• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.04a
• /
• pp.69-70
• /
• 2006

고주파 유도가열 연소합성법에 의해 2분 이내의 짧은 시간에 단일 공정으로 ZrC와 3Si의 혼합 분말로부터 $ZrSi_2-SiC$ 복합재료의 합성과 치밀화가 동시에 이루어졌다. 60MPa의 압력과 90%의 고주파 출력을 가하여 제조된 복합재료의 상대밀도는 약 97%였으며, $ZrSi_2$ 상과 SiC의 평균 결정립 크기는 약154nm와 78nm이었다. 비커스 경도계를 이용하여 측정된 $ZrSi_2-SiC$ 복합 재료의 경도와 파괴인성 값은 각각 $1180kg/mm^2$과 $2.5MPa{\cdot}m^{1/2}$ 이었다.

• Journal of the Korean Society of Manufacturing Process Engineers
• /
• v.3 no.1
• /
• pp.45-51
• /
• 2004

In this paper, the relationship between the mechanical properties of alumina abrasives and grinding performance was investigated. Micro vickers hardness and fracture strength of all abrasives used in this study were measured. The grinding experiments were earned out with alumina grinding wheels made by various kinds of alumina abrasives including 32A, WA, ART, ALOMAX, and RA. The performance of such grinding wheel for grinding SKD11 was evaluated by specific grinding energy, grinding-ratio, and surface roughness. The grinding wheels composed by the harder abrasives and the lower fracture strength abrasives showed better grinding performance.

• Journal of Advanced Marine Engineering and Technology
• /
• v.23 no.6
• /
• pp.806-813
• /
• 1999

The effect of Post-Weld Heat Treatment(PWHT) of SS400 Steel was investigated with parameters such as micro vickers hardness corrosion potential polarization behaviors galvanic current Al anode generating current Al anode weight loss etc. Hardness of each parts(HAZ, BM, WM)by PWHT is lower than that of each parts by Non Post-Weld Heat Treatment(NPWHT) However hardness of WM of HAZ part was the highest among those three parts and HAZ area were also acted as cathode without any case of heat treatment. Potential difference between each three parts by PWHT was also smaller compared to NPWHT. Therefore it is suggested that Corrosion resistance property is increased by PWHT. However both Al anode generating current and anode weight loss was also decreased by PWHT compared to NPWHT when SS400 steel is cathodically protected by Al anode.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2012.11a
• /
• pp.140-140
• /
• 2012

로듐은 열전도성 및 전기전도도가 우수할 뿐 아니라 산/알칼리에 잘 부식되지 않으며 강한 내구성을 지니고 있어서 장식 및 액세서리의 표면처리 및 각종 전기/전자산업의 부품으로 널리 이용되어지고 있다. 본 연구에서는 반도체 검사 장비인 프로브 카드에 조립되어 있는 프로브 니들의 내마모성을 향상시키기 위하여 로듐도금의 특성을 연구하였다. 로듐의 이온 공급원으로 Rhodium sulfate 를 사용하였다. 시편은 황동 시편($0.5cm{\times}2cm$)을 사용하였다. 로듐 도금 시 여러 가지 제어인자 중도금욕의 온도(상온, $40^{\circ}C$, $60^{\circ}C$)와 황산농도(10ml/l, 50ml/l, 100ml/l) 그리고 전류밀도(0.2ASD, 0.5ASD, 1.0ASD)를 변수로 하여 실험을 하였다. 각각의 변수에 따라 전류 효율 및 전착 속도를 분석하였으며, 현미경을 이용하여 표면을 관찰하였다. 그리고 비커스 경도계를 이용하여 경도를 측정하였다.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2013.05a
• /
• pp.192-192
• /
• 2013

하이브리드 표면처리는 다른 표면처리법을 동시 또는 연속적으로 행하여 단일표면처리에 비해 더욱 우수한 특성을 부여시키기 위한 표면처리법이다. 본 연구는 붕소와 질소 원소를 이용한 하이브리드 표면처리를 오스테나이트계 스테인리스강인 STS 316L 소재에 적용하여 변화된 특성을 평가하였다. 본 실험에 사용된 하이브리드 표면처리법으로는 붕소분말을 이용한 보로나이징처리와 활성스크린을 이용한 이온질화처리법을 적용하였다. 하이브리드 표면처리된 STS 316L시편은 FE-SEM을 이용하여 표면형상 및 단면조직을 관찰하였으며 GDS와 XRD를 이용하여 깊이에 따른 원소 및 상분석을 실시하였다. 또한 마이크로비커스 경도계와 마모시험기를 이용하여 경도와 마모특성을 측정하였고, 염수분무시험을 통하여 해수환경에서 부식거동을 평가하였다.

• Journal of Ocean Engineering and Technology
• /
• v.15 no.2
• /
• pp.61-65
• /
• 2001

The fracture toughness of ceramics can be measure by such various methods as DT (double torsion), CN (chevron notch) etc. But, the application of these methods to the engineering ceramics is very difficult because of its very high hardness. So, IF (indentation fracture) method is generally used for the evaluation of fracture toughness of ceramics. The Median crack induced by the sharp Vickers indenter was compared with the detected AE (acoustic emission) signal. On the silicon nitride ceramics, the AE test results agree fairly well with the median crack occurance and growth process. But, on the alumina, very many complicated crack signals were detected besides median crack. It can be considered that the IF methods must be used in limited engineering ceramics materials.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2011.05a
• /
• pp.156-157
• /
• 2011

고경도 Ni-Co 합금 도금액 개발을 위하여 Ni과 Co의 함량 조성비와 전류밀도에 따라 전기도금을 실시하였다. Ni과 Co의 함량비는 Ni의 농도를 일정하게 유지시키고 Co의 농도를 10~30g/${\ell}$로 하여 실험을 하였다. Ni과 Co의 함량 조성비에 따른 합금 도금층의 성분을 EDS를 이용하여 분석하였고 전류밀도별 표면형상을 FE-SEM을 이용하여 분석하였다. 그리고 도금층의 성분에 따른 경도값을 비커스 경도계를 이용하여 분석하였다.

• Journal of Dental Rehabilitation and Applied Science
• /
• v.36 no.3
• /
• pp.168-175
• /
• 2020

Purpose: The purpose is to test and evaluate the physical properties of commonly used temporary restoration materials and newly emerged materials. Materials and Methods: Four groups of polymer materials were evaluated: Polymethyl methacrylate (PMMA) 2 groups, Polyetheretherketone (PEEK), Polycarbonate. Four physical properties were tested: surface hardness, bending strength, abrasion resistance during wear, wear behavior. The 3-axis bending strength and Vickers hardness test were measured using a universal testing machines respectively. The microstructure was observed with a scanning electron microscope and weight comparison was evaluated after 100,000 chewing tests using a chewing simulator. Kruskal wallis test was performed to evaluate statistical significance. Results: The four groups showed the highest flexural strength and Vickers hardness of PEEK, followed by PC, PMMA-H, PMMA-T. Microstructure observation also showed the least surface roughness in the PEEK group, followed by PC, PMMA-H, PMMA-T. Conclusion: PC is considered to have sufficient mechanical properties that can be applied to the manufacture of temporary teeth. However, further studies, such as biocompatibility, are considered to be necessary for practical clinical applications.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.20 no.9
• /
• pp.382-389
• /
• 2019

A novel folding process is proposed using a repeated cold-die forging and annealing to form a sterling silver ring. Sterling silver plate was cut into a doughnut shape, and lattices with 0.43-mm line-width were imprinted on it. The sample was folded by forging using dies with slopes of $45^{\circ}$, $60^{\circ}$, and $75^{\circ}$ and annealing. For comparison, samples were also fabricated without annealing. Strain was identified by measuring the length of lattices. Vernier calipers, a Vickers hardness tester, an optical microscope, and a UV-VIS colorimeter were used to determine the size, hardness, microstructure, and body color. Without annealing, cracks occurred. However, successful deformation was possible when annealing was used. The results of macro strain measurements show that the outer diameter and width decreased, while the inner diameter and thickness increased after the final process. The maximum strain was increased 0.128 toward the parallel direction. The Vickers hardness decreased after annealing and increased after the folding process. The microstructure results showed that the grain size increased after annealing but decreased after folding. The color difference based on the Lab index was under 10 for all processes. Eventually, a doughnut-shaped silver plate was successfully deformed into a ring shape by the folding process.

• Journal of the korean academy of Pediatric Dentistry
• /
• v.36 no.3
• /
• pp.440-447
• /
• 2009

This study was performed to compare the wear resistance of sealant and flowable resins for analyzing the effect of flowable resin as a sealant in preventive resin restorations. Specimens were made and Vicker's hardness number and surface roughness were measured. SEM observations of the polished and abraded surfaces were established. Kruskal-Wallis rank test and Mann-Whitney U test at the significant level of ${\alpha}$=0.05 were used. The following results were obtained: 1. The microhardness was decreased among groups in following order: Z350 (3M ESPE, U.S.A), Estelite (Tokuyama Dental, Japan) and Ultraseal (Ultradent, U.S.A). There were significant differences in all groups (p<0.0001). 2. The surface roughness was decreased among groups in following order: Ultraseal XT plus, Palfique Estelite LV and Filtek Z350 flowable. However, there is no statistically significant differences in roughness among Estellite, Z350 and Ultraseal at the significance level of ${\alpha}$=0.05, with p=0.116 3. SEM observation of the unworn and worn surfaces revealed the qualitative differences in the wear appearance among groups. The results in this study indicate that flowable resin is better than sealant in aspect of physical properties.