• Journal of the Korea institute for structural maintenance and inspection
• /
• v.23 no.7
• /
• pp.16-24
• /
• 2019

The corrosion amounts of steel structures can be different depending on their installation condition and height. Thus, their corrosion maintenance should be considered depending on installation conditions of local structural members. In this study, an atmospheric exposure test was conducted to evaluate the corrosion amount and the corrosion rate depending on the installation condition and height of a steel water gate using monitoring steel plates and corrosion environment measuring sensors. The mean corrosion depth was evaluated using the weight loss method and the galvanic corrosion current was measured by corrosion environment measuring sensors. Local corrosion rate of local structural member in steel water gate was estimated using measured mean corrosion depths and galvanic corrosion currents. From this measurement results, the corrosion damage in horizontal member of the cross beam was highly evaluated than those of other structural member as skin plate, etc. The relative difference in the corrosion rate of a local structural member could be highly affected by local corrosion environments of steel water gate members. Therefore, an appropriate maintenance method should be considered for local corrosion damages of local structural members determined by local corrosion environments of a steel water gate.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.21 no.2
• /
• pp.619-626
• /
• 2020

The development of new antifreeze mixtures containing non-amine-type corrosion inhibitors, which considers environmental protection, has become a major issue. In this study, four non-amine-type corrosion inhibitors were synthesized and used to produce five kinds of new antifreeze for automobiles to evaluate the rate of copper corrosion. The effects were evaluated by the weight change, surface observation, roughness measurement, and measurement of copper elution in the solution. The amount of copper eluted measured by ICP from Sample 4 was small, and the elution rate was prolonged. Sample 4 showed the best anti-corrosion performance owing to a corrosion suppression effect by passivating copper because the metal surface was smooth after the test, and the corrosion product layer was formed evenly on the surface as small local corrosion was observed. The major corrosion inhibitor added to Sample 4 was 1-aminomethyl(N',N'-di(2-hydroxyethyl)benzotrazole, which contained a certain amount in Sample 5 to show relatively high local corrosion but passivation in progress. Therefore, among the four corrosion inhibitors, 1-aminomethyl(N',N'-di(2-hydroxyethyl)benzotrazole had the highest corrosion inhibitory effect. This corrosion inhibitor prevents corrosion by promoting the passivation of copper on the antifreeze.

• Korean Journal of Materials Research
• /
• v.5 no.4
• /
• pp.458-467
• /
• 1995

여러가지 Zr합금에 대한 부식시험을 autoclave를 이용하여 물과 여러가지 Li 용액에서 수행하였다. 합금은 11종의 신합금을 사용하였는데 크게 나누어 Zircaly형 합금(ZrSnFeCr), ZnNbFeCr, ZrSnNbFeCr과 ZrFeCr 합금으로 대별되며, 비교평가를 위해 표준 Zircaloy-4 합금에 대해서도 부식시험을 수행하였다.모든 합금에서 Li을 일정농도이상 첨가할 때 부식은 가속되는데, 부식은 Li의 농도가 2.2와 30ppm 사이일 때 가속되기 시작한다. Li은 부식거동에 있어서 천이후 영역에서의 부식속도보다는 천이시간과 무게 증가량에 더 영향을 끼치는 것으로 나타났다. 수소 흡수율은 Li 농도와 합금에 따라서 강하게 영향을 받는것으로 나타났으며, Li 농도가 30ppm이상에서는 Li 가속부식과 함께 Li가속 수소흡수현상이 나타났다. ZrSnFeCr합금들은 낮은 부식속도와 늦은 천이현상을 보이며 표준 Zircaloy보다 훨씬 우수한 부식저항성을 보인 반면에 대부분의 Nb첨가 합금은 높은 부식속도와 빠른 천이 현상을 보였다.

• Proceedings of the Korean Nuclear Society Conference
• /
• 1995.05b
• /
• pp.623-628
• /
• 1995

여러 가지 Zr합금에 대한 부식시험을 autoclave를 이용하여 물과 여러 가지 Li 용액에서 수행하였다. 합금은 11종의 신합금을 사용하였는데 크게 나누어 Zircaloy형 합금(ZrSnFeCr), ZrNbFeCr, ZrSnNbFeCr과 ZrFeCr 합금으로 대별되며, 비교평가를 위해 표준 Zircaloy-4 합금에 대해서도 부식시험을 수행하였다. 모든 합금에서 Li을 일정농도이상 첨가할 때 부식은 가속되는데, 부식은 Li의 농도가 2.2와 30 ppm 사이일 때 가속되기 시작한다. Li은 부식거동에 있어서 천이후 영역에서의 부식속도 보다는 천이시간과 무게 증가량에 더 영향을 끼치는 것으로 나타났다. 수소흡수율은 Li 농도와 합금에 따라서 강하게 영향을 받는 것으로 나타났으며, Li 농도가 30 ppm 이상에서는 Li 가속부식과 함께 Li가속 수소흡수현상이 나타났다. ZrSnFeCr합금들은 낮은 부식속도와 늦은 천이현상을 보이며 표준 Zircaloy보다 훨씬 우수한 부식저항성을 보인 반면에, 대부분의 Nb첨가 합금은 높은 부식속도와 빠른 천이 현상을 보였다.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2014.11a
• /
• pp.193-194
• /
• 2014

원전은 고온기능시험 이후 2차계통 내부를 상대습도 40%이하로 관리하여 계통 재질 부식을 최소화하고 있다. 일반적으로 발전소에서는 운전 정지 후 상대습도 40%이하로 낮추는데 15일정도 소요되지만, 발전소 계통 중 일부 곡관부위는 약 60일정도 소요된다. 본 연구는 일부 계통 재료가 상대습도 제한치(<40%) 이상의 환경에서 장기간(최대 60일) 노출시 재료 건전성에 미치는 영향 평가이다. 평가를 위해 시편의 실험 전, 후 무게변화를 이용한 부식률 측정과 표면분석을 위해 광학현미경을 이용하였다. 사용 시편의 재료는 SA516 Gr.70이며 표면상태를 인위적으로 산화피막을 생성 시킨 것(2개)과 산화피막이 없는 것(6개)으로 2종류로 제작하였다. 총 시험기간은 60일이고 시험기간 중 산화피막이 없는 시편은 7일, 21일, 60일에 시편을 2개씩 꺼내어 무게를 측정하여 부식률을 계산하였다. 실험결과, 산화피막이 없는 시편은 노출되는 시간에 따라 부식률이 각각 0.35(7일), 0.21(21일), 0.67(60일) mpy이었고 산화피막이 있는 시편은 0.06(60일) mpy였다. 산화표면 분석결과, 산화피막이 없는 시편은 노출되는 시간에 관계없이 물방울이 맺힌 부분에 pitting을 확인하였다. 하지만, 산화피막이 있는 시편은 pitting의 흔적은 없었다. 산화피막이 없는 시편의 경우 시간에 따라 부식률은 높아지지만 학계에서 통용되는 뛰어난 내부식성 재료의 부식률 기준인 < 1 mpy이하기 때문에 재료 건전성에 미치는 영향은 거의 없을 것으로 판단된다. 또한, 대부분 원전의 경우 고온기능시험 또는 운전기간 동안에 2차계통 구성 재료 표면에 산화막이 생성되었기 때문에 산화피막이 있는 시편의 결과로 판단하면 상대습도 40%이상에 60일 이상 노출되어도 부식은 거의 일어나지 않았을 것으로 사료된다. 실증실험결과를 가지고 종합적으로 평가하면 상대습도 40%이상 환경에서 곡관부위가 60일이상 노출되어도 재료 건전성에 미치는 영향은 거의 없을 것으로 판단된다.

• Journal of the Korea Concrete Institute
• /
• v.25 no.6
• /
• pp.621-630
• /
• 2013

Several techniques for steel corrosion detection are proposed and HCP (half cell potential) technique is widely adopted for field investigation. If concrete has cracks on surface, steel corrosion is rapidly accelerated due to additional intrusion of chloride and carbon dioxide ions. This study is for an evaluation of HCP in cracked concrete exposed chloride attack. For this work, RC (reinforced concrete) beams are prepared considering 3 w/c ratios (0.35, 0.55, and 0.70) and several cover depths (10~60 mm) and various crack widths of 0.0~1.0 mm are induced. For 35 days, SST (salt spraying test) is performed for corrosion acceleration, and HCP and corrosion length of rebar are evaluated. With increasing crack width, w/c ratios, and decreasing cover depth, HCP measurements increase. HCP evaluation technique is proposed considering the effects of w/c ratios, crack width, and cover depth. Furthermore anti-corrosive cover depths are obtained through Life365 program and the results are compared with those from this study. The results shows relatively big difference in cracked concrete, however provide similar anti-corrosive conditions in sound concrete.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.25 no.1
• /
• pp.67-74
• /
• 2021

This paper evaluated the structural safety of an aging PSC I-girder bridge with rebar corrosion in the deck. The geometry and rebar of the bridge were designed based on an actual PSC I-girder bridge, and the numerical analysis was performed considering the crack of concrete and yielding of steel rebar. According to the evaluation criteria of Korea Infrastructure Safety and Technology Corporation, this study defined two criteria of rebar exposure and corrosion rates to construct a total of 32 corrosion scenarios. Rebar exposure was defined as the exposure of tensile rebars in the bridge deck due to the removal of cover concrete. The results of the analysis showed that the safety and rating factors of the bridge decreased with increasing rebar exposure and corrosion rates. For the rebar corrosion rate more than 50%, the safety grade of the bridge should be carefully evaluated for all the rebar exposure rate. When the rebar corrosion rate exceeds 57%, the bridge was evaluated as E grade regardless of rebar exposure rate. A correlation analysis for a 2% of rebar exposure rate found that the bridge was evaluated as A grade up to 55.8% corrosion rate, C grade up to 56.9%, D grade up to 58.5%, and E grade for corrosion rate greater than 58.5%. This study indicates the necessity of a quantitative evaluation of rebar corrosion for evaluating the structural safety of aging bridges.

• Journal of the Korean Society for Nondestructive Testing
• /
• v.33 no.5
• /
• pp.409-414
• /
• 2013

In this work, corrosion of 304 stainless steel was evaluated by using acoustic emission(AE) technique. AE measurement system was set for detecting acoustic signal during accelerated corrosion test of the specimen. AE signal started to be detected after the time of pitting corrosion initiation was evaluated by anodic polarization curve. Pitting corrosion damage was confirmed by optical microscopic observation of the surface morphology. AE cumulative counts and amplitude according to corrosion time could be divided into three stages. These trends were discussed in relation with changing pitting corrosion mechanism. Feasibilities of AE technique for evaluation of corrosion damage and mechanism were suggested.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2012.11a
• /
• pp.124-124
• /
• 2012

부식 현상은 산업과 실생활에서 경제적, 인간의 생활과 안전에서 손실을 일으키는 요인이다. 자동차 부품, 선박 부품 및 전자 부품 산업 등 다양한 분야에서 수명 및 고장율 시험에 대한 관심이 증가하고 있다. 넓은 분야에서 염수분무시험을 적용하고 있지만, 실제 야외환경에서 발생하는 부식과의 상관관계가 확실하게 규명되어 있지 않다. 그리고 이렇게 넓은 산업전반에서 적용하고 있는 염수분부시험 방법은 시료의 부식 저항성을 판단하기 위한 시험시간이 오래 걸리고 이런 이유로 적정한 시험시간을 설정하기 어려울 뿐만 아니라 고내식성 시료의 부식평가가 어렵다는 단점을 가지고 있다. 본 연구에서는 부식의 형태에서 균일부식 현상을 이용하여 옥외 노출 부식시험과 염수분무시험, 가속부식시험 환경에 노출된 시료의 무게 감량을 측정하여 가속계수 도출과 함께 부식 정도를 예측할 수 있는 방법을 연구하였다.

• Proceedings of the Korean Nuclear Society Conference
• /
• 1996.11b
• /
• pp.481-486
• /
• 1996

원자력 발전소의 증기 발생기 전열관으로 사용되는 합금 600MA는 미세 구조에 관계없이 가성 용액에서 입계 균열이 발생한다. 본 연구에서는 합금 600 2종과 합금 690 2종의 이음매없는 관 및 진공 용해한 합금 690M 2종의 MA 및 TT재에 대한 부식 조건의 변화에 응력 부식 균열 특성을 일정연신율법(CERT) 및 C-ring법으로 평가하였다. 가성 응력 부식 균열 저항성에 미치는 TT처리의 효과는 용액 조건에 관계없이 TT처리를 행하게 되면 응력 부식 균열에 대한 저항성이 증가하는 것으로 나타났으며, 분극 저항성과는 직접적인 관계가 나타나지 않고 다른 미세 조직 등에 의한 영향을 더 크게 받고 있는 것으로 판단된다. 가성 용액에서의 응력 부식 균열 저항성에 미치는 SO$_4$$^{=}$ 이온의 첨가 효과는 TT처리의 유무에 관계없이 응력 부식 균열 저항성을 크게 감소시키고 있다. 한편 합금 690의 가성 응력부식 균열 저항성에 미치는 Mo의 효과는 Mo이 첨가될수록 응력 부식 균열 저항성이 증가하는 것으로 나타났다.