• Transactions of the Korean Society of Mechanical Engineers
• /
• v.15 no.5
• /
• pp.1462-1471
• /
• 1991

본 연구에서는 미소 결함주위에서 발생, 전파하는 균열들에 미치는 초기 결함 깊이와 상호 간섭 영향을 검토하기 위하여 기존 재료가 갖고 있는 결함이나 비금속 개 재물로 대신할 수 있다고 생각되는 미소 원공의 크기를 변화시킨 모델에 대해 유한 요 소법을 이용하여 3차원적으로 응력을 해석하였다. 실제 사용하고 있는 부재에 결함 들이 존재할 경우 응력장의 간섭으로 피로 균열 진전이 가속화됨으로 미소 원공 주위 의 응력 분포 및 미소 원공사이의 응력장의 간섭과 미소 원공에서 발생, 전파하는 표 면 균열의 응력 확대 계수에 미치는 영향에 대하여 비교검토 하였다.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2003.10a
• /
• pp.222-222
• /
• 2003

• The Journal of Engineering Geology
• /
• v.16 no.2 s.48
• /
• pp.179-187
• /
• 2006

Two specimens of mortar containing artificial slit and Geochang granite containing the straight notch were selected to be used in this research. Source mechanism of micro-crack by radiation pattern based on dislocation the-ory was estimated by the first motion of longitudinal wave and spatial distribution between the location of transducers for monitoring acoustic emission and source coordinates determined by the application of the least square method. Result of analysis showed that the orientation of dislocation surfaces due to shear dislocation and tensile dislocation squares considerably with crack direction visually observed. The ultimate goal of this study is to provide fundamental information for source mechanism of micro-crack within materials.

• Tunnel and Underground Space
• /
• v.9 no.4
• /
• pp.364-372
• /
• 1999

In this paper, mechanical characteristics of micro-defects in granitic rock was studied. Crack spacing and length were investigated by scanline survey in specimen of granite. To estimate the direction and distribution of potential microcrack in granite, thin sections were made for three direction of Rift, Grain and Hardway axis of the rock specimen. The density and length of microcrack were investigated quantitatively. Three directions of microcracks are comparatively perpendicular. Crack density varies as direction differs, but crack length doesn't show influence of direction.

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.16 no.1
• /
• pp.53-62
• /
• 1992

Material can be degraded by using it for a long service under the high temperature and pressure circumstances, Therefore, material degradation can affect the strength of mechanical structures. At present, the life prediction of the degraded structures is considered as an important technical problem. In this paper, the degraded 21/4Cr-lMo steel is the material used for about 10 years around 400.deg. C in an oil refinery plant. The recovered one was prepared out of the above degraded steel by heat treatment for one hour at 650.deg. C. The degradation effect was investigated through the tension test, Hardness test and Charpy impact test. On the smooth surface material, the fatigue crack initiation, growth and coalescence stages of the distributed small cracks were investigated with photographs, and the crack length and density were measured. The measuring results were analyzed by quantative and statistical methods.

• Bulletin of the Society of Naval Architects of Korea
• /
• v.27 no.3
• /
• pp.100-106
• /
• 1990

Microcracking of type 304 stainless steel at $593^{\circ}C(1,100^{\circ}F)$ has been studied, in particular, initiation, growth, and coalescence of fatigue and creep microcracks on smooth specimens and small notch specimens via surface replicas and photomicrographs. Quantitative information, such as, initiation period, growth, and coalescence behavior, statistical distributions of crack length, density of cracks, distribution patterns and crack growth properties, were obtained. From this study, the fracture process, fatigue life, and creep life prediction characterized by the growth of surface microcracks have been analysed by a new approach unifying the conventional approaches based on the final fracture of materials with the fracture mechanics approach. Knowledge of these parameters is critical for the application of fracture mechanics to fatigue and creep life assessment, and the damage evaluation of structures at elevated temperature.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.24 no.5 s.176
• /
• pp.1288-1296
• /
• 2000

In this study, fatigue crack behavior between arbitrarily located defects was investigated by experiment. Especially, stress interaction between micro hole defects and fatigue cracking, and fatigue crack initiation life following the variation of location of micro hole defects were considered. In addition, crack initiation position by micro hole stress interaction and the relationship between stress concentration factor and fatigue initiation life are studied in detail.

• Journal of the Korean Society for Precision Engineering
• /
• v.10 no.3
• /
• pp.97-106
• /
• 1993

This is the study on fracture life under the interaction of creep and fatigue. It is difficult to explain the interaction of the creep and fatigue with indication of frequency but the dependency of the time should be considered. The formulation of material varieties causing by interaction of creep and fatigue is required in the accumulative damage method. The strain range partition method requires some of modification corresponding to the changes in temperature and load. All of other method also comprehended with above mentioned problems. Generally, in this field, the variety of stress-strain and suitable parameter is required and connective study between the macro and micro results seems to be insufficient. The linear damage rule is acquiring the support generally but it requires modification in the hgigh temperature instruments. The variety of stress effecting on crack and variety of stress on the metallurgical side are considered to be problems in the future days.

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.12 no.6
• /
• pp.1320-1326
• /
• 1988

This paper deals with the behavior of surface crack growth and the characteristics of surface micro-crack distribution under creep and creep-fatigue with 1 min. and 10 min. of load holding times at 593.deg.C, in air. The test specimen is a plate type with a small artificial defect of type 304 the small defect has been carried out by the surface replica method and optical microphotography. The experimental results have been interpreted from the view-point of fracture mechanics. It can be concluded that the longer the hold time the longer the total life time. Most of surface micro-cracks initiate at grain boundaries before the specimen reaches 20% of its total life time, a few of them lead to fracture by coalescence with the main crack.

• Journal of the Korean Society for Precision Engineering
• /
• v.18 no.1
• /
• pp.201-212
• /
• 2001

If defects are located far apart, fatigue cracks are independently initiated from them and gradually approach other cracks so that the fatigue life becomes influenced by the crack growth behavior of those interacting cracks. In this study, the effect of the stress interaction between defects on the fatigue crack propagation behavior is investigated experimentally and these results are verified by finite element method. In addition, fatigue crack propagation behaviors under micro hole interaction field are studied.