• Journal of Korean Society of Steel Construction
• /
• v.9 no.4 s.33
• /
• pp.515-521
• /
• 1997

The effects of heat treatment and fiber orientation on tensile strength and fatigue behavior were studied in a continuously reinforced. magnesium-based composite Following an earlier TEM investigation, specimens were thermally aged to modified the interfacial zone between the alumina fibers and the magnesium alloy matrix. From the tensile experimental results, the ultimate tensile strength of the aged specimens were lower than that of the as-fabricated due to weak fiber-matrix interfacial strength with chemical reaction during the thermal processing. The fatigue crack growth experiments were conducted with specimens having the fiber orientation normal to the crack growth direction (longitudinal) and also specimens with the fibers oriented parallel to the crack growth direction(transverse). A comparison of the fatigue crack growth behavior indicates that aged longitudinal specimens are more resistant to fatigue crack growth the as-fabricated longitudinal specimens. Conversely, as-fabricated transverse specimens are more resistant to fatigue crack growth than aged transverse specimens.

• 기계와재료
• /
• v.16 no.2 s.60
• /
• pp.81-94
• /
• 2004

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2012.11a
• /
• pp.14-14
• /
• 2012

상용 마그네슘합금에 Ca+Y를 복합 첨가하여 부식특성의 변화를 평가하였다. Ca+Y를 복합 첨가한 경우 표면에 형성되는 피막의 안정성이 증가하여 내식성이 현저하게 향상되었다. AZx1-aCa-0.2Y 합금의 부식양상은 제2상과 기지간의 미소갈바닉 부식에 의해 국부부식 양상을 나타내었다.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2018.06a
• /
• pp.26.2-26.2
• /
• 2018

최근 연구결과에 따르면, 상용 AZ91D 마그네슘합금에 Ca과 Y을 복합 첨가함으로써 마그네슘합금의 문제점인 발화저항성을 크게 향상시키는 동시에 충분한 기계적 특성을 확보할 수 있어 마그네슘합금의 적용분야 확대에 대한 기대가 높아지고 있다. 한편 Ca과 Y을 복합 첨가된 마그네슘합금은 기존의 상용합금에 비해서 매우 우수한 내식성을 나타내는 것으로 알려져 마그네슘합금의 또 하나의 장애물로 여겨졌던 부식 문제 또한 해결할 수 있을 것으로 기대되고 있다. 선행연구결과, 이러한 내식성의 향상은 Ca과 Y의 첨가에 따라 이차상의 조성이 변하게 되면서 상과 기지간의 부식 전위의 차이가 감소하고, 이로 인해 미세 갈바닉 부식 발생이 감소하게 되었기 때문으로 판단된다. 본 연구에서는 이러한 Ca 과 Y의 첨가가 이차상의 부식 전위 뿐 만 아니라 AZ91D 합금의 표면 특성을 어떻게 변화시키고 이러한 특성의 변화가 내식성에 어떠한 영향을 미치는 지에 대하여 평가하였다. 다양한 전기화학적 분석을 통해 각 합금의 표면 특성과 내식성을 평가하였고, 표면 산화층 분석 및 TEM 분석 등을 통해 표면 피막의 구조와 조성을 분석하여 차이를 비교하였다.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2016.11a
• /
• pp.123.1-123.1
• /
• 2016

마그네슘 및 마그네슘 합금은 차세대 경량 구조 재료로서 많은 각광을 받고 있지만, 상대적으로 높은 반응성과 낮은 부식저항성으로 인해 사용에 제한이 있어왔다. 최근 연구결과에 따르면, 상용으로 널리 쓰이는 AZ91 마그네슘합금에 Ca과 Y을 복합 첨가하였을 경우 마그네슘합금의 발화저항성을 크게 향상시키는 것으로 알려져 있어 마그네슘합금의 적용분야를 확대할 수 있을 것으로 많은 기대를 받고 있다. 그러나 이러한 합금이 실제적으로 적용되기 위해서는 반드시 내식성에 대한 평가와 연구가 수반되어야 하며, 이를 통해 부식거동에 대한 메커니즘을 규명함으로써 고내식 합금 개발을 위한 연구로 이어질 수 있도록 해야 한다. 따라서 본 연구에서는 기존의 AZ91D 합금과 Ca, Y이 복합 첨가된 modified AZ91D 합금 다이캐스트 주조재에 대하여 내식성을 평가 및 비교하고 부식 메커니즘을 규명하기 위한 미세조직 분석 및 부식거동 평가를 실시하였다. 본 연구결과에 따르면, AZ91D 합금 주조재에 Ca과 Y을 복합첨가한 합금은 발화저항성 뿐만 아니라 내식성도 크게 향상되는 것으로 나타났다. 이러한 내식성의 향상은 Ca과 Y의 첨가에 따른 Fe와 같은 불순물의 영향 감소 및 Ca과 Y이 포함된 이차상의 형성으로 인한 상과 기지간의 부식 전위의 차이 감소로 인한 미세 갈바닉 부식 발생의 감소 효과에 기인한 것으로 판단된다.

• Composites Research
• /
• v.33 no.5
• /
• pp.256-261
• /
• 2020

In this study, the ignition temperature of the Al-Ti-C reaction system, the microstructure and the mechanical properties of the TiC/Mg composite which produced by the self-propagating high-temperature synthesis (SHS) followed by stir casting process were investigated. Mg based composite with uniformly dispersed 0, 10, 20, and 30 vol.% TiC were fabricated, and higher volume fraction of TiC reinforced composite showed superior compressive strength and wear resistance as compared with Mg matrix. It is attributed to the less contamination, defects, impurities in TiC/Mg composite by the in-situ SHS yield effective load transfer from the matrix to the reinforcement.

• Composites Research
• /
• v.33 no.5
• /
• pp.247-250
• /
• 2020

In this study, the possibility of manufacturing a magnesium (Mg) composites reinforced with continuous silicon carbide (SiC) fibers was examined using a liquid pressing process. We fabricated uniformly dispersed SiC fiberAZ91 composites using a liquid phase pressing process. Furthermore, the precipitates were controlled through heat treatment. As a continuous Mg₂Si phase was formed at the interface between the SiC fiber and the AZ91 matrix alloy, the interfacial bonding strength was improved. The tensile strength at room temperature of the prepared composite was 479 MPa, showing excellent mechanical properties.

• Composites Research
• /
• v.25 no.4
• /
• pp.93-97
• /
• 2012

Carbon nano fibers (CNFs) reinforced magnesium alloy (AZ91) matrix composites have been fabricated by liquid pressing process. In order to improve the dispersibility of CNFs and the wettability with magnesium alloy melt, CNFs were mixed with submicron sized SiC particles ($SiC_p$). Also, the mixture of CNFs and $SiC_p$ were coated with Ni by electroless plating. In liquid pressing process, AZ91 melts have been pressed hydrostatically and infiltrated into three reinforcement preforms of only CNFs, the mixture of CNFs and $SiC_p$ (CNF+$SiC_p$), and Ni coated CNFs and $SiC_p$ ((CNF+$SiC_p$)/Ni). Some CNFs agglomerates were observed in only CNFs reinforced composite. In cases of the composites reinforce with CNF+$SiC_p$ and (CNF+$SiC_p$)/Ni, CNFs were dispersed homogeneously in the matrix, which resulted in the improvement of mechanical properties. The compressive strengths of CNF+$SiC_p$ and (CNF+$SiC_p$)/Ni reinforced composites were 38% and 28% higher than that of only CNFs composite.