• 대한기계학회논문집
• /
• 제11권6호
• /
• pp.867-876
• /
• 1987

본 연구에서는 보통강재인 SS 41 강을 열처리하여 얻은 M.E.F.복합조직강의 모상입경변화와 3.5% NaCl수용액의 pH변화 조건하에서 반복굽힘피로실험을 하여 부식 피로파괴에 미치는 영향에 대해 고찰하였다.

• 한국기계가공학회지
• /
• 제6권1호
• /
• pp.62-70
• /
• 2007

The development of new materials that are light-weight, yet high in strength has become vital to the machinery, aircraft and auto industries. However, there are a lot of problems with developing such materials that require expensive tools, and a great deal of time and effort. Therefore, the improvement of fatigue strength and fatigue life are mainly focused on by adopting residual stress. The fatigue crack growth rate of the Shot-peened material was lower than that of the Un-peened material. And in stage I, threshold stress intensity factor of the shot-peen processed material is high in critical parts unlike the Un-peened material. Also, fatigue crack growth exponent and number of cycle of the Shot-peened material was higher than that of the Un-peened material. That is concluded from effect of da/dN. And Fatigue life shows more improvement in the Shot-peened material than in the Un-peened material. And compressive residual stress of surface on the Shot-peen processed operate resistance force of fatigue crack propagation.

• 대한토목학회논문집
• /
• 제13권3호
• /
• pp.35-44
• /
• 1993

저렴한 가격이면서 새로운 PVDC Latex의 제조, 이것을 활용한 다양한 색채의 고강도 폴리머콘크리트의 생산, 그리고 이것의 전단거동에 관한 이론을 정립하여 건설공사에 활용토록 하는 것을 목적으로 한다. 본 연구의 내용으로서는 이것을 사용한 신폴리머 콘크리트의 설계에 있어서 혼합특성, 물리적 특성을 연구한다. 이 중에서 가장 중요한 것은 압축강도, 휨강도, 정적극한강도, 피로강도 등이다. 이것을 이용한 보에 있어서는 중앙처짐, 반복횟수와 변형률관계, 파괴양식 등을 연구하여 본 목적의 활용성을 검증토록 한다. 그래서 콘크리트의 단점인 취성파괴를 보완하고 화학적인 성질로 일어날 수 있는 콘크리트의 부식이나 파손을 방지하도록 한다. 연구결과 피로실험에서 이형철근이나 스터럽의 파단은 순간적으로 일어나며 파단된 단면은 매끄러웠다. 또한 이러한 부분의 재질분석을 통하여 피로하중이 작용할 때 미세균열이 일어나고 있었다는 사실을 확인 할 수 있었다.

• 마이크로전자및패키징학회지
• /
• 제27권2호
• /
• pp.45-51
• /
• 2020

미래의 유연 전자 기기는 고온, 고습 환경 조건에서 사용될 수 있으며 반복적으로 굽히고 펴기를 반복하기 때문에 장기 신뢰성 확보를 위해서는 환경 조건과 반복 기계적 변형의 효과를 동시에 고려해야 한다. 본 연구에서는 전자기기에서 가장 일반적으로 사용되는 Al, Ag, Cu 전극을 유연 기판상에 진공 증착한 뒤 환경적인 요건을 상온/일반습도와 85℃/85% 습도 두 가지로 조건에서, 기계적 변형이 없는 평평한 상태와 반복적으로 굽힘 변형을 가해주는 조건의 총 4가지 환경 및 피로 복합 실험을 실시하였다. Al, Ag, Cu 전극 모두 기계적 변형이 없는 평평한 경우에 일반 환경 조건 및 고온/고습 조건 모두 10시간 동안 전기 저항 변화가 발생하지 않았다. 일반 환경 조건에서 굽힘 피로 실험을 진행한 경우, Al, Ag, Cu 전극 모두 금속의 피로 파괴 현상에 의해 10만 싸이클 이후 전기 저항이 약 400%~600% 증가하였다. 고온/고습에서 피로 실험의 경우, Al, Ag 전극은 일반 조건 피로 실험과 결과가 유사하였으나, Cu의 경우 고온/고습 피로실험의 경우 10만 싸이클 이후 전기 저항이 90000% 이상 증가하였다. 이는 부식과 기계적 피로가 동시에 발생할 경우 금속 전극에 매우 심각한 신뢰성 문제를 유발한다는 것을 의미하며, 환경 조건과 기계적 변형을 동시에 고려한 전극 소재 디자인이 필요하다는 것을 의미한다.

• 비파괴검사학회지
• /
• 제23권2호
• /
• pp.156-164
• /
• 2003

STS316L은 인성, 연성, 부식저항성 등 우수한 기계적 성질 때문에 에너지환경설비 등 구조물에 널리 이용되고 있다. 그러나, 용접구조물은 가혹한 환경하에서 경년열화가 심각하다. 지금까지의 연구들은 주로 용접부의 피로균열진전거동에 관하여 수행되었고, 피로균열진전속도식의 재료상수와 비파괴적 평가의 상관성에 관한 연구는 거의 없었다. 본 연구는 SIS316L 용접부의 피로균열진전 거동을 조사하고, 초음파 파라미터로 열화특성을 평가하고 시간-주파수 분석으로 해석을 하였다. 본 연구 결과는 용접구조물의 사용기간 중 피로수명 등을 예측하기 위한 기초 데이터로서 사용될 수 있다.

• 한국해양공학회지
• /
• 제10권3호
• /
• pp.14-23
• /
• 1996

The corrosion fatigue test were carried out to evaluate the fatigue characteristics of accelerated cooled (ACC) TMCP high tensile strength steels and weld joint with high heat input by one side one run submerged are welding. In this paper, the fatigue crack growth behaviors were investigated with the center crack tension specimen of base metal and heat affected zone in substitute sea water and air, respectively Main results obtained are sunnarized as follows: 1. The fatigue crack growth rates in sea water faster than those in air environment for the different heat input values, crack growth rate of base metal is very fast and effect of heat input is not remarkable. 2. In HAZ (82kJ/cm, 116kJ/cm), the crack branching phenomena were observed in both air and sea water environment, 3. In SEM observation, the corrosion effect on base metal was larger than that on HAZ in corrosion environment.

• 한국철도학회논문집
• /
• 제5권1호
• /
• pp.32-39
• /
• 2002

As most railways are gradually electrified with modernized electric cars, the demand for catenary wires and their facilities are also increased. Catenary Wires are exposed to the marine area with air-borne salt or severely polluted industrial area with much corrosive emission gases depending on the locations. Corrosion of catenaty wires can make their actual lifetime shorter than that originally designed. Thus, the messenger and ACSR wires, kinds of catenary wire system, were investigated with respect to corrosion, which include new and used ones collected at the field. Tensile strengths and elongations appeared to decrease when the wires were exposed to corrosive environments. The amount of decrease was more prominent as environmental conditions became more corrosive. They are also vibrated with some amplitude everytime pentographs touch contact line. The frequent cyclic load on the wire may result in a fatigue damage. Surface damage by corrosion can make fatigue crack initiate with ease. In the present study, the fatigue life of the used wire was measured 50 to 60% compared with that of new one in average.

• 대한기계학회논문집A
• /
• 제24권1호
• /
• pp.156-162
• /
• 2000

Sensitized STS 304 stainless steel crack growth rate(CGR) in high temperature water was investigated under trapezoidal wave loading test using fracture mechanics techniques. The CGR, due to stress corrosion cracking(SCC), were systematically measured as a function of the stress intensity factor and stress. holding time under trapezoidal wave loading. In high temperature water, CGR was enhanced by a synergistic effects in combination with an aggressive environment and mechanical damage. The CGR, $(da/dN)_{env}$ was basically described as a summation of the environmentally assisted crack growth rate $(da/dN)_{SCC}$, $(da/dN)_{CF}$ and fatigue crack growth rate in air $(da/dN)air,. The CGR, $(da/dN)_{env}$, increased linearly with increasing stress holding time. The CGR, $(da/dN)_{SCC}$ decreased linearly with increasing stress holding time. Fracture surface mode varied from trans-granular cracking to inter-granular cracking with increasing stress holding time.

• 한국표면공학회:학술대회논문집
• /
• 한국표면공학회 2018년도 춘계학술대회 논문집
• /
• pp.116-116
• /
• 2018

부식은 재료와 사용 환경과의 상호작용에 의한 결과로서 일반적으로 두께의 감소와 균열의 발생 및 파손 등의 문제로 나타난다. 특히 사용환경 중에서 해수 분위기는 금속의 부식에 가장 유리한 조건이다. 따라서 해양환경 중 항만이나 조선 및 해양 산업 등에 많이 이용되는 강 구조물은 이에 대응하기 위하여 도장방식이나 음극방식을 사용하고 있다. 여기서 음극방식은 피방식체를 일정전위로 음극 분극하는 원리로써 외부전원을 인가하거나 비전위의 금속을 전기적으로 연결하여 방식하는 방법이다[1]. 한편, 해수 중에서 이와 같은 원리로 음극방식 할 경우에는 피방식체인 강재표면에 부분적으로 칼슘 또는 마그네슘 화합물 등의 생성물이 부착하는 현상을 볼 수 있게 된다. 이와 같이 수산화마그네슘($Mg(OH)_2$)및 탄산칼슘($CaCO_3$)을 주성분으로 하여 석출되는 석회질 피막(calcareous deposits)은 피방식체에 유입되는 음극방식 전류밀도를 감소시켜 주거나 물리적 장벽의 역할을 함으로써 외부의 산소와 물 등 부식환경으로부터 소지금속을 보호한다[2]. 그러나 석회질 피막은 소지금속과의 결합력, 막의 균일한 분포, 내식성 및 제작시간의 단축 등 해결해야 할 과제가 있다. 또한 여러 가지 환경 조건 등의 영향을 받아 그 피막의 형성 정도도 가늠하기 어렵기 때문에 음극방식 설계 시 그 정도에 따른 영향을 고려-반영하기가 곤란하다. 따라서 본 연구에서는 석출속도, 밀착성 및 내식특성을 향상시키기 위해 전착프로세스를 통해 해수 중 기체를 용해시켜 석회질 피막을 제작하고 막의 결정구조 제어 및 특성을 분석-평가하였다. 본 연구에 사용된 강 기판(Steel Substrate)은 일반구조용강(KS D 3503, SS400)을 사용하였으며, 외부전원은 정류기(Rectifier, xantrex, XDL 35-5T)를 사용하여 3 및 $5A/m^2$의 조건으로 인가하였다. 양극의 경우에는 해수에 녹아있는 이온 이외에 다른 성분들이 환원되는 것을 방지하기 위해 불용성 양극인 탄소봉(Carbon Rod)을 사용하였다. 이때 석출속도, 밀착성 및 내식특성 향상을 위해 해수에 주입한 기체의 양은 0.5 NL/min였으며, 기판 근처에 고정하여 음극 부근에서의 반응을 유도하였다. 각 조건별로 제작된 막의 표면 모폴로지, 조성원소 및 결정구조 분석을 실시하였으며, 석회질 피막의 밀착성과 내식특성을 평가하기 위해 규격에 따른 테이핑 테스트(Taping Test, ISO 2409)와 3 % NaCl 용액에서 전기화학적 양극 분극 시험을 진행하여 제작된 막의 내구성과 내식성을 분석-평가하였다. 시간에 따른 전착막의 외관관찰 결과 전류밀도의 증가와 함께 상대적으로 많은 피막이 형성되었고, 용해시킨 기체에 의해 더 치밀하고 두터운 피막이 형성됨을 확인할 수 있었다. 성분 및 결정구조 분석 결과 $Mg(OH)_2$ 성분의 Brucite 및 $CaCO_3$ 성분의 Calcite 및 Aragonite 구조를 확인하였으며, 용해시킨 기체의 영향으로 $CaCO_3$ 성분의 Aragonite 구조가 상대적으로 많이 검출되었다. 밀착성 및 내식성 평가를 실시한 결과 해수 중 용해시킨 기체에 의해 제작한 시편의 경우 견고하고 화학적 친화력이 높은 Aragonite 결정이 표면을 치밀하게 덮어 전해질로부터 산소와 물의 침입을 차단하는 역할을 하여 기체를 용해시키지 않은 3 및 $5A/m^2$ 보다 비교적 우수한 밀착성 및 내식 특성을 보이는 것으로 사료된다.

• 한국방재학회:학술대회논문집
• /
• 한국방재학회 2007년도 정기총회 및 학술발표대회
• /
• pp.67-70
• /
• 2007

A methodology to evaluate fatigue vulnerability of steel bridge members affected by corrosion and truck traffic variation is proposed. A fatigue limit state function including corrosion and traffic variation effects is established to make the criterion whether the steel bridge member is damaged by fatigue. Corrosion effects are expressed as increase of the average corrosion depth, and the traffic variation effects are modeled as the accumulated number of stress cycles. Reliability analysis is carried out by Monte-Carlo simulation method for the fatigue limit state function. The methodology Proposed is verified by comparing reference study and applying for the steel bridge in service.