• Proceedings of the Korea Institute of Fire Science and Engineering Conference
• /
• 2011.11a
• /
• pp.382-385
• /
• 2011

본 논문은 초고강도콘크리트의 폭렬현상을 연구해 보고자 실리카흄 유무와 PP섬유의 혼입량을 변수로 하여 공시체와 벽체의 폭렬현상을 관찰한 후 변수가 초고강도콘크리트에 어떠한 영향을 주는지를 실험적으로 규명하는 것을 목적으로 하였다. KS F 2257 화재온도이력곡선을 30분 적용하여 콘크리트의 초기 폭렬특성을 실험적으로 검토하였다. 그 결과 공시체의 경우 압축강도가 100 MPa 초고강도콘크리트의 경우에는 실리카흄 여부와 PP섬유 혼입량이 폭렬억제에 관계되는 주요 인자인 것을 알 수 있었으며, 벽체의 경우에는 벽체 시험체의 부분 가열 및 전면 가열 실험을 실시했다. 폭렬 최대 깊이, 시간, 소리 발생 회수를 비교하면 부분 가열이 전체 가열에 비해 폭렬이 빠르고 깊게 발생하는 것으로 나타났다.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2013.05a
• /
• pp.323-325
• /
• 2013

This study on the proposes a spalling mechanism based on the results of a fire resistance test of HSC(High Strength Concrete) considering important factors of spalling occurrence. The factors considered in this two-sided are fire resistance test to ISO 834 fire curve. In this study, explosive spalling phenomena in the specimens were investigation.

• Fire Science and Engineering
• /
• v.25 no.3
• /
• pp.91-98
• /
• 2011

This study is about fire resistance performance of wood framed lightweight wall including a middle lintel as a traditional wall form in Korea. The target wall is non-loadbearing system which constructed with $38{\times}89$ mm ($2"{\times}4"$) wood frame and fireproof gypsum board covering, including a middle lintel made of $150{\times}150$ mm section glue-laminated timber. As a test results, all specimens have showed fire resistant performance over 90 minutes and tests were maintained until flame occuring on Specimen-l, 2, 3 at 91 min, 97 min and 98 min respectively. Fire resistance of the heat side gypsum board was 45 minutes and charring rate of middle lintel was equivalant with that of usual timber. The wood stud inside wall system showed relatively quick combution characteristic when exposed to high temperature with no temperature rising delaying time caused by moisture evaporation because of the dehydration preceded during the early period of fire side gypsum board resist to heat.

• Fire Science and Engineering
• /
• v.33 no.1
• /
• pp.60-68
• /
• 2019

The paper reports the characteristics of conduction heat transfer to the backside part according to the heating temperature of a composite wall in a lightweight partition used for indoor space compartments. Stud partitions, SGP partitions, sandwich panels, urethane foam panels, and glass wool panels. which are generally used as light-weight partition walls, were selected as experiment samples, and the characteristics of conduction heat transfer to the backside part as the top surface were analyzed by applying heating temperatures of $200^{\circ}C$, $300^{\circ}C$, $400^{\circ}C$, and $500^{\circ}C$ to the bottom surface for 1800 s. According to the experimental results, the maximum backside temperatures at the maximum heating temperature of $500^{\circ}C$ was $51.6^{\circ}C$, $63.6^{\circ}C$, $317.2^{\circ}C$, $124.9^{\circ}C$, and $42.2^{\circ}C$ for the stud partition, SGP partition, sandwich panel, urethane foam panel, and glass wool panel, respectively. The maximum conduction heat- transfer rates at $500^{\circ}C$ were 17.16 W, 18.39 W, 136.65 W, 14.34 W, and 5.57 W for the stud partition, SGP partition, sandwich panel, urethane foam, and glass wool panel, respectively.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2011.11a
• /
• pp.205-206
• /
• 2011

Inorganic Polymer Concrete, a type of Alkali activated cement and concrete, is known for various excellent performances, especially for better performance in the area of high temperature heat resistance(thermal characteristic) than portland cement concrete.In this study, light weight concrete panel was manufactured using this Inorganic Polymer Concrete and then evaluated for fire resistance with a small-scale heating furnace. Since the result showed excellent fire resistance, it is considered usable for manufacturing fire resistant concrete panel wall.

• Journal of the Korean Wood Science and Technology
• /
• v.36 no.6
• /
• pp.41-48
• /
• 2008

The required energy for the heat treatment of pine log was evaluated in this study. A proper heat treatment of pine log infected by pinewood nematode (Bursaphelenchus xylophilus) can prevent spreading of the infection by pinewood nematode and make the infected pinewood valuable again. The FAO (Food and Agriculture Organization of the United Nations) heat treatment standard for various types of infected wood for which a heat treatment of the core part of the wood is necessary is 30 minutes at $56^{\circ}C$, taking into account the international standards for phytosanitary measures (ISPM No. 15). In this study, the energy consumption during the heat treatment was separated into two kinds of energy, initial energy for heating kiln drier and to reach set point temperature and relative humidity and the required energy supplementing heat loss. The initial required energy per unit time is greater than that during the treatment. The energy consumption per unit time varied little during the heat treatment. As a result, the set point relative humidity with set dry bulb temperature and density of wood dependent on moisture content are very important factors to change energy consumption in the experiment. The heat treatment at higher temperature and higher humidity levels requires more energy consumption but less treatment time. It is expected that a more effective energy program could be planed for the heat treatment of pine log through this study.

• Journal of the Korea Concrete Institute
• /
• v.18 no.3 s.93
• /
• pp.431-438
• /
• 2006

The determination of the depth of deteriorated concrete is one of the main problems in the structural assessment of concrete structures that have been subjected to a fire. This information is particularly important in order to optimize the future operations of repair/strengthening, or in decision-making concerning a possible demolition. The purpose of this study is to propose evaluation technique of damaged depth of concrete exposed at high temperature. In order to evaluate damaged depth of core picked at member under fire, the 24 specimens have been made with variables of concrete strength(20 MPa, 40 MPa, 60 MPa) and heating exposure condition in 600 and 800 for 2 hours. Color change analysis and water absorption after heating have been measured and split tensile stress test was performed to ka the residual compressive strength against the depth of specimen. The results show that the deeper of the depth from heating face, water absorption ratio is smaller and residual stress ratio is larger and the color of heated face is changed to red color. Using this technique at damage evaluation of fired structure, We evaluate damaged depth of member under fire and determine the reasonable strengthening range.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2013.02a
• /
• pp.351-351
• /
• 2013

한국 전체 에너지 사용량 중약 24%의 에너지가 건축물 부분에 소비되고 있다. 건축물의 벽체나 유리창 등을 통해서 에너지 손실이 이루어지는데 유리창은 벽체에 비해 약 10배 이상 낮은 단열 특성을 가지고 있기 때문에 유리창을 통한 열손실량은 더 크다. 이러한 유리창 부분의 열손실 문제를 해결할 수 있는 방안으로 좋은 단열 특성 및 낮은 방사율을 가지고 있는 Low-e coating 방법을 사용하였다. 본 실험에서는 XG glass 기판 위에 IGZO/Ag/IGZO OMO 구조의 다층 박막을 증착하였다. RF magnetron sputtering방법을 이용하여 OMO 구조의 상부와 하부의 Oxide layer로 IGZO 박막을 증착하였다. 사용된 IGZO 타겟은 $In_2O_3$ (99.99%), $Ga_2O_3$ (99.99%), ZnO (99.99%)의 분말을 각각 1:1:1 mol% 조성비로 혼합하여 소결하여 제작하였다. Thermal Evaporator 장비를 이용하여 OMO 구조의 Metal layer로 Ag (99.999%)를 증착하였다. 실험 기판은 크기 $30{\times}30mm$의 0.7T XG glass를 사용하였다. OMO 구조의 산화층 IGZO 박막은 상/하층 동일 조건으로 기판 온도는 실온으로 고정하였으며, 초기 압력 $3.0{\times}10^{-6}$ Torr, 증착 압력 $3.0{\times}10^{-2}$ Torr, RF 파워 50W, Ar 유량 50 sccm로 고정시키고 증착 시간이 변화하면서 박막을 증착하였다. OMO 구조의 Metal layer로 Ag 증착 조건은 초기 진공도가 약 $6.0{\times}10^{-6}$ Torr 이하로 유지하고 기판을 2 Rpm의 속도로 회전시켰다. 이후 0.3 V로 Ag를 10분간 가열하여 충분히 녹인 후 Film Thickness Monitor로 두께를 확인하였다. OMO 다층 박막의 산화물층 변화에 따라 로이다층 박막의 구조적, 광학적 및 전기적 특성을 분석하였다. XRD 분석결과에 의하여 Bragg's 법칙을 만족하는 피크가 나타나지 않는 비정질 구조임을 확인할 수 있으며, AFM 분석결과에 통해서 최소 1.3 nm의 Roughness를 나타내었다. UV-Visible-NIR 분광광도계를 이용하여 다층 박막은 가시광선 영역에서 평균 80%의 광 투과성을 보여 IR 영역에서 평균 30% 투과하고 좋은 차단 특성을 나왔다. Low-e 특성을 갖는 유리창을 통해서 에너지 절약을 이룰 수 있는 것을 확인할 수 있었다.

• Proceedings of the Korea Institute of Fire Science and Engineering Conference
• /
• 2001.11a
• /
• pp.301-310
• /
• 2001

본 연구는 내화성능을 가진 수막보호유리벽을 실제 건축물에 적용하는데 있어서 필수적으로 고려해야 할 가상시나리오 중에서 수막이 유리면을 보호하기 이전에 유리면에 근접되어 있는 화염으로부터 방출되는 복사열이 유리면이 가열된 상태에서 수막이 형성될 경우 유리면의 온도가 급속히 냉각됨으로서 발생할 수 있는 급냉파열특성을 규명하기 위해 실험한 연구로서 가열면온도범위에 따라 유리면에$150^{\circ}C$이상 $250^{\circ}C$이하에서 수막이 형성될 경우 급냉파열은 일어나지 않았으나 일반유리는 $100^{\circ}C$이상 $150^{\circ}C$이하에서 급냉파열이 일어남을 확인하였다. 즉 방화구획벽에 적용가능한 수막형성유리벽의 유리가 강화유리인점을 착안하면 수막의 도포이전에 강화유리면의 온도가 $250^{\circ}C$까지 올라가기 전에는 수막을 유리면에 접촉하여도 유리면의 급냉파열이 일어나짐 않음을 확인할 수 있었다. 이점은 일정한 구획내에서 유리면의 직근에 설치된 감지기에 의해 수막형성시스템의 가동을 할 경우 급내파열형상이 발생하지 않는 온도범위를 설정할 때 중요한 데이터로 활용가능하다. 결과적으로 국부복사열에 의하여 온도범위를 설정할 때 중요한 데이터로 활용가능하다. 결과적으로 국부복사열에 의하여 유리면의 온도가 급냉파열현상을 일으키는 한계온도에 이르기 전에 유리벽체 상부의감지기의 작동이 필수적으로 일어날 수 있음을 증명한다면 수막을 이용한 유리벽체를 일정시간이상의 내화성능이 요구되는 방화구획의 수직부재로 활용하는데 있어서 걸림돌이 되는 급냉파열에 대한 우려를 종식시키는데 이바지할 수 있다.l류 11.56%, acid류 38.87%, hydrocarbon류 2.89%, ester류 0.80%, 총 70.32%가 확인되었다. Alcohol류에서 linalool가 3.78%, acid류에서는 caproic acid류가 14.40%, carbonyl류에서 2-hydroxy-4-methoxyacetophenone이 2.99%, hydrocabon류에서는 aromadendrene가1.59% 그리고 ester류에서는 methyl palmitate가 0.43%으로 가장 많이 함유하고 있었다.0ppm에서 약 25.6%흡수되었고 ferric citrate 100ppm은 24.7%, ferrous sulfate는 19.7%흡수되었다. ILC를 첨가하지 않은 100ppm 철분염 용액은 ferrous sulfate를 제외하고는 흡수도가 감소되었다. 철분 결핍된 쥐에게 gavage 방법에 의하여 철분강화우유를 투여하였을 때 철분 25ppm 시료에서는 ferrous sulfate가 12.5%로 가장 높았고 ferrous lactate는 8.1%, ferric citrate는 6.5% 흡수되었다. 철분 100ppm수준에서는 흡수율이 낮아져 ferrous sulfate는 25ppm 시료보다 절반이하 수준이었다. Ferric citrate는 차이가 거의 없었으며 ferrous lactate는 70%수준이었다. 이상의 결과에서 철분강화우유에 사용하기 적합한 철분염은 ferrous lactate, ferric citrate였는데 특히 ferrous lactate는 제품의 이화학적 품질, 생이용성 측면 모두에서 가장 좋은 것으로 나타났다.다 높았으며, 1회당 평균 8.1$\pm$5.1개의 난포란을 회수하였다.

• Journal of the Korea Institute of Building Construction
• /
• v.16 no.1
• /
• pp.67-76
• /
• 2016

Concrete exposed to severely low temperature below $-20^{\circ}C$ should be provided with proper heat supplying curing to protect the concrete from early frost damage at the time of pouring.meanwhile, so far, effective heat curingmethods of the concrete under severely low temperature are not well established in Korea. For this reason, the objective of this paper is to provide effective heat curingmethod of concrete exposed to severely low temperature to protect early frost damage by varying the combination of heat curingmaterial combinations. Temperature history,maturity development and core strength results are investigated. Fourmock-up specimens simulating slab, wall and column were prepared and heat insulation, heat supplying and both were applied. Test results indicate that the combination of quadruple layer bubble sheet(4BS) and embedding of heating cable has desirable performance for a slab, and heat supplying curing inside heat enclosure and heat generationmat also shows desirable performance for a wall, and for a column, use of EPS heat insulation has proper performance against early frost damage, which reaches $45^{\circ}D{\cdot}D$ and helps the concretemaintain above $0^{\circ}C$ within 3 days. Themethodsmentioned above are believed to be optimum protection from early frost damage of the concrete under $-20^{\circ}C$.