• Journal of the Korea Concrete Institute
• /
• v.27 no.2
• /
• pp.127-136
• /
• 2015

To evaluate the effects of limestone powder and silica fume on the properties of high-strength high-volume ground granulated blast-furnace slag (GGBFS) blended cement concrete, this study investigated the rheology, strength development, hydration and pozzolanic reaction characteristics, porosity and pore size distribution of high-strength mortars with the water-to-binder ratio of 20, 50 to 80% GGBFS, up to 20% limestone powder, and up to 10% silica fume. According to test results, compared with the Portland cement mixture, the high-volume GGBFS mixture had much higher flow due to the low surface friction of GGBFS particles and higher strength in the early age due to the accelerated cement hydration by increase of free water; however, because of too low water-to-binder ratio and cement content, and lack of calcium hydroxide content, the pozzolanic reactio cannot be activated and the long-term strength development was limited. Limestone powder did not affect the flowability, and also accelerate the early cement hydration. However, because its effect on the acceleration of cement hydration is not greater than that of GGBFS, and it does not have hydraulic reactivity unlikely to GGBFS, compressive strength was reduced proportional to the replacement ratio of limestone powder. Also, silica fume and very fine GGBFS lowered flow and strength by absorbing more free water required for cement hydration. Capillary porosities of GGBFS blended mortars were smaller than that of OPC mortar, but the effect of limestone powder on porosity was not noticeable, and silica fume increased porosity due to low degree of hydration. Nevertheless, it is confirmed that the addition of GGBFS and silica fume increases fine pores.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.13 no.3 s.55
• /
• pp.119-126
• /
• 2009

This study investigated the fire resistance of RC columns applying Fiber addition method, Fire board attaching method, and Fire proof sparying method. The results were summarized as following. The test showed that increase of fiber content, as expected, decreased the fluidity of fresh concrete, but for the types of fiber, the specimens containing nylon(NY) was favorable. The incline of fiber content also affected on the air content of concrete, which the specimens adding polypropylene(PP) fiber was the lowest, followed by a less decrease in polyvinyl alchhol(PVA) and then NY respectively. For the compressive strength at 28days, it was over 50MPa and showed slight increasing tendency by rising fiber contents. After the fire test completed, control concrete exhibited the severe demage, while the specimens containing more than 0.05vol.% of PP and NY was able to protect from spalling. In the case of splay, the partly spalling occurred at the all finishing material, however the RC columns were protected from spalling. For the methods attached with boards, all RC columns were protected except the dry attaching method. The reduced weight ratio was favorable because it was below 8 % except for plain concrete.

• Journal of the Korea Concrete Institute
• /
• v.15 no.5
• /
• pp.670-678
• /
• 2003

Recently, since industrial waste and life waste leaped into a pollution source, the building material used now a days is striking the limit. The purpose of this paper is to investigate an application of recycled coal ash using non-sintering method in the construction field. Accordingly, compressive strength, elastic modulus and drying shrinkage were experimentally studied for hardened coal ash using the non-sintering method. Also, Lineweaver and Burk method were applied to the regression analysis of drying shrinkage for the proposal equation. Elastic modulus, compressive strength of material become the basis properties of structural design. And these properties by age for hardened coal ash are important because of change by pozzolan reaction. This hardened coal ash is weak for tensile stress like that of concrete. And drying shrinkage is very important factor to make huge tensile force in early age. In the results, although some differences were shown when comparing coal ash with mortar or concrete, the application as a building material turned out to be possible if further researches were carried out. And the shrinkage characteristic of hardened coal-ash reveals to be similar to that of moderate heat cement.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.30 no.4
• /
• pp.156-161
• /
• 2020

Recently, as there has been growing demand for aesthetic quality in structural materials, the development of excellent color cement concrete having good coloration properties has become a requirement. This study is designed to analyze the basic physical properties of mortar and the properties of keeping the coloration under an ultraviolet ray accelerated weathering test environment according to changes in the mixing ratio between carbon black and iron oxide used as colorants. The test results show that the use of carbon black and iron oxide reduces the initial flow by 6.3~17.2 % and the air content by 3.5~31.5 % but increases the unit volume weight by 3.4~5.5 %, compared to ordinary Portland cement (OPC). In addition, the study shows that the addition of iron oxide increases the self drying shrinkage. So, caution needs to be taken on the workability of the concrete. The brightness value L^⁎ represented by black showed the most excellent black colour when carbon black 3 % and iron oxide 5 % are added. According to UV accelerated weatherproof test, the brightness value L^⁎ was found to increase in all experiment specimens by 4.28~11.97 %, and the color change by UV was found to be higher for the case where carbon black colorant was not used. Therefore, in terms of color revelation characteristics, the case using carbon black 3 % and iron oxide 5 % was found to show the best black color.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.5 no.4
• /
• pp.129-136
• /
• 2010

This study is to investigate experimentally the engineering characteristics of cement mortar according to the replacement method and contents of recycled aggregate powder (RP) by collecting the recycled aggregate powder with the maximum size of below 0.08 mm and 0.15 mm. then, the results of the study can be summarized as follows. The flow of flesh mortar represented a trend in decreasing while the recycled aggregate powder was substituted as it is compared with that of plain. In addition, in case of correlation between tests, it appeared that the correlation between flow and ring flow is big. In the case of the characteristics of hardened mortar, the strength showed more improvements as the RP was substituted to aggregate than the case, which is substituted to aggregate. In addition, it was verified that the results in which the RP was substituted to aggregate by 5% represented similar values to that of the plain according to the passage of age.

• Journal of the Korea Concrete Institute
• /
• v.17 no.1 s.85
• /
• pp.69-76
• /
• 2005

In this study, the high qualify recycled fine aggregate manufacturing system by the drying specific gravity separation method was evaluated. For the evaluation of the performance of the recycled aggregate, the engineering properties and durability of recycled aggregate has been tested. From the test results, the quality of recycled fing aggregates was improved by high quality recycled fine aggregate manufacturing system and satisfied with the quality standards of KS and JASS 5. Also, compressive and tensile strengths of recycled concrete show no critical difference caused by recycled fine aggregate replacement ratio. However, durability such as carbonation depth chloride ion penetration depth and drying shrinkage shows more deterioration than the concrete without recycled fine aggregate

• Magazine of the Korea Concrete Institute
• /
• v.6 no.5
• /
• pp.131-139
• /
• 1994

The min aim of thls study was to evaluate the effect of particle slze of the fly ash as a cement additive. Experimental work was carried out with three different sizes of fly ash. 18.58, 8.95 and 4.02{$mu}m$ in average radius. Namely, the effect of particle size variation of fly ash on the physical properties of cement paste was investigated. The jluidity was decreased with increasing the addition of fly ash to cement paste regardless of the particle size variation. The decrement of the fluidity of the pulverized fly ash was higher than that of the spherical fly ash. On the other hand, the pozzolan reactivity increased with lowering particle size. In the case of specimens with 5% up to 10% addition of fly ash having a particle size of 4.02{$mu}m$. the compressive strength was increased as compared with the plain specimens before curing for 28 days and showed higher value above 800kg /$cm^2$ when cured for 60 days.This increased compressive strength was ascribed to both the closer packlng of fine particles and the pozzolan reactivity of fly ash. These results were comfirmed by measuring both the porosity of the specimens and Ca(OH ), contents remained in specimens. This work showed that could be effectively ut~lized as a blending material without any de crease in the strength of early hydration stage if we can control the particle size of fly ashes by sizing or pulverizing.

• Korean Journal of Agricultural Science
• /
• v.5 no.2
• /
• pp.120-126
• /
• 1978

Comparative studies have been carried out to elucidate effects of 3 types of Japanese hardening agents and cement on the compressive and tensil strength of solidified briquette ashes with different ages, when various mixing ratio were applied. 1. The hardening agent, especially type C, were appeared to be better than the cement to obtain higher compressive and tensil strength of the products. 2. The compressive strength when mixing ratio of 1 : 3 applied were : $177.6kg/cm^2$. for type C; $168.6kg/cm^2$ for type A; and $155.94kg/cm^2$ for type B. 3. The tensil strength when mixing ratio of 1 : 3 applied were: $24.63kg/cm^2$ for type C ; $23.14kg/cm^2$ for type B; and $22.45kg/cm^2$ for type A. 4. Although the solidified briquette ashes were found to be not as strong as cement mortar, it is (considered that they could be used instead of low-strength concrete, and that they could contribute to reduce the amount of terminal city-wastes then to reduce pollutions caused by the wastes.

• Magazine of the Korean Society of Agricultural Engineers
• /
• v.27 no.1
• /
• pp.46-61
• /
• 1985

This study was performed to obtain the basic data which can be applied to the use of foaming mortars. The data was based on the properties of foaming mortars depending upon various mixing ratios and addings to compare those of cement mortar. The foaming agents which was used at this experiment were pre-foamed type and mix-foaming type which is being used as mortar structures. The foaming mortar, mixing ratios of cement to fine aggregate were 1:1, 1: 2, 1 : 3 and 1 : 4. The addings of foaming agents were 0.0%, 0.5%, 1.0%, 1.5%, 2.0%, 2.5% and 3.0% of cement weight. The results obtained were summarized as follows; 1. At the mixing ratio of 1 : 1, the lowest water-cement ratios were showed by foaming mortars, respectively. But it gradually was increased in poorer mixing ratio and decreased in more addition of foaming agent. The water-cement ratios were decreased up to 1. 8~22. 0% by G, 2. 2~24. 1 % by U and 0. 7~53. 1% by J foaming mortar than cement mortar. 2, At the mixing ratio of 1 : 1, the highest bulk densities were showed by foaming mortars, respectively. But, it gradually was decreased in poorer mixing ratio and more addition of foaming agent. The bulk densities were decreased up to 1. 4~20. 7% by G, 2. 3~23. 7% by U and 26. 5~56. 5% by J foaming mortar than cement mortar. Therefore, foaming mortar could be utilized to the constructions which need low strengths. 3. At the mixing ratio of 1:1, the lowest absorption rates were showed by foaming mortars, respectively. But, it gradually was increased in poorer mixing ratio and more addition of foaming agent. Specially, according to the absorption rate when immersed in 72 hours, the absorption rates were showed up to 1. 01~1. 24 times by G, 1. 03~1. 58 times by U and 1. 10~5. 91 times by J foaming mortar than cement mortar. It was significantly higher at the early stage of immersed time than cement mortar. 4. At the mixing ratio of 1:1, the lowest air contents were showed by foaming mortars, respectively. But, it gradually was increased in poorer mixing ratio and more addition of foaming agent. Air contents were contented up to 4. 0~17. 2 times by G, 5. 2~23. 2 times by U and 23. 8~74. 5 times by J foaming mortar than cement mortar. 5. At the mixing ratio of 1 : 1, the lowest decreasing rates of strengths were showed by foaming mortars, respectively. But, it gradually was increased in poorer mixing ratio and more addition of foaming agent. Specially, the strengths of 28 days were decreased 0. 4~2. 2% than those of 7 days by foaming mortar, respectively. Also, the correlations between compressive and tensile strength, compressive and ending strength, tensile and bending strength were highly significant as a straight line shaped, respectively. 6. The correlations between absorption rate, air content, compressive strength and bulk density, absorption rate, compressive strength and air content were highly significant, respectively. The multiple regression equations of water-cement ratio, bulk density, absorption ate, air content, compressive strength, tensile strength and bending strength were computed depending on a function of mixing ratio and addition of foaming agent. It was highly significant, respectively. 7. At the mixing ratio of 1 : 1, the highest strengths were showed by cement mortar and foaming mortars, by chemical reagents. But, it gradually was decreased in poorer mixing ratio. The decreasing rates of strengths were in order of H $_2$S0 $_4$, HNO$_3$ and HCI, J,U,G foaming mortar and cement mortar. Specially, at the each mixing ratio, each chemical reagent and 3.0% of foaming agent, J foaming mortar was collapsed obviously. Therefore, for the structures requiring acid resistence, adding of foaming agent should be lower than 3.0%.

• Magazine of the Korean Society of Agricultural Engineers
• /
• v.26 no.1
• /
• pp.52-72
• /
• 1984

This study was performed to obtain the basic data which can be applied to the use of epoxy resin mortars. The data was based on the properties of epoxy resin mortars depending upon various mixing ratios to compare those of cement mortar. The resin which was used at this experiment was Epi-Bis type epoxy resin which is extensively being used as concrete structures. In the case of epoxy resin mortar, mixing ratios of resin to fine aggregate were 1: 2, 1: 4, 1: 6, 1: 8, 1:10, 1 :12 and 1:14, but the ratio of cement to fine aggregate in cement mortar was 1 : 2.5. The results obtained are summarized as follows; 1.When the mixing ratio was 1: 6, the highest density was 2.01 g/cm$^3$, being lower than 2.13 g/cm$^3$ of that of cement mortar. 2.According to the water absorption and water permeability test, the watertightness was shown very high at the mixing ratios of 1: 2, 1: 4 and 1: 6. But then the mixing ratio was less than 1 : 6, the watertightness considerably decreased. By this result, it was regarded that optimum mixing ratio of epoxy resin mortar for watertight structures should be richer mixing ratio than 1: 6. 3.The hardening shrinkage was large as the mixing ratio became leaner, but the values were remarkably small as compared with cement mortar. And the influence of dryness and moisture was exerted little at richer mixing ratio than 1: 6, but its effect was obvious at the lean mixing ratio, 1: 8, 1:10,1:12 and 1:14. It was confirmed that the optimum mixing ratio for concrete structures which would be influenced by the repeated dryness and moisture should be rich mixing ratio higher than 1: 6. 4.The compressive, bending and splitting tensile strenghs were observed very high, even the value at the mixing ratio of 1:14 was higher than that of cement mortar. It showed that epoxy resin mortar especially was to have high strength in bending and splitting tensile strength. Also, the initial strength within 24 hours gave rise to high value. Thus it was clear that epoxy resin was rapid hardening material. The multiple regression equations of strength were computed depending on a function of mixing ratios and curing times. 5.The elastic moduli derived from the compressive stress-strain curve were slightly smaller than the value of cement mortar, and the toughness of epoxy resin mortar was larger than that of cement mortar. 6.The impact resistance was strong compared with cement mortar at all mixing ratios. Especially, bending impact strength by the square pillar specimens was higher than the impact resistance of flat specimens or cylinderic specimens. 7.The Brinell hardness was relatively larger than that of cement mortar, but it gradually decreased with the decline of mixing ratio, and Brinell hardness at mixing ratio of 1 :14 was much the same as cement mortar. 8.The abrasion rate of epoxy resin mortar at all mixing ratio, when Losangeles abation testing machine revolved 500 times, was very low. Even mixing ratio of 1 :14 was no more than 31.41%, which was less than critical abrasion rate 40% of coarse aggregate for cement concrete. Consequently, the abrasion rate of epoxy resin mortar was superior to cement mortar, and the relation between abrasion rate and Brinell hardness was highly significant as exponential curve. 9.The highest bond strength of epoxy resin mortar was 12.9 kg/cm$^2$ at the mixing ratio of 1:2. The failure of bonded flat steel specimens occurred on the part of epoxy resin mortar at the mixing ratio of 1: 2 and 1: 4, and that of bonded cement concrete specimens was fond on the part of combained concrete at the mixing ratio of 1 : 2 ,1: 4 and 1: 6. It was confirmed that the optimum mixing ratio for bonding of steel plate, and of cement concrete should be rich mixing ratio above 1 : 4 and 1 : 6 respectively. 10.The variations of color tone by heating began to take place at about 60˚C, and the ultimate change occurred at 120˚C. The compressive, bending and splitting tensile strengths increased with rising temperature up to 80˚ C, but these rapidly decreased when temperature was above 800 C. Accordingly, it was evident that the resistance temperature of epoxy resin mortar was about 80˚C which was generally considered lower than that of the other concrete materials. But it is likely that there is no problem in epoxy resin mortar when used for unnecessary materials of high temperature resistance. The multiple regression equations of strength were computed depending on a function of mixing ratios and heating temperatures. 11.The susceptibility to chemical attack of cement mortar was easily affected by inorganic and organic acid. and that of epoxy resin mortar with mixing ratio of 1: 4 was of great resistance. On the other hand, when mixing ratio was lower than 1 : 8 epoxy resin mortar had very poor resistance, especially being poor resistant to organicacid. Therefore, for the structures requiring chemical resistance optimum mixing of epoxy resin mortar should be rich mixing ratio higher than 1: 4.