• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.7 no.2
• /
• pp.324-333
• /
• 1997

Porous alumina specimens with 80~92% relative densities were prepared from ultrasonic spray pyrolyzed alumina Powders by sintering at $1600^{\circ}$~ $1700^{\circ}C$. The exaggerated grain growth appeared to high sintering temperature and long soaking time. The microstructural development during sintering was investigated using image analysis. In the study of grain growth kinetics for sintering for spray prolyzed alumina powder, the activation energy for normal grain growth was 386.77 kJ/mol.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2009.04b
• /
• pp.73-76
• /
• 2009

ZnBo이 첨가된 (Ba,Sr)$TiO_3$ 후막을 이용한 planner capacitor의 전기적 특성을 조사하였다. 후막은 알루미나 기판에 스크린 프린팅기법에 의해서 제작되었고 $1200^{\circ}C$의 온도에서 소결하였다. 출발 물질인 BST의 저온 소결을 위해서 ZnBO를 첨가하였다. ZnBO가 1, 3, 5 wt% 첨가된 경우 소결온도가 $1200^{\circ}C$의 낮은 온도에서 소결되는 것을 확인했으며 ZnBO의 첨가랑이 증가함에 따라서 유전율은 감소하고 유전손실는 증가 하는 현상이 나타났다. 1, 3, 5 wt%의 ZnBO가 첨가된 (Ba,Sr)$TiO_3$는 각각 756, 624, 554의 유전율를 보였다. 또한 ZnBO의 양이 증가함에 따라서 누설전류가 감소되는 것을 확인하였고, ZnBO의 첨가가 grain의 성장과 density가 증가되어 누설전류의 양이 감소하게 되는 것으로 분석되었다.

• Journal of the Korean Ceramic Society
• /
• v.38 no.5
• /
• pp.466-473
• /
• 2001

Ni-YSZ 음극의 미세구조와 임피던스특성에 미치는 YSZ 입자크기 및 소결온도의 영향을 고찰하였다. 0.3~0.6$\mu\textrm{m}$의 미세한 NiO 분말을 사용할 경우에는 NiO 분말과 크기가 비슷한 미세한 YSZ 분말(TZ8Y, 0.3$\mu\textrm{m}$)을 첨가했을 때 NiO의 입성장을 억제하는 효과가 가장 크고 환원후 Ni의 입자크기를 미세하게 유지할 수 있는 미세구조를 형성하였다. 또한 미세한 YSZ 분말 (TZ8Y, 0.3$\mu\textrm{m}$)과 조대한 YSZ 분말(FYT13.0, 2$\mu\textrm{m}$)의 혼합비를 달리하여 후막을 제조하였을 때에 TZ8Y 분말만 첨가한 조성이 가장 낮은 분극 저항을 나타내었다. 한편 소결온도는 삼상계면의 양과 분극저항에 영향을 주었으며, 140$0^{\circ}C$에서 소결한 시편의 분극저항이 가장 낮은 값을 나타내었다.

• Journal of the Korean Ceramic Society
• /
• v.37 no.11
• /
• pp.1065-1070
• /
• 2000

TiO$_2$의 첨가가 Mn-Zn ferrites의 전자기적 물성에 미치는 효과에 대해 연구하였다. TiO$_2$의 첨가량이 증가함에 따라 밀도와 전기비저항이 증가된 반면 초기투자율은 감소하였다. TiO$_2$의 첨가에 따라 Fe$^{2+}$ ion의 증가에 기인하여 전력손실의 최소 값을 나타내는 온도가 저온으로 이동하였다. TiO$_2$를 0.12wt% 첨가한 시편의 경우, 100 kHz, 200 mT, 8$0^{\circ}C$ 측정 조건에서는 소결온도가 증가함에 따라 전력손실이 감소하였으며 125$0^{\circ}C$ 소결한 시편이 340 mW/㎤으로 가장 낮은 값을 보였다. 500 kHz, 50 mT, 8$0^{\circ}C$의 측정 조건에서는 소결 온도가 감소함에 따라 전력손실이 감소하였으며 115$0^{\circ}C$ 소결한 시편이 105 mW/㎤으로 가장 낮은 전력손실 값이 관찰되었다.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.17 no.2
• /
• pp.75-81
• /
• 2007

Densification and grain growth have been investigated in 5 wt% $U_3O_8$ seeded $UO_2$ and compared with those of the common $UO_2$ pellet. $UO_2$ compacts and $U_3O_8$ seeded $UO_2$ compacts were sintered at $1300{\sim}1700^{\circ}C$ for 0 h to 4 h. Density and grain size of the sintered pellets were measured by the water immersion method and the image analyzer, respectively. The seeded pellet has a slightly lower density during the intermediate sintering stage. However, the difference of density between two pellets decreases to about 0.5%TD with increasing the sintering temperature. The grain size of the two pellets is similar until $1600^{\circ}C$ but that of the seeded pellet rapidly increases with increasing the sintering temperature.

• Transactions of the Korean Society of Mechanical Engineers B
• /
• v.34 no.11
• /
• pp.975-982
• /
• 2010

In this study, the laser sintering of inkjet-printed silver lines was evaluated. Silver-nanoparticle ink and a drop-ondemand (DOD) inkjet printer were used for printing on glass and polyethylene terephthalate (PET) substrates with various thicknesses. To sinter the printed silver nanoparticles, the silver layer printed on the transparent substrates was irradiated by focused CW laser beams that were incident normal to the substrates; the irradiation was carried out for various beam intensities and for various irradiation times. The electrical conductivity of the laser-sintered silver patterns was measured and compared with the conductivity of silver patterns sintered by using an oven. The increase in the temperature caused by laser irradiation was also calculated on the basis of the laser beam intensity, irradiation time, surface reflectivity, and thermophysical property of the substrate in order to estimate the increase in the electrical conductivity caused by laser sintering.

• Proceedings of the Korean Nuclear Society Conference
• /
• 1998.05b
• /
• pp.186-191
• /
• 1998

$UO_2$-5wt%CeO$_2$ 분말에서 소결온도(1600, 1$700^{\circ}C$), 소결분위기(H$_2$, $N_2$-7vol.%H$_2$) 및 Li$_2$O 첨가량(0.05-2wt%)에 따른 소결성의 변화를 관찰하였다. $UO_2$-5wt%CeO$_2$를 attrition mill에서 2 시간까지 분쇄한 후, 1$700^{\circ}C$에서 H$_2$, N2-7vol.%H$_2$ 분위기에서 소결하면 소결밀도가 각각 10.46, 10.36 g/㎤이지만, 각 분위기에서 소결체내의 결경립크기가 일정하지 않고 Ce agg1omerate도 소결체내의 여러 곳에 분포되어 있어 분말처리만으로 소결성을 개선하는데는 한계가 있었다. 반면에, $UO_2$-5wt%CeO$_2$에 0.lwt%Li$_2$O를 첨가하여 1 시간동안 분쇄란 후, 1$600^{\circ}C$에서 H$_2$$N_2$-7vol.%H$_2$ 분위기로 소결하면 밀도는 각각 10.51, 10.48 g/㎤이었고, 결정립크기는 각각 8.9, 42.1 $\mu\textrm{m}$이었다. 즉, Li$_2$O의 첨가에 의해 밀도와 결정립크기가 모두 증가했으며, H$_2$ 분위기보다는 $N_2$-7vol.%H$_2$ 분위기에서 결정립이 더 크게 성장하였고, 1$700^{\circ}C$에서도 유사한 경향을 나타내었다. $UO_2$-5wt%CeO$_2$와 이 조성에 0.lwt%Li$_2$O를 첨가한 분말들을 H$_2$ 및 $N_2$-7vol.%H$_2$ 분위기에서 소결하여 기공크기 및 기공부피의 변화를 관찰한 결과, H2 분위기에서 소결하였을 때는 Li$_2$O의 첨가에 의해 치밀화가 주로 일어났고, 반면에 $N_2$-7vol.%H$_2$ 분위기에서 소결하면 Li$_2$O의 첨가에 의해 작은 기공은 소멸되고 큰 기공이 생성되었다.

• Proceedings of the Korea Society for Energy Engineering kosee Conference
• /
• 2000.11a
• /
• pp.105-109
• /
• 2000

종래의 핵연료소결체가 혼합산화물 혹은 이산화우라늄중 한가지 핵연료만으로 구성한 것과 달리 내부를 저농축 이산화우라늄 핵연료로 채우고 그 외부를 링형태의 혼합산화물 핵연료로 둘러 싼 이중구조를 특징으로 한다. 이러한 형태의 핵연료소결체는 중심영역의 핵분열반응률 줄임으로써 핵분열 기체생성, 핵연료봉 중심온도와 평균온도를 낮추어 준다. 이는 핵분열 기체방출을 낮추어 혼합산화물 핵연료봉 성능을 향상시키고 방출 연소도를 증가시키는 효과가 있다.

• Journal of the Korean Magnetics Society
• /
• v.13 no.1
• /
• pp.29-35
• /
• 2003

Anisotropic Sr-ferrites were prepared by the spark plasma sintering process (SPS). The Ferrite particles were oriented and densified during sintering process, and the anisotropic ferrites were manufactured at low sintering temperature and a remarkable short time processing by SPS method. It was showed that the anisotropy of ferrite particles at the specimen outer side was more higher than that at the specimen center, and it seems possible that the orientation of ferrite particles was related to DC current. Magnetic and physical properties of sintered Sr-ferrites are Br = 3.15 kG, iHc : 2.67 kOe, and density : 5.033 g/cm$^3$ when the samples were sintered for 8 minutes at 106$0^{\circ}C$.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.10 no.2
• /
• pp.134-139
• /
• 2000

Ternary system of 40PMN-30PT-30PMW was prepared by using different reaction process. The PMN-PT was synthesized firstly, then it reacted to $PbWO_4$ as PbO and $WO_3$ sources. The dielectric constants were dependent on the density of sintered body and decreased with sintering temperature above $950^{\circ}C$. The highest dielectric constant was 24,000 in a sample sintered at $950^{\circ}C$ with the dielectric loss of 3 %. The temperature dependence of the dielectric constant were decreased with the increase of sintering temperature due to the appearance of double peak maxima. The lowest change in dielectric constant was -37-0 % from -55 to $125^{\circ}C$in a sample sintered at $1150^{\circ}C$ with dielectric constant of 9,900 at room temperature.