• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.20 no.4
• /
• pp.1123-1132
• /
• 1996

It has been reported that high temperature structural components represent the phenomenon of material degradation according to a long term service under high temperature and pressure. Especially, fossile power plant components using the fossil fuel and heavy oil are affected by dewpoint corrosion of $H_2SO_4$produced during a combustion. Therefore, the service materials subjected to high temperature and pressure may occur the stress corrosion cracking. The object of this paper is to investigate SCC susceptibility according to the material degradation of the high temperature structural materials in dewpoint corrosive environment-$H_2SO_4$.The obtained results are summarized as follows : 1) In case of secondary superheater tube, the fractograph of dimple is observed at the concentration of $H_2SO_4$-5%. When the concentration of $H_2SO_4$ is above 10%, the fracture mode is shifted from a transgranular fracture to an quasi-intergranular fracture according to the increment of concentration. 2) In the relationship between [$\Delta$DBTT]$_sp$ and SCC susceptibility, it is confirmed that the greater material degradation degree is, the higher SCC susceptibility is. In addition, it can be known that SP test is useful test method to evaluate SCC susceptibility for high temperature structural components. 3) When [$\Delta$DBTT]$_sp$ is above 17$17^{\circ}C$ the SCC fracture behavior is definitely observed with SCC susceptibility of above 0.4.

• Journal of the Korean Society for Nondestructive Testing
• /
• v.22 no.3
• /
• pp.267-274
• /
• 2002

This research is described on the applicability of a electrochemical techniques for evaluating nondestructive material degradation with various polarization characteristics for Cr-Mo-V steel. The applied electrochemical technique is anodic polarization test which are widely used to evaluate the corrosion rate and/or sensitization at depleted zone of strengthening elements mainly caused by thermal experience for stainless steels. The evaluation of material degradation is performed by small punch test which has been well known as micromechanics test method using specimen size of $10{\times}10{\times}0.5mm$. The 1,000hrs aged material at $630^{\circ}C$ shows the highest material degradation$({\Delta}[DBTT]_{SP})$, but the 2,000hrs and 3,000hrs aged materials show the decrease of ${\Delta}[DBTT]_{SP}$ as aging time increases. It is observed that the difference of current density $({\Delta}I_{FP}\;and\;{\Delta}I_{SP})$.

• Transactions of the Korean hydrogen and new energy society
• /
• v.31 no.3
• /
• pp.284-292
• /
• 2020

In this study, hydrogen charging was conducted for API X70 steel by the electro-chemical hydrogen charging method. Right after hydrogen was diffused from the specimen surface to the inside of the X70, the small punch tests and hydrogen concentration analysis was conducted within 5 minutes. Hydrogen was analyzed by melting the whole specimen and detect the gas after melting. Mechanical properties were measured by the small punch (SP) testing. Fracture surface and specimen surface were observed using scanning electron microscope. Three tests were repeated for study sensitivity of the SP test results under a same charging condition. It was observed that the variation of the maximum load, SP displacement at failure, hydrogen concentration as the charging period was not much in the case of X70 as the other steel such as Inconel. It can be argued that X70 base metal may have high hydrogen damage resistance and hydrogen diffusion in the base metal would not cause much embrittlement. Limitations of the SP test with 0.5 mm thickness for hydrogen damage test for X70 were discussed.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.29 no.10 s.241
• /
• pp.1407-1415
• /
• 2005

Strength change of an over-aged A12024 material was studied after being subjected to stages of severe plastic deformation by ECAP (Equal Channel Angular Pressing). Various kinds of strength value were measured using the conventional tensile test, Rockwell and Vickers hardness and the SP (small punch) test Due to limitation of the specimen size, tension test in transverse direction could not be conducted. Hence, SP test was employed for assessing the strength in transverse direction. Based on TEM observation the measured strength characteristics were explained based on the relation between microstructure, dislocation and strength. As the number of ECAP pass increases, the strength of A12024 was also increased. However, considerable change of strength, which is generally predicted, was not observed in this study. For the strength in transverse direction even decrease of the strength was observed after 6 passes of ECAP. It was argued that this decrease was due to dynamic recovery of dislocation density during or after ECAP processes at $150^{\circ}C$. The strength assessment equation proposed by the authors in the previous paper was shown to be very accurate. This argument was supported by comparing the results of conventional tensile test with those of SP test. It was also pointed that the Rockwell har(3ness value seemed to be able to represent the strength in the transverse direction.