• Applied Chemistry for Engineering
• /
• v.16 no.5
• /
• pp.648-652
• /
• 2005

A super ionic conductor, $K^+$-beta-aluminas, which is known to be difficult to obtain in the form of dense sintered density under atmospheric pressure, was pulverized to 350 nm mean particle size using attrition mill. The sample were pressed into tablet form by uniaxial pressing. The specimen was sintered under atmospheric pressure in powder form. Sintering temperature range was $1400^{\circ}C$ to $1650^{\circ}C$ at $50^{\circ}C$ intervals. Additionally, zone sintering was carried out to control the growth grain at high temperature ($1600^{\circ}C$). The density of specimens that were sintered at $1600^{\circ}C$ and $1650^{\circ}C$, and sintered at $1600^{\circ}C$ by zone sintering were about 93% and 95%, respectively. In the case of the lengthened sintering time to 2 h, the density of specimen was reduced to lower than 90%, since the particles were grown to the duplex microstructure.

• Journal of the Korean Ceramic Society
• /
• v.36 no.3
• /
• pp.284-292
• /
• 1999

고체함량을 변화시킨 NiCuZn 페라이트 페이스트를 사용하여 스크린 인쇄법으로 7.7$\times$4.5$\times$1.0 nm 크기의 칩인덕터를 제조한 후, 페라이트 페이스트의 고체함량에 따른 수축률, 소결밀도, 미세구조, 계면반응 등의 물리적 특성 및 자기적 특성 변화를 분석하였다. 조온소결을 위하여 attrition milling 공정을 통하여 미세분말을 준비하였으며, 소결온도는 880~94$0^{\circ}C$로 변화시켰다. 90$0^{\circ}C$에서 2시간 열처리된 페라이트 후막의 소결밀도는 고체함량이 50,55,60%로 증가할수록 5.12,5.14,5.18g/㎤로 증가하였으며, 이에 따라 칩 인덕터 시편들의 주파수 10 MHz에서 L값이 2.1,2.3,2.5 $\mu$H로 커졌다.Q값은 소결밀도 증가에 의한 Q값 증가효과와 아울러 입자가 커짐에 따른 반대효과로 인하여 고체함량에 따라 87,90,94로 큰 변화가 없었다. 페라이트 페이\ulcorner의 고체함량 및 소결온도와 무관하게 Ag 성분의 페라이트 쪽으로의 확산현상은 나타나지 않았다.

• Journal of the Microelectronics and Packaging Society
• /
• v.5 no.2
• /
• pp.1-6
• /
• 1998

B2O3F2를 함유한 Fluormica glass-ceramics 분말과 Potashborosilicate glass 분말을 이용하여 저온소결용 기판을 제조하기 위하여 제조한 그린시트의 특성 및 소결체의 소결 특 성을 평가하였다. 기판 제조용 슬러리를 제조하기 위해 결정화유리분말에 Potashborosilicate glass 분말을 각각 0. 25, 50wt%를 혼용하였다. Doctor blade법으로 그린시트를 제조한후 그 특성을 평가한 결과 건조수축률은 15.2~30.7% 온도상승에 따른 유기물의 탈지온도는 414$^{\circ}C$(2시간)로 선정하였다. 그린시트는 800~120$0^{\circ}C$사이에서 소성하여 소결특성을 평가하였 다. 소결 수축률은 17.5~18.5% 겉보기 기공률은 16.53~20.07%였다.

• Korean Journal of Materials Research
• /
• v.7 no.5
• /
• pp.374-380
• /
• 1997

열전재료 분말을 AI관에 진공봉입하고 형틀가입한 후 소결하는 새로운 방법으로 n형 B $i_{2}$T $e_{2.4}$S $e_{0.6}$를 제조하여 소결조건에 따른 소결성과 열전특성을 조사.분석하였다. AI은 소결시 열전재료와 반응하지 않아 보호 용기로 적합하였으며, 평균입도 195$\mu\textrm{m}$의 분말을 사용하여 성형압 280 MPa, 온도 400에서 50$0^{\circ}C$에서 소결할 경우 성능지수는 1.9x $10^{-3}$K였다.다.

• Proceedings of the KIEE Conference
• /
• 2007.07a
• /
• pp.1355-1356
• /
• 2007

SMD type 압전레조네이터 제작을 위한 압전 조성물을 찾고자 PLT 세라믹스에 B-site Ti 자리에 Mn을 치환시키고 소결첨가제로서 CuO를 첨가하였다. $0{\sim}0.4wt%$ CuO를 첨가하여 1150, 1200, $1250^{\circ}C$로 각각 소결한 후 소결온도 및 CuO 첨가량에 따른 압전 및 유전특성을 관찰하였다. CuO 첨가량에 따라 1150, $1200^{\circ}C$ 소결시 밀도가 증가하였고, $1250^{\circ}C$ 소결시 기계적 품질계수가 증가하였다. 소결온도 $1250^{\circ}C$, 0.1wt% CuO 첨가시 밀도, 전기기계 결합계수(kp), 유전상수, 기계적 품질계수는 7.5[g/cm3], 0.1, 253, 1776을 각각 나타내었다.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2004.11a
• /
• pp.396-399
• /
• 2004

저온 동시소성용 glass-ceramics의 소결 경향성 연구를 위해 lead-borosilicate계 glass를 frit화하여 알루미나분말과 $TiO_2$분말을 $10{\sim}50\;vol%$로 각각 혼합한 후 여러 온도에서 소결하여 소결과 유전 특성을 조사하였다. 그 결과 glass의 연화온도(Ts)가 낮을수록 최대 치밀화 온도가 낮았으며, 반면에 소결밀도는 Ts가 높을수록 높았는데, 이는 glass-ceramicss에서의 결정화도와 관계하였다. 본 연구를 통해 glass-ceramic에서의 소결특성은 glass와 ceramic의 반응성에 의한 2상 석출 정도에 큰 영향을 받음을 알 수 있었으며, ceramic filler로서 알루미나와 $TiO_2$를 이용하여 $900^{\circ}C$에서 소성이 가능하였다. 알루미나의 경우 유전특성$({\epsilon}r=8.5,\;Q{\times}fo=6000)$이 기판용 저유전율 재료로 사용이 가능하였고, $TiO_2$의 경우도 유전특성($({\epsilon}r=17,\;Q{\times}fo=4000)$)이 필터용 고유전율 재료로 사용 가능하도록 높게 나타났다.

• Journal of Energy Engineering
• /
• v.10 no.3
• /
• pp.278-285
• /
• 2001

In this study, the effects of the variables on sintering of simulated fuel to simulate the spent fuel are described. Mainly, the effects of compaction pressure, sintering temperature and time on the density of pellet are described. The experimental is performed with compaction pressure of 1 ton/$\textrm{cm}^2$~4 ton/$\textrm{cm}^2$, sintering temperature of 167$0^{\circ}C$, 173$0^{\circ}C$ and 178$0^{\circ}C$ and sintering time of 4 hr, 8 hr and 24 hr. The green density of simulated fuel is proportional to the one third power of compaction pressure and the sintered density is 90.5~99.6% of theoretical density. The grain growth exponent and activation energy of simulated fuel is 2.5 and 287.97 kJ/mol, respectively.

• Journal of the Korean Ceramic Society
• /
• v.39 no.1
• /
• pp.51-56
• /
• 2002

The effect of kind of starting materials used for a sintering additive. magnesium acetate and magnesium nitrate, on the mechanical properties of alumina sintered body made by adding 1000 ppm of the additives, respectively, was investigated. As for the alumina sintered bodies prepared from magnesium acetate and magnesium nitrate, we observed that their relative densities decreased rapidly with increasing sintering temperature 1$600^{\circ}C$. Outer layer of alumina bodies had a duplex microstructure consisting of pores and grain growth. Also the inner layer had a second phase between alumina grain boundaries. By EPMA analysis, we confirmed that the grain boundary phase was a compound containing Mg.

• Electrical & Electronic Materials
• /
• v.6 no.5
• /
• pp.436-445
• /
• 1993

2단계하소법에 의해 낮은 하소온도에서 미세하고도 균일한 PZT분말을 합성하였다. 우선 Zr $O_{2}$와 Ti $O_{2}$ 혼합분말을 1차하소하여 (Z $r_{0.53}$ $Ti_{0.47}$) $O_{3}$(ZTO) 분말을 합성하고 이 ZTO 고용분말에 PbO와 N $b_{2}$ $O_{5}$을 혼합한 후 650-800.deg.C에서 2시간 하소하여 PZT 분말을 합성하였는데 얻어진 분말은 고상반응법에 비해 미세할 뿐만 아니라 XRD 분석결과 710.deg.C의 낮은 하소온도에서도 PZT 단일상을 나타내었다. 2단계하소법에 의해 하소온도를 낮출 수 있는 주된 이유로는 고상반응법에서는 중간생성물인 PbTi $O_{3}$상의 생성이 수반됨으로 850.deg.C 이상 되어야만 안전한 PZT가 생성될 수 있는 점을 들 수 있다. 또 2단계하소법에 의하면 950.deg.C이하의 낮은 소결온도에서도 치밀화가 미루어지는 소결이 가능함을 알 수 있었는데 이와같이 소결온도를 낮출 수 있는 것은 고상반응법에 비해 미세한 PZT 분말을 사용하였기 때문이라 풀이된다.이된다.

• Proceedings of the International Microelectronics And Packaging Society Conference
• /
• 2002.05a
• /
• pp.121-125
• /
• 2002

이동통신기기 등의 고주파용 LTCC(Low Temperature Co-fired Ceramic) LC filter의 소결결에 있어 기존의 소결공정인 전기로 소결공정과 microwave를 이용한 소결공정을 이용하여 소결하였을때 LC filter의 수축율과 무게감소, 그에 따른 밀도의 변화, SEM을 이용한 표면형상 분석을 통해 급속가열을 통한 공정시간의 단축, 낮은 에너지 소비로 인한 제조단가의 절감, 균일한 가열로 인한 소결온도의 저하 등의 장점을 갖는 microwave sintering을 적용할 수 있는 가능성을 제시하였다.