Abstract
This study is about fire resistance performance of wood framed lightweight wall including a middle lintel as a traditional wall form in Korea. The target wall is non-loadbearing system which constructed with $38{\times}89$ mm ($2"{\times}4"$) wood frame and fireproof gypsum board covering, including a middle lintel made of $150{\times}150$ mm section glue-laminated timber. As a test results, all specimens have showed fire resistant performance over 90 minutes and tests were maintained until flame occuring on Specimen-l, 2, 3 at 91 min, 97 min and 98 min respectively. Fire resistance of the heat side gypsum board was 45 minutes and charring rate of middle lintel was equivalant with that of usual timber. The wood stud inside wall system showed relatively quick combution characteristic when exposed to high temperature with no temperature rising delaying time caused by moisture evaporation because of the dehydration preceded during the early period of fire side gypsum board resist to heat.
이 연구는 전통 벽체 형식으로서 중인방을 포함한 목골조 경량벽체의 내화성능에 대한 것이다. 대상으로 한 경량벽체는 $38{\times}89$ mm($2"{\times}4"$) 목재를 골구로 하고 방회석고보드로 마감하는 형식의 비내력구조 이다. 벽체의 중간부에는 $150{\times}150$ mm 단면의 집성목 중인방을 설치하였다. 실험체는 단열재 유무 등에 따라 3가지 타입으로 제작하였다. 내화실험 결과 실험체-1, 2, 3 모두 90분 이상의 내화성능을 확보하는 것으로 나타났고, 각각 92분, 98분, 99분만에 중인방의 측면과 하부에서 불꽃이 발생하여 실험을 중단하였다. 가열면의 방화석고보드($12.5mm{\times}2$겹)는 약 45분간 내화성능을 유지하는 것으로 나타났고, 중인방의 연소는 일반적인 목재의 탄화속도와 유사한 거동을 보였다 벽체 내부의 목재스터드는 방화석고보드의 기여로 연소가 지연되는 동안 탈수가 일어나 고온에 노출된 이후에는 수분에 의한 온도상승 지연효과가 일어나지 않고 비교적 빠른 연소가 진행되는 것으로 나타났다.