• Journal of the Society of Cosmetic Scientists of Korea
• /
• v.40 no.3
• /
• pp.221-226
• /
• 2014

IIn this study, O/W type nano-emulsions were prepared by phospholipid-nonionic surfactant mixtures and octyldodecylmyristate using the phase transition low-energy emulsification method. The nano-emulsions were formed only in the very narrow area of the concentration of mixed surfactant and oil molar ratio of around 1 : 1. The particle size of the emulsions was decreased as adding the aqueous phase into the emulsions after phase inversion point unlike the emulsions formed only with nonionic surfactant. Nano-emulsion was stable at room temperature for more than a month. Thus, the nano-emulsions containing phospholipids can be widely used as a cosmetic formulations.

• Proceedings of the Korea Association of Crystal Growth Conference
• /
• 1996.06b
• /
• pp.239-257
• /
• 1996

$\beta$-BaB2O4는 고출력 가시광선 및 적외선을 발진시키는데 유용한, 비선형 특성을 가진 물질이다. $\alpha$-$\beta$ 상전이 온도가 녹는점보다 18$0^{\circ}C$ 낮기 때문에 보통 flux법으로 단결정을 성장시킨다. 수년전 Itoh등은 $\beta$-BaB2O4단결정을 congruent조성의 용액으로부터 Czochralski법으로 metastable한 상태에서 직접 성장시켰다. 그렇지만 그 공정은 잘 이해되지 않고 있으며 재현하기가 매우 어렵다. 저자들은 $\beta$-BaB2O4단결정을 용액표면온도도 1034$^{\circ}$-1085$^{\circ}C$, pulling rate 3mm/h, 10-30 rpm의 범위에서 성장시켰으며 융액표면의 온도구배는 $\beta$-상으로 성장시키는데 매우 중요한 인자로 여겨진다. Seed로는 직경 1-2mm의 c축방향 $\beta$-BaB2O4단결정 봉이 상용되어 성장방향을 조절하고 열응력을 최소화시켰다. 성장된 $\beta$-상의 단결정들은 6-fold모양을 하며 표면에 작은 비늘같은 것들이 붙어있고 중심부에 core가 있는 것을 알았다. Flux법으로 성장시킨 $\beta$-BaB2O4단결정을 사용한 seeds는 단결정 성장 및 냉각 중에 cracks이 자주 발생하였으며, boule의 cracks은 afterheater를 사용할 경우 다소 줄일 수 있었다. 성장된 단결정의 광학특성이 측정되었다.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.7 no.3
• /
• pp.359-365
• /
• 1997

$K_2CoCl_4$, single crystals were grown by the Czochralski method in Ar atmosphere. The thermal hysteresis of the dielectric constant at $T_c$ was investigated. $K_2CoCl_4$ crystal shows ionic hopping mechanism due to $K^+$ ion and the activation energy is nearly 0.62 eV. Thermal expansions along a-, b-, and c-axis of $K_2CoCl_4$, were measured on heating and the thermal expansion coefficients in each phase were calculated. From the result of the optical absorption measurement, we interpreted the absorption peak as transition energy between the splitted energy levels of the Co ion in the crystal field and it showed the possibility of the application to the optical band filter between 800 nm and 1200 nm.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.14 no.6
• /
• pp.267-271
• /
• 2004

Lithium cobalt oxide $(LiCoO_2)$ cathode powders for rechargeable battery have been successfully prepared using urea hydrolysis method. The obtained hydrolysis-derived precursors with different Li/Co molar ratio were calcined at various temperatures. Low temperature phase $(LT-LiCoO_2)$ and high temperature phase $(HT-LiCoO_2)$ were obtained after calcination at $500^{\circ}C$ for 2 hr, and phase transformation from $LT-LiCoO_2{\;}to{\;}HT-LiCoO_2$ was completely occurred over $700^{\circ}C$. The layered structure of $LiCoO_2$ was well developed with a rise in the calcination temperature. Charge-discharge test show that the lithium cobalt oxide with 1.2 molar ratio prepared at $800^{\circ}C$ has an initial discharge capacity as high as 152 mAh/g, and the relatively stable cycling characteristic with 9.2 % of capacity fading was obtained after 40th charge-discharge test.

• Journal of the Korean Ceramic Society
• /
• v.41 no.12 s.271
• /
• pp.900-906
• /
• 2004

Solid oxide fuel cells have a limitation in their low-temperature application due to the low ionic conductivity of electrolyte materials and difficulties in thin film formation on porous gas diffusion layer. These problems can be solved by improvement of ionic conductivity through controlled nanostructure of electrolyte and adopting nanoporous electrodes as substrates which have homogeneous submicron pore size and highly flattened surface. In this study, ultra-thin oxide films having submicron thickness without gas leakage are deposited on nanoporous substrates. By oxidation of metal thin films deposited onto nanoporous anodic alumina substrates with pore size of $20nm{\sim}200nm$ using dc-magnetron sputtering at room temperature, ultra-thin and dense ionic conducting oxide films with submicron thickness are realized. The specific material properties of the thin films including gas permeation, grain/gran boundaries formation, change of crystalline structure/microstructure by phase transition are investigated for optimization of ultra thin film deposition process.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.7 no.4
• /
• pp.640-647
• /
• 1997

Wagnerite ($Mg_2PO_4F)$ was successfully synthesized in a sealed platinum tube and the complete substitutions of $Co^{++}, Ni^{++}, Cu^{++} \;and\;Zn^{++}$for Mg were made in the wagnerite structure. Wagnerite did not decompose until it reached its melting temperature. It was observed that wagnerite underwent only one inversion at $1255^{\circ}C$, prior to melting at $1340^{\circ}C$. The lattice parameters of wagnerites were linearly increased by the substitutions of $Co^{++}$ and $Zn^{++}$ and decreased by the substitutions of $Ni^{++}$ and $Cu^{++}$. The substitutions of wagnerite with $Co^{++}, Ni^{++}$ and $Cu^{++}$ resulted in purple, orange and green colors, respectively, The colors of pigments became more intense and suitable for coloring of glazes and plastics as the amount of metal ions increased.

• Applied Microscopy
• /
• v.32 no.4
• /
• pp.311-317
• /
• 2002

There is great requirement on the TEM specimen preparation method with particle size selectivity as a prerequisite for the quantitative structure analysis on the materials such as gibbsite powder, which generally forms a large agglomerate and shows a variation of transition process depending on their sizes. In this experiment, we made an attempt to give a methodology for the TEM specimen preparation of powder with the size selectivity. After mixing 1 wt% gibbsite powder with ethanol solvent, gibbsite suspension was prepared by application of ball-milling and ultrasonification with addition of 0.25 vol% dispersion agent, Darvan C, which was diluted into distilled water by the ratio 1:19. Appling the static sedimentation method to gibbsite suspension after estimation of the sedimentation time by the measurement of accumulative concentration variation, we acquired TEM specimens with well-dispersed and size selected gibbsite particles in nm scale. Overall picture of each sample was taken by SEM and morphology of each dispersed particle was imaged by TEM. Raw and processed gibbsite powders were also examined by XRD to investigate whether they were suffered from phase change during the process or not.

• Korean Journal of Materials Research
• /
• v.5 no.1
• /
• pp.3-11
• /
• 1995

$(TiO_{2})$ thin films were deposited on p-Si(100) substrate by APMOCVD using titanium isopropoxide as a source material. The deposition mechanism was well explained by the simple boundary layer theory and the apparent activation energy of the chemical reaction controlled process was 18.2kcal /mol. The asdeposited films were polycrystalline anatase phase and were transformed into rutile phase after postannealing. The postannealing time and the film thikness as well as the postannealing temperature also affected the phase transition. The C-V plot exhibited typical charateristics of MOS diode, from which the dielectric constant of about 80 was obtained. The capacitance of the annealed film was decreased but those of the Nb or Sr doped films were not changed. I-V characteristics revealed that the conduction mechanism was hopping conduction. The postannealing and the doping of Nb or Sr cause to decrease the leakage current and to increase the breakdown voltage.

• KIPS Transactions on Computer and Communication Systems
• /
• v.3 no.9
• /
• pp.273-278
• /
• 2014

Recent use of electricity during peak hours electricity supply-demand imbalance is inevitable that limit power use force. Therefore, in this paper, a circuit of parallel power operation equipment for peak power reduction which saves the power to electricity storage device during the non-peak power time and supply from the storage power during the expected power shortages time is designed Through this circuitry, the peak power of the commercial power supply with the parallel operation and connection of the commercial power supply and the power supply of the inverter from electricity storage that is a key feature of PRS(Peak power Reduction System) can be controlled. In addition, in order to increase the efficiency, a Transless Power Circuit DC-AC inverter is developed. Moreover, a variable impedance control is applied to the storage of electric power of an Uninterruptible Power Supply associated with a commercial power source.

• Korean Journal of Materials Research
• /
• v.10 no.1
• /
• pp.34-40
• /
• 2000

The $Pb_{0.94}Y_{0.04}[(Zr_{0.6}Sn_{0.4})_{0.915}Ti_{0.085}]O_3$ ceramics which corresponded to the antiferroelectric-ferroelectric phase boundary composition were prepared for digital-type-piezoelectric/electrostrictive device application. Their dielectric, field-induced polarization (P) and strain (X) behaviors were studied with variations in sintering condition and excess PbO content. The orthorhombic structure of specimens was hardly affected either by excess PbO addition or sintering temperature. With increasing excess PbO content, grains tended to be smaller and rounded ones, and the optimum sintering temperature was lowered. Excess PbO addition stabilized the antiferroelectric phase of the specimen effectively, which was confirmed by P-E and X-E analyses. Also the digital-type-strain character was found to be enhanced despite of slight increase in phase transition (AFE-FE) field and electrical resistivity, and decrease in maximum strain. These results were explained in terms of possible lattice defects and domain wall motion.