• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.16 no.2
• /
• pp.53-58
• /
• 2006

When external field was applied to congruent $LiNbO_3$, it was investgated for domain formation and expansion of $LiNbO_3$. The domain wall velocities of 0.5 mm thickness $LiNbO_3$ were 28.70, 16.02 and $5.75{\mu}m/sec$ under poling field of 23.5, 22.0 and 21.0 kV/mm, respectively. As $1 M{\Omega}$ resistor was used in domain inversion system, harmonic domain inversion was not achieved by rapid domain expansion. And 50% duty cycle periodically poled $LiNbO_3$ have been fabricated by charge control using $10 M{\Omega}$ resistor.

• Journal of the Korean Institute of Gas
• /
• v.5 no.4 s.16
• /
• pp.33-39
• /
• 2001

This paper was studied on corrosion behavior of absorption refrigeration systems using $LiBr-H_2O$ working fluids. In the various concentration of lithium bromide solution, polarization test of SS 400, Cu(C1220T-OL) and Al-Ni bronze is carried out. And the corrosion behavior of materials forming absorption refrigeration systems is investigated. The main results are as following: 1) As concentration of lithium bromide solution increases, polarization resistance of materials of each kinds is low. And open circuit potential becomes less noble, the corrosion current density is high drained 2) Open circuit potential of SS 400 is less noble than that of Cu and Al-Ni bronze, corrosion current density of SS5 400 is high drained than that of Cu and Al-Ni bronze. 3) Anodic polarization of Cu and Al-Ni bronze in $62\%$ LiBr solution continues the active state. that of Cu and Al-Ni bronze in the natural sea water maintains the active state and the critical current for passivation appears.

• Journal of the Institute of Electronics Engineers of Korea SD
• /
• v.38 no.3
• /
• pp.166-173
• /
• 2001

Hysteresis loops of the ferroelectric thin films such as PLZT(10/30/70), PLT(10) and PZT(30/70) was simulated using the field-dependent polarization model and compared to the measured loops. In case of PZT(30/70) thin film, as the real saturation or polarization at the applied voltage or larger than 5V appears slack and its value is quite different from the simulated one, it is deduced that the ferroelectric polarization of PZT(30/70) is generated not only by the pure dipoles but also by various electric charges. The drain current of quasi-MFISFET is expressed by using the square-law FET and field-dependent polarization models. The modeling results are analogous to the experimental values. The channel of quasi-MFISFET using PZT(30/70) forms more quickly compared to that of quasi-MFISFET using PLZT(10/30/70) or PLT(10) in the state of 'write' gate voltage of -10V. This may be because the decrease rate of the polarization in the PZT(30/70) thin film is 3~4 times more rapid than that of the polarization in the PLZT(10/30/70) or the PLT(10) thin film in the retention characteristics.

• Journal of the Korea Convergence Society
• /
• v.8 no.11
• /
• pp.287-292
• /
• 2017

The electrodeposition of Zn on the automotive parts has been adapted However, because Zn electrodeposit needs to increase thickness for corrosion protection, it has problem of destruction of electrodeposit Zn-based electrodeposit have teen studied for corrosion protection and decreasing electrodeposit thickness. Especially; Zn-Co electrodeposit have much attention In this study, the Composition of Zn-Co electrodeposit in various manufacturing condition such as temperature, current density and electrolyte content was investigated to understand effect of electrolysis condition on Co content of specimen. The results were explained by cathode overvoltage and diffusion coefficient. As the current density increases, the electrolyte temperature decreases, and as the electrolyte concentration decreases, the overvoltage of the cathode increases. As the overvoltage of the cathode increases, the concentration polarization becomes more important than the activation polarization. Concentration polarization is determined by the diffusion of the mass transfer in the diffusion layer. In a constant concentration polarization, a large amount of elements with a large diffusion coefficient is diffused. That is, as the overvoltage of the cathode increases, the Zn content having a large diffusion coefficient increases.

• Electrical & Electronic Materials
• /
• v.10 no.3
• /
• pp.239-246
• /
• 1997

The ZnO is stabilize dielectric constant over a broad temperature range because its addition makes the relaxation time short. In this study, the composite oxide material (B $a_{0.85}$ $Ca_{0.15}$)Ti $O_{3}$ was mixed by ZnO additive material and the dielectric polarization characteristics was studied. The relative density was over 90[%] at all specimen in the structural characteristics. Among of the specimen, the relative density of (B $a_{0.85}$ $Ca_{0.15}$)Ti $O_{3}$ with ZnO (0.4mol) has a 95[%]. The grain size of composite oxide material with an increasing ZnO increased and it was 1.0[.mu.m]-1.22[.mu.m]. In the electrical characteristics, the charge and discharge current was increased by ZnO addition. The dielectric relaxation time was increased by space charge polarization at above 110[.deg. C] and the dielectric relaxation time was fixed by space charge polarization of para-dielectric layer at below 110[.deg. C]. The dielectric relaxation time was maximum when the grain size was small. The dielectric relaxation time is decreased with an additive material ZnO and interface polarization, existing void at the grain and grain boundary. The remnant polarization is increased and the coercive electric field is decreased by ZnO.

• Journal of the Korean Geotechnical Society
• /
• v.21 no.2
• /
• pp.93-103
• /
• 2005

This study was performed to identify the presence of measurement distortions such as electrode polarization and to investigate the influence of soil water content on complex permittivity at low frequency. In low frequency measurement using two-terminal electrode system, electrode polarization effect was observed at frequencies less than approximately 100 HBz. The analysis for real permittivity should be performed at frequencies above 100 kHz in order to exclude electrode polarization effect in the analysis of real permittivity at low frequency measurements. For a given soil, both of real and effective imaginary permittivity of wet soil increased continuously with volumetric water content. This is evidenced by the facts that the real permittivity is proportional to the number of dipole moments per unit volume and effective imaginary permittivity is effected by the conduction due to water. However, proportional relation between real permittivity and volumetric water content is valid at upper MHz frequencies.

• Journal of the Korean Society of Fisheries and Ocean Technology
• /
• v.36 no.1
• /
• pp.66-72
• /
• 2000

In these days, with development of industry, the use of machines and structures like ships, airplanes, bridges, power plants, and structure for construction has increased and these machines and structures are used in various corrosive environment. Especially, in case of STS 304, which is material for every kind of machine and chemical plant, it makes many problems related with corrosion and as a result of this, there are happening tremendous economic loss. Therefor, in this study, the test for polarization characteristics was carried out to study characteristics of crevice corrosion of STS 304 which is austenitic stainless steel, in NaCl environment.The main results obtained are as follows :1) Part of crevice is corroded, neighboring outside surface of crevice is passivation. 2) In polarization behavior, corrosion potential of STS 304 become more noble as the concentration of NaCl solution increased by 3.5% but the concentration increased over 3.5% that of STS 3.4 become less noble. 3) The current density under corrosion potential was high drained as concentration of NaCl solution increased by 3.5% but the concentration increased over 3.5%, the current density was low drained.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2018.06a
• /
• pp.112-112
• /
• 2018

알루미늄 합금은 내구성과 내식성이 우수한 경량 재료이다. 그 중 Al-Mg계 5083 Al 합금은 가공성 및 용접성이 우수하여 선체 재료로 널리 이용되고 있다. 이는 선체 중량의 경량화로 인해, 연료비 절감과 빠른 선속 등 다양한 이점을 지니기 때문이다. 그러나 선박의 고속화에 따라 선체에 가해지는 유체충격이 증가하고, 압력 저하에 기인하여 캐비테이션-침식 손상이 증가할 뿐만 아니라, 염소이온이 존재하는 해수환경에서는 침식과 부식의 시너지효과로 인하여 재료의 손상이 더욱 가속화된다. 이에 대한 다양한 방지책들이 제안되고 있으나, 강한 충격압을 동반한 캐비테이션 침식-부식 복합 손상 환경에서는 다소 한계가 있다. 따라서 본 연구에서는 알루미늄 5083에 대하여 캐비테이션 환경 하에서 일정 전위를 인가하며 침식-부식 손상이 최소화 되는 전위 구간을 규명하고자 하였다. 먼저, 분극 실험을 선행하여 재료의 전기화학적 거동을 파악 한 후 적용 전위구간을 선정하여, 해당 전위를 인가한 상태에서 캐비테이션 실험을 실시하였다. 전기화학적 분극실험과 캐비테이션-전기화학 복합 실험은 $25^{\circ}C$의 해수 하에서 실시하였으며, 시험편의 노출면적은 $3.24cm^2$으로 하였다. 분극 실험은 개로전위로부터 +3 V까지 2 mV/s의 분극속도로 전위를 인가하였고, 기준전극으로 Ag/AgCl, 대극으로 백금전극을 사용하였다. 캐비테이션-전기화학 복합 실험은 정전위를 인가한 상태에서 대향형 진동법으로 진동수 20 kHz, 진폭 $30{\mu}m$ 진동을 20분간 가하였으며, 혼팁과 시험편 사이의 거리는 1 mm로 일정하게 유지하였다. 실험 후 표면 손상의 정량적 분석을 위해 인가된 전위별 전류밀도를 비교하고, 무게감소량을 측정하였으며, 손상경향 파악을 위하여 3D광학현미경과 주사전자현미경(SEM)을 통해 표면을 분석하였다.

• Korean Journal of Materials Research
• /
• v.9 no.10
• /
• pp.1032-1036
• /
• 1999

The electron emission and degradation of the ferroelectric Pb($\textrm{Zr}_{0.5}\textrm{Ti}_{0.5}$)$\textrm{O}_3$ ceramics by the pulse electric field have been investigated as a function of the upper electrode diameter. Polarization increased with the decrease of the upper electrode diameter due to the increase of the volume fraction participated in the polarization reversal near the electrode edge. Simulation using ANSYS 5.3 for the electric field distribution showed that the electric field increased near the upper electrode edge of the asymmetric electrode structure. The ferroelectric volume near the upper electrode edge which contributed to the increase of the polarization and the emission charge per electrode diameter were independent on the upper electrode diameter. Polarization and dielectric constant were decreased due to the erosion of the upper electrode with repeating the emission cycles, but they were recovered by the electrode regeneration. The degradation of the ferroelectric surface resulted in the increase of the coercive field and dielectric loss.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2016.11a
• /
• pp.143-143
• /
• 2016

알루미늄 합금은 내구성과 내식성이 우수할 뿐만 아니라 다양한 표면개질을 통해 그 표면 특성을 더욱 향상시킬 수 있다. 특히 Al-Mg계 5083-H321 Al 합금의 경우 가공성 및 용접성이 우수하여 선체 재료로 널리 이용되는데, 이는 선체중량의 경량화가 가능하여 연료비 절감과 빠른 선속 등 다양한 이점을 지니기 때문이다. 그러나 선속의 고속화에 따라 선체에 가해지는 유체충격이 증가하고 정압 저하에 기인하여 캐비테이션-침식 손상이 증가할 뿐만 아니라 해수환경 특성 상염소이온의 존재로 부식이 가속화되는 등 침식 및 부식의 시너지효과로 손상은 크게 증가한다. 이에 대한 방지대책으로 다양한 표면개질 기법이 제안되고 있으나 강한 충격압이 동반된 캐비테이션 침식-부식 복합 손상 환경에서는 표면처리만으로는 불가능할 수 있다. 따라서 본 연구에서는 양극산화된 5083-H321을 대상으로 캐비테이션 환경 하에서 일정 전위를 인가하여 침식-부식 손상이 최소화되는 최적전위를 규명하고자 한다. 이를 위해 먼저 분극 실험을 통해 재료의 전기화학적 거동을 바탕으로 임의의 전위를 선정하고 해당 전위를 인가한 상태에서 캐비테이션 실험을 실시하였다. 이때 분극실험과 캐비테이션-전기화학 복합실험 모두 $25^{\circ}C$의 해수에서 실시하였으며, 전기화학적 분극실험은 유효면적이 $3.24cm^2$인 시편에 2 mV/s의 분극속도로 0 ~ -3 V 까지 인가하였고, Ag/AgCl 기준전극과 백금대극을 사용하였다. 캐비테이션-전기화학 복합 실험은 정전위를 인가한 상태에서 $30{\mu}m$의 진폭으로 20분간 실시하였으며, 혼팁과 시험편 사이의 거리는 1 mm로 일정하게 유지하였다. 실험 후 표면 손상의 정량적 분석을 위해 인가된 전위별 전류밀도를 비교하고, 무게감소량을 측정하였으며, 손상특성 분석을 위해 3D현미경과 주사전자현미경(SEM)을 통해 표면을 분석하였다.