• Composites Research
• /
• v.26 no.1
• /
• pp.14-20
• /
• 2013

The electrospun PVDF containing CNT was made for fabricating materials of the actuator. The electrochemical and their actuating movement were evaluated for the actuator performance in the electrochemical environment. The actuator (which was fabricated by electrospinning) had some advantages, i.e., good dispersion and flexible properties. In the electrospinning process, the final product would have different forms based on different essential factors. In this work, electrospun nanofibers were aligned by using the drum-type collector, and the morphology was identified via the field emission-scanning electron microscope (FE-SEM). The uniform dispersion of CNT in PVDF nanofiber was observed by electron probe X-ray micro-analysis (EPMA) test. The results of tensile strength and electrical resistivity provided the aligned state. The electrospun CNT/PVDF nanofiber sheet on the aligned direction showed better mechanical and electrical properties than the case of the vertically-aligned direction. The efficiency and electrical capacities of electrospun CNT/PVDF nanofiber sheets were compared with the cast PVDF sheet for actuator application. Electrospun CNT/PVDF nanofiber sheet exhibited much better the case of actuator performance than cast neat PVDF actuator, due to the excellent electrical connecting areas.

• Journal of the Korean Geosynthetics Society
• /
• v.1 no.1
• /
• pp.53-61
• /
• 2002

Even though a lot of laboratory and field tests for asphalt pavements using geosynthetics have been conducted recently, any rational and systematic analysis for the economic efficiency of the asphalt pavement systems reinforced by using geosynthetics has not been proposed yet. In this study, the economic analysis considering the traffic characteristics for the glass fiber sheet reinforced asphalt pavement was performed using the Life Cycle Cost Analysis(LCCA) which is commonly used for the economic analysis technique. The economic efficiency for the glass fiber sheet reinforcement and the traffic characteristics was examined by applying the test results from the literature review to the economic analysis model.

• Journal of the Korean Wood Science and Technology
• /
• v.43 no.6
• /
• pp.861-867
• /
• 2015

The Compact Tension (CT) type test was performed in order to evaluate the fracture toughness performance of glass fiber-reinforced laminated timber. Glass fiber textile and sheet Glass fiber reinforced plastic were used as reinforcement. The reinforced laminated timber was formed by inserting and laminating the reinforcement between laminated woods. Compact tension samples are produced under ASTM D5045. The sample length was determined by taking account of the end distance of 7D, and bolt holes (12 mm, 16 mm, 20 mm) had been made at the end of artificial notches in advance. The fracture toughness load of sheet fiberglass reinforced plastic reinforced laminated timber was increased 33 % in comparison to unreinforced laminated timber while the glass fiber textile reinforced laminated timber was increased 152 %. According to Double Cantilever Beam theory, the stress intensity factor was 1.08~1.38 for sheet glass fiber reinforced plastic reinforced laminated timber and 1.38~1.86 for glass fiber textile reinforced laminated timber, respectively. That was because, for the glass fiber textile reinforced laminated timber, the fiber array direction of glass fiber and laminated wood orthogonal to each other suppressed the split propagation in the wood.

• Composites Research
• /
• v.33 no.5
• /
• pp.282-287
• /
• 2020

In the present study, a high-strength polyethylene terephthalate (PET) sheet was fabricated through a densification process of low melting PET fiber (LMF) combined PET sheet. During the thermal heat treatment process of the combined LMF, individual PET fiber was connected, which in turn leads to the improvement of the interfacial bonding force between the fibers. Also, the densification of the PET sheet leads to reduce macrospore density and in return could enhance the binding force between the overlapped PET networks. Consequently, the asprepared LMF-PET sheet showed about 410% improved tensile strength and the same elongation compared to before compression. Besides, the enhanced bonding force can prevent the shrinkage of the PET fiber network and exhibited excellent dimensional stability.

• Journal of the Korean Geotechnical Society
• /
• v.20 no.1
• /
• pp.13-19
• /
• 2004

The major distress types in the domestic asphalt pavement are fatigue cracking, reflection cracking, thermal cracking, and rutting. To decrease the pavement distress by reinforcing asphalt pavement with reinforcement interlayer in geosynthetics to the traditional pavement systems can improve these problems. This study conducted laboratory test with asphalt pavement reinforced by glass fiber sheet to fix systematically geosynthetic asphalt pavement system. Laboratory tests like wheel tracking test and crack resistance test are conducted to analyze the controlling effect of glass fiber sheet on cracking and rutting of asphalt pavement.

• Fiber Technology and Industry
• /
• v.11 no.1 s.41
• /
• pp.28-37
• /
• 2007

• Proceedings of the Korea Concrete Institute Conference
• /
• 2003.11a
• /
• pp.359-362
• /
• 2003

Carbon fiber sheet is attractive due to its good tensile strength, resistance to corrosion, and low weight. The strengthening of concrete structures with externally bonded carbon fiber sheets is increasingly being used for repair and rehabilitation of existing structures. However CFS strengthened beams break down under the service loads. As rupture strain is not reached ultimate value, reduction of the tensile strength is recommended. This study evaluate CFS tensile strength reduction factor which is required to analyze bending moment.

• KSCE Journal of Civil and Environmental Engineering Research
• /
• v.31 no.6A
• /
• pp.457-464
• /
• 2011

An experimental study was performed to evaluate the possibility of using stiff type PolyUrea(PU) on RC slab as a strengthening material. Stiff type PU(STPU) was sprayed on the bottom surface of the slab specimens, which were then attached with CFRP or GFRP sheets. Also the evaluation of the bond capacity, the single most influential parameter on strengthening of RC structures, was carried out the flexural capacity evaluation test results showed that the load carrying capacity of the PU specimen was greater and less than the unstrengthened and FRP sheet attached specimens, respectively. The STPU specimens showed a ductile flexural behavior in the plastic displacement range. With respect to bond capacity, the bond strength of all of the specimen exceeded the code required bond strength of 1.5 MPa. Also, the STPU sprayed specimen without using epoxy resin did not peel off when the tensile grip was applied for testing. The stability of the PU bond failure indicate a good bond strength of PU when applied to concrete.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.14 no.5
• /
• pp.79-86
• /
• 2010

This study was performed to evaluate the flexural behavior of Hybrid fiber sheet (HFC) and Hybrid fiber bar (HFB) strengthened reinforced concrete (RC) beams. According to test results, Hybrid fiber reinforcement strengthened RC beams showed approximately 60 to 200% higher reinforcing effects than that of un-reinforced specimens. In addition, the reinforced beams showed the ideal failure pattern, which is failed presenting the ductile behavior after yielding of the reinforcing bar. More specifically, in the case of HFB reinforced RC beams, the difference with puttying method was not apparent since HFB beams reinforced using the injection of epoxy and bonding of putty showed the similar failure patterns.

• Journal of the Korea Concrete Institute
• /
• v.23 no.4
• /
• pp.405-411
• /
• 2011

Using combinations of carbon and glass fiber composites normally used for strengthening of concrete structures, the hybrid effect from strengthening concrete structures using the composite is studied. To produce the hybrid effects, the specimens were made with optimum proportions of carbon fibers with glass fibers. Then, direct tensile tests were conducted on the hybrid FRP (fiber reinforced polymer) specimens. Unlike the woven fiber sheet currently used in construction sites, the FRP specimens have to be directly combined with the fibers, which make the work very complicated. Therefore, direct tensile test specimens manufacturing method based on the combination of high-tension carbon fibers and E-type glass fibers was proposed and the effects of hybridization is studied through the direct tensile test. By comparing the ductility index, the modulus of elasticity, and the stress-strain curves of the specimens, the most optimum glass to carbon fiber combination ratio for the hybrid FRP was found to be 9 to 1 with ductile K-type epoxy. The study results are discussed in detail in the paper.