The sintering properties of hydroxyapatite isolated from tuna bone and hydroxyapatite-containing wollastonite sintered by solid-state reaction was investigated. As the sinterability of hydroxyapatite dependent upon the particle size by dry milling, it showed a sintering. But the hydroxyapatite-containing wollastonite was appeared good sinterability. On X-ray measurements, the major phases of hydroxyapatite-containing wollastonite by solid state reaction at $1250^{\circ}C$ were identified as hydroxyapatite and pseudowollastonite(${\alpha}-CaSiO_3$). And the phases appeared as whitlockite [$Ca_3(PO_4)_2$] by decomposition of hydroxyapatite at higher temperature above $1250^{\circ}C$. The shapes of microstructure on SEM images changed from porous to dense bulk by elevating temperature. The mean bending strength of hydroxyapatite-containing wollastonite sintered by solid-state reaction at $1300^{\circ}C$ was about 18 MPa, it was close to the cancellous bone's maximum strength, 20 MPa.

• Ceramist
• /
• v.17 no.4
• /
• pp.5-14
• /
• 2014

• Proceedings of the Materials Research Society of Korea Conference
• /
• 1998.05a
• /
• pp.103-103
• /
• 1998

• Proceedings of the Korean Radioactive Waste Society Conference
• /
• 2009.06a
• /
• pp.142-143
• /
• 2009

• Proceedings of the KWS Conference
• /
• v.43
• /
• pp.109-111
• /
• 2004

20 vol.$\%$ SiC를 포함한 두 층간의 $Si_{3}N_{4}/SiC$ 나노 복합재료는$\alpha$ $-Si_3N_4$,13 nm 크기의 나노탄소 분말 그리고 $5\;wt$\%\;Y_2O_3$의 분말로 두 단계 소결을 통하여 제작된다. $Si_3N_4$ 입계 사이의 결합은 소결 후 변하지 않고 남은 compact와 $51\~62\%$의 기공으로 얻어진 표면적 사이의 반응에 의해 생성된다. 이 연구에서는 Ti 합금을 SiC 층에 브레이징을 이용하여 제작하고 기계적 특성을 연구하였다. 다양한 변형율과 결합물의 강도, 변형율 증가에 따른 층간 변화를 연구하였다. 층간 파괴 형태는 금속과 브레이징 합금 사이의 파괴, 세라믹과 브레이징 합금 사이의 파괴, 그리고 세라믹 내부에서의 파괴를 보였다.

• Journal of the Korean Ceramic Society
• /
• v.36 no.2
• /
• pp.210-219
• /
• 1999

The fundamental dispersion property of Si2N4 and a combination of AlN and Nd2O3 as sintering additives in a variety of organic solvents such as alcohols, hydrocarbons, ketones, and ethers was investigated. The stabilization mechanism and interaction between organic functional groups of the various organic additives were studied to clarify the dispersibility of the ceramic particles in the nonaqueous suspending medium. characterization of the suspensions was based mainly on electrokinetic sonic amplitude(ESA) measurements and the flow curves obtained from the rheological studies as well as estimated Hamaker constants. It was found that the contribution of electrostatic repulsive forces to the Si3N4, AlN and Nd2O3 stabilization in organic media is appreciably greater than anticipated and is dependent on the physicochemical properties of organic solvents.

• Journal of the Korean Ceramic Society
• /
• v.50 no.3
• /
• pp.180-185
• /
• 2013

We investigated the characteristics of hot-pressed pure yttria ceramics, and annealed them in an oxidation atmosphere. Regardless of the heat treatment in the oxidation atmosphere, XRD analysis showed that all the samples had a $Y_2O_3$ phase without structural change. Even though the color variation of the hot-pressed $Y_2O_3$ ceramics was due to the sintering temperatures, the oxidation process turned the color of the $Y_2O_3$ ceramics into white. The color change during oxidation treatment appears to be related to oxygen defects. In addition, oxygen defects also affected the weight change and microstructure of the $Y_2O_3$ ceramics. The $Y_2O_3$ ceramic sintered at $1600^{\circ}C$ had a $5.03g/cm^3$ density, which is close to the theoretical density of $Y_2O_3$. As the sintering temperature increased, small homogeneous grains grew to large grains which affected the Vickers hardness. $Y_2O_3$ ceramics hot-pressed at $1600^{\circ}C$ and annealed at $1200^{\circ}C$ had a flexural strength of 140MPa.

• Journal of the Korean Ceramic Society
• /
• v.48 no.5
• /
• pp.354-359
• /
• 2011

Silicon nitride ceramics were prepared by microwave gas phase reaction sintering. By this method higher density specimens were obtained for short time and at low temperature, compared than ones by conventional pressureless sintering, even though sintering behaviors showed same trend, the relative density of sintered body inverse-exponentially increases with sintering temperature and/or holding time. And grain size of ${\beta}$-phase of the microwave sintered body is bigger than one of the conventional pressureless sintered one. Also they showed good bending strengths and thermal shock resistances.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2004.05a
• /
• pp.308-308
• /
• 2004

쾌속조형기술은 설계형상의 확인, 시작품의 제작, 금속 및 세라믹 부품에의 응용, 동시공학, 의료, 마이크로 머신 둥 제조업 전반에 걸쳐서 많은 응용이 이루어지고 있다 여러 가지의 기술들이 개발되고 이를 응용한 장비들이 생산되어 보급됨으로써 이러한 적용분야들은 점차 확대되고 있다. 본 연구에서는 분말을 소결, 적층하여 원하는 형상을 만들어내는 SLS(Selective Laser Sintering) 장비를 개발하는데 있어서 레이저 경로의 제어를 통한 분말을 소결시키는 부분인 레이저 주사 시스템(laser scanning system)을 개발하고자 한다.(중략)

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2009.11a
• /
• pp.77-77
• /
• 2009

$Pb(Zr,Ti_O_3$계 세라믹스는 우수한 압전 특성으로 인하여 압전변압기 및 액츄에이터, 센서 등 많은 분야에 응용이 되어져 왔다. 그러나, 최근 들어 $1000^{\circ}C$에서 급속도로 많은 휘발을 하는 PbO는 환경 및 인체에 나쁜 영향을 미칠 뿐 아니라 사용 후의 처리도 어려워 선진국에서는 사용을 제한하거나 줄이고 있는 추세에 있다. 따라서, PbO를 포함하지 않은 무연 (Lead-free)계 압전 세라믹스에 대한 연구가 많은 관심을 끌고 있으며 앞으로는E 장래성 있는 하나의 이슈 분야가 될 것이다. 이러한 Pb-based System 세라믹스를 대체 할 재료로서 $(Bi_{1/2}Na_{1/2})TiO_3$나 Tungsten-Bronze type, $(K_{1/2}Na_{1/2})NbO_3$ 등이 주로 연구가 되고 있다. 특히, alkali niobate를 기초로 한 $(K_{1/2}Na_{1/2})NbO_3(NKN)$은 무연 압전 물질로서 많은 주목을 받고 있다. 그러나, NKN의 주요 성분인 K 의 높은 조해성 때문에 일반적인 고상방법으로는 고 밀도의 세라믹을 얻기 힘들뿐더러 낮은 상전이 온도 때문에 많은 응용에는 제약이 되고 있다. 이러한 세라믹의 단점을 보완하고자 Hot forging, RTGG, SPS 등 과 같이 특수한 소결방법을 사용하여 고밀도의 세라믹을 제작하지만 이 방법들은 제품 대량 생산에 있어 경제적으로나 복잡한 제조과정을 고려할 때 매우 비효율적이라고 판단된다. 그러므로 $BaTiO_3$, $LiTaO_3$, Mg, Ca등을 첨가 시켜 소결을 향상시키고 고밀도를 얻기 위해 많은 연구가 진행 중이다. 따라서 본 연구에서는 Pb-based계의 세라믹스를 대체할 우수한 특성의 세라믹스를 제작하고자 기존의 $(K_{1/2}Na_{1/2})NbO_3(NKN)$세라믹스에서 낮은 용융온도 때문에 소결하기 어려운 $KNbO_3$를 제거한 $NaNbO_3$에 $LiNbO_3$와 $BaTiO_3$를 추가한 $NaLiNbO_3-BaTiO_3$세라믹스에 $K_4CuNb_8O_{23}$(KCN)을 첨가함으로서 이에 따른 압전 및 유전 특성을 조사하였다.