• 대한기계학회:학술대회논문집
• /
• 대한기계학회 2007년도 춘계학술대회A
• /
• pp.706-711
• /
• 2007

Numerical studies were performed to examine the effects of notch location of impact specimens on the failure behavior of HAZ (heat affected zone) when Charpy V-notch impact test were made at a low temperature ($1^{\circ}C$). Carbon steel plate (SA-516 Gr. 70) with thickness of 25mm for pressure vessel was welded by SMAW (shielded metal-arc welding) and specimens were fabricated from the welded plate. Charpy tests were then performed with specimens having different notch positions of specimens varying from the fusion line through HAZ to base metal. A series of finite element analysis which simulates the Charpy test and crack propagation initiating at the tip of V-notch was carried out as well. The finite element analysis takes into account the irregular fusion line and non-homogenous material properties due to the notch location of the specimen in HAZ. Results reveals that the energies absorbed during impact test depend significantly on the notch location and direction of specimen. Finite element analysis also demonstrates that the notch location of specimens, to a great extent, influences the reliability and consistency of the test.

• Journal of Welding and Joining
• /
• 제13권1호
• /
• pp.89-102
• /
• 1995

The evaluation of reheat cracking susceptibility in CrMoV turbine rotor steel was performed using thermally simulated heat affected zones. The examinations were carried out in terms of microstructural characterization, microhardness measurement and a Charpy type notch opening three point bend test. It was found that reheat cracking susceptibility increased as the peak temperature increased. This effect was due to the combined effects of the carbide dissolution and unrestricted grain growth at 1350.deg. C peak temperature. Reheat cracking susceptibility was estimated based on microhardness measurement and prior austenite grain size. It was established that for this particular material, reheat cracking in coarse grained heat affected zone can be eliminated if the microhardness is below about 360DPH and the grain size is below about 30.mu.m. It is evident that reheat cracking susceptibility can be eliminated or reduced by carefully controlling the welding parameters such that a refined structure is produced in the coarse grained heat affected zone.

• Journal of Advanced Marine Engineering and Technology
• /
• 제40권9호
• /
• pp.774-779
• /
• 2016

본 연구에서는 선박의 곡 외판 구조에 TMCP 강재의 사용 범위 확대 가능성을 연구하고자 노말라이징강 및 TMCP 강 DH32 재질 강재에 선상가열 후 기계적 물성 시험을 실시하여 DNV 선급 및 IACS 규정의 품질 요구 기준에 적합한지 연구하였다. TMCP강재 인장시험에서 요구기준 YS = 315 MPa 대비 385 Mpa로서 약 18% 높게 나타났고, TS = 440 ~ 570 MPa 기준 대비 525 MPa로 요구 기준에 적합하였다. 샤르피 V-노치 $-20^{\circ}C$ 충격시험에서도 요구 기준에 적합하였으며 경도시험에서 평균 T : 216, L : 275로서 규정인 Hv10 = 130 ~320 범위에 만족 하였다.

• 한국강구조학회 논문집
• /
• 제10권1호통권34호
• /
• pp.85-99
• /
• 1998

본 논문은 케이슨의 인양작업중 Fitting Anchor의 취성파괴로 인한 들고리의 붕괴원인을 조사하기 위한 실험적 연구이다. 또한, 본 연구에서는 응력해석을 통하여 들고리의 붕괴메카니즘을 분석하고 이를 실제 붕괴과정과 비교한다. 본 연구에서는 파괴된 강재에 대한 파면해석 뿐만아니라 화학성분시험, 인장시험 및 샤르피 V-노치 충격시험을 실시한다. 그리고 이의 시험 결과를 정상적인 강재에 대한 시험결과와 비교한다. 본 연구의 거시적, 미시적인 방법으로 결함을 관찰한 결과, Fitting Anchor 내부에 원주방향으로 나타난 표면결함은 케이슨의 진수시 발생하는 들고리의 인장응력이 작용하기 전에 발생한 것임을 확인할 수 있었다. 이는 균열선단의 응력집중이 발생하여 작용응력보다 큰 응력이 결함에 발생한 것임을 알 수 있다. 또한, 잠재한 결함의 크기가 임계값 이상으로 증가하여 본 연구대상 강재의 응력확대계수가 증가하였을 것으로 판단된다. 그래서 균열선단의 응력확대계수가 본 강재의 파괴인성보다 크게 되어 케이슨의 인양작업중에 취성파괴를 일으킨 것으로 사료된다. 본 연구결과에 따르면 케이슨 들고리의 붕괴는 Fitting Anchor의 취성파괴로 발생한 것으로 사료된다.