• Journal of the Korea Concrete Institute
• /
• v.20 no.2
• /
• pp.131-138
• /
• 2008

Humidity and strain were estimated for understanding the relation between humidity change by self-desiccation and shrinkage in high-performance concrete with low water binder ratio. Internal humidity change and shrinkage strain were about 10%, 4% and $320\times10^{-6}$, $120\times10^{-6}$ respectively on concrete with water binder ratio 0.3, 0.4 and from the results, humidity change and shrinkage represented the strong linear relation regardless of mixture. For specifying the relation on internal humidity change and autogenous shrinkage strain, shrinkage model was established which is driven by capillary pressure in pore water and surface energy in hydrates on the assumption of a single network and extended meniscus in pore system of concrete. This model and experimental results had a similar tendency so it would be concluded that the internal humidity change by self-desiccation in HPC originated in small pores less than 20 nm, therefore controlling plan on autogenous shrinkage might be focused on surface tension of water and degree of saturation in small pore.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.17 no.5
• /
• pp.612-618
• /
• 2016

The aim of this study is to investigate the effects of stray light originating from the blue-light blocking lens on the quality of the image. After designing the ideal spectacle lens, anti-reflection spectacle lens without internal reflection, anti-reflection spectacle lens with internal reflection, and blue-light blocking lens with internal reflection, the light intensity distribution and stray light distribution were derived. The designed spectacle lenses are meniscus lenses with a refractive power of 0.00 D, refractive index of 1.56, and a radius of 155.15 mm. The peaks of reflectance of the 4 types of blue-light blocking lenses are in the range between 430 nm and 440 nm, and their reflectances are 5%, 10%, 15%, and 20%, respectively. According to the analysis results, as the reflectance of the blue-light blocking lens increases, the light intensity in the center of the lens decreases and the intensity of the stray light in the center-periphery and periphery of the lens increases. This trend appeared to intensify with increasing reflectance of the blue-light blocking lenses. Because the increase in the reflectance of the blue-light blocking lens degrades the quality of the image by increasing the intensity of the stray light in the center-periphery and periphery of the lens, its reflectance needs to be adjusted by varying the blue-light blocking ratio and the luminous transmittance, in order to diminish the level of visual discomfort.

• Journal of Adhesion and Interface
• /
• v.20 no.1
• /
• pp.1-8
• /
• 2019

Fabrication of monolayer is important method for enhancing physical and chemical characteristics such as light shielding and antireflection while maintaining thin film properties. In previous studies, monolayers were fabricated by various methods on small substrates, but processes were complicated and difficult to form monolayers with large area. We used rod coating equipment with a small amount of coating liquid to form a HCP (hexagonal closed packing) coating of PMMA beads on PET(poly(ethylene terephthalate)) substrate with $20cm{\times}20cm$ size. We observed that changes in morphologies of monolayers by using the solvents with different boiling points and vapor pressures, by adapting surfactants on particles and by applying plasma treatment on substrates. The coverage was increased by 20% by optimizing the coating conditions including meniscus of beads, control of the attraction - repulsion forces and surface energy. This result can potentially be applied to optical films and sensors because it is possible to make a uniform and large-scale monolayer in a simple and rapid manner when it is compared to the methods in previous studies.

• Journal of Korea Foundry Society
• /
• v.41 no.3
• /
• pp.241-251
• /
• 2021

7000-series aluminum alloys are noted for their superior strength compared with other Al alloys, and their billets are generally fabricated by direct-chill (DC) casting. Surface defects in a DC-cast aluminum billet are mainly related to exudation and the meniscus freezing phenomenon, which are influenced by alloy compositions, casting speed, and casting temperature. 7000-series aluminum alloys have a wide freezing range during solidification, which makes it easy for casting defects to occur. In this study, we investigated surface defect evolution in casting billets of Al-8Zn-2Mg-2Cu alloy fabricated by a DC casting process. The billets showed "wavy" or "dotted" surfaces. The wavy surface was formed by meniscus freezing at a lower casting speed (200 mm/min) and temperature (655 ℃). In the wavy surface, refined dendritic cells were observed in a concave region due to the constitutional supercooling caused by meniscus freezing. Meanwhile, at a higher casting temperature (675 ℃), the dotted surface was formed by pore formation. In the dotted surfaces in the billet formed at a high casting speed (230 mm/min), an exudation layer was formed by the high metallostatic head pressure. The dotted region and the smooth region had a refined dendritic morphology and a columnar morphology at the exudation layer, respectively. This is attributed to the formation of gas pores in the dotted region.