• Transactions of the Korean Society of Mechanical Engineers B
• /
• v.41 no.6
• /
• pp.389-395
• /
• 2017

This study was performed to provide the information of the soot formation behavior of octane single fuel droplet under the identical combustion conditions. To achieve this, this experimental study provide the results of the soot formation characteristics of octane droplet in accordance with different initial droplet diameter($d_0$), at the same time, experiment was conducted under the same combustion conditions which are 1.0atm of ambient pressure($P_{amb}$), 21% of oxygen concentration($O_2$) and 79% of nitrogen concentration($N_2$). Visualization of octane droplet combustion was performed by visualization system with high speed camera. The results of maximum soot volume fraction($f_{vmax}$) was almost the same under the equivalent ambient conditions regardless of initial droplet diameter. Furthermore, maximum soot volume fraction was showed the higher value in the measuring direction between $135^{\circ}$ and $315^{\circ}$ since the soot-tail is generated during two opposing igniters movement process.

• Composites Research
• /
• v.30 no.1
• /
• pp.71-76
• /
• 2017

The purpose of this study was to predict the long-term performance using the interlaminar shear strength of carbon fiber/epoxy composites exposed to environmental factors. Interlaminar shear specimens, manufactured by the filament winding method, were exposed to the conditions of drying at $50^{\circ}C$, $70^{\circ}C$, and $100^{\circ}C$ and of immersion at $25^{\circ}C$, $50^{\circ}C$, and $70^{\circ}C$ for up to 3000 hours, respectively. According to the results, the interlaminar shear strength did not vary significantly with the exposure time for the drying at $50^{\circ}C$ and $70^{\circ}C$, but it increased somewhat for the drying at $100^{\circ}C$ due to the post curing as the exposure time increased. The interlaminar shear strength of the specimens exposed to the immersion at $25^{\circ}C$ did not change significantly at the beginning of exposure, but it decreased with the exposure time and the degree of decrease increased as the environmental temperature increased. The linear regression equations for the environmental temperatures were obtained from the interlaminar shear strength of the specimens exposed to the immersion for up to 3000 hours. Using these linear regression equations, the interlaminar shear strength was estimated to be within 5.5% of the measured value at $25^{\circ}C$ and $50^{\circ}C$, and 2.3% of the measured value at $70^{\circ}C$. Therefore, the proposed performance prediction procedures can predict well the long-term interlaminar shear strength of carbon fiber/epoxy composites exposed to environmental factors.

• Journal of the Korean Ceramic Society
• /
• v.38 no.4
• /
• pp.380-387
• /
• 2001

140$0^{\circ}C$ 환원 분위기(질소-수소) 조건에서 열처리하여 반도성 SrTiO$_3$하소분말을 제조하였다. 하소분말을 이용하여 135$0^{\circ}C$에서 2시간동안 상압 소결하여 소결체를 제조하였으며, 이때 소결 분위기에 따른 소결체 입계의 전기적 특성을 고찰하였다. 이들 소결체는 전형적인 바리스터 특성을 나타내었으며, 특히 소결 분위기를 질소-수소로부터 공기로 변화시킴에 따라서 소결체의 문턱 전압, 입계 비저항 그리고 입계 전위 장벽은 430V/cm, 10MΩ.cm 그리고 2.0$\times$$10^{-3}$eV로부터 1000V/cm 이상, 240 MΩ.m 그리고 1.1eV로 변하였다.

• Journal of the Korean Ceramic Society
• /
• v.38 no.1
• /
• pp.28-33
• /
• 2001

WC-6%Co 소결체를 열처리할 때 발생하는, 시편 표면에서의 급격한 입자 성장 거동을 열처리 분위기를 변수로 하여 관찰하였다. 열처리 분위기로 수소와 메탄을 각각 사용하였고, 온도는 1400~145$0^{\circ}C$, 압력은 1~3 Torr, 그리고 시간은 100분까지 변화시켰다. 표면에서의 입자 성장은 수소 분위기보다 메탄 분위기를 사용하는 경우 훨씬 빠르게 일어났다. 그리고 열처리 온도가 증가할수록, 압력이 감소할수록 입자 성장 속도가 증가하였다. 이때 성장한 입자의 크기 분포는 비정규 분포를 보였다. 한편, 입자 성장은 열처리시 증발하는 시편의 Co 무게 감소와 밀접한 관계를 보였다. 이러한 표면에서의 입자 성장 현상을 열처리한 조건과 관련되어 WC-Co 상태도에서 예측할 수 있는, 탈탄-탄화 반응 및 비정상 입자 성장 현상 관점으로 설명하였다.

• Journal of Hydrogen and New Energy
• /
• v.10 no.1
• /
• pp.27-40
• /
• 1999

By hydrogen induced planetary ball milling process, $Mg_2NiH_x$ hydrogen absorbing materials were successfully alloyed mechanically at room temperature, using pure Mg and Ni chips. The Mg & Ni chips were mixed by 45:55 weight ratio and Mechanical Alloying(M.A.) was carried out : the hydrogen pressure induced in the jar was varied from 1 to 20 bars and the M.A. times were 24 and 48 hours. The XRD results revealed that the homogeneous $Mg_2NiH_x$ was incresed with the hydrogen pressure increasing, and that $MgH_x$ was detected by unalloyed Ni chips. The shape and size of the mechanically alloyed particles didn't depend on the induced hydrogen pressure. The results of TGA showed that the hydrogen quantities of $Mg_2NiH_x$ has 1.1~3.9 wt%.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.1 no.2
• /
• pp.15-22
• /
• 1991

When $YBa_2Cu_3Ox$ is liquid-phase sintered at $925^{\circ}C$ in $O_2$ for 16h, liquid pockets are entrapped within the grains. The liquid pockets show a thin parallelepiped shape with short edge lengths in the c axis, even after reannealing $925^{\circ}C$ in $O_2$ for 16h. All grains in contact with the liquid matrix show the same shape. However, when liquid-phase sintered at 925^{circ}C in $N_2$ for 16h, the grains dispersed in the liquid matrix show a thicker parallelepiped shape than in $O_2$, and their shape remains intact even after reannealing at $925^{\circ}C$ in $N_2$ for 16h. The effect of atmosphere on the grain shape is expected to be due to the variation of oxygen vacancy concentraion in $CuO_2$ plane of tetragonal unit cell.

• Journal of Energy Engineering
• /
• v.28 no.2
• /
• pp.55-62
• /
• 2019

The purpose of this research is to find the optimum combustion conditions for the celadon using a gas kiln. It is clearly defined by the amount of CO gas in the kiln that it is fired in the commonly used oxidation and reduction atmosphere. As a result, while celadon was fired at $1250^{\circ}C$, oxidation happened when the amount of CO was 0~4,500 PPM, a neutral condition happened when the of CO was 4,500~25,000PPM and a reducing process was happened when the of CO was more that 25,000PPM. To reduce gas and firing time while keeping uniformly the firing temperature and firing condition of the gas kiln, you can partially block the gas corridor and adjust it as a damper. This adjustment reduces gas consumption by 40% and shortens the firing time by 1 hour.

• 한국태양에너지학회:학술대회논문집
• /
• 2012.03a
• /
• pp.391-393
• /
• 2012

CuInGa 전구체를 여러 분위기에서 급속 열처리 공정 (rapid thermal processing; RTP)을 이용하여 셀렌화하여 CuInGaSe 박막을 제작하였다. 공정조건은 각각 진공상태, 아르곤 가스 유동 상압상태, 아르곤 분위기 상압밀폐에서 덮개 유리를 사용한 상태 및 아르곤 밀폐상압에서 추가로 Se을 공급한 상태이었다. 제작된 CuInGaSe의 특성을 ICP 측정을 통하여 분석하였다. 열처리 조건에서 시스템이 밀폐상태에 가까울수록 Se 증기압이 높을수록 CuInGaSe 박막의 Se 함량이 증가하였다. 아르곤 분위기 상압 밀폐상태에서 제작된 CuInGaSe 박막을 이용하여 제작한 태양전지의 효율은 9.6%이었다.

• Journal of Energy Engineering
• /
• v.4 no.3
• /
• pp.324-330
• /
• 1995

석탄 연소로에 사용 적합한 석탄의 선정 및 조업조건의 설정에 도움을 주고, 석탁회분의 슬래깅 성향을 파악하기 위해서 갈탄부터 역청탄에 이르는 4종의 시료를 사용하여 산화성 분위기에서 고온 회전 점도계를 사용하여 석탄회분 슬래그의 점도를 온도의 함수로서 측정하였다. 또한 석탄회분의 슬래깅 성향을 해석하기 위해서, 석탄회분 조성을 사용한 Base/Acid Ratio, Lignite Factor 및 Silica Ratio 등의 주요한 인자들이 슬래그 점도에 미치는 영향을 고찰하였다.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 1999.10a
• /
• pp.51-52
• /
• 1999

각기 녹색, 적색의 발광특성플 갖는 $ZnGa_20_4:Mn,{\;}CaTi0_3:Pr$을 rf 마그네트론 스퍼터링법으로 박막을 제조하였다. 박막증착변수가 성장특성 및 발광특성에 미치는 영향을 분석한 결과, 산소분압 및 기판온도조건에 따라서 결정화 및 발광특성이 크게 달라짐을 확인할수 있었다. 열처리후에는 진공분위기보다는 $N_2$가스분위기에서 열처리를 한 시편이 발광특성이 우수하 게 나타났으며, 기판의 종류에 따라서 박막의 성장기구와 발광특성이 다르며, 특히 결정질의 기판이 형광체 박막 합성에 적합함을 알 수 있었다.