• Journal of the Korea Concrete Institute
• /
• v.23 no.3
• /
• pp.321-330
• /
• 2011

Recently, the effects of high temperature and fiber content on the residual mechnical properties of high-strength concrete were experimentally investigated. In this paper, residual mechanical properties of concrete with water to cement (w/c) ratios of 0.55, 0.42 and 0.35 exposed to high temperature are compared with those obtained in fiber reinforced concrete with similar characteristics ranging from 0.05% to 0.20% polypropylene (PP) fiber volume percentage. Also, factors including pre-load levels of 20% and 40% of the maximum load at room temperature are considered. Outbreak time, thermal strain, length change, and mass loss were tested to determine compressive strength, modulus of elasticity, and energy absorption capacity. From the results, in order to prevent the explosive spalling of 50 MPa grade concretes exposed to high temperature, more than 0.05 vol. % of PP fibers is needed. Also, the cross-sectional area of PP fiber can influence the residual mechanical properties and spalling tendency of fiber reinforced concrete exposed to high temperature. Especially, the external loading increases not only the residual mechanical properties of concrete but also the risk of spalling and brittle failure tendency.

• The Korean Journal of Pesticide Science
• /
• v.19 no.3
• /
• pp.230-240
• /
• 2015

An IOM sampler equipped with glass fiber filter has been recently utilized instead of solid adsorbent, which was used to measure the inhalation exposure of agricultural operator to pesticides. The aim of this study is to validate the efficacy of an IOM sampler by measuring the trapping efficiency and breakthrough using kresoxim-methyl water-dispersible granule and fenthion emulsifiable concentrate. On LC-MS/ MS, minimum detection level was 12.5 pg and method limit of detection was 5.0 ng/mL. Good linearity ($R^2$ > 0.999) for matrix matched standards was obtained. Recoveries of pesticides from glass fiber filter were 102-109% (kresoxim-methyl) and 97-104% (fenthion) while those from XAD-2 resin were 94-98% (kresoxim methyl) and 93-100% (fenthion). Trapping efficiency test was performed with personal air pumps and IOM sampler (glass fiber filter) connected with solid adsorbent (XAD-2 resin) with two types of formulation (solid and liquid) which were diluted by standard rate and sprayed to IOM sampler. Those pesticides were trapped only in glass fiber filter without any breakthrough to solid adsorbent. After spiking of pesticides to glass fiber filter, breakthrough test was carried out with IOM sampler (glass fiber filter) which was connected with solid adsorbent. As a results, 87-101% of kresoxim-methyl and 96-105% of fenthion remained in spiked glass fiber filter, however, no pesticides were detected in second glass fiber filter and solid adsorbent. In conclusion, IOM sampler which equipped with glass fiber filter can be applied widely for pesticide inhalation exposure study since it has good trapping efficiency and adsorption capacity, regardless of the solid or liquid formulation.

• Korean Journal of Environmental Biology
• /
• v.32 no.1
• /
• pp.49-57
• /
• 2014

Orb-web spiders can be considered as an effective bio-indicative animal to monitor the ecological air pollution of certain habitat since they have limited shifting ability during their life spans. In this study we revealed the fine structural characteristics of booklung in the orb-web spider Nephila clavata, and its bio-indicative significance in the monitoring environmental asbestos exposure. The high resolution scanning electron microscopy results suggest that the cuticular spikes near the atrium could be act as an effective filtering structure for dust materials. Furthermore, inner cuticular spikes which protruded across the air sacs, have the functions not only sustaining appropriate respiratory volume of each air sac but also help to enhance respiratory capacity by maximizing the gross surface area for gas exchange. Interestingly, in spite of short exposure, the asbestose fibrils were effectively captured on the surface of the atrial cuticular spikes. Furthermore, histologic damages were observed due to penetration of asbestos fibrils through air sacs and fixed on the hemolymph space. In addition, although accumulated mass of hemocytes were observed near the fibrils, there were no asbestos bodies or coagulated hemocytes were found on the surface of the fibrils, This could be mainly due to the short exposure period towards asbestos. Briefly, these results indicate the spider's booklung could be valuable tool in the detection ecological air pollutants.

• Composites Research
• /
• v.30 no.2
• /
• pp.116-125
• /
• 2017

The purpose of this study is to develop silicon carbide fiber showing an excellent mechanical properties under highly oxidative conditions at high temperature. Polycarbosilane(PCS) as a preceramic precursor was used for making the SiC fiber. PCS fiber was taken by melt spinning method followed by melting the PCS at $300{\sim}350^{\circ}C$ in N2 gas. The Curing of PCS fiber was carried out in air oxygen chamber, prior to high temperature pyrolysis. Degree of cure was calculated by characteristic peak's ratio of Si-H to $Si-CH_3$ in FT-IR spectra before and after curing of PCS fiber. The properties of SiC fiber was affected greatly by the degree of cure. The SiC fiber produced by controlling fiber tension during heat treatment showed good properties. The SiC fiber exposed to $1000^{\circ}C$ at air from 1 min. up to maximum 50 hrs showed around 60% reduction in tensile strength. We found that large amount of carbon content on the fiber surface after long-term exposure has resulted in lower tensile strength.

• The Korean Journal of Financial Management
• /
• v.16 no.2
• /
• pp.383-404
• /
• 1999

본 연구는 우레나라 기업 및 산업의 환노출을 측정하고 이를 기업의 특성변수로 설명하려는 것이다. 기존 연구가 주별 및 월별 자료를 사용해서 특정 산업에 국한했던 것과는 달리 금융업을 포함한 전 산업을 대상으로 하였으며, 일별 자료를 사용해 이를 분석하였다. 환노출 추정을 위해, 1987년 1월부터 1997년 6월까지 상장된 우리나라 기업 및 산업의 일별 수익률을 종속변수로 하고 대미달러의 원화 환율 및 대엔화의 원화 환율, 달러대 엔화 환율 등의 변화율을 독립변수로 하는 모형을 설정하였으며, 이를 기존에 논의된 여러 모형을 통해 측정하였다. 측정결과 이자율을 차감하고 종속변수의 1차자기상관을 고려한 GARCH(1,1)모형의 설명력이 높았다. 우리나라 산업중에서는 섬유제품, 펄프 종이, 자동차판매 및 도매, 숙박 운송 등에서 유의한 환노출을 보였으며, 개별기업의 경우에는 1987년 1월부터 1990년 7월까지 대미달러 환율에 많이 노출되었으나, 1990년 8월부터 1994년 7월까지는 상대적으로 노출된 기업의 수가 적었다. 따라서 우리나라 산업 및 기업은 환노출에 있어서 산업효과와 기간효과를 갖고 있음을 알 수 있다. 기업특성변수와 환노출과의 관계를 분석한 결과는 일관되게 유의한 변수는 발견되지 못하였으며, 다만 특정 기간별 그리고 대미달러환율에 대해 기업규모와 금융비용부담률 등의 변수들이 유의하게 반응하고 있는 것으로 나타났다.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2007.04a
• /
• pp.133-136
• /
• 2007

It has been applied the self adhesion waterproofing sheet which is developed from exist asphalt waterproofing sheet by heat and torch in domestic construction field. However, the problem of waterproofing have constantly happened due to air pocket condition and defect of joint part in waterproofing construction. Therefore, in this study, we would like to analyze the field application as testing in side of materials and construction method of self adhesion butyl rubber sheet and study of the materials performance.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.16 no.3
• /
• pp.1-10
• /
• 2012

In spite of high resistant to corrosion and its strength, over the last two decades, concerns still remain about the durability of FRP materials under severe environmental and thermal exposures. In this paper, authors experimentally examine the combined degradation by thermal and chemical attacks in heterogeneous FRP rebar be made up with various fibers and resins. Five types of Carbon, Glass and Hybrid FRP rebars had manufactured by different process and surface patterns are adopted for the experiments such as weight change, interlaminar shear strength, SEM and FT-IR analysis. FRP specimens were immersed in alkaline or distilled solution up to 150 days and then thermal exposed on 60, 100, 150 and $300^{\circ}C$ for 30 minutes. From the test results, the degradation of FRP bars are influnced by the resin type and manufacturing process as well as the fiber, and ILSS of exposed FRP bar in solutions is slightly increased in initial stage and then decresed with the passing of immersed time. But, in this test, it is observed that the discrepancy of ILSS between degraded by alkaline solution and distilled water is negligible value.

• Fire Science and Engineering
• /
• v.25 no.5
• /
• pp.8-13
• /
• 2011

High strength concrete is the occurrence of explosive spalling associated with high temperature such as a fire. The spalling causes the sever reduction of the cross sectional area with the exposure of the reinforcing steel, which originates a problem in the structural behaviour. The purpose of this study is to investigate the mechanical properties of lightweight mortar using perlite and polypropylene fiber for fire protection covering material. For this purpose, selected test variables were the ratio of water to cement, the ratio of cement to perlite, contents of polypropylene fiber. As a result of this study, it has been found that addition of perlite and polypropylene fiber to mortar modifies its pore structure and reduces its density. And it has been found that a new lightweight mortar can be used in the fire protection covering material.

• Journal of the Korea Concrete Institute
• /
• v.14 no.2
• /
• pp.148-155
• /
• 2002

This research investigates the moisture and aging effects of wastepaper fiber-cement composites. Wastepaper fibers is obtained by a dry process. Wastepaper fiber-cement composites was manufactured by the hatscheck process. The effects of moisture and aging on the performance of wastepaper fiber-cement composites were investigated through accelerated laboratory tests simulating the effects of moisture sensitivity and wet-dry cycles as well as freeze-thaw cycles and long-term drying. They were shown to possess acceptable moisture and aging performance compared with virgin fiber cement composites.

• 월간산업보건
• /
• s.283
• /
• pp.51-62
• /
• 2011