• Restorative Dentistry and Endodontics
• /
• v.26 no.2
• /
• pp.171-179
• /
• 2001

The purpose of this study was to evaluate the shear bond strength of compomers according to dentin surface treatment. Two materials of compomer were devided into six groups. The compomer used in this study were Dyract AP(D) and F2000(F), Group 1 (DN) and 4(FN) were treated according to manufacturers instructions as control groups. Group 2(DE) and 5(FE) were treated with 37％ phosphoric acid and group 3(DA) and 6(FA) were treated with air abrasion unit (80 psi, 50 m aluminum oxide particles) respectively as experimental groups. After dentin surface treatment, compomers were bonded. Completed samples were stored in 100％ humidity. 37C during 7 days, and then, the shear bond strength of specimens were evaluated. The results were as follows: 1. In the case of Dyract AP, the shear bond strength was showed the highest value of 9.10 MPa in dentin surface treatment with air abrasion unit. but there were no significant differences to the other groups. 2. In the case of F2000. the shear bond strength was showed the highest value of 13.51MPa and there were significant differences to the other groups(p<0.05). 3. The shear bond strength of F2000 was higher than Dyract AP in each dentin surface treatment. and in the case of etching and air abrasion. there were significant differences(p<0.05). 4. As a result of observation of SEM. the most of fracture pattern was adhesive failure in group 1(DN), 2(DE) and 4(FN), and cohesive failure in group 3(DA), S(FE) and 6(FA).

• The Journal of Korean Academy of Prosthodontics
• /
• v.51 no.1
• /
• pp.20-26
• /
• 2013

Purpose: The purpose of this study was to evaluate the bond strengths between the latest CAD/CAM ceramic inlay and various resin cements which are used primarily for esthetic restoration. Materials and methods: Cylindrical ceramic blocks(Height: 5 mm, diameter: 3 mm) were fabricated by using Cerec3 and bonded on the dentin of the ninety extracted caries-free molars using three different kinds of resin cement(Unicem$^{(R)}$, Biscem$^{(R)}$, and Variolink II$^{(R)}$) according to the manufacturer's instructions. Ninety specimens were divided into 3 groups according to three different kinds of resin cement. Half of each group were conducted thermocycling under the conditions of the $5-55^{\circ}C$, 5,000 cycle but the other half of them weren't. All specimens were kept in normal saline $37^{\circ}C$, for 24 hours before measuring the bond strength. The shear bond strength was measured by Universal testing machine with a cross head speed of 0.5 mm/min. The results were analyzed statistically by t-test and one-way ANOVA. Results: Unicem$^{(R)}$ group showed the highest shear bond strength despite a slight decline by thermocycling. The shear bond strength of Unicem$^{(R)}$ group and ValiolinkII$^{(R)}$ group were significantly influenced by thermocycling, whereas Biscem$^{(R)}$ group was not influenced (P<.05). There were no significant differences in the bond strength between the three groups without thermocycling, but there was significant differences between Unicem$^{(R)}$ group and Valiolink II$^{(R)}$ group with thermocycling(P<.05). Conclusion: It has been shown to be clinically effective when the self-adhesive resin cements Unicem$^{(R)}$ and Biscem$^{(R)}$ were used instead of the etch-and-rinse resin cement Valiolink II$^{(R)}$ during the bonding of CAD/CAM ceramic inlay restorations with teeth.

• Restorative Dentistry and Endodontics
• /
• v.25 no.4
• /
• pp.550-560
• /
• 2000

In this study, shear bond strength of two bonding systems were measured and appearance of dentin surfaces were observed with SEM according to the storage time of eugenol on dentin surface, thus evaluated the effect of eugenol on bond strength of two dentin bonding systems. Control groups were directly bonded to dentin surface with One Step, Prime & Bond 2.1. Experimental groups were divided into experimental I and II according to dentin bonding agents. After eugenol application, dentin surfaces were bonded with One Step and Prime & Bond 2.1 according to the each storage time of immediately, 3min, 24hour, 48hour and 1week, and then control and experimental groups were filled with light cured composite resin(Z-100). After 24 hours water storage at $37^{\circ}C$, all samples were subjected to a shear load to fracture at a cross head 1.0mm/min with Instron universal testing machine(No. 4467). Etched dentin surface storaged for each time of immediately, 3min, 24hour, 48hour and 1 week after eugenol application were observed under Scanning Electron Microscope(Hitachi S-2300) at 20kvp. The data were evaluated statistically with two-way ANOVA and Tukey's HSD. The results were as follows; 1. Shear bond strengths were higher in control groups than in the experimental groups. 2. As storage time was increased after eugenol application, the shear bond strengths were decreased in experimental groups. 3. In experimental I, II the shear bond strengths were the lowest in which storage time was 1 week after eugenol application. 4. As storage time was increased after eugenol application, etched dentin surfaces showed obstructed dentinal tubule.

• Restorative Dentistry and Endodontics
• /
• v.29 no.4
• /
• pp.339-345
• /
• 2004

The aim of this study was to measure and compare the micro shear bond strengths of the following dentin bonding systems to the dentin surfaces under simulated pulpal pressure: All Bond $2^{\circledR},{\;}Second^{\circledR},{\;}AdheSE^{\circledR}$, Adper Prompt $L-Pop^{\circledR}$. The occlusal surfaces of 180 extracted human molars were prepared so the dentin bonding surfaces could be exposed. The teeth were randomly assigned to 3 equal groups of 60 each and subdivided. The dentin surfaces were treated with the above mentioned bonding system and resin composite cylinders were built up under a simulated pulpal pressure when saline (Group II) or diluted bovine serum (Group III) was used as the pulpal fluid. As a control. the same procedures were performed in the dried dentin surfaces (Group I). After one day of storage in water. the micro shear bond strengths were measured using an EZ tester. Group II and III showed significantly lower shear bond strength than Group I statistically (p < 0.05). $SEbond^{\circledR}{\;}and{\;}AdheSE^{\circledR}$ showed no difference among the different dentin condition. In the Adper Prompt $L-Pop^{\circledR}$. a simulated pulpal pressure were applied to the specimens using diluted bovine serum. which showed a higher strength than the specimens in which saline was used (p < 0.05).

• Journal of the korean academy of Pediatric Dentistry
• /
• v.29 no.1
• /
• pp.107-114
• /
• 2002

The purpose of this study was to determine and compare the shear bond strength of two self-etching primer systems to primary teeth contaminated with saliva and blood. Clearfil SE Bond and AQ Bond were evaluated. One hundred specimens were made by seventy-five deciduous teeth(fifty anterior and twenty-five posterior teeth) and divided randomly into ten groups. Small flat dentinal surfaces were prepared by grinding the buccal, lingual and labial areas. Specific surface treatments were applied to each group: (1) a self-etching primer application(control group), (2) saliva contamination followed by primer(Group I), (3) primer curing followed by saliva contamination (Group II), (4) blood contamination followed by primer(Group III), (5) primer curing followed by blood contamination(Group IV). After bonding of composite resin(Z100, 3M, USA) to contaminated sample surfaces and thermocycling(1,000 cycles), shear bond strengths were measured using Universal Testing Machine(Zwick Z020, Zwick Co., Germany). The results were as follows; 1. Group I showed lower shear bond strength than control group but no statistically significant difference was found(P>0.05). 2. Group II and blood contamination group(Group III & IV) showed significantly lower shear bond strength than control group(P<0.01). 3. The shear bond strength of Clearfil SE Bond was significantly higher than that of AQ Bond(P<0.05).

• Restorative Dentistry and Endodontics
• /
• v.24 no.3
• /
• pp.465-472
• /
• 1999

The aim of this study was to determine the shear bond properties of four dentin bonding systems to internal cervical dentin, and to investigate the effect of the pretreatment for removing smear layer and position of dentin on shear bond strength of dentin bonding agents. The materials tested in this study were consisted of four commercially available dentin bonding systems[Allbond 2(AB), Clearfil Linerbond 2(CL), Optibond FL(OP), Scotchbond Multi-purpose(SB)], a restorative light-cured composite resin[Z100]J and a chelating agent[RC-prep(RC)]. Fifty-six freshly extracted human molars were used in this study. Dentin specimens were prepared by first cutting the root of the tooth 1mm below the cementoenamel junction with a diamond bur in a high speed handpiece under air-water coolant, and then removing occlusal part at pulp horn level by means of a second parallel section, The root canal areas were exposed by means of cutting the dent in specimens perpendicular to the root axis. Dentin specimens were randomly assigned to two groups(pretreated group, not-pretreated group) based on the pretreatment method of dentin surface. In pretreated group, RC was applied to dentin surface for 1minute and then rinsed with NaOCl. In not-pretreated group, dentin surface was rinsed with saline Each groups were subdevided into four groups according to dentin bonding systems. Four dentin bonding systems and a restorative resin were applied according to the directions of manufacturer. The dentin-resin specimens were embedded in a cold cure acrylic resin, and were cut with a low speed diamond saw to the dimension of $1{\times}1mm$. The cut specimens were divided into three groups according to the position of internal cervical dentin. The shear bond properties of dentin-resin specimens were measured with Universal testing machine (Zwick, 020, Germany) with the cross head speed of 0.5mm/min. From this experiment. the following results were obtained : 1. In case of shear bond strength, there was no significant difference among dentin bonding systems in not-pretreated groups, whereas in pretreated groups, the shear bond strengths of AB and of SB were statistically significantly higher than those of CL and of OP. 2. The shear bond strengths of AB and of SB in pretreated groups were significantly higher than those in not-pretreated groups. 3. The shear bond strengths of radicular layer of OP were higher than those of occlusal layer of OP in not-pretreated groups, and of AB in pretreated groups. The shear bond strengths of radicular layer of AB and of CL in not-pretreated groups were higher than those in pretreated group.

• Restorative Dentistry and Endodontics
• /
• v.23 no.2
• /
• pp.597-606
• /
• 1998

The purpose of this study was to evaluate the shear bond strength of the Compoglass Carvifil bonded on the dentin surface according to etching or non-etching and two time application or three time application of single component. Human non-carious 60 extracted 3rd molar were used. The occlusal dentin surfaces of all teeth were exposed with Diamond Wheel Saw and polished with Lapping & Polishing machine(South Bay Technology Co., U.S.A). The teeth were then distributed randomly into four groups of 15 teeth each and dentin surface were conditioned as following. Control group : Non-etching, two times application of Syntac Single Component. (According to manufacture's instruction) Experimental group 1 : Non-etching, three times application of Syntac Single Component. Experimental group : 2 Etching, two times application of Syntac Single Component. Experimental group 3 : Etching, three times application of Syntac Single Component. Compoglass were bonded to exposed dentin surfaces and all samples were placed in distilled water for 7 days. The shear bond strengths were measured by universal testing machine (SHIMADAZU AUTOGRAPH, AGS-4D., Japan). The results were as follows : 1. Experimental group 3 revealed the highest value (30.75${\pm}$4.74 MPa) and control group revealed the lowest value(14.85${\pm}$2.69 MPa). There was significant difference of shear bond strength among four groups(P<0.01) 2. The acid-etching groups (experimental group 2, 3) had higher shear bond strengths than non etching groups(control group and experimental group 1). 3. The additional application of Syntac single component groups revealed a higher bond strength than two times application groups (control group and experimental group 2).

• Journal of the korean academy of Pediatric Dentistry
• /
• v.23 no.4
• /
• pp.867-886
• /
• 1996

The purpose of this study was to evaluate the shearbond strength and resin-dentin interface of three different dentinal bonding systems in primary and permanent teeth. Thirty extracted human primary molars and premolars, which were non-carious and free of obvious defect, were selected for this study. All specimens were divided into six groups with two groups allocated for each of the three dentinal bonding system(All-bond 2, Scotchbond Multi-Purpose, Gluma bonding system). After completion of bonding composite to dentin using each tested dentin bonding system, bond strength measurement and histological observation were performed. The results are as follows: 1. All-bond 2 and Scotchbond Multi-Purpose, A good quality hybrid layer was identified, the morphology of which could be equated with the zone of H-E and Brown-Brenn staining. In Gluma bonding system, hybrid layer was very thin, and separated from the solid polymer. 2. All-bond 2 had the highest mean shearbond strength, followed by Scotchbond Multi-Purpose and Gluma bonding system in both primary and permanent teeth. There was no statistically significant difference between All-bond 2 and Scotchbond Multi-Purpose. Statistically significant difference could be found between Gluma bonding system and the other two groups(p<0.05). 3. The fracture patterns observed were mainly the mixture of adhesive failure and dentin dettachment pattern in All-bond 2 and Scotchbond Multi-Purpose while adhesive failure prevailed in Gluma bonding system.

• Restorative Dentistry and Endodontics
• /
• v.29 no.4
• /
• pp.353-364
• /
• 2004

The purpose of this study was to compare and to evaluate the combination use of 5 kinds of dentin adhesive systems and 5 kinds of composite resins using micro-shear bond test. Five adhesive systems (Prime & Bond NT (PBN). Onecoat bond (OC), Excite (EX), Syntac (SY), Clearfil SE bond (CS)) and five composite resins (Spectrum (SP), Synergy Compact (SC), Tetric Ceram (TC), Clearfil AP-X (CA), Z100 (Z1)) were used for this study ($5{\;}{\times}{\;}5{\;}={\;}25group$, n =14/group). The slices of horizontally sectioned human tooth were bonded with each bonding system and each composite resin, and tested by a micro-shear bond strength test. These results were analyzed statistically. The mean micro-shear bond strength of dentin adhesive systems were in order of CS (22.642 MPa), SY (18.368 MPa), EX (14.599 MPa). OC (13.702 MPa). PBN (12.762 MPa). The mean bond strength of self-etching primer system group (CS, SY) in dentin was higher than that of self-priming adhesive system groups (PBN, EX, OC) significantly (P<0.05). The mean bond strength of composite resins was in order of SP (19.008 MPa), CA (17.532 MPa). SC (15.787 MPa), TC (15.068 MPa). Z1 (14.678 MPa). Micro-shear bond strength of SP was stronger than those of other composite resins significantly (P < 0.05). And those of TC and Z1 were weaker than other composite resins significantly (P < 0.05). No difference was found in micro-shear bond strength of composite resin in self-etching primer adhesive system groups (CS, SY) statistically. However, there was significant difference of micro-shear bond strength of composite resin groups in self-priming adhesive systems group (PBN, EX, OC). The combination of composite resin and dentin adhesive system recommended by manufacturer did not represent positive correlation. It didn't seem to be a significant factor.

• Restorative Dentistry and Endodontics
• /
• v.23 no.1
• /
• pp.401-412
• /
• 1998

The aim of this study was to measure the regional micro-shear bond strength of dentin bonding agents to dentin, and to investigate the relationship between the micro-shear bond strength and two dentinal characteristics ; Vickers hardness and remaining dentin thickness. Twenty-four freshly extracted, noncarious human molars were selected for this study. The materials tested in this study consisted of two commercially available dentin bonding agents (MAC-BOND, ONE-STEP) and two restorative light-cured composite resins (AELITEFIL, Z100). The occlusal or side surface of tooth crown was sectioned to expose dentin, and the exposed surface was finally polished with # 600 sandpaper. Four groups of application methods were used combining the filling materials and the dentin bonding agents. The composite resin-attached tooth specimens were embeded in a cold cure acrylic resin, and were cut with a low speed diamond saw to the dimension of 1mm $\times$ 1mm. Nine specimens were obtained from each tooth. The cut specimens were divided into three groups depending on the position of the dentin bonding surface. The micro-shear bond strength, remaining dentin thickness, and dentinal hardness were measured. Experimental results were then statistically analyzed with ANOVA. t-test, Scheffe test, and regression analysis. From this experiment, the following results were obtained : 1. In the case of occlusal surface bonding, the pooled micro-shear bond strength of ONST-AELIT group (16.62 MPa) was significantly higher than that of MACB-AELIT group (9.91 MPa) (p<0.05). However, there was no significant difference in the micro-shear bond strength depending on the dentin position (p>0.05). 2. In the case of side surface bonding of crown, the pooled micro-shear bond strength of four different bonding groups was not significantly different among each other (p>0.05). However, in three of the test groups (ONST-AELIT, MACB-Z100, ONST-Z100), the micro-shear bond strength to the lower 1/3(III) position was significantly lower than that to middle 1/3(II) position of surface (p<0.05). 3. In the ONST-AELIT bonding group, the pooled micro-shear bond strength to the occlusal surface was significantly lower than that to the side surface of crown (p<0.05). 4. There was no significant correlation between the micro-shear bond strength and dentin hardness / remaining dentin thickness (p>0.05).