
• 2008

Microstructures and chemical compositions of 24 bronze mirrors recovered from the Korean peninsula were examined using the scanning electron microscope equipped with the energy dispersive spectrometer in an effort to characterize the treatments applied on their surface. Their provenance and chronology are mostly unspecified except for two objects from a Koryo burial site. In antiquity the surface of bronze mirrors was frequently finished by mere polishing when their tin content was high enough to guarantee the required reflectivity. In many cases, however, their surface was given a special treatment. The most typical treatment was to coat the surface with tin in two different processes referred to as wipe-tinning and amalgam-tinning. In wipe-tinning only tin was used, but in amalgam-tinning tin and mercury were used together. The surface was often coated with mercury in a process known as mercury-polishing. The present mirrors showed that all these techniques were in fact practiced, not only on the reflective surface but, in some cases, on the decorative surface. The detection of mercury played a crucial role in the assessment of a specific technique applied in each mirror. Mercury often remained in the substrate in the form of sulfide and thereby allowed the method of surface treatment to be estimated even when the coated layer was completely lost. The future study is expected to uncover the regional and temporal variation of the surface treatments to the better understanding of bronze mirrors with respect to provenance and chronology.

• Journal of Conservation Science
• /
• v.27 no.1
• /
• pp.41-47
• /
• 2011

If the nondestructive analysis is carried out by using an X-ray Fluorescence Analyzer(XRF) for ingredient analysis with the target of gold plated silverware that plates gold on a silver basis, a singular point showing big difference at the value of weight percent(wt.%) according to the electron orbit of the principal ingredient can be confirmed. The present research made reproduced samples and carried out comparative analysis in order to suggest a basis that can judge whether the technique of gold plated silverware was used in case of remains uneasy to understand with eyes by using this singular point. As a result, the same result as analysis results of actual remains could be seen in specimens manufactured by a mercury amalgam plating method. However, in case of gold and silver alloy specimens, it could be confirmed that the difference according to the electron orbit of the principal ingredients is slight unlike plated specimens. The reason appearing at plated specimens seems to be generated while absorbing XRF beam at plated layers by double structure due to plating instead of single material. Accordingly, if this result appearing at nondestructive analysis is used, it was confirmed that the application of the technique of gold plated silverware can be judged without observing its section.